CN102776363A - 200目天青石矿粉和还原煤混合造球工艺 - Google Patents

200目天青石矿粉和还原煤混合造球工艺 Download PDF

Info

Publication number
CN102776363A
CN102776363A CN2012102984326A CN201210298432A CN102776363A CN 102776363 A CN102776363 A CN 102776363A CN 2012102984326 A CN2012102984326 A CN 2012102984326A CN 201210298432 A CN201210298432 A CN 201210298432A CN 102776363 A CN102776363 A CN 102776363A
Authority
CN
China
Prior art keywords
raw coal
celestite
polypropylene glycol
spheroid
lazurite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102984326A
Other languages
English (en)
Other versions
CN102776363B (zh
Inventor
杨占寿
祁瑞清
王树轩
邹兴武
祁米香
王舒娅
李宁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qinghai Institute of Salt Lakes Research of CAS
Original Assignee
Qinghai Institute of Salt Lakes Research of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qinghai Institute of Salt Lakes Research of CAS filed Critical Qinghai Institute of Salt Lakes Research of CAS
Priority to CN201210298432.6A priority Critical patent/CN102776363B/zh
Publication of CN102776363A publication Critical patent/CN102776363A/zh
Application granted granted Critical
Publication of CN102776363B publication Critical patent/CN102776363B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种200目天青石矿粉和还原煤混合造球工艺，该工艺包括以下步骤：⑴将天青石矿粉、还原煤和膨润土经搅拌、混合均匀，得到原料；⑵将工业聚丙烯醇用水搅拌，使其完全溶解，配置成20g/L的聚丙烯醇溶液，然后加水稀释至浓度为2~4g/L的聚丙烯醇溶液；⑶所述原料中喷淋加入所述聚丙烯醇溶液，经搅拌、混合均匀后，在压球机上挤压造球至球体的粒径为15mm且球体的水份含量为球体总质量的5~7%；⑷将所述步骤⑶所得的球体干燥至恒重后，该干燥后的球体按常规工艺经焙烧后即可用于生产碳酸锶。本发明投入设备少，成本低，工艺简单，原料中未引入影响碳酸锶品质的杂质。

