CN102765923A - 一种利用电石渣生产加气空心砖方法 - Google Patents

一种利用电石渣生产加气空心砖方法 Download PDF

Info

Publication number
CN102765923A
CN102765923A CN2012102217076A CN201210221707A CN102765923A CN 102765923 A CN102765923 A CN 102765923A CN 2012102217076 A CN2012102217076 A CN 2012102217076A CN 201210221707 A CN201210221707 A CN 201210221707A CN 102765923 A CN102765923 A CN 102765923A
Authority
CN
China
Prior art keywords
parts
carbide slag
slag
ceramic waste
hollow brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102217076A
Other languages
English (en)
Other versions
CN102765923B (zh
Inventor
强晓震
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Original Assignee
ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd filed Critical ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority to CN2012102217076A priority Critical patent/CN102765923B/zh
Publication of CN102765923A publication Critical patent/CN102765923A/zh
Application granted granted Critical
Publication of CN102765923B publication Critical patent/CN102765923B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种利用电石渣生产加气空心砖方法，该方法包括有以下步骤：（1）将石膏、陶粒和磷矿渣分别进行破碎后，并按质量份取6-10份的水泥、3-5份的石膏、7-8份的陶粒和10-21份的磷矿渣；（2）在质量份取60-70份的电石渣和0.01-0.03份的铝粉、10-12份生石灰、2-5份可再分散性乳胶粉，步骤（1）、（2）物料混合；（3）将陶瓷废料进行破碎，并按质量份取12-25份的陶瓷废料；本发明的电石渣用量大、节能环保，缓解电石渣堆存处理带来的环境污染问题，同时为空心砖提供了新的原料。

Description

一种利用电石渣生产加气空心砖方法
技术领域
本发明涉及新型建材领域，具体属于一种利用电石渣生产加气空心砖方法。
背景技术
电石渣浆的产生量大大超过了PVC的产量。大多数PVC生产厂家将电石渣浆经重力沉降分离后，上清液循环利用；电石渣经进一步脱水，其含水率仍达40%～50%，呈浆糊状，在运输途中易渗漏污染路面，长期堆积不但占用大量土地，而且对土地有严重的侵蚀作用。 
　　长期以来，电石渣的综合利用一直是个世界性难题，尽管国内外对电石渣的综合利用进行了大量的研究，但是由于技术上和经济上的种种原因，大多数未付诸工业实现。
综合所述，用电石渣为辅助原料生产水泥、墙体砖、道路材料已有报道，以电石渣作为主要原料用于加气砌块的生产还未见报导。
发明内容
本发明的目的在于提供一种利用电石渣生产加气空心砖方法，电石渣用量大、节能环保，缓解电石渣堆存处理带来的环境污染问题，同时为空心砖提供了新的原料来源。
本发明的技术方案如下：
一种利用电石渣生产加气空心砖方法，其特征在于，该方法包括有以下步骤：
（1）、将石膏、陶粒和磷矿渣分别进行破碎后，并按质量份取6-10份的水泥、3-5份的石膏、7-8份的陶粒和10-21份的磷矿渣；
（2）、在质量份取60-70份的电石渣和0.01-0.03份的铝粉、10-12份生石灰、2-5份可再分散性乳胶粉，步骤（1）、（2）物料混合；
（3）、将陶瓷废料进行破碎，并按质量份取12-25份的陶瓷废料；
（4）、将破碎后陶瓷废料和混合物料、放入到搅拌设备中，并加水进行充分搅拌，并加入2-4份浓度为8-9%三乙醇胺溶液、0.1-0.4份甲基纤维素醚、1-2份甘油三醋酸酯，每立方米加气搅拌原料中放3-4kg的纯碱；
（5）将上述步骤（4）搅拌后的浆料在60-75℃温度下，发泡时间30-40min；
（6）、将发泡浆料注入到成型模具内形成生坯，生坯经过蒸汽养护得加气空心砖成品。
所述步骤（5）中，搅拌后的浆料在68℃温度下，发泡时间35min。
本发明与现有技术相比具有如下优点：
与其他建筑砌块相比，本发明生产的加气砌块容重轻，强度高，特别适用于高层建筑的承重墙或内墙隔断用。
与加气砌块相比，本发明的主要原料为电石渣，有利于解决电石渣堆存处理而带来的环境污染问题，为电石渣的资源化利用开辟了一条新的利用途径。
具体实施方式
一种利用电石渣生产加气空心砖方法，该方法包括有以下步骤：
   （1）、将石膏、陶粒和磷矿渣分别进行破碎后，并按质量份取8份的水泥、5份的石膏、8份的陶粒和15份的磷矿渣；
（2）、在质量份取60份的电石渣和0.02份的铝粉、12份生石灰、2份可再分散性乳胶粉，步骤（1）、（2）物料混合；
（3）、将陶瓷废料进行破碎，并按质量份取20份的陶瓷废料；
（4）、将破碎后陶瓷废料和混合物料、放入到搅拌设备中，并加水进行充分搅拌，并加入2份浓度为8%三乙醇胺溶液、0.16份甲基纤维素醚、1份甘油三醋酸酯，每立方米加气搅拌原料中放3-4kg的纯碱；
（5）将上述步骤（4）搅拌后的浆料在68℃温度下，发泡时间30-40min；
（6）、将发泡浆料注入到成型模具内形成生坯，生坯经过蒸汽养护得加气空心砖成品。
本发明生产的空心砖在实验室中进行力学性能和其他性能检测如下：
将本发明生产的空心砖切割成100mm×100mm×100mm的立方体进行性能检测，检测结果如下：抗压强度3.98Mpa，容重0.68g/m3，收缩值0.45mm/m，重量损失3.5%，抗冻强度损失18.45%。

Claims (2)

1.一种利用电石渣生产加气空心砖方法，其特征在于，该方法包括有以下步骤：
   （1）、将石膏、陶粒和磷矿渣分别进行破碎后，并按质量份取6-10份的水泥、3-5份的石膏、7-8份的陶粒和10-21份的磷矿渣；
（2）、在质量份取60-70份的电石渣和0.01-0.03份的铝粉、10-12份生石灰、2-5份可再分散性乳胶粉，步骤（1）、（2）物料混合；
（3）、将陶瓷废料进行破碎，并按质量份取12-25份的陶瓷废料；
（4）、将破碎后陶瓷废料和混合物料、放入到搅拌设备中，并加水进行充分搅拌，并加入2-4份浓度为8-9%三乙醇胺溶液、0.1-0.4份甲基纤维素醚、1-2份甘油三醋酸酯，每立方米加气搅拌原料中放3-4kg的纯碱；
（5）将上述步骤（4）搅拌后的浆料在60-75℃温度下，发泡时间30-40min；
（6）、将发泡浆料注入到成型模具内形成生坯，生坯经过蒸汽养护得加气空心砖成品。
2.根据权利要求1所述的利用电石渣生产加气空心砖方法，其特征在于，所述步骤（5）中，搅拌后的浆料在68℃温度下，发泡时间35min。
CN2012102217076A 2012-06-30 2012-06-30 一种利用电石渣生产加气空心砖方法 Active CN102765923B (zh)