CN102690131A - Manufacturing method of underglaze flashing K gold glazed brick - Google Patents
Manufacturing method of underglaze flashing K gold glazed brick Download PDFInfo
- Publication number
- CN102690131A CN102690131A CN2012100535801A CN201210053580A CN102690131A CN 102690131 A CN102690131 A CN 102690131A CN 2012100535801 A CN2012100535801 A CN 2012100535801A CN 201210053580 A CN201210053580 A CN 201210053580A CN 102690131 A CN102690131 A CN 102690131A
- Authority
- CN
- China
- Prior art keywords
- brick
- glazed
- gold
- flash
- thrown
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a manufacturing method of an underglaze flashing K gold glazed brick, which comprises the following steps: wiping the surface of the bottom brick, and printing a pattern and a flashing material on the bottom brick with a printing machine; covering a fusion cake layer on the patterned brick; firing the printed brick covered with the fusion cake layer in a kiln at 960-990 DEG C for 80-100 minutes, so that the surface fusion cake is fused into a transparent vitreous body, the pattern colors under the fusion cake are displayed, and the flashing material has a flashing effect after the high-temperature firing; and plating platinum or gold on the fired product in a vacuum plating furnace, and polishing with a polishing machine. The method provided by the invention combines the unique effects of the K gold glazed brick and uses a material capable of generating a flashing effect after high-temperature firing, so that the product has elegance and magnificence of artwork, and is suitable for large area application in households and high-grade spaces.
Description
Technical field
The present invention relates to a kind of under glazed flash of light karat gold and throw the glazed brick making method, belong to the glazed brick manufacture technology field.
Background technology
The existing main raw as interior decoration of ceramic tile, through nearly twenties years development, manufacturing technology has been advanced by leaps and bounds and early stage product cannot be mentioned in the same breath.Particularly in recent years, along with the emergence of under glazed on market such as microlite, karat gold bricks, ceramic tile was more and more to high-end development.Under glazed brick on the present market, no matter be to use what explained hereafter, it all is floral designs below the glaze layer, does not have the decorative effect that can glisten.
Summary of the invention
The objective of the invention is in order to solve the under glazed brick on the present market; Use any explained hereafter no matter be; It all is floral designs below the glaze layer, the problem of the decorative effect that does not have to glisten, and then provide a kind of under glazed flash of light karat gold to throw the glazed brick making method.
The objective of the invention is to realize through following technical scheme:
A kind of under glazed flash of light karat gold is thrown the glazed brick making method, and process step is following: one, brick surface, the end is wiped clean, on end brick, stamped pattern with printing machine, stamp glittering material simultaneously; Two, covering frit layer on the brick of printed pattern again; Three, the brick of frit layer is gone up in printed flower and covering; Under the kiln 960-990 ℃ condition, burnt till in 80～100 minutes after; The surface frit fuses into transparent vitreum, and the pattern color below the frit shows, and glittering material shows flash effect behind high-temperature firing simultaneously; Four, the product after burning till is after plating platinum or gold in the vacuum plating stove; Again through the polishing machine polishing; The frit on surface is thrown flat, polished and add lustre to wool wheel and the rare earth powder that adds lustre to again, make product surface after the polishing grinding demonstrate the effect as the jade; Five, through obtaining final product after edging, sorting, the packing.
Beneficial effect of the present invention: method of the present invention is to use a kind of material that behind high-temperature firing, can produce flash effect again after having combined karat gold to throw the effect unique of glazed brick.The product of producing had both had the exquisite and magnificent of artwork, and the big area that is fit to family and high-grade place is again used, and belonged to initiative in the industry, had filled up the market vacancy.
Description of drawings
Fig. 1 is the product synoptic diagram of stamp on end brick (pattern);
Fig. 2 is the product synoptic diagram at the frit layer that covers different pattern on the brick of printed pattern again;
Fig. 3 is printed flower and covers the product synoptic diagram of going up frit layer;
Fig. 4 is a product synoptic diagram gold-plated, polishing;
Fig. 5 is through obtaining final final product synoptic diagram after the edging packing.
Embodiment
To combine accompanying drawing that the present invention is done further detailed description below: present embodiment provided detailed embodiment, but protection scope of the present invention is not limited to following embodiment being to implement under the prerequisite with technical scheme of the present invention.
Like Fig. 1～shown in Figure 5, the related a kind of under glazed flash of light karat gold of present embodiment is thrown the glazed brick making method, and its process step is: one, brick surface, the end is wiped clean, on end brick, stamped the pattern of different colours and effect with printing machine, stamp glittering material simultaneously; Two, at the frit layer that covers different pattern on the brick of printed pattern again; Three, the brick of frit layer is gone up in printed flower and covering; Under the kiln 960-990 ℃ condition, burnt till in 80～100 minutes after; The surface frit fuses into transparent vitreum, and the pattern color below the frit shows, and glittering material shows flash effect behind high-temperature firing simultaneously; Four, the product after burning till is after plating platinum or gold in the vacuum plating stove; Again through the polishing machine polishing; The frit on surface is thrown flat, polished and add lustre to wool wheel and the rare earth powder that adds lustre to again, make product surface after the polishing grinding demonstrate the effect as the jade; Simultaneously, flashlight powder shows special flash effect under the mapping of light; Five, through obtaining final final product after edging, sorting, the packing.
