CN102690131B - Manufacturing method of underglaze flashing K gold glazed brick - Google Patents
Manufacturing method of underglaze flashing K gold glazed brick Download PDFInfo
- Publication number
- CN102690131B CN102690131B CN 201210053580 CN201210053580A CN102690131B CN 102690131 B CN102690131 B CN 102690131B CN 201210053580 CN201210053580 CN 201210053580 CN 201210053580 A CN201210053580 A CN 201210053580A CN 102690131 B CN102690131 B CN 102690131B
- Authority
- CN
- China
- Prior art keywords
- brick
- glazed
- gold
- flash
- thrown
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a manufacturing method of an underglaze flashing K gold glazed brick, which comprises the following steps: wiping the surface of the bottom brick, and printing a pattern and a flashing material on the bottom brick with a printing machine; covering a fusion cake layer on the patterned brick; firing the printed brick covered with the fusion cake layer in a kiln at 960-990 DEG C for 80-100 minutes, so that the surface fusion cake is fused into a transparent vitreous body, the pattern colors under the fusion cake are displayed, and the flashing material has a flashing effect after the high-temperature firing; and plating platinum or gold on the fired product in a vacuum plating furnace, and polishing with a polishing machine. The method provided by the invention combines the unique effects of the K gold glazed brick and uses a material capable of generating a flashing effect after high-temperature firing, so that the product has elegance and magnificence of artwork, and is suitable for large area application in households and high-grade spaces.
Description
Technical field
The present invention relates to a kind of under glazed flash of light karat gold and throw the glazed brick making method, belong to the glazed brick manufacture technology field.
Background technology
The existing main raw as interior decoration of ceramic tile, through nearly twenties years development, manufacturing technology is advanced by leaps and bounds, and early stage product cannot be mentioned in the same breath.Particularly in recent years, along with the emergence of under glazed on market such as microlite, karat gold bricks, ceramic tile was more and more to high-end development.The present under glazed brick on the market is no matter be that it all is floral designs below the glaze layer, does not have the decorative effect that can glisten with what explained hereafter.
Summary of the invention
The objective of the invention is in order to solve the under glazed brick on the present market, no matter be with what explained hereafter, it all is floral designs below the glaze layer, does not have the problem of the decorative effect that can glisten, and then provides a kind of under glazed flash of light karat gold to throw the glazed brick making method.
The objective of the invention is to be achieved through the following technical solutions:
A kind of under glazed flash of light karat gold is thrown the glazed brick making method, and processing step is as follows: one, brick surface, the end is wiped clean, stamped pattern with printing machine at end brick, stamp simultaneously glittering material; Two, covering again frit layer on the brick of printed pattern; Three, the brick of printed flower and the upper frit layer of covering, under the kiln 960-990 ℃ condition, burnt till in 80～100 minutes after, the surface frit fuses into transparent vitreum, and the pattern color below the frit presents, and glittering material shows flash effect behind high-temperature firing simultaneously; Four, the product after burning till is after plating platinum or gold in the vacuum plating furnace, again through the polishing machine polishing, the frit on surface is thrown flat, polished and add lustre to wool wheel and the rare earth powder that adds lustre to again, make product surface after the polishing grinding present effect as the jade; Five, through obtaining final product after edging, sorting, the packing.
Beneficial effect of the present invention: method of the present invention is to combine to use a kind of material that can produce flash effect behind high-temperature firing after karat gold is thrown the effect unique of glazed brick again.The product of producing had both had the exquisite and magnificent of artwork, and the big area that is fit to again family and high-grade place is used, and belonged to pioneering in the industry, had filled up the market vacancy.
Description of drawings
Fig. 1 is the product synoptic diagram of stamp on end brick (pattern);
Fig. 2 is the product synoptic diagram at the frit layer that covers again different pattern on the brick of printed pattern;
Fig. 3 is printed flower and the product synoptic diagram that covers upper frit layer;
Fig. 4 is product synoptic diagram gold-plated, polishing;
Fig. 5 is through obtaining final final product synoptic diagram after the edging packing.
Embodiment
The present invention is described in further detail below in conjunction with accompanying drawing: present embodiment is implemented under take technical solution of the present invention as prerequisite, has provided detailed embodiment, but protection scope of the present invention is not limited to following embodiment.
