CN102765909B - 一种利用废建筑垃圾制备加气空心砖的方法 - Google Patents

一种利用废建筑垃圾制备加气空心砖的方法 Download PDF

Info

Publication number
CN102765909B
CN102765909B CN2012102217112A CN201210221711A CN102765909B CN 102765909 B CN102765909 B CN 102765909B CN 2012102217112 A CN2012102217112 A CN 2012102217112A CN 201210221711 A CN201210221711 A CN 201210221711A CN 102765909 B CN102765909 B CN 102765909B
Authority
CN
China
Prior art keywords
construction waste
raw material
mentioned steps
slurry
dry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2012102217112A
Other languages
English (en)
Other versions
CN102765909A (zh
Inventor
强晓震
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Original Assignee
ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd filed Critical ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority to CN2012102217112A priority Critical patent/CN102765909B/zh
Publication of CN102765909A publication Critical patent/CN102765909A/zh
Application granted granted Critical
Publication of CN102765909B publication Critical patent/CN102765909B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种利用废建筑垃圾制备加气空心砖的方法,按照如下步骤进行:(1)按下列干基质量份混合原料:经粉碎处理后废建筑垃圾,生石灰,水泥等;(2)按上述步骤(1)混合原料干基质量的85-95%加水,混合原料干基质量的0.04-0.06%加废铝粉,生石灰质量的9-11%加石膏等;(3)将上述步骤(2)搅拌后的浆料在65-75℃温度下,发泡时间30-40min;(4)将上述步骤(3)的发泡浆料在常压下蒸汽养护得生坯,并切割成相应的尺寸。本发明的废建筑垃圾用量大、节能环保,缓解废建筑垃圾堆存处理带来的环境污染问题,同时为空心砖提供了新的原料。

Description

一种利用废建筑垃圾制备加气空心砖的方法
技术领域
本发明涉及新型建材领域,具体属于一种利用废建筑垃圾制备加气空心砖的方法。
背景技术
建筑垃圾是指建设、施工单位或个人对各类建筑物、构筑物、管网等进行建设、铺设或拆除、修缮过程中所产生的渣土、弃土、弃料、余泥及其他废弃物。
目前,我国建筑垃圾的数量已占到城市垃圾总量的30%-40%。以500-600吨/万平方米的标准推算,到2020年建筑垃圾我国还将新增建筑面积约300亿平方米,新产生的建筑垃圾将是一个令人震撼的数字。然而,绝大部分建筑垃圾未经任何处理,便被施工单位运往郊外或乡村,露天堆放或填埋,耗用大量的征用土地费、垃圾清运费等建设经费,同时,清运和堆放过程中的遗撒和粉尘、灰砂飞扬等问题又造成了严重的环境污染。
长期以来,建筑垃圾的综合利用一直是个世界性难题,尽管国内外对建筑垃圾的综合利用进行了大量的研究,但是由于技术上和经济上的种种原因,大多数未付诸工业实现。
综合所述,用建筑垃圾为辅助原料生产水泥、墙体砖、道路材料已有报道,以建筑垃圾作为主要原料用于加气砌块的生产还未见报导。
发明内容
本发明的目的在于提供一种利用废建筑垃圾制备加气空心砖的方法,废建筑垃圾用量大、节能环保,缓解废建筑垃圾堆存处理带来的环境污染问题,同时为空心砖提供了新的原料。
本发明的技术方案如下:
一种利用废建筑垃圾制备加气空心砖的方法,其特征在于按照如下步骤进行:
    (1)、按下列干基质量份混合原料:
     经粉碎处理后废建筑垃圾            55-70份
     陶粒                              10-15份
     生石灰                            10-15份
     水泥                              10-15份
     石膏                               3-4份
    (2)、按上述步骤(1)混合原料干基质量的85-95%加水,混合原料干基质量的0.04-0.06%加废铝粉、0.5-0.9%加甲基纤维素醚、1-2%加乙酰柠檬酸三乙酯,石灰重量的0.2-0.3%加三乙醇胺;
(3)、将上述步骤(2)搅拌后的浆料在65-75℃温度下,发泡时间30-40min;
(4)、将上述步骤(3)的发泡浆料在常压下蒸汽养护得生坯,并切割成相应的尺寸;
(5)、将上述步骤(4)的生坯在0.7-0.9Mpa蒸汽养护18-22h,即得加气空心砖成品。
在步骤(2)中加入纯碱,加入量为每立方米混合浆料中放3-4kg纯碱。
本发明与现有技术相比具有如下优点:
与其他建筑砌块相比,本发明生产的加气砌块容重轻,强度高,特别适用于高层建筑的承重墙或内墙隔断用。
与加气砌块相比,本发明的主要原料为废建筑垃圾,有利于解决废建筑垃圾堆存处理而带来的环境污染问题。
总之,本发明结合我国废建筑垃圾量大、利用率低的实际情况,充分利用了各种物料的组成结构和化学特性,形成了以硅铝酸钙、水化硅酸钙等为主体的矿物结构,其产品性能符合建筑用承重和非承重墙体材料质量要求。砌块主要原材料为废建筑垃圾,使用量大,有利于解决废建筑垃圾堆存处理而带来的环境污染问题,为废建筑垃圾的资源化利用开辟了一条新的利用途径。
具体实施方式
参见附图,一种利用废建筑垃圾制备加气空心砖的方法,按照如下步骤进行:
   (1)、按下列干基质量份混合原料:
     经粉碎处理后废建筑垃圾            55份
     陶粒                              15份
     生石灰                            10份
     水泥                              12份
     石膏                               3份
    (2)、按上述步骤(1)混合原料干基质量的85%加水,混合原料干基质量的0.05%加废铝粉、0.8%加甲基纤维素醚、2%加乙酰柠檬酸三乙酯,石灰重量的0.2%加三乙醇胺;
(3)、将上述步骤(2)搅拌后的浆料在65℃温度下,发泡时间30-40min;
(4)、将上述步骤(3)的发泡浆料在常压下蒸汽养护得生坯,并切割成相应的尺寸;
(5)、将上述步骤(4)的生坯在0.7-0.9Mpa蒸汽养护18-22h,即得加气空心砖成品。
将本发明生产的空心砖切割成100mm×100mm×100mm的立方体进行性能检测,检测结果如下:抗压强度3.01Mpa,容重0.61g/m3,收缩值0.49mm/m,重量损失4.5%,抗冻性强度损失19.45%。

Claims (2)

1.一种利用废建筑垃圾制备加气空心砖的方法,其特征在于按照如下步骤进行:
(1)、按下列干基质量份混合原料:
(2)、按上述步骤(1)混合原料干基质量的85-95%加水,混合原料干基质量的0.04-0.06%加废铝粉、0.5-0.9%加甲基纤维素醚、1-2%加乙酰柠檬酸三乙酯,石灰重量的0.2-0.3%加三乙醇胺;
(3)、将上述步骤(2)的浆料搅拌后在65-75℃温度下发泡,时间30-40min;
(4)、将上述步骤(3)的发泡浆料在常压下蒸汽养护得生坯,并切割成相应的尺寸;
(5)、将上述步骤(4)的生坯在0.7-0.9Mpa蒸汽养护18-22h,即得加气空心砖成品。
2.根据权利要求1所述利用废建筑垃圾制备加气空心砖的方法,其特征在于:在步骤(2)中加入纯碱,加入量为每立方米混合浆料中放3-4kg纯碱。
CN2012102217112A 2012-06-30 2012-06-30 一种利用废建筑垃圾制备加气空心砖的方法 Active CN102765909B (zh)