Description

200目天青石矿粉和还原煤混合造球工艺
技术领域
本发明涉及碳酸锶生产技术领域，尤其涉及200目天青石矿粉和还原煤混合造球工艺。
背景技术
青海柴达木盆地大风山一带已探明的天青石矿储量达2000万吨以上，是世界上最大的锶矿床。锶矿品位低，天青石矿中硫酸锶含量在30~50%之间，嵌布粒度细，矿体浅露地表，露天开采，经浮选后硫酸锶含量达到70%，粒度在200目以下。常规黑灰法制备碳酸锶的焙烧工艺是粒径为1~5mm天青石和无烟煤在1000~1200℃发生氧化还原反应生成硫化锶。天青石矿粉和煤粉在回转窑按常规工艺焙烧，回转窑内负压使矿粉被引风机抽走，锶收率下降，锶资源浪费严重，对环境造成污染，无法用常规焙烧工艺还原硫酸锶得到硫化锶。200目天青石精矿造块工艺，在圆盘造球机滚动使相互碰撞致密进行造球，球体的粒径控制在10~12mm，制成球团落下强度为4.6~4.7次·0.5m-1，在黑灰法生产碳酸锶焙烧工艺中，矿粉的球体粒径太大，反应不完全，锶的收率下降，造成锶资源浪费。
发明内容
本发明所要解决的技术问题是提供一种成本低、工艺简单的200目天青石矿粉和还原煤混合造球工艺。
为解决上述问题，本发明所述的200目天青石矿粉和还原煤混合造球工艺，包括以下步骤：
⑴将粒径200目的天青石矿粉、粒径180目的还原煤和膨润土经搅拌、混合均匀，得到原料；所述天青石矿粉中的硫酸根与所述还原煤中的固定碳的质量比为1：2~1：3；所述膨润土占所述天青石矿粉和所述还原煤总质量的2~5%；
⑵将工业聚丙烯醇用80~85℃的水搅拌，使其完全溶解，配置成20g/L的聚丙烯醇溶液，然后加水稀释至浓度为2~4g/L的聚丙烯醇溶液；
⑶所述原料中喷淋加入所述聚丙烯醇溶液，经搅拌、混合均匀后，在压球机上挤压造球至球体的粒径为15mm且球体的水份含量为球体总质量的5~7%；
⑷将所述步骤⑶所得的球体在100~105℃温度下干燥至恒重后，该干燥后的球体按常规工艺经焙烧后即可用于生产碳酸锶。
所述步骤⑴中的天青石矿粉是指硫酸锶含量为30~50%的天青石采用常规浮选工艺后得到的硫酸锶含量为70%的天青石矿粉。
所述步骤⑴中的还原煤为固定碳含量为60%的无烟煤。
所述步骤⑴中的膨润土为钙基膨润土。
所述步骤⑶中压球机的挤压压力为8~16KN。
本发明与现有技术相比具有以下优点：
1、本发明以硫酸根和固定碳作为原料配比，确定天青石和还原煤反应的较优配比，减少了还原煤的用量（原工艺硫酸根和固定碳的配比为1:4.5）；同时本发明在原料中喷入聚丙烯醇溶液，使硫酸根和固定碳有效接触，反应完全。
2、本发明中压球机保持恒定的供料压力，保证了球团质量稳定，颗粒均匀，所得球体的生球落下强度为6~8次·0.5m-1，满足了常规工艺焙烧天青石和煤粉的工艺要求。同时球团粒径控制在15mm，使压球机的磨具容易脱模。
3、本发明投入设备少，成本低，工艺简单，原料中未引入影响碳酸锶品质的杂质。
具体实施方式
实施例1    200目天青石矿粉和还原煤混合造球工艺，包括以下步骤：
⑴将50kg粒径200目的天青石矿粉、9.5kg粒径180目的还原煤和1.02kg膨润土经搅拌、混合均匀，得到原料。
其中：天青石矿粉中的硫酸根与还原煤中的固定碳的质量比（kg/kg）为1：2.5；膨润土占天青石矿粉和还原煤总质量的2%。
⑵将0.5kg工业聚丙烯醇用80℃的25L水搅拌，使其完全溶解，配置成20g/L的聚丙烯醇溶液，然后加水稀释至浓度为2g/L的聚丙烯醇溶液。
⑶原料中喷淋加入聚丙烯醇溶液，经搅拌、混合均匀后，在压球机上挤压造球至球体的粒径为15mm且球体的水份含量为球体总质量的7%。
其中：压球机的挤压压力为16KN。
⑷将步骤⑶所得的球体在102℃温度下干燥至恒重后，该干燥后的球体按常规工艺经焙烧后即可用于生产碳酸锶。
测定干燥后球体的生球落下强度为7.2次·0.5m-1。
实施例2    200目天青石矿粉和还原煤混合造球工艺，包括以下步骤：
⑴将50kg粒径200目的天青石矿粉、6.35kg 粒径180目的还原煤和2.8kg膨润土经搅拌、混合均匀，得到原料。
其中：天青石矿粉中的硫酸根与还原煤中的固定碳的质量比（kg/kg）为1：2；膨润土占天青石矿粉和还原煤总质量的5%。
⑵将0.5kg工业聚丙烯醇用85℃的25L水搅拌，使其完全溶解，配置成20g/L的聚丙烯醇溶液，然后加水稀释至浓度为3g/L的聚丙烯醇溶液。
⑶原料中喷淋加入聚丙烯醇溶液，经搅拌、混合均匀后，在压球机上挤压造球至球体的粒径为15mm且球体的水份含量为球体总质量的5%。
其中：压球机的挤压压力为8KN。
⑷将步骤⑶所得的球体在105℃温度下干燥至恒重后，该干燥后的球体按常规工艺经焙烧后即可用于生产碳酸锶。
测定干燥后球体的生球落下强度为6.6次·0.5m-1。
实施例3    200目天青石矿粉和还原煤混合造球工艺，包括以下步骤：
⑴将50kg粒径200目的天青石矿粉、11.4kg粒径180目的还原煤和1.8kg膨润土经搅拌、混合均匀，得到原料。
其中：天青石矿粉中的硫酸根与还原煤中的固定碳的质量比（kg/kg）为1：3；膨润土占天青石矿粉和还原煤总质量的3%。
⑵将0.5kg工业聚丙烯醇用82℃的25L水搅拌，使其完全溶解，配置成20g/L的聚丙烯醇溶液，然后加水稀释至浓度为4g/L的聚丙烯醇溶液。
⑶原料中喷淋加入聚丙烯醇溶液，经搅拌、混合均匀后，在压球机上挤压造球至球体的粒径为15mm且球体的水份含量为球体总质量的6%。
其中：压球机的挤压压力为12KN。
⑷将步骤⑶所得的球体在100℃温度下干燥至恒重后，该干燥后的球体按常规工艺经焙烧后即可用于生产碳酸锶。
测定干燥后球体的生球落下强度为7.3次·0.5m-1。
上述实施例1~3步骤⑴中的天青石矿粉是指硫酸锶含量为30~50%的天青石采用常规浮选工艺后得到的硫酸锶含量为70%的天青石矿粉；还原煤为固定碳含量为60%的无烟煤；膨润土为钙基膨润土。

Claims (5)

1.200目天青石矿粉和还原煤混合造球工艺，包括以下步骤：
⑴将粒径200目的天青石矿粉、粒径180目的还原煤和膨润土经搅拌、混合均匀，得到原料；所述天青石矿粉中的硫酸根与所述还原煤中的固定碳的质量比为1：2~1：3；所述膨润土占所述天青石矿粉和所述还原煤总质量的2~5%；
⑵将工业聚丙烯醇用80~85℃的水搅拌，使其完全溶解，配置成20g/L的聚丙烯醇溶液，然后加水稀释至浓度为2~4g/L的聚丙烯醇溶液；
⑶所述原料中喷淋加入所述聚丙烯醇溶液，经搅拌、混合均匀后，在压球机上挤压造球至球体的粒径为15mm且球体的水份含量为球体总质量的5~7%；
⑷将所述步骤⑶所得的球体在100~105℃温度下干燥至恒重后，该干燥后的球体按常规工艺经焙烧后即可用于生产碳酸锶。
2.如权利要求1所述的200目天青石矿粉和还原煤混合造球工艺，其特征在于：所述步骤⑴中的天青石矿粉是指硫酸锶含量为30~50%的天青石采用常规浮选工艺后得到的硫酸锶含量为70%的天青石矿粉。
3.如权利要求1所述的200目天青石矿粉和还原煤混合造球工艺，其特征在于：所述步骤⑴中的还原煤为固定碳含量为60%的无烟煤。
4.如权利要求1所述的200目天青石矿粉和还原煤混合造球工艺，其特征在于：所述步骤⑴中的膨润土为钙基膨润土。
5.如权利要求1所述的200目天青石矿粉和还原煤混合造球工艺，其特征在于：所述步骤⑶中压球机的挤压压力为8~16KN。
CN201210298432.6A 2012-08-21 2012-08-21 200目天青石矿粉和还原煤混合造球工艺 Expired - Fee Related CN102776363B (zh)