CN103045130B - 一种聚苯乙烯用热封粘合剂及其制备方法 - Google Patents

一种聚苯乙烯用热封粘合剂及其制备方法 Download PDF

Info

Publication number
CN103045130B
CN103045130B CN201210526912.3A CN201210526912A CN103045130B CN 103045130 B CN103045130 B CN 103045130B CN 201210526912 A CN201210526912 A CN 201210526912A CN 103045130 B CN103045130 B CN 103045130B
Authority
CN
China
Prior art keywords
heat
sealing adhesive
copolymer resin
polystyrene
sealing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210526912.3A
Other languages
English (en)
Other versions
CN103045130A (zh
Inventor
徐根华
伏阳
吴新上
张红军
单宁
张军
何建忠
周忠武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Zhongjin Matai Medicinal Packaging Co Ltd
Original Assignee
Jiangsu Zhongjin Matai Medicinal Packaging Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Zhongjin Matai Medicinal Packaging Co Ltd filed Critical Jiangsu Zhongjin Matai Medicinal Packaging Co Ltd
Priority to CN201210526912.3A priority Critical patent/CN103045130B/zh
Publication of CN103045130A publication Critical patent/CN103045130A/zh
Application granted granted Critical
Publication of CN103045130B publication Critical patent/CN103045130B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种聚苯乙烯用热封粘合剂，由以下重量百分比组成：丙烯酸酯共聚树脂10-25%；氯乙烯共聚树脂2-10%；苯乙烯共聚树脂2-10%；混合溶剂70-85%。本发明提供了一种可以与聚苯乙烯材料热封的粘合剂，该热封粘合剂具有较高的热封强度和宽泛的热封温度范围，各项指标均符合国家药品包装材料标准，而且本发明制备方法简单易行。本发明的热封粘合剂不仅适用于泡罩包装的热封胶，还适合聚苯乙烯薄膜及聚苯乙烯复合材料热封胶等。

