CN113429155B - 一种抗发花真石漆及其制备方法 - Google Patents
一种抗发花真石漆及其制备方法 Download PDFInfo
- Publication number
- CN113429155B CN113429155B CN202110871464.XA CN202110871464A CN113429155B CN 113429155 B CN113429155 B CN 113429155B CN 202110871464 A CN202110871464 A CN 202110871464A CN 113429155 B CN113429155 B CN 113429155B
- Authority
- CN
- China
- Prior art keywords
- parts
- blooming
- real stone
- stone paint
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种抗发花真石漆及其制备方法，主要由以下组分按照以下质量份数比制备而成：水78.5‑83.2份、羟乙基纤维素0.5‑1份、水性改性聚酰胺蜡0.8‑1.5份、纳米锂基硅酸盐1‑2份、多功能助剂1‑2份、抗冻融稳定剂2‑3份、成膜助剂6‑7份、消泡剂0.5‑1份、聚丙烯酸酯乳液150‑170份、增稠剂1‑2份、硅藻土1‑2份、杀菌防腐剂1‑2份和天然彩色石英砂730‑750份。本发明的抗发花真石漆雾化性能好，所形成的漆膜遮盖力好、光泽较低、质感均匀，不容易发花。
Description
技术领域
本发明涉及涂料领域，具体涉及一种抗发花真石漆及其制备方法。
背景技术
真石漆主要采用丙烯酸聚合物为粘结剂，以颜色各异的天然彩砂为主要骨料成分，并配以各类助剂加工制成的厚浆型涂料，能将天然石材自然、稳重和气派等特性表现得淋漓尽致，适用于装饰各类建筑物内外墙，因而目前市场上被广泛使用。
但目前市场真石漆由于喷涂雾化性能差、光泽偏高、漆膜遮盖力差，在施工过程中会经常遇到发花的通病，不但影响美观，而且处理发花问题都是对人工、材料和资源的浪费，因此需要发明一种可以解决发花问题的真石漆。
发明内容
本发明提供一种抗发花真石漆及其制备方法，本发明的抗发花真石漆雾化性能好，所形成的漆膜遮盖力好、光泽较低、质感均匀，不容易发花。
本发明通过以下技术方案实现：
一种抗发花真石漆，主要由以下组分按照以下质量份数比制备而成：
水78.5-83.2份、羟乙基纤维素0.5-1份、水性改性聚酰胺蜡0.8-1.5份、纳米锂基硅酸盐1-2份、多功能助剂1-2份、抗冻融稳定剂2-3份、成膜助剂6-7份、消泡剂0.5-1份、聚丙烯酸酯乳液150-170份、增稠剂1-2份、硅藻土1-2份、杀菌防腐剂1-2份和天然彩色石英砂730-750份。
进一步地，所述的水性改性聚酰胺蜡为艾伯塔化学生产的E505。它具有改善砂粒间表面张力，提高漆膜内聚力，并提高喷涂雾化性和初粘性，使漆膜更致密，遮盖力更好，呈现粗砂浮现、细砂沉底的效果。
进一步地，所述的纳米锂基硅酸盐为瓦尼迈阿密V-448。它的纯度在95-99％之间，具有防沉、增稠、触变、提高雾化等功能。提高触变性，改善施工雾化性能，使漆膜更均匀，质感更好。
进一步地，所述的聚丙烯酸酯乳液为陶氏化学的TX-100纯丙烯酸酯乳液。
进一步地，所述的石英砂的粒度在10-200目之间，其中SiO2含量在90-99％之间且Fe2O3含量在0.06-0.02％之间。它是由南召嘉诚矿业所生产。
进一步地，所述的羟乙基纤维素为亚什兰的HBR250。2％水溶液粘度在25000-50000CP之间。
