CN102719207B - 一种热熔胶 - Google Patents

一种热熔胶 Download PDF

Info

Publication number
CN102719207B
CN102719207B CN201210215031XA CN201210215031A CN102719207B CN 102719207 B CN102719207 B CN 102719207B CN 201210215031X A CN201210215031X A CN 201210215031XA CN 201210215031 A CN201210215031 A CN 201210215031A CN 102719207 B CN102719207 B CN 102719207B
Authority
CN
China
Prior art keywords
parts
hot melt
melt adhesive
foaming
molecular weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210215031XA
Other languages
English (en)
Other versions
CN102719207A (zh
Inventor
刘道礼
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGZHOU HAOTE BONDING MATERIAL Co Ltd
Original Assignee
CHANGZHOU HAOTE BONDING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGZHOU HAOTE BONDING MATERIAL Co Ltd filed Critical CHANGZHOU HAOTE BONDING MATERIAL Co Ltd
Priority to CN201210215031XA priority Critical patent/CN102719207B/zh
Publication of CN102719207A publication Critical patent/CN102719207A/zh
Application granted granted Critical
Publication of CN102719207B publication Critical patent/CN102719207B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种热熔胶，旨在提供一种贴合后在高温条件下不会发生起泡和分层的热熔胶；其技术要点是：该热熔胶包括下述重量份的组分：甲基丙烯酸甲酯与丙烯酸丁酯的共聚物1~70份，苯乙烯丁二烯异戊二烯嵌段共聚物1~40份，增粘剂1~40份，填充剂1~10份；稳定剂1~5份，蜡5~10份；属于胶体制备技术领域。

