CN102719140B - 用于水性防伪油墨的调墨油及用其制备的水性防伪油墨 - Google Patents
用于水性防伪油墨的调墨油及用其制备的水性防伪油墨 Download PDFInfo
- Publication number
- CN102719140B CN102719140B CN 201210192467 CN201210192467A CN102719140B CN 102719140 B CN102719140 B CN 102719140B CN 201210192467 CN201210192467 CN 201210192467 CN 201210192467 A CN201210192467 A CN 201210192467A CN 102719140 B CN102719140 B CN 102719140B
- Authority
- CN
- China
- Prior art keywords
- water
- linseed oil
- stand linseed
- propylene glycol
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种用于水性防伪油墨的调墨油及用其制备的水性防伪油墨。用于水性防伪油墨的调墨油,按重量计由以下组份组成:纯净水20-25份,水性聚氨酯树脂40-45份,丙二醇5-7份,水性成膜增塑剂3-5份,消泡剂0.2-0.5份,流平润湿剂0.5-1份,纳米碳酸钙20-25份,增稠剂CP-801 0.5-1份;将纯净水、水性聚氨酯树脂、丙二醇、成膜增塑剂、A34消泡剂、流平润湿剂放置到高速搅拌机中进行搅拌,边搅拌边加入纳米碳酸钙和增稠剂,加完后搅拌15分钟,直至完全搅拌均匀即可。本发明制得的水性防伪油墨具有在印刷过程中不易塞版、耐候性好、储存稳定性好的优点。
Description
技术领域
本发明属于油墨技术领域,更具体地说,涉及一种用于水性防伪油墨的调墨油及用其制备的水性防伪油墨。
技术背景
刮刮卡是指卡上的一种覆盖数字和字母密码等文字的涂层,因此刮刮卡也叫密码覆膜卡、帐户卡或记账密码卡。刮刮卡的品种很多,在市场上广泛使用的有有奖刮刮卡引、剥剥卡、充值卡、密码卡、消费券、积分卡等等。
现在市场上所使用的刮刮卡防伪油墨绝大多数是溶剂型的油墨,都是由有机溶剂(如:甲苯、二甲苯、环己酮、防白水等)、EVA树脂、填料、颜料、助剂等组成,它们都是易燃易爆的有毒化学品,在施工使用过程中有机溶剂都挥发到大气中,从而污染环境、危害人体健康。而且溶剂型刮刮卡油墨印刷后会随着时间延长而变得难刮,给生产商带来很大的风险。为此水性刮刮卡防伪油墨是我们要研究的方向,因为水性材料用于配制刮刮卡防伪油墨有如下几个优点:1、环保、安全、气味低;2、成膜遮盖好,抗磨而又易刮;3、印刷后不会随着放置时间延长而变得难刮除;需要解决的问题:1、水性刮刮卡防伪油墨在印刷过程中易塞网版;2、耐候性差;3、储存稳定性差。
发明内容
本发明的目的在于提供用于水性防伪油墨的调墨油,有效解决水性防伪油墨在印刷过程中易塞版、耐候性差、储存稳定性差。
用于水性防伪油墨的调墨油,其特征在于,按重量计由以下组份组成:
纯净水20-25份
水性聚氨酯树脂40-45份
丙二醇5-7份
水性成膜增塑剂3-5份
消泡剂0.2-0.5份
流平润湿剂0.5-1份
纳米碳酸钙20-25份
增稠剂CP-801 0.5-1份;
将纯净水、水性聚氨酯树脂、丙二醇、成膜增塑剂、A34消泡剂、流平润湿剂放置到高速搅拌机中进行搅拌,边搅拌边加入纳米碳酸钙和增稠剂,加完后搅拌15分钟,直至完全搅拌均匀即可。
应用如上述所述的调墨油制备水性防伪银墨,其特征在于,按重量计由以下组份组成:丙二醇6-10份,806蜡浆1-3份,水性银粉12-15份,调墨油75-80份,将丙二醇、806蜡浆、水性银粉加入搅拌机缓慢搅拌,使之充分润湿均匀;搅拌均匀后加入调墨油,然后继续缓慢搅拌,直至完全搅拌均匀即可包装。
应用如上述所述的调墨油制备水性防伪金墨,其特征在于,按重量计由以下组份组成:丙二醇7-10份,806蜡浆1-3份,水性金粉12-15份,调墨油75-80份,将丙二醇、806蜡浆、水性银粉加入搅拌机缓慢搅拌,使之充分润湿均匀;搅拌均匀后加入调墨油,然后继续缓慢搅拌,直至完全搅拌均匀即可包装。
应用如上述所述的调墨油制备水性防伪色墨,其特征在于,按重量计由以下组份组成:调墨油75-80份,水性色浆25-20份,将调墨油和水性色浆加入搅拌机搅拌均匀,搅拌均匀后用三辊机研磨一遍后包装。