进一步地，所述的杀菌防腐剂为索尔生产的MBS。由MIT和BIT复配的不含甲醛、溶剂及有机卤素的长效杀菌防腐剂。
进一步地，所述的成膜助剂是伊士曼TEXANOL。它具有优异的水解稳定性、聚结效率高、挥发率适中、凝固点低，可有效降低涂料的最低成膜温度和改善涂料中颜料的稳定性和均匀性，也可软化乳液粒子并使其粘结在一起，并提升漆膜的耐擦洗性和耐候性。
进一步地，所述的多功能助剂为陶氏AMP-95。具有调节PH值、分散、润湿作用。
进一步地，所述的消泡剂为罗地亚的F5800C。
进一步地，所述的抗冻融稳定剂是罗地亚生产的FT-100。它是一种零VOC、不含APE环保类型助剂，可调高涂料冻融稳定性、光泽、耐沾污性的作用。
进一步地，所述的硅藻土是日本昭和的RADIOLITE F。它不仅能吸附有害物质，而且能降低光泽，改善由于真石漆光泽太高，墙体不平造成的侧光发花。
进一步地，所述增稠剂是陶氏RM-8W聚氨酯增稠剂。
一种抗发花真石漆的制备方法，具体步骤如下：
将78.5-83.2份水放入分散机中，然后在转速为1000-1200转/分钟下加入羟乙基纤维素0.5-1份、水性改性聚酰胺蜡0.8-1.5份、纳米锂基硅酸盐1-2份和硅藻土1-2份，搅拌3-5分钟；
然后在转速为500-800转/分钟下加入1-2份多功能助剂和0.5-1份消泡剂，搅拌2-3分钟；
然后在转速调为1000-1200转/分钟下加入150-170份聚丙烯酸酯乳液，搅拌2-3分钟，接着加入2-3份抗冻融稳定剂、6-7份成膜助剂和1-2份增稠剂，搅拌2-3分钟，再加入1-2份杀菌防腐剂，搅拌2-3分钟；
最后在转速为300-500转/分钟下加入天然彩色石英砂730-750份，搅拌均匀即可制得抗发花真石漆。
与现有技术相比，本发明具有如下优点：
本发明使用水性改性聚酰胺蜡具有改善砂粒间表面张力，提高漆膜内聚力，并提高喷涂雾化性和初粘性，使漆膜更致密，遮盖力更好，呈现粗砂浮现、细砂沉底的效果；
本发明使用纳米锂基硅酸盐是一种无机硅酸盐矿提纯而成的无机矿物质，纯度95-99％，2％水溶液粘度为20000-25000CP，由于其有很好的触变性，在施工时可以使真石漆很好的雾化，所以形成的漆膜更均匀，质感更强，更不容易发花；
硅藻土不仅具有很强的吸附性，还可有效降低真石漆光泽，防止由于墙体不平造成的侧光发花。
具体实施方式
下面结合具体实施方式对本发明进一步阐述
本发明中，表示原料含量的单位均基于质量份计，单位为千克，除非另外说明。
另外，作为本发明中的其它原材料均指本领域内通常使用的原材料。
下面通过本发明的优选实例来进一步说明本发明，需要说明的是，下述实例仅为说明目的，并非意欲限定本发明。
实施例1
将水放入分散机中，然后在转速为1000转/分钟下加入羟乙基纤维素、水性改性聚酰胺蜡、纳米锂基硅酸盐和硅藻土，搅拌5分钟；
然后在转速为500转/分钟下加入多功能助剂和消泡剂，搅拌3分钟；
然后在转速调为1000转/分钟下加入聚丙烯酸酯乳液，搅拌3分钟，接着加入抗冻融稳定剂、成膜助剂和增稠剂，搅拌3分钟，再加入杀菌防腐剂，搅拌3分钟；
最后在转速为400转/分钟下加入天然彩色石英砂，搅拌均匀即可制得抗发花真石漆。
实施例2
将水放入分散机中，然后在转速为1200转/分钟下加入羟乙基纤维素、水性改性聚酰胺蜡、纳米锂基硅酸盐和硅藻土，搅拌3分钟；
然后在转速为800转/分钟下加入多功能助剂和消泡剂，搅拌2分钟；
然后在转速调为1200转/分钟下加入聚丙烯酸酯乳液，搅拌2分钟，接着加入抗冻融稳定剂、成膜助剂和增稠剂，搅拌2分钟，再加入杀菌防腐剂，搅拌2分钟；
最后在转速为500转/分钟下加入天然彩色石英砂，搅拌均匀即可制得抗发花真石漆。