Such as Fig. 1～shown in Figure 5, the related a kind of under glazed flash of light karat gold of present embodiment is thrown the glazed brick making method, and its processing step is: one, brick surface, the end is wiped clean, stamped the pattern of different colours and effect with printing machine at end brick, stamp simultaneously glittering material; Two, at the frit layer that covers again different pattern on the brick of printed pattern; Three, the brick of printed flower and the upper frit layer of covering, under the kiln 960-990 ℃ condition, burnt till in 80～100 minutes after, the surface frit fuses into transparent vitreum, and the pattern color below the frit presents, and glittering material shows flash effect behind high-temperature firing simultaneously; Four, the product after burning till is after plating platinum or gold in the vacuum plating furnace, again through the polishing machine polishing, throw the frit on surface flat, polish and add lustre to wool wheel and the rare earth powder that adds lustre to again, make polishing grinding product surface later present effect as the jade, simultaneously, flashlight powder shows special flash effect under the mapping of light; Five, through obtaining final final product after edging, sorting, the packing.
Described glittering material is by following chemical ingredients AL by weight
2O
3: 27.3%, SiO
2: 49.5%, Fe
2O
3: 3%, MgO:1.8%, K
2O:10.6%, Na
2O:1.5%, surplus SiO
2Form, make the oiliness stamp-pad ink and print loss on ignition:＜6.3%.
The material of described frit layer is by following chemical ingredients AL by weight
2O
3: 6.5%, Fe
2O
3: 0.07%, CaO:3.48%, MgO:0.43%, K
2O:2.32%, Na
2O:3.65%, TiO
2: 0.02%, B
2O
3: 11.95%, PbO:＜0.01%, ZnO:1.05%, ZrO
2:＜0.02%, BaO:4.30%, Li
2O:＜0.01%, surplus SiO
2Form loss on ignition:＜0.05%.(annotating: after frit layer is polished into particulate state with frit exactly, again by manually by 40 purpose silk screens it being covered on the brick face)
The temperature of described kiln is 975 ℃.
Described firing time is 90 minutes.
What under glazed flash of light karat gold of the present invention was thrown the glazed brick employing is the production technique of under glazed, stamp again simultaneously glittering material, by producing flash effect behind the high-temperature firing, carry out polishing grinding by abrasive disc and wool wheel, the powder that adds lustre to again, its surface is glittering and translucent, and meeting presents unique flash effect under the setting off of light.
Under glazed flash of light karat gold of the present invention is thrown glazed brick except unique flash effect is arranged, and Protean channel patterns can be made in its surface, has special stereoscopic sensation.
Under glazed flash of light karat gold of the present invention is thrown glazed brick and is also had unique gold and silver color effect.After product after burning till is gold-plated in vacuum plating furnace, polish off by the gold of polishing grinding with the surface, the gold thread that can not polish off in the groove has just formed various Protean gold thread patterns.
The present invention has also improved the intensity of throwing glazed brick, has increased its wear resistance and non-skid property.
The above; only be the better embodiment of the present invention; these embodiments all are based on the different implementations under the general idea of the present invention; and protection scope of the present invention is not limited to this; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; the variation that can expect easily or replacement all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain of claims.
Claims (4)
1. under glazed flash of light karat gold is thrown the glazed brick making method, it is characterized in that, and one, brick surface, the end is wiped clean, stamp pattern with printing machine at end brick, stamp simultaneously glittering material; Described glittering material is by following chemical ingredients AL by weight
2O
3: 27.3%, Fe
2O
3: 3%, MgO:1.8%, K
2O:10.6%, Na
2O:1.5%, surplus SiO
2Form; Two, covering again frit layer on the brick of printed pattern; Three, the brick of printed flower and the upper frit layer of covering, under the kiln 960-990 ℃ condition, burnt till in 80～100 minutes after, the surface frit fuses into transparent vitreum, and the pattern color below the frit presents, and glittering material shows flash effect behind high-temperature firing simultaneously; Four, the product after burning till is after plating platinum or gold in the vacuum plating furnace, again through the polishing machine polishing, the frit on surface is thrown flat, polished and add lustre to wool wheel and the rare earth powder that adds lustre to again, make product surface after the polishing grinding present effect as the jade; Five, through obtaining final product after edging, sorting, the packing.
2. under glazed according to claim 1 flash of light karat gold is thrown the glazed brick making method, it is characterized in that, the material of described frit layer is by following chemical ingredients AL by weight
2O
3: 6.5%, Fe
2O
3: 0.07%, CaO:3.48%, MgO:0.43%, K
2O:2.32%, Na
2O:3.65%, TiO
2: 0.02%, B
2O
3: 11.95%, PbO:＜0.01%, ZnO:1.05%, ZrO
2:＜0.02%, BaO:4.30%, Li
2O:＜0.01%, surplus SiO
2Form.
3. under glazed flash of light karat gold according to claim 1 is thrown the glazed brick making method, it is characterized in that the temperature of described kiln is 975 ℃.
4. under glazed flash of light karat gold according to claim 1 is thrown the glazed brick making method, it is characterized in that described firing time is 90 minutes.