CN102718936A - 聚氨酯泡沫塑料 - Google Patents
聚氨酯泡沫塑料 Download PDFInfo
- Publication number
- CN102718936A CN102718936A CN2012102169759A CN201210216975A CN102718936A CN 102718936 A CN102718936 A CN 102718936A CN 2012102169759 A CN2012102169759 A CN 2012102169759A CN 201210216975 A CN201210216975 A CN 201210216975A CN 102718936 A CN102718936 A CN 102718936A
- Authority
- CN
- China
- Prior art keywords
- parts
- urethane foam
- foamed plastic
- urethane foamed
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种聚氨酯泡沫塑料,所述的聚氨酯泡沫塑料,由如下重量份数的原料制成:聚醚多元醇A 40~60;POP聚醚40~60;胺催化剂0.4~0.7;有机锡催化剂0.1~0.2;硅油0.4~0.8;去离子3;交联剂1~2;MDI 40~45;所述的聚醚多元醇A为DEP-330N。本发明的聚氨酯泡沫塑料,具有较好的硬度的同时提高了产品的柔韧度,具有优异的密度、压陷比及回弹率。
Description
技术领域
本发明涉及一种聚氨酯泡沫塑料。
背景技术
聚氨酯泡沫塑料是一种较好的原材料,应用于沙发、床垫、鞋材、高档家具等领域,在国民经济中发挥越来越重要的作用。但是目前市场上用POP所做产品硬度较好但柔韧度较差,在特殊行业达不到要求。
发明内容
本发明的目的是提供一种聚氨酯泡沫塑料,该塑料具有较好硬度的同时提高了产品的柔韧度,具有优异的密度、压陷比及回弹率。
本发明所述的聚氨酯泡沫塑料,由如下重量份数的原料制成:
其中:
所述的聚醚多元醇A优选DEP-330N,德信联邦化学工业有限公司生产。
所述的POP聚醚优选3628T,德信联邦化学工业有限公司生产。
所述的胺催化剂优选美国气体A-33。
所述的有机锡催化剂优选二月桂酸二丁基锡。
所述的硅油优选迈图L-3150。
所述的聚氨酯交联剂优选BMN-300,德信联邦化学工业有限公司的产品。
所述的MDI优选改性MDI 2158,烟台合力的产品;MDI的名称为4,4′-二苯基甲烷二异氰酸。
本发明具有的有益效果如下:
本发明的聚氨酯泡沫塑料,具有较好硬度的同时提高了产品的柔韧度,具有优异的密度、压陷比及回弹率。
具体实施方式
以下结合实施例对本发明做进一步描述。
实施例1:
本发明所述的聚氨酯泡沫塑料,由如下重量份数的原料制成:
实施例2:
本发明所述的聚氨酯泡沫塑料,由如下重量份数的原料制成:
实施例3:
本发明所述的聚氨酯泡沫塑料,由如下重量份数的原料制成:
实施例1~3所得泡沫塑料具有以下指标,如下表1所示:
表1实施例1~3所得泡沫塑料性能表
项目 | 实施例1 | 实施例2 | 实施例3 |
密度 | 40 | 40 | 40 |
压陷比 | 2.72 | 2.68 | 2.62 |
回弹率 | 72 | 69 | 65 |
由表1可知,制备的聚氨酯泡沫塑料的密度、压陷比及回弹率都说明了该聚氨酯泡沫塑料具有较好的柔韧度。
Claims (4)