CN102786069B - 无尘级单水氢氧化锂的制备方法 - Google Patents
无尘级单水氢氧化锂的制备方法 Download PDFInfo
- Publication number
- CN102786069B CN102786069B CN201210329808.5A CN201210329808A CN102786069B CN 102786069 B CN102786069 B CN 102786069B CN 201210329808 A CN201210329808 A CN 201210329808A CN 102786069 B CN102786069 B CN 102786069B
- Authority
- CN
- China
- Prior art keywords
- lioh
- preparation
- solution
- liquid
- dustless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
主含量% | Fe% | Na+K% | Ca% | Cl-% | SO4 2-% | CO2% | 酸不溶物 | 水不溶物 | |
实施例1 | 56.7 | 0.0012 | 0.008 | 0.006 | 0.0013 | 0.015 | 0.23 | 0.002 | 0.006 |
实施例2 | 56.5 | 0.0010 | 0.012 | 0.005 | 0.0010 | 0.016 | 0.26 | 0.002 | 0.008 |
实施例3 | 56.6 | 0.0015 | 0.007 | 0.005 | 0.0014 | 0.012 | 0.21 | 0.003 | 0.008 |
实施例4 | 56.8 | 0.0013 | 0.009 | 0.007 | 0.0015 | 0.014 | 0.22 | 0.004 | 0.005 |
实施例5 | 56.7 | 0.0011 | 0.010 | 0.006 | 0.0012 | 0.012 | 0.24 | 0.003 | 0.004 |
实施例6 | 56.9 | 0.0012 | 0.008 | 0.008 | 0.0013 | 0.011 | 0.20 | 0.002 | 0.005 |
实施例7 | 56.6 | 0.0010 | 0.007 | 0.008 | 0.0011 | 0.013 | 0.22 | 0.003 | 0.006 |
实施例8 | 57.0 | 0.0016 | 0.011 | 0.005 | 0.0014 | 0.015 | 0.25 | 0.004 | 0.006 |
实施例9 | 56.7 | 0.0014 | 0.010 | 0.004 | 0.0015 | 0.013 | 0.24 | 0.003 | 0.006 |
实施例10 | 56.5 | 0.0013 | 0.007 | 0.005 | 0.0013 | 0.011 | 0.26 | 0.004 | 0.005 |
实施例11 | 56.5 | 0.0014 | 0.009 | 0.006 | 0.0010 | 0.013 | 0.25 | 0.002 | 0.007 |
实施例12 | 56.8 | 0.0015 | 0.011 | 0.006 | 0.0010 | 0.014 | 0.27 | 0.004 | 0.006 |
实施例13 | 56.7 | 0.0012 | 0.010 | 0.007 | 0.0013 | 0.012 | 0.22 | 0.002 | 0.005 |
实施例14 | 57.0 | 0.0013 | 0.012 | 0.005 | 0.0012 | 0.015 | 0.25 | 0.003 | 0.007 |
实施例15 | 56.8 | 0.0010 | 0.007 | 0.008 | 0.0015 | 0.010 | 0.23 | 0.003 | 0.004 |
实施例16 | 56.5 | 0.0010 | 0.008 | 0.006 | 0.0010 | 0.012 | 0.26 | 0.004 | 0.005 |
实施例17 | 56.6 | 0.0014 | 0.010 | 0.005 | 0.0012 | 0.014 | 0.25 | 0.002 | 0.006 |
实施例18 | 56.6 | 0.0011 | 0.009 | 0.007 | 0.0011 | 0.010 | 0.21 | 0.004 | 0.006 |
实施例19 | 56.9 | 0.0013 | 0.012 | 0.006 | 0.0012 | 0.012 | 0.26 | 0.002 | 0.005 |
实施例20 | 57.0 | 0.0015 | 0.011 | 0.005 | 0.0013 | 0.013 | 0.23 | 0.003 | 0.004 |
实施例21 | 56.7 | 0.0014 | 0.009 | 0.007 | 0.0015 | 0.015 | 0.23 | 0.002 | 0.004 |
实施例22 | 56.8 | 0.0010 | 0.007 | 0.004 | 0.0013 | 0.010 | 0.21 | 0.002 | 0.006 |
实施例23 | 56.7 | 0.0012 | 0.010 | 0.005 | 0.0015 | 0.012 | 0.22 | 0.004 | 0.007 |
实施例24 | 56.5 | 0.0011 | 0.012 | 0.006 | 0.0011 | 0.015 | 0.24 | 0.004 | 0.005 |
实施例25 | 56.5 | 0.0013 | 0.008 | 0.005 | 0.0012 | 0.011 | 0.25 | 0.002 | 0.005 |
实施例26 | 56.6 | 0.0015 | 0.009 | 0.004 | 0.0014 | 0.013 | 0.21 | 0.003 | 0.006 |
实施例27 | 56.9 | 0.0012 | 0.007 | 0.004 | 0.0014 | 0.013 | 0.20 | 0.004 | 0.007 |
实施例28 | 56.8 | 0.0010 | 0.010 | 0.006 | 0.0010 | 0.010 | 0.25 | 0.002 | 0.006 |
实施例29 | 56.7 | 0.0010 | 0.010 | 0.007 | 0.0010 | 0.012 | 0.24 | 0.003 | 0.008 |
实施例30 | 56.5 | 0.0011 | 0.009 | 0.005 | 0.0012 | 0.014 | 0.23 | 0.004 | 0.008 |
实施例31 | 56.5 | 0.0014 | 0.007 | 0.005 | 0.0013 | 0.015 | 0.21 | 0.004 | 0.005 |
实施例32 | 56.5 | 0.0012 | 0.011 | 0.006 | 0.0012 | 0.013 | 0.20 | 0.002 | 0.004 |
实施例33 | 56.9 | 0.0011 | 0.010 | 0.005 | 0.0014 | 0.011 | 0.25 | 0.003 | 0.005 |
实施例34 | 56.8 | 0.0013 | 0.012 | 0.004 | 0.0010 | 0.013 | 0.23 | 0.002 | 0.006 |
实施例35 | 56.5 | 0.0015 | 0.008 | 0.006 | 0.0012 | 0.012 | 0.21 | 0.002 | 0.006 |
实施例36 | 56.6 | 0.0012 | 0.009 | 0.005 | 0.0011 | 0.014 | 0.24 | 0.003 | 0.007 |
Claims (16)