Said glittering material is by following chemical ingredients AL by weight
2O
3: 27.3%, SiO
2: 49.5%, Fe
2O
3: 3%, MgO:1.8%, K
2O:10.6%, Na
2O:1.5%, surplus SiO
2Form, process the oiliness stamp-pad ink and print loss on ignition:＜6.3%.
The material of said frit layer is by following chemical ingredients AL by weight
2O
3: 6.5%, Fe
2O
3: 0.07%, CaO:3.48%, MgO:0.43%, K
2O:2.32%, Na
2O:3.65%, TiO
2: 0.02%, B
2O
3: 11.95%, PbO:＜0.01%, ZnO:1.05%, ZrO
2:＜0.02%, BaO:4.30%, Li
2O:＜0.01%, surplus SiO
2Form loss on ignition:＜0.05%.(annotate: frit layer is covered it on brick face through 40 purpose silk screens by manual work after exactly frit being polished into particulate state again)
The temperature of said kiln is 975 ℃.
Said firing time is 90 minutes.
What under glazed flash of light karat gold of the present invention was thrown the glazed brick employing is the production technique of under glazed; Stamp simultaneously glittering material again; Through producing flash effect behind the high-temperature firing; Carry out polishing grinding through abrasive disc and wool wheel, the powder that adds lustre to again, its surface is glittering and translucent, under the setting off of light, can demonstrate the flash effect of uniqueness.
Under glazed flash of light karat gold of the present invention is thrown glazed brick except unique flash effect is arranged, and Protean channel patterns can be made in its surface, has special stereoscopic sensation.
Under glazed flash of light karat gold of the present invention is thrown glazed brick and is also had unique gold and silver color effect.Product after burning till in the vacuum plating stove gold-plated after, polish off through the gold of polishing grinding the surface, the gold thread that can not polish off in the groove has just formed various Protean gold thread patterns.
The present invention has also improved the intensity of throwing glazed brick, has increased its wear resistance and non-skid property.
The above; Be merely the preferable embodiment of the present invention; These embodiments all are based on the different implementations under the general idea of the present invention, and protection scope of the present invention is not limited thereto, and any technician who is familiar with the present technique field is in the technical scope that the present invention discloses; The variation that can expect easily or replacement all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain of claims.
Claims (5)
1. under glazed flash of light karat gold is thrown the glazed brick making method, it is characterized in that, and one, brick surface, the end is wiped clean, on end brick, stamp pattern with printing machine, stamp glittering material simultaneously; Two, covering frit layer on the brick of printed pattern again; Three, the brick of frit layer is gone up in printed flower and covering; Under the kiln 960-990 ℃ condition, burnt till in 80～100 minutes after; The surface frit fuses into transparent vitreum, and the pattern color below the frit shows, and glittering material shows flash effect behind high-temperature firing simultaneously; Four, the product after burning till is after plating platinum or gold in the vacuum plating stove; Again through the polishing machine polishing; The frit on surface is thrown flat, polished and add lustre to wool wheel and the rare earth powder that adds lustre to again, make product surface after the polishing grinding demonstrate the effect as the jade; Five, through obtaining final product after edging, sorting, the packing.
2. under glazed according to claim 1 flash of light karat gold is thrown the glazed brick making method, it is characterized in that, said glittering material is by following chemical ingredients AL by weight
2O
3: 27.3%, Fe
2O
3: 3%, MgO:1.8%, K
2O:10.6%, Na
2O:1.5%, surplus SiO
2Form.
3. under glazed according to claim 1 flash of light karat gold is thrown the glazed brick making method, it is characterized in that, the material of said frit layer is by following chemical ingredients AL by weight
2O
3: 6.5%, Fe
2O
3: 0.07%, CaO:3.48%, MgO:0.43%, K
2O:2.32%, Na
2O:3.65%, TiO
2: 0.02%, B
2O
3: 11.95%, PbO:＜0.01%, ZnO:1.05%, ZrO
2:＜0.02%, BaO:4.30%, Li
2O:＜0.01%, surplus SiO
2Form.
4. under glazed flash of light karat gold according to claim 1 is thrown the glazed brick making method, it is characterized in that the temperature of said kiln is 975 ℃.
5. under glazed flash of light karat gold according to claim 1 is thrown the glazed brick making method, it is characterized in that said firing time is 90 minutes.