实施例3
将水放入分散机中，然后在转速为1100转/分钟下加入羟乙基纤维素、水性改性聚酰胺蜡、纳米锂基硅酸盐和硅藻土，搅拌4分钟；
然后在转速为600转/分钟下加入多功能助剂和消泡剂，搅拌2.5分钟；
然后在转速调为1100转/分钟下加入聚丙烯酸酯乳液，搅拌2.5分钟，接着加入抗冻融稳定剂、成膜助剂和增稠剂，搅拌2.5分钟，再加入杀菌防腐剂，搅拌2.5分钟；
最后在转速为300转/分钟下加入天然彩色石英砂，搅拌均匀即可制得抗发花真石漆。
上述三个实施性能测试结果如下：
与实施例1不同的是，对比例1有加水性改性聚酰胺蜡，没有加锂基硅酸盐和硅藻土；对比文件2加了锂基硅酸盐，没有加水性改性聚酰胺蜡和硅藻土，对比文件3加了硅藻土，没有加改性聚酰胺蜡和锂基硅酸盐，从结果上看对比例1-对比例3均耐沾污性、施工性不佳和光泽度较高；说明只加其中的一种不能达到较好的耐沾污性、施工性和光泽度；如果三种物质都不加或者加其中的任意两种也不能达到较好的耐沾污性、施工性和光泽度。
以上所述仅为本发明的较佳实施例，凡依本发明申请专利范围所做的均等变化与修饰，皆应属本发明的涵盖范围。
Claims (10)
1.一种抗发花真石漆，其特征在于：主要由以下组分按照以下质量份数比制备而成：
水78.5-83.2份、羟乙基纤维素0.5-1份、水性改性聚酰胺蜡0.8-1.5份、纳米锂基硅酸盐1-2份、陶氏AMP-95 1-2份、抗冻融稳定剂2-3份、成膜助剂6-7份、消泡剂0.5-1份、聚丙烯酸酯乳液150-170份、增稠剂1-2份、硅藻土1-2份、杀菌防腐剂1-2份和天然彩色石英砂730-750份。
2.根据权利要求1所述的一种抗发花真石漆，其特征在于：所述的水性改性聚酰胺蜡为艾伯塔化学E505。
3.根据权利要求1所述的一种抗发花真石漆，其特征在于：所述的纳米锂基硅酸盐为瓦尼迈阿密V-448。
4.根据权利要求1所述的一种抗发花真石漆，其特征在于：所述的聚丙烯酸酯乳液为陶氏化学的TX-100纯丙烯酸酯乳液。
5.根据权利要求1所述的一种抗发花真石漆，其特征在于：所述的石英砂的粒度在10-200目之间，其中SiO2含量在90-99％之间且Fe2O3含量在0.06-0.02％之间。
6.根据权利要求1所述的一种抗发花真石漆，其特征在于：所述的羟乙基纤维素为亚什兰的HBR250。
7.根据权利要求1所述的一种抗发花真石漆，其特征在于：所述的杀菌防腐剂为索尔的MBS。
8.根据权利要求1所述的一种抗发花真石漆，其特征在于：所述的成膜助剂是伊士曼TEXANOL；所述的消泡剂为罗地亚的F5800C；所述的抗冻融稳定剂是罗地亚生产的FT-100；所述增稠剂是陶氏RM-8W聚氨酯增稠剂。
9.根据权利要求1所述的一种抗发花真石漆，其特征在于：所述的硅藻土是日本昭和的RADIOLITE F。
10.一种制备权利要求1-9中任意一项所述的一种抗发花真石漆的制备方法，具体步骤如下：
将78.5-83.2份水放入分散机中，然后在转速为1000-1200转/分钟下加入羟乙基纤维素0.5-1份、水性改性聚酰胺蜡0.8-1.5份、纳米锂基硅酸盐1-2份和硅藻土1-2份，搅拌3-5分钟；
然后在转速为500-800转/分钟下加入1-2份多功能助剂和0.5-1份消泡剂，搅拌2-3分钟；
然后在转速调为1000-1200转/分钟下加入150-170份聚丙烯酸酯乳液，搅拌2-3分钟，接着加入2-3份抗冻融稳定剂、6-7份成膜助剂和1-2份增稠剂，搅拌2-3分钟，再加入1-2份杀菌防腐剂，搅拌2-3分钟；
最后在转速为300-500转/分钟下加入天然彩色石英砂730-750份，搅拌均匀即制得抗发花真石漆。