CN102040399A - Method for manufacturing three-dimensional artistic glazed brick - Google Patents

Method for manufacturing three-dimensional artistic glazed brick Download PDF

Info

Publication number
CN102040399A
CN102040399A CN200910193083XA CN200910193083A CN102040399A CN 102040399 A CN102040399 A CN 102040399A CN 200910193083X A CN200910193083X A CN 200910193083XA CN 200910193083 A CN200910193083 A CN 200910193083A CN 102040399 A CN102040399 A CN 102040399A
Authority
CN
China
Prior art keywords
brick
patterns
frit
pattern
frit layer
Prior art date
Application number
CN200910193083XA
Other languages
Chinese (zh)
Inventor
章云树
Original Assignee
章云树
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 章云树 filed Critical 章云树
Priority to CN200910193083XA priority Critical patent/CN102040399A/en
Publication of CN102040399A publication Critical patent/CN102040399A/en

Abstract

The invention discloses a method for manufacturing a three-dimensional artistic glazed brick, which comprises the following processes of: 1) selecting a white finished brick blank as a bottom brick; 2) designing various different patterns as required, and manufacturing the patterns into a silk screen for printing; 3) wiping the surface of the bottom brick, and printing patterns of different colors and patterns on the bottom brick by using an automatic printer; 4) covering a fusion cake layer of different patterns on the bottom brick printed with different colors and patterns; 5) sintering the bottom brick covered with the fusion cake layer in a kiln; 6) polishing the sintered brick through a polisher; and 7) obtaining a final product after sorting and packing. The surface of the product obtained by using the manufacturing method becomes crystal clear, the colors below the fusion cake layer are clear and rich, the whole product has strong third dimension, and dirt absorbing problem of many polished bricks is avoided.

Description

Three-dimensional art is thrown the glaze brick producing process
Technical field
What the present invention relates to is that a kind of three-dimensional art is thrown the glaze brick producing process.
Background technology
City's ceramic tile has now become the main raw of house decoration, and through nearly twenties years development, the manufacturing technology of ceramic tile has been advanced by leaps and bounds and early stage product cannot be mentioned in the same breath.But the ceramic tile product on the market, though more and more abundanter on the decoration of surface effect, do not have all the time a kind of promptly have artistic charm, again can widely used mannerism product.
Summary of the invention
The technical issues that need to address of the present invention provide a kind of three-dimensional art and throw the glaze brick producing process, this kind three-dimensional art is thrown the product that the glaze brick producing process is produced, its concave-convex surface causes, high bright and clean, high brightness, the tectum above the pattern resemble transparent limpid as the crystal, promptly have the exquisite and magnificent of artwork, the big area that is fit to family and high-grade place is again used, and has filled up the market vacancy.
Technical solution problem of the present invention can be by taking following technical scheme:
Three-dimensional art is thrown the glaze brick producing process, comprises following processing step,
1) select for use the finished product adobe of white to do end brick;
2) design various pattern according to demand, and be made into the silk screen that stamp is used;
3) brick surface, the end is wiped clean, on end brick, stamped the pattern of different colours and effect with automatic printing machine;
4) stamping the frit layer that covers different pattern on the end brick of different colours and effect again;
5) end brick of frit layer in the above-mentioned covering is burnt till through kiln, under the temperature of 920 to 1020 ℃ of kilns, after burning till in about one hour, make brick surface, end frit layer fuse into transparent vitreum, the pattern color below the frit presents;
6) the brick body after burning till through polishing machine polishing, the frit on surface is thrown flat, again through the machine that adds lustre to automatically add lustre to handle after, make product surface will become glittering and translucent, the color below the frit layer is clear abundant;
7) obtain final finished product through after the sorted and packaged.
The present invention has following technique effect:
It is glittering and translucent that the product surface that manufacture method of the present invention draws will become, and the color below the frit layer is clear abundant.And because does not polish at the groove place of frit pattern, the gloss of its gloss and surface finish place forms the intensive contrast, and the whole prod stereoscopic sensation is strengthened.Compare with traditional polished tile and ornamental brick, the surface gloss height, color is full, and absolute not soil pick-up has been avoided the soil pick-up problem of a lot of polished tile, and has been not an even curface as polished tile and ornamental brick, there is not stereoscopic sensation, also can make various single-pieces and picture mosaic according to demand simultaneously, have the unreachable decorative effect of traditional ceramic tile, belong to the product of a kind of brand-new technology and technology.
Embodiment
Below in conjunction with specific embodiment the present invention is specifically described.
Three-dimensional art is thrown the glaze brick producing process, adopts following processing step,
1) select for use the finished product adobe of white to do end brick.
2) design various pattern according to demand, and be made into the silk screen that stamp is used.
3) brick surface, the end is wiped clean, on end brick, stamped the pattern of different colours and effect with automatic printing machine.
4) stamping the frit layer that covers different pattern on the end brick of different colours and effect again.
5) end brick of frit layer in the above-mentioned covering is burnt till through kiln, under the temperature of 920 to 1020 ℃ of kilns, after burning till in about one hour, make brick surface, end frit layer fuse into transparent vitreum, the pattern color below the frit presents.The end brick of frit layer is gone up in printed flower and covering, because its surface is loose, must burn till through kiln.
6) the brick body after burning till through polishing machine polishing, the frit on surface is thrown flat, again through the machine that adds lustre to automatically add lustre to handle after, make product surface will become glittering and translucent, the color below the frit layer is clear abundant.Because does not polish at the groove place of frit pattern, the gloss of its gloss and surface finish place forms the intensive contrast, and the whole prod stereoscopic sensation is strengthened.
7) obtain final finished product through after the sorted and packaged.
It is glittering and translucent that the product surface that manufacture method of the present invention draws will become, and the color below the frit layer is clear abundant, and the whole prod stereoscopic sensation strengthens.Compare with traditional polished tile and ornamental brick, the surface gloss height, color is full, and absolute not soil pick-up, has avoided the soil pick-up problem of a lot of polished tile.Manufacturing process of the present invention, the manufacturing process of alternative polished tile and ornamental brick.

Claims (1)

1. three-dimensional art is thrown the glaze brick producing process, it is characterized in that: comprise following processing step,
1) select for use the finished product adobe of white to do end brick;
2) design various pattern according to demand, and be made into the silk screen that stamp is used;
3) brick surface, the end is wiped clean, on end brick, stamped the pattern of different colours and effect with automatic printing machine;
4) stamping the frit layer that covers different pattern on the end brick of different colours and effect again;
5) end brick of frit layer in the above-mentioned covering is burnt till through kiln, under the temperature of 920 to 1020 ℃ of kilns, after burning till in about one hour, make brick surface, end frit layer fuse into transparent vitreum, the pattern color below the frit presents;
6) the brick body after burning till through polishing machine polishing, the frit on surface is thrown flat, again through the machine that adds lustre to automatically add lustre to handle after, make product surface will become glittering and translucent, the color below the frit layer is clear abundant;
7) obtain final finished product through after the sorted and packaged.
CN200910193083XA 2009-10-15 2009-10-15 Method for manufacturing three-dimensional artistic glazed brick CN102040399A (en)