与现有技术相比,本发明具有如下优点:
1、水性聚氨酯树脂柔韧性非常好,该树脂对颜料的分散包裹能力强,不易结皮,回溶还原性好,从而解决易塞网版的难题;
2、加入水性成膜增塑剂,可以改变丙烯酸和聚氨酯的玻璃化温度和成膜温度,可根据不同气候去调整油墨的耐候性能。
3、选用增稠剂CP-801,为缔合型碱溶性增稠剂,使油墨增稠后处于长期稳定的粘度范围内,对储存稳定性有良好的效果。
4、由于丙二醇具有吸湿、防腐性能,对印刷过程中防止易塞网和储存稳定性起到很大作用。
本发明制备的水性防伪油墨达到如下标准:细度为10-50微米;粘度为日本理音粘度计30-50单位帕斯卡/秒;PH值为8.0±0.5;固含量为25-40%。
具体实施方式
下面通过实施例对本发明作进一步的详述,所述实施例仅用于说明本发明技术方案,并不构成对本发明保护范围的限定。
以下各实施例中,水性聚氨酯树脂AMD-F206由山东奥德美高分子材料有限公司提供;水性成膜增塑剂ELOP由广州芯联化工贸易有限公司提供;A34消泡剂由深圳海川化工提供;纳米碳酸钙NPCC-103由芮城华纳纳米材料有限公司提供;流平润湿剂104E美国气体公司生产;增稠剂CP-801广州卓厚化工科技有限公司提供;800目水性金、银粉由深圳市庄彩科技有限公司提供;水性色浆由珠海吉力化工有限公司提供;806蜡浆由佛山翁开尔贸易有限公司提供。
实施例:
第一步、配制调墨油
在搅拌缸内加入纯净水20-25份,水性聚氨酯树脂40-45份,丙二醇5-7份,水性成膜增塑剂3-5份,A34消泡剂0.2-0.5份,流平润湿剂0.5-1份,加好后将物料放置到高速搅拌机中进行搅拌,在搅拌过程中边搅边加入纳米碳酸钙20-25份,增稠剂0.5-1份(投料时的转速500-1500r/min),加完后搅拌15分钟,直至完全搅拌均匀即可。
第二步、调配各种效果的水性刮刮防伪油墨
1、水性刮刮银墨
在搅拌缸内加入丙二醇6-10份,806蜡浆1-3份,水性银粉12-15份,加好后将物料放置到搅拌机缓慢搅拌,使之充分润湿均匀;搅拌均匀后加入调墨油75-80份,加入后续继用搅拌机缓慢搅拌(转速500r/min),直至完全搅拌均匀即可包装。
2、水性刮刮金墨
在搅拌缸内加入丙二醇7-10份,806蜡浆1-3份,水性金粉12-15份,加好后将物料放置到搅拌机缓慢搅拌,使之充分润湿均匀;搅拌均匀后加入调墨油75-80份,加入后续继用搅拌机缓慢搅拌(转速500r/min),直至完全搅拌均匀即可包装。
3、水性刮刮色墨(包括各种颜色都是同样实施方法)
在搅拌缸内加入调墨油75-80份,水性色浆25-20份,加入后用搅拌机搅拌均匀(转速500-1000r/min),搅拌均匀后用三辊机研磨一遍后包装。
上述实施例经检测,均符合以下标准:
细度:10-50微米;
粘度:日本理音粘度计30-50单位帕斯卡/秒
PH值:8.0±0.5;
固含量:25-40%。
Claims (4)
1.用于水性防伪油墨的调墨油,其特征在于,按重量计由以下组份组成:
纯净水20-25份
水性聚氨酯树脂40-45份
丙二醇5-7份
水性成膜增塑剂3-5份
消泡剂0.2-0.5份
流平润湿剂0.5-1份
纳米碳酸钙20-25份
增稠剂CP-801 0.5-1份;
将纯净水、水性聚氨酯树脂、丙二醇、水性成膜增塑剂、消泡剂、流平润湿剂放置到高速搅拌机中进行搅拌,边搅拌边加入纳米碳酸钙和增稠剂,加完后搅拌15分钟,直至完全搅拌均匀即可。
2.应用如权利要求1所述的调墨油制备的水性防伪银墨,其特征在于,按重量计由以下组份组成:丙二醇6-10份,806蜡浆1-3份,水性银粉12-15份,调墨油75-80份,将丙二醇、806蜡浆、水性银粉加入搅拌机缓慢搅拌,使之充分润湿均匀;搅拌均匀后加入调墨油,然后继续缓慢搅拌,直至完全搅拌均匀即可包装。
3.应用如权利要求1所述的调墨油制备的水性防伪金墨,其特征在于,按重量计由以下组份组成:丙二醇7-10份,806蜡浆1-3份,水性金粉12-15份,调墨油75-80份,将丙二醇、806蜡浆、水性银粉加入搅拌机缓慢搅拌,使之充分润湿均匀;搅拌均匀后加入调墨油,然后继续缓慢搅拌,直至完全搅拌均匀即可包装。
4.应用如权利要求1所述的调墨油制备的水性防伪色墨,其特征在于,按重量计由以下组份组成:调墨油75-80份,水性色浆25-20份,将调墨油和水性色浆加入搅拌机搅拌均匀,搅拌均匀后用三辊机研磨一遍后包装。