CN102719091B - 导电的无卤阻燃pa/pe合金材料 - Google Patents
导电的无卤阻燃pa/pe合金材料 Download PDFInfo
- Publication number
- CN102719091B CN102719091B CN2012101989021A CN201210198902A CN102719091B CN 102719091 B CN102719091 B CN 102719091B CN 2012101989021 A CN2012101989021 A CN 2012101989021A CN 201210198902 A CN201210198902 A CN 201210198902A CN 102719091 B CN102719091 B CN 102719091B
- Authority
- CN
- China
- Prior art keywords
- parts
- alloy material
- halogen
- conductive
- polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种导电的无卤阻燃的PA/PE合金材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：尼龙6树脂180～200份；聚乙烯树脂55～70份；偶联剂1.5～3.2份；金属氧化物20～30份；固体磷酸盐40～55份；抗氧剂0.7～1.5份；导电碳纤维15～26份；玻璃纤维80～100份；表面改性剂1.2～2.0份。优点：不含有卤素而可体现安全性；拉伸强度大于140MPa，弯曲强度大于230MPa，悬臂梁缺口冲击强度大于25kj/m2，熔融指数大于24g/10min，阻燃性达到V-0（UL-94-3mm）；具有导电性而能消除静电。
Description
技术领域
本发明属于高分子材料技术领域，具体涉及一种导电的无卤阻燃PA/PE合金材料。
背景技术
向PA（尼龙）材料中添加含卤素类阻燃剂可使其体现人们期望的阻燃效果，但是含卤阻燃剂会导致材料燃烧时产生有毒有害气体或称烟雾，造成对围困于火灾环境中的人员的二次伤害。据统计，在火灾发生造成的伤亡人员中，前述的二次伤害的比例始终约占40%左右。因此开发无卤阻燃的PA材料具有积极意义，并且如果还能将该材料具有优异的强度和消静电效果，那么更会受到人们的青睐，为此本申请人作了积极而有益的探索，下面将要介绍的技术方案便是在这种背景下产生的。
发明内容
本发明的任务在于提供一种不含有卤素而藉以体现环保安全、有助于保障优异的物理机构强度、有利于具备消静电效果的导电的无卤阻燃的PA/PE合金材料。
本发明的任务是这样来完成的，一种导电的无卤阻燃的PA/PE合金材料，其是由以下重量份数的原料组成：
尼龙6树脂180～200份；
聚乙烯树脂55～70份；
偶联剂1.5～3.2份；
金属氧化物20～30份；
固体磷酸盐40～55份；
抗氧剂0.7～1.5份；
导电碳纤维15～26份；
玻璃纤维80～100份；
表面改性剂1.2～2.0份。
在本发明的一个实施例中，所述的尼龙6树脂为熔点在230℃的树脂。
在本发明的另一个实施例中，所述的聚乙烯树脂为中密度聚乙烯。
在本发明的又一个实施例中，所述的偶联剂为异丙基三乙氧基硅烷。
在本发明的再一个实施例中，所述的金属氧化物为经过表面处理的氢氧化铝。
在本发明的还有一个实施中，所述的固体磷酸盐为三聚氰胺尿酸盐。
在本发明的更而一个实施例中，所述的抗氧剂为四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯。
在本发明的进而一个实施例中，所述的导电剂碳纤维为纳米碳管。
在本发明的又更而一个实施例中，所述的玻璃纤维为长度为3mm的无碱短切玻璃纤维。
在本发明的又进而一个实施例中，所述的表面改性剂为单硬脂酸酰胺。
本发明提供的导电无卤阻燃PA/PE合金材料由于使用了固体磷酸盐，因此不含有卤素而可体现安全性；拉伸强度大于140MPa，弯曲强度大于230MPa,悬臂梁缺口冲击强度大于25kj/m2,熔融指数大于24g/10min，阻燃性达到V-0（UL-94-3mm）；具有导电性而能消除静电。
具体实施方式
实施例1：
按重量份数，熔点在230℃的树脂即尼龙6树脂（PA）180份，中密度聚乙烯树脂70份，偶联剂即异丙基三乙氧基硅烷2份，金属氧化物即经过表面处理的氢氧化铝20份，固体磷酸盐即三聚氰胺尿酸盐50份，抗氧剂即四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯0.7份，由纳米碳管充任的导电剂碳纤维20份，长度为3mm的无碱短切玻璃纤维90份和表面改性剂即单硬脂酸酰胺1.2份。
实施例2：
按重量份数，熔点在230℃的树脂即尼龙6树脂（PA）190份，中密度聚乙烯树脂55份，偶联剂即异丙基三乙氧基硅烷1.5份，金属氧化物即经过表面处理的氢氧化铝24份，固体磷酸盐即三聚氰胺尿酸盐40份，抗氧剂即四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯0.9份，由纳米碳管充任的导电剂碳纤维15份，长度为3mm的无碱短切玻璃纤维80份和表面改性剂即单硬脂酸酰胺1.6份。
实施例3：
按重量份数，熔点在230℃的树脂即尼龙6树脂（PA）200份，中密度聚乙烯树脂60份，偶联剂即异丙基三乙氧基硅烷2.5份，金属氧化物即经过表面处理的氢氧化铝27份，固体磷酸盐即三聚氰胺尿酸盐45份，抗氧剂即四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯1.5份，由纳米碳管充任的导电剂碳纤维20份，长度为3mm的无碱短切玻璃纤维95份和表面改性剂即单硬脂酸酰胺2份。
实施例4：
按重量份数，熔点在230℃的树脂即尼龙6树脂（PA）195份，中密度聚乙烯树脂65份，偶联剂即异丙基三乙氧基硅烷3.2份，金属氧化物即经过表面处理的氢氧化铝30份，固体磷酸盐即三聚氰胺尿酸盐55份，抗氧剂即四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯1份，由纳米碳管充任的导电剂碳纤维26份，长度为3mm的无碱短切玻璃纤维100份和表面改性剂即单硬脂酸酰胺1.8份。
由上述实施例1至4得到的导电的无卤阻燃繁荣PA/PE合金材料经测试具有下表所示的技术效果：
Claims (1)
1.一种导电的无卤阻燃的PA/PE合金材料，其特征在于其是由以下重量份数的原料组成：
尼龙6树脂 180～200份；聚乙烯树脂 55～70份；偶联剂 1.5～3.2份；金属氧化物 20～30份；固体磷酸盐 40～55份；抗氧剂 0.7～1.5份；导电碳纤维 15～26份；
玻璃纤维 80～100份；表面改性剂 1.2～2.0份，所述的尼龙6树脂为熔点在230℃的树脂，所述的聚乙烯树脂为中密度聚乙烯，所述的偶联剂为异丙基三乙氧基硅烷，所述的金属氧化物为经过表面处理的氢氧化铝，所述的固体磷酸盐为三聚氰胺尿酸盐，所述的抗氧剂为四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯，所述的导电剂碳纤维为纳米碳管，所述的玻璃纤维为长度为3mm的无碱短切玻璃纤维，所述的表面改性剂为单硬脂酸酰胺。