CN102766396B - 一种鞋材罩光用水性聚氨酯光油 - Google Patents

一种鞋材罩光用水性聚氨酯光油 Download PDF

Info

Publication number
CN102766396B
CN102766396B CN201210279413.9A CN201210279413A CN102766396B CN 102766396 B CN102766396 B CN 102766396B CN 201210279413 A CN201210279413 A CN 201210279413A CN 102766396 B CN102766396 B CN 102766396B
Authority
CN
China
Prior art keywords
waterborne polyurethane
add
polyurethane resin
minutes
react
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210279413.9A
Other languages
English (en)
Other versions
CN102766396A (zh
Inventor
丁军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefeng new Mstar Technology Ltd
Original Assignee
丁军
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 丁军 filed Critical 丁军
Priority to CN201210279413.9A priority Critical patent/CN102766396B/zh
Publication of CN102766396A publication Critical patent/CN102766396A/zh
Application granted granted Critical
Publication of CN102766396B publication Critical patent/CN102766396B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种鞋材罩光用水性聚氨酯光油，其配方为：水性聚氨酯树脂、润湿剂、流平剂和消泡剂。它高亮光，又具备耐高温性能。

Description

一种鞋材罩光用水性聚氨酯光油
技术领域：
本发明涉及一种高光水性聚氨酯的制备方法，也涉及这种高光水性聚氨酯树脂的耐高温性能。
背景技术：
传统的溶剂型罩光光油，是一种含有20-40％的醋酸丁酯和醋酸乙酯的湿气固化型、以异氰酸酯封端的聚氨酯树脂，通过在晾置过程中吸收空气中水分而交联固化。固化后的光油层具有亮度好光泽高，耐高温。这种印刷光油层的部位，大部分都会高频处理。对光油层高频热压，使其具有突出的立体效果。增加其Logo的突出性。高频也叫高周波，其过程使光油层在2-3秒中内产生100℃以上的高温，如果光油不耐高温，熔融软化会造成光油层脱落。
发明内容
本发明的目的是：提供一种高亮光，又具备耐高温性能的一种替代溶剂型的水性环保聚氨酯鞋材用的一种鞋材罩光用水性聚氨酯光油。
本发明是这样实现的：一种鞋材罩光用水性聚氨酯光油，其配方的重量份数比为：
水性聚氨酯树脂  100            润湿剂    2-5
流平剂          0.5-1          消泡剂    0.1-0.5
水性聚氨酯树脂的配方的重量份数比为：
所述催化剂为有机铋催化剂或有机银催化剂。
一种鞋材罩光用水性聚氨酯光油，其特殊之处在于：水性聚氨酯树脂其制造方法包括以下步骤：
(1)在装有搅拌器，温度计，回流冷凝器的反应釜中，加入聚碳酸酯二醇，聚酯二醇，异佛尔酮二异氰酸酯，催化剂和丁酮，升温至80-90℃，反应2小时；然后加入N-甲吡咯基烷酮溶解好的二羟甲基丙酸，在温度80-90℃下，反应3小时；
(2)降温至50℃加入的丙酮搅拌均匀，取样测异氰酸酯-NC0含量；
(3)加入三乙胺，在40-50℃下反应20分钟；
(4)在40℃下加入乙二氨基磺酸钠，反应20分钟，把温度升到50℃；
(5)加入氨乙基氨丙基三乙氧基硅烷、异佛尔酮二胺的水溶液及去离子水乳化，反应30分钟；
(6)升温抽真空，脱除溶剂；降温过滤，得到外观微浊的水性聚氨酯树脂。
具体实施方式
下面结合实施例对本发明作进一步描述。
实施例1
一种鞋材罩光用水性聚氨酯光油，其配方的重量份数比为：
水性聚氨酯树脂  100            润湿剂  2
流平剂          0.5            消泡剂  0.1
水性聚氨酯树脂的配方的重量份数比为：
一种鞋材罩光用水性聚氨酯光油，其水性聚氨酯树脂其制造方法包括以下步骤：
(1)在装有搅拌器，温度计，回流冷凝器的反应釜中，加入聚碳酸酯二醇，聚酯二醇，异佛尔酮二异氰酸酯，有机铋催化剂，丁酮升温至80-90℃反应2小时；加入N-甲吡咯基烷酮溶解好的二羟甲基丙酸，80-90℃反应3小时；在步骤(1)也可以用有机银催化剂替换有机铋催化剂；
(2)降温至50℃加入的丙酮搅拌均匀，取样测异氰酸酯-NCO含量；
(3)加入三乙胺，在40-50℃下反应20分钟；
(4)在40℃下加入乙二氨基磺酸钠水溶液反应20分钟，把温度升到 50℃；
(5)加入氨乙基氨丙基三乙氧基硅烷、异佛尔酮二胺的水溶液及去离子水乳化，反应30分钟；
(6)升温抽真空，脱除溶剂；降温过滤，得到外观微浊的水性聚氨酯树脂。
润湿剂(阿克苏诺贝尔1008)；
流平剂(德国明凌化工PUR80)；
消泡剂(迪高805)。
A  本配方中二元醇中羟基(-OH)官能团与异氰酸酯(IPDI)中异氰酸根(-NCO)的摩尔比为2；
B  A-95不挥发物占整个配方体系中不挥发物的质量比为3％。
C  二羟甲基丙酸(DMPA)的中和度为30％，即二羟甲基丙酸占整个不挥发物的有效成份为0.25％，其未中和的-COOH在烘焙过程中提供有效的交联成份。
D  测定-NCO采用ABB(中国有限公司的HOYA(羟值分析仪)同时可以分析异氰酸酯，酸值水分等分拆速度快，小于2分钟。
E  乙二氨基磺酸钠上海和氏璧公司生产的商品名为A-95亲水扩链剂，其浓度为50％的溶液。
实施例2
一种鞋材罩光用水性聚氨酯光油，其配方的重量份数比为：
水性聚氨酯树脂 100            润湿剂  5
流平剂         1              消泡剂  0.5；
水性聚氨酯树脂的配方的重量份数比为：
实施例3
一种鞋材罩光用水性聚氨酯光油，其配方的重量份数比为：
水性聚氨酯树脂   100         润湿剂   3
流平剂           0.7         消泡剂   0.3；
水性聚氨酯树脂的配方的重量份数比为：
所述催化剂为有机铋催化剂或有机银催化剂。
其重点体现在原材料的优化选择上，具体做法如下：
(1)多元醇的选取，选取耐高温性能最好的聚碳酸酯二醇(PCDL)，作为核心多元醇原料，当然进一步优选PCDL结构中带有支链小分子二醇为起始剂，常温下为液态，透明性好，分子量M＝2000左右的聚碳酸酯二醇；例如旭化成化学株式会社的一些液态PCDL.T5652等。由于PCDL价格高昂；光泽度、柔韧性还不是很令人满意。需搭配部分带有支链。透明度，柔韧性佳，具有中等耐热性能，分子量在1000-2000的低聚物多元醇；在这里优选德国Degussa公司供应的OxyesterT1136分子量为1000的聚酯二醇，T1136是一种线性的聚酯二元醇，T1136拥有普通聚酯无法达到的低温柔韧性，拥有普通聚酯不具有的低粘度性，拥有接近聚醚的高耐水解性。
(2)异氰酸酯；以优选具有典型非结晶结构的异佛尔酮二异氰酸酯作为活性反应单体。由异佛尔酮二异氰酸酯制成的聚氨酯树脂具有非常好的透明度和光泽度，耐高温性能及其光稳定性和耐化学品性。
(3)扩链剂：分亲水扩链剂和功能性扩链剂
亲水扩链剂：优选含-COOH基的二羟甲基丙酸(DMPA)和含-SO3Na的乙二氨基磺酸钠；两种完全不同亲水基因，由于脲基的引入，也提高了耐热性。含-COOH基和-SO3Na基配合的水性聚氨酯乳液稳定性更好。
功能性扩链剂：A优选具有异佛尔酮二氰酸酯相似结构的异佛尔酮二胺(IPDA)进一步提高树脂的耐热性，光泽度，及其他性能。异氟尔酮二胺(IPDA)，异氟尔酮二胺：BASF公司注册名称为IPDA，德国萨公司注册名称为IPD是异氟尔酮氰酸酯的上一级产品是一种中等活性的二胺，其做成的聚氨酯树脂具有非常好的力学性能和对基材的粘附性。
B  能够大幅度提高耐水性能和耐热性能的双氨基硅氧烷，这里优选 氨乙基氨丙基三乙氧基硅烷。
(4)催化剂：由于对锡类催化剂的限制，可以选择有机鉍类催化剂，例如美国空气化学的8108；或有机银类催化剂，如韩国世好化学的100AG-18-KM。
在整个反应过程中用的溶剂优选丁酮，丙酮，N-甲吡咯基烷酮(NMP)。
(一)测定-NCO采用ABB(中国有限公司的HOYA(羟值分析仪)同时可以分析异氰酸酯，酸值水分等分拆速度快，小于2分钟。
(二)乙二氨基磺酸钠商品名为上海和氏璧公司的A-95(50％水溶液)亲水扩链剂。
本发明水性聚氨酯树脂光油的技术指标：
以上所述的仅是本发明优先实施方式。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明理的情况下，还可以作出若干改进和 变型，这也视为本发明的保护范围。