Description

一种聚苯乙烯用热封粘合剂及其制备方法
技术领域
 本发明涉及食品、药品泡罩包装用热封胶，具体涉及一种聚苯乙烯用热封粘合剂，本发明还涉及该粘合剂的一种制备方法。
背景技术
泡罩包装应用非常广泛，是近几年来发展最快的软包装材料。在药品包装中，它是将药品置于经吸塑成型的塑料硬片的泡罩内，再用一张涂有热封粘合剂的铝箔与该塑料硬片粘接热封合而成，从而使药品得到安全保护。
目前，泡罩包装成泡基材所用的材料绝大多数都是聚氯乙烯片材；而泡罩包装的覆盖材料基本上都是铝箔，通常称为PTP铝箔。PTP铝箔一般的结构为：保护层/（印刷层）/铝箔层/（印刷层）/粘合层。PTP铝箔中最基本的组成有保护层、铝箔层和粘合层。其中粘合层涂布用的热封粘合剂，一般称为VC剂，通常为氯乙烯-醋酸乙烯酯共聚物和一些增粘树脂的混合物。
随着包装形式的多样化，以及对包装材料中有机卤素含量日益严格的要求，越来越多的成泡基材受到大家的关注。其中聚苯乙烯（PS）材料已经在许多产品中得到应用，而传统的VC剂却不能封合聚苯乙烯材料。因此需要一种和聚苯乙烯材料配套使用的热封粘合剂。
发明内容
本发明要解决的技术问题就是针对现有技术的不足，提出了一种能够与聚苯乙烯材料热封的粘合剂，并提供了该聚苯乙烯用热封粘合剂的制备方法。
本发明要解决的技术问题是通过以下技术方案来实现的，一种聚苯乙烯用热封粘合剂，其特征在于，该粘合剂按以下重量百分比组成：
丙烯酸酯共聚树脂 10-25%；
氯乙烯共聚树脂 2-10%；
苯乙烯共聚树脂 2-10%；
混合溶剂 70-85%。
本发明要解决的技术问题还可以通过以下技术方案来进一步实现，所述的丙烯酸酯共聚树脂是一种甲基丙烯酸甲酯和丙烯酸正丁酯的自由基共聚物，其质均分子量Mw范围为50000-300000，其玻璃化转变温度Tg范围为40-70℃；
所述的氯乙烯共聚树脂是一种氯乙烯-醋酸乙烯酯-马来酸酐三元共聚树脂，其质均分子量Mw范围为50000-120000，其玻璃化转变温度Tg范围为70-80℃；
所述的苯乙烯共聚树脂是一种苯乙烯和马来酸酐的共聚物，其质均分子量Mw范围为50000-200000；
所述的混合溶剂为醋酸乙酯、醋酸正丙酯、丁酮的混合物；该混合溶剂中醋酸乙酯、醋酸正丙酯、丁酮的质量比为45%-55%：15%-25%：25%-30%；
本发明另一要解决的技术问题是通过以下技术方案来实现的，上述聚苯乙烯用热封粘合剂的具体制备方法，工艺步骤如下：
（1）将混合溶剂投入带有搅拌和冷凝回流的反应釜中，以800-1000r/min的转速充分搅拌；
（2）保持800-1000r/min转速继续搅拌，依次向反应釜中投入氯乙烯共聚树脂、苯乙烯共聚树脂、丙烯酸酯共聚树脂，并升温至45-60℃，保温持续搅拌2-2.5小时；
（3）冷却、过滤即得聚苯乙烯用热封粘合剂。
本发明与现有的技术相比，提供了一种可以与聚苯乙烯材料热封的粘合剂。该热封粘合剂所用原料的质均分子量范围和玻璃化转变温度范围提供了较高的热封粘合强度和宽泛的热封温度范围，各项指标均符合国家药品包装材料标准，而且本发明制备方法简单易行。本发明的热封粘合剂不仅适用于泡罩包装的热封胶，还适合聚苯乙烯薄膜及聚苯乙烯复合材料热封胶等。
具体实施方式
一种聚苯乙烯用热封粘合剂，该粘合剂按以下重量百分比组成：
丙烯酸酯共聚树脂 10-25%；
氯乙烯共聚树脂 2-10%；
苯乙烯共聚树脂 2-10%；
混合溶剂 70-85%。
所述的丙烯酸酯共聚树脂是一种甲基丙烯酸甲酯和丙烯酸正丁酯的自由基共聚物，其质均分子量Mw范围为50000-300000，其玻璃化转变温度Tg范围为40-70℃。
所述的氯乙烯共聚树脂是一种氯乙烯-醋酸乙烯酯-马来酸酐三元共聚树脂，其质均分子量Mw范围为50000-120000，其玻璃化转变温度Tg范围为70-80℃。
所述的苯乙烯共聚树脂是一种苯乙烯和马来酸酐的共聚物，其质均分子量Mw范围为50000-200000。
所述的混合溶剂为醋酸乙酯、醋酸正丙酯、丁酮的混合物；该混合溶剂中醋酸乙酯、醋酸正丙酯、丁酮的质量比为45%-55%：15%-25%：25%-30%。
上述聚苯乙烯用热封粘合剂的具体制备方法，工艺步骤如下：
（1）将混合溶剂投入带有搅拌和冷凝回流的反应釜中，以800-1000r/min的转速充分搅拌；
（2）保持800-1000r/min转速继续搅拌，依次向反应釜中投入氯乙烯共聚树脂、苯乙烯共聚树脂、丙烯酸酯共聚树脂，并升温至45-60℃，保温持续搅拌2-2.5小时；
（3）冷却、过滤即得聚苯乙烯用热封粘合剂。
以下通过具体的实施例进一步说明本发明的技术方案：
实施例1
一种聚苯乙烯用热封粘合剂，按以下质量分组成配料：
在容量为1L且带有加热套、温度计、冷凝器和机械搅拌装置的三口烧瓶中加入醋酸乙酯、醋酸正丙酯、丁酮的混合溶剂，开启搅拌；边搅拌边加入氯乙烯共聚树脂、苯乙烯共聚树脂、丙烯酸酯共聚树脂，并且升温至50℃，保持2小时；停止加热，边搅拌边冷却至室温，过滤后得到750g无色透明聚苯乙烯用热封粘合剂。
得到的聚苯乙烯用热封粘合剂涂布于0.02mm硬质铝箔上烘干后在热封仪上与聚苯乙烯片材热封（热封条件为0.2MPa、150℃、1s），测量其热封强度达到9.8N/15mm。
实施例2
一种聚苯乙烯用热封粘合剂，按以下质量分组成配料：
在容量为1吨的带有加热、回流冷凝器、机械搅拌的反应釜中加入醋酸乙酯、醋酸正丙酯、丁酮的混合溶剂，开启搅拌；边搅拌边加入氯乙烯共聚树脂、苯乙烯共聚树脂、丙烯酸酯共聚树脂，并且升温至50℃，保持2小时；停止加热，边搅拌边降温，冷至室温后，过滤可得到1000kg无色透明聚苯乙烯用热封粘合剂。
得到的聚苯乙烯用热封粘合剂，在铝箔印刷涂布机上涂布于0.02mm硬质铝箔上，干燥收卷，在泡罩包装机上与配套规格的的聚苯乙烯片材热封（包装机热封条件为0.4MPa、200℃、0.7s），测量其热封强度达到11N/15mm。
实施例3
一种聚苯乙烯用热封粘合剂，按以下质量分组成配料：
在容量为1吨的带有加热、回流冷凝器、机械搅拌的反应釜中加入醋酸乙酯、醋酸正丙酯、丁酮的混合溶剂，开启搅拌；边搅拌边加入氯乙烯共聚树脂、苯乙烯共聚树脂、丙烯酸酯共聚树脂，并且升温至50℃，保持2小时；停止加热，边搅拌边降温，冷至室温后，过滤可得到1000kg无色透明聚苯乙烯用热封粘合剂。
得到的聚苯乙烯用热封粘合剂，在印刷涂布机上涂布于0.037mm软质铝箔上，干燥收卷，在热封仪上与聚苯乙烯薄膜（热封条件为0.2MPa、130℃、1s），测量其热封强度达到8.5N/15mm。