Description

一种热熔胶
技术领域
    本发明公开一种熔胶，具体的说是，适用高温条件下适用的溶胶，属于胶体制备技术领域。
背景技术
金属眼镜盒需要外包PU或PVC膜材，以增强美观及防护，内层植绒处理。传统的外包PU、PVC等合成材料均使用溶剂胶贴合，存在挥发性成分多、污染环境等诸多缺陷。而采用传统的热熔胶，贴合后的耐热性能基本不超过40℃，就会起层（鼓泡），达不到使用要求。
发明内容
 针对上述问题，本发明公开一种贴合后在较高的使用高温条件下不会发生起泡和分层的热熔胶。
 本发明的技术方案是这样的：一种热熔胶，该热熔胶包括下述质量百分比的组分：甲基丙烯酸甲酯与丙烯酸丁酯的共聚物1~70份，苯乙烯丁二烯异戊二烯嵌段共聚物1~40份，增粘剂1~40份，填充剂1~10份；稳定剂1~5份，蜡5~10份。
上述的热熔胶，所述的甲基丙烯酸甲酯与丙烯酸丁酯的共聚物的分子量为80000-120000；所述的苯乙烯丁二烯异戊二烯嵌段共聚物的分子量为80000-120000。
进一步的，上述的热熔胶，所述的增粘剂是松香季戊四醇酯或C5-C9石油树脂；所述的填充剂为碳酸钙、二氧化硅或高岭土的其中之一或它们的组合；所述的稳定剂为2，6-二叔丁基对甲酚；所述的蜡为分子量为3000-5000的微晶蜡。
与现有技术相比，本发明所提供的技术方案自动化程度高、基本没有污染和挥发物，环保，贴合后的使用温度70-80℃不会发生起泡和分层现象，满足使用要求。
具体实施方式
    下面结合具体实施方式，对本发明技术方案作进一步的详细说明，但不构成对本发明的任何限制，任何人在本发明权利要求范围内所作的有限次的修改，仍在本发明的权利要求范围内。  
实施例1
    一种热熔胶，该热熔胶包括下述质量百分比的组分：分子量为80000的甲基丙烯酸甲酯与丙烯酸丁酯的共聚物1份，甲基丙烯酸甲酯占45%，丙烯酸丁酯占55%，分子量为120000的苯乙烯丁二烯异戊二烯嵌段共聚物70份，松香季戊四醇酯30份，碳酸钙5份；2，6-二叔丁基对甲酚5份，分子量为3000微晶蜡5份。
实施例2
   一种热熔胶，该热熔胶包括下述质量百分比的组分：甲基丙烯酸甲酯与丙烯酸丁酯的共聚物70份，甲基丙烯酸甲酯占50%，丙烯酸丁酯占50%，苯乙烯丁二烯异戊二烯嵌段共聚物1份，C9石油树脂40份，碳酸钙10份；2，6-二叔丁基对甲酚2份，分子量为4000、熔点为70℃的微晶蜡10份。
实施例3
   一种热熔胶，该热熔胶包括下述质量百分比的组分：分子量为100000甲基丙烯酸甲酯与丙烯酸丁酯的共聚物20份，甲基丙烯酸甲酯占35%，丙烯酸丁酯占65%，分子量为110000苯乙烯丁二烯异戊二烯嵌段共聚物50份，C5石油树脂20份，碳酸钙2份；2，6-二叔丁基对甲酚0.5份，分子量为4000、熔点为70℃的微晶蜡7份。
实施例4
   一种热熔胶，该热熔胶包括下述质量百分比的组分：分子量为110000甲基丙烯酸甲酯与丙烯酸丁酯的共聚物35份，甲基丙烯酸甲酯占30%，丙烯酸丁酯占70%，分子量为100000苯乙烯丁二烯异戊二烯嵌段共聚物50份，C7石油树脂20份，碳酸钙3份；2，6-二叔丁基对甲酚3份，分子量为4000、熔点为70℃的微晶蜡8份。
实施例5
一种热熔胶，该热熔胶包括下述质量百分比的组分：分子量为120000甲基丙烯酸甲酯与丙烯酸丁酯的共聚物35份，甲基丙烯酸甲酯占50%，丙烯酸丁酯占50%，分子量为80000苯乙烯丁二烯异戊二烯嵌段共聚物50份，C7石油树脂20份，二氧化硅1份；2，6-二叔丁基对甲酚3份，分子量为4000、熔点为70℃的微晶蜡8份。
实施例6
一种热熔胶，该热熔胶包括下述质量百分比的组分：分子量为90000甲基丙烯酸甲酯与丙烯酸丁酯的共聚物40份，甲基丙烯酸甲酯占60%，丙烯酸丁酯占40%，分子量为80000苯乙烯丁二烯异戊二烯嵌段共聚物45份，C7石油树脂20份，高岭土4份；2，6-二叔丁基对甲酚3份，分子量为4000、熔点为70℃的微晶蜡6份。
   制备方法：按常规热熔胶的制备方法，密练后成块状胶120-200℃。
   使用方法：热熔、过胶机过胶，上胶量25-50g/m2，然后机器上于80-100℃热压贴合即可，上胶可采用辊涂、刮涂工艺。
    测试结果
耐热实验结果：在低于85℃以下可以长期使用，表一为不同温度下的测试结果，测试时间为24小时。表二为不同时间段的测试结果，测试温度为80℃。
表一 不同温度下的测试实验结果
测试品温度 30℃ 50℃ 70℃ 85℃
实施例1 不起泡 不起泡 不起泡 不起泡
实施例2 不起泡 不起泡 不起泡 不起泡
实施例3 不起泡 不起泡 不起泡 不起泡
实施例4 不起泡 不起泡 不起泡 不起泡
实施例5 不起泡 不起泡 不起泡 不起泡
实施例6 不起泡 不起泡 不起泡 不起泡
市场常规产品 不起泡 轻微起泡 起泡 起泡
 表二 不同时间段的测试实验结果
测试品温度 5h 10h 15h 20h
实施例1 不起泡 不起泡 不起泡 不起泡
实施例2 不起泡 不起泡 不起泡 不起泡
实施例3 不起泡 不起泡 不起泡 不起泡
实施例4 不起泡 不起泡 不起泡 不起泡
实施例5 不起泡 不起泡 不起泡 不起泡
实施例6 不起泡 不起泡 不起泡 不起泡
市场常规产品 起泡 起泡 起泡 起泡

Claims (4)

1.一种热熔胶，其特征在于，该热熔胶包括下述重量份的组分：甲基丙烯酸甲酯与丙烯酸丁酯的共聚物1~70份，苯乙烯丁二烯异戊二烯嵌段共聚物1~40份，增粘剂1~40份，填充剂1~10份；稳定剂1~5份，蜡5~10份；
其中，所述的增粘剂是松香季戊四醇酯或C5-C9石油树脂；所述的填充剂为碳酸钙、二氧化硅或高岭土的其中之一或它们的组合；所述的稳定剂为2，6-二叔丁基对甲酚。
2.根据权利要求1所述的热熔胶，其特征在于，所述的甲基丙烯酸甲酯与丙烯酸丁酯的共聚物的分子量为80000-120000。
3.根据权利要求1所述的热熔胶，其特征在于，所述的苯乙烯丁二烯异戊二烯嵌段共聚物的分子量为80000-120000。
4.根据权利要求1所述的热熔胶，其特征在于，所述的蜡为分子量为3000-5000的微晶蜡。
CN201210215031XA 2012-06-27 2012-06-27 一种热熔胶 Active CN102719207B (zh)