Claims (1)

1.一种鞋材罩光用水性聚氨酯光油，其特征在于：其配方的重量份数比为：
水性聚氨酯树脂的配方的重量份数比为：
所述催化剂为有机铋催化剂或有机银催化剂；
水性聚氨酯树脂其制造方法包括以下步骤：
(1)在装有搅拌器，温度计，回流冷凝器的反应釜中，加入聚碳酸酯二醇，聚酯二醇，异佛尔酮二异氰酸酯,催化剂和丁酮，升温至80-90℃，反应2小时；然后加入N-甲吡咯基烷酮溶解好的二羟甲基丙酸,80-90℃反应3小时；
(2)降温至50℃，加入的丙酮搅拌均匀，取样测异氰酸酯-NCO含量；
(3)加入三乙胺，在40-50℃下，反应20分钟；
(4)在温度40℃下，加入乙二氨基磺酸钠，反应20分钟；然后把温度升到50℃；
(5)加入氨乙基氨丙基三乙氧基硅烷、异佛尔酮二胺及去离子水乳化，反应30分钟；
(6)升温抽真空，脱除溶剂；降温过滤，得到外观微浊的水性聚氨酯树脂。
CN201210279413.9A 2012-08-07 2012-08-07 一种鞋材罩光用水性聚氨酯光油 Active CN102766396B (zh)