CN102702720B - 高硬度pop聚醚及其应用 - Google Patents

高硬度pop聚醚及其应用 Download PDF

Info

Publication number
CN102702720B
CN102702720B CN201210217425.9A CN201210217425A CN102702720B CN 102702720 B CN102702720 B CN 102702720B CN 201210217425 A CN201210217425 A CN 201210217425A CN 102702720 B CN102702720 B CN 102702720B
Authority
CN
China
Prior art keywords
pop
hardness
polyether
polyethers
polyurethane foam
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210217425.9A
Other languages
English (en)
Other versions
CN102702720A (zh
Inventor
耿佃勇
荆晓东
王国强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zibo Dexin Lianbang Chemical Industry Co Ltd
Original Assignee
Zibo Dexin Lianbang Chemical Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zibo Dexin Lianbang Chemical Industry Co Ltd filed Critical Zibo Dexin Lianbang Chemical Industry Co Ltd
Priority to CN201210217425.9A priority Critical patent/CN102702720B/zh
Publication of CN102702720A publication Critical patent/CN102702720A/zh
Application granted granted Critical
Publication of CN102702720B publication Critical patent/CN102702720B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高硬度POP聚醚及其应用。本发明所述的高硬度POP聚醚，是在聚醚多元醇B中添加增硬剂混合均匀后制得，其中聚醚多元醇B为90~97重量份，增硬剂为3~10重量份，聚醚多元醇B为接枝聚醚POP-45。本发明的高硬度POP聚醚，配比合理，粘度适中，该高硬度POP聚醚硬度高，满足了其应用领域对POP产品的硬度需求。由此制备出的聚氨酯泡沫硬度高，可较大地提高泡沫硬度，可应用于沙发、床垫、鞋材、高档家具等相关领域。

Description

高硬度POP聚醚及其应用
技术领域
本发明涉及一种高硬度POP聚醚及其应用。 
背景技术
聚氨酯泡沫塑料是一种较好的原材料，应用于沙发、床垫、鞋材、高档家具等领域，在国民经济中发挥越来越重要的作用。但是现有POP产品在鞋材等要求硬度较高的特殊行业无法满足要求。 
发明内容
本发明的目的是提供一种高硬度POP聚醚及其应用，该高硬度POP聚醚硬度高，满足了其应用领域对POP产品的硬度需求。 
本发明所述的高硬度POP聚醚，是在聚醚多元醇B中添加增硬剂混合均匀后制得，其中聚醚多元醇B为90~97重量份，增硬剂为3~10重量份。 
所述的聚醚多元醇B为接枝聚醚POP-45，淄博德信联邦化学工业有限公司生产。 
所述的增硬剂为特制小分子醇，是由甘油和季戊四醇为起始剂，环氧丙烷开环聚合制得，甘油和季戊四醇的质量比为1:0.8~1.2，分子量为300。 
所述的高硬度POP聚醚的应用，是将高硬度POP聚醚作为组分制成聚氨酯泡沫，该聚氨酯泡沫由如下重量份的原料制成： 
A组分： 
Figure BDA00001821817100011
B组分： 
高硬度POP聚醚           60 
其中： 
所述的聚醚多元醇A为德信联邦化学工业有限公司聚醚DEP-560D。 
所述的胺催化剂A-33，为美国气体A-33。 
所述的有机锡催化剂T-12，为广州伟伯化工有限公司提供。 
所述的硅油优选迈图L-580。 
所述的TDI为甲苯二异氰酸酯，优选亨斯曼TDI-80。 
本发明的有益效果如下： 
本发明的高硬度POP聚醚，配比合理，粘度适中，该高硬度POP聚醚硬度高，满足了其应用领域对POP产品的硬度需求。由此制备出的聚氨酯泡沫硬度高，可较大地提高泡沫硬度，可应用于沙发、床垫、鞋材、高档家具等相关领域。 
具体实施方式
以下结合实施例对本发明做进一步描述。 
对比例1 
聚氨酯泡沫各组分以重量份数计： 
Figure BDA00001821817100021
按照以上配比，将各个原料进行混合生产即可制得聚氨酯泡沫。 
实施例1 
聚氨酯泡沫各组分以重量份数计： 
A组分： 
Figure BDA00001821817100022
B组分： 
高硬度POP聚醚       60 
按照以上配比，将各个原料进行混合生产即可制得聚氨酯泡沫，高硬度POP聚醚按照如下制备：聚醚多元醇POP-45为97重量份，增硬剂为3重量份。所述的增硬剂为特制小分子醇，是由甘油和季戊四醇为起始剂，环氧丙烷开环制得，甘油和季戊四醇的质量比为1:1，分子量为300。 
实施例2 
聚氨酯泡沫各组分以重量份数计： 
A组分： 
Figure BDA00001821817100031
B组分： 
高硬度POP聚醚          60 
按照以上配比，将各个原料进行混合生产即可制得聚氨酯泡沫，高硬度POP聚醚按照如下制备：聚醚多元醇POP-45为95重量份，增硬剂为5重量份。所述的增硬剂为特制小分子醇，是由甘油和季戊四醇为起始剂，环氧丙烷开环制得，甘油和季戊四醇的质量比为1:1，分子量为300。 
实施例3 
聚氨酯泡沫各组分以重量份数计： 
A组分： 
Figure BDA00001821817100032
B组分： 
高硬度POP聚醚       60 
按照以上配比，将各个原料进行混合生产即可制得聚氨酯泡沫，高硬度POP聚醚按照如 下制备：聚醚多元醇POP-45为90重量份，增硬剂为10重量份。所述的增硬剂为特制小分子醇，是由甘油和季戊四醇为起始剂，环氧丙烷开环制得，甘油和季戊四醇的质量比为1:1，分子量为300。 
对实施例1~3和对比例所得到的聚氨酯泡沫进行性能测试，如下表1所示： 
表1聚氨酯泡沫的性能表 。
   项目   对比例1   实施例1   实施例2   实施例3
   泡沫回弹率   30   29   27   25
   泡沫压陷比   2.2   2.4   2.5   2.62
   泡沫拉伸率   13.54   13.42   13.39   13.28

Claims (2)

1.一种高硬度POP聚醚，其特征在于在聚醚多元醇B中添加增硬剂混合均匀后制得，其中聚醚多元醇B为90～97重量份，增硬剂为3～10重量份，聚醚多元醇B为接枝聚醚POP-45，增硬剂为特制小分子醇，是由甘油和季戊四醇为起始剂，环氧丙烷开环聚合制得，甘油和季戊四醇的质量比为1:0.8～1.2，分子量为300。
2.一种权利要求1所述的高硬度POP聚醚的应用，其特征在于将高硬度POP聚醚作为组分制成聚氨酯泡沫，该聚氨酯泡沫由如下重量份的原料制成：
A组分：
Figure FDA0000428564400000011
CN201210217425.9A 2012-06-28 2012-06-28 高硬度pop聚醚及其应用 Active CN102702720B (zh)