Claims (4)

1.一种聚苯乙烯用热封粘合剂，其特征在于，该粘合剂按以下重量百分比组成：
丙烯酸酯共聚树脂10-25％；
氯乙烯共聚树脂2-10％；
苯乙烯共聚树脂2-10％；
混合溶剂70-85％；
所述的丙烯酸酯共聚树脂是一种甲基丙烯酸甲酯和丙烯酸正丁酯的自由基共聚物，其质均分子量Mw范围为50000-300000，其玻璃化转变温度Tg范围为40-70℃；
所述的氯乙烯共聚树脂是一种氯乙烯-醋酸乙烯酯-马来酸酐三元共聚树脂，其质均分子量Mw范围为50000-120000，其玻璃化转变温度Tg范围为70-80℃；
所述的苯乙烯共聚树脂是一种苯乙烯和马来酸酐的共聚物，其质均分子量Mw范围为50000-200000。
2.根据权利要求1所述的聚苯乙烯用热封粘合剂，其特征在于，所述的混合溶剂为醋酸乙酯、醋酸正丙酯、丁酮的混合物。
3.根据权利要求2所述的聚苯乙烯用热封粘合剂，其特征在于，所述的混合溶剂中醋酸乙酯、醋酸正丙酯、丁酮的质量比为45％-55％：15％-25％：25％-30％。
4.权利要求1所述的聚苯乙烯用热封粘合剂的一种制备方法，其特征在于，按照如下工艺步骤进行：
(1)将混合溶剂投入带有搅拌和冷凝回流的反应釜中，以800-1000r/min的转速充分搅拌；
(2)保持800-1000r/min转速继续搅拌，依次向反应釜中投入氯乙烯共聚树脂、苯乙烯共聚树脂、丙烯酸酯共聚树脂，并升温至45-60℃，保温持续搅拌2-2.5小时；
(3)冷却、过滤即得聚苯乙烯用热封粘合剂。
CN201210526912.3A 2012-12-10 2012-12-10 一种聚苯乙烯用热封粘合剂及其制备方法 Active CN103045130B (zh)