CN102676959A - 铝合金高低温去应力时效方法 - Google Patents

铝合金高低温去应力时效方法 Download PDF

Info

Publication number
CN102676959A
CN102676959A CN2012101703645A CN201210170364A CN102676959A CN 102676959 A CN102676959 A CN 102676959A CN 2012101703645 A CN2012101703645 A CN 2012101703645A CN 201210170364 A CN201210170364 A CN 201210170364A CN 102676959 A CN102676959 A CN 102676959A
Authority
CN
China
Prior art keywords
high temperature
low temperature
heating apparatus
furnaces heating
temperature furnace
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012101703645A
Other languages
English (en)
Other versions
CN102676959B (zh
Inventor
李坚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU NEW HONGJI PRECISION PART CO Ltd
Original Assignee
SUZHOU NEW HONGJI PRECISION PART CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU NEW HONGJI PRECISION PART CO Ltd filed Critical SUZHOU NEW HONGJI PRECISION PART CO Ltd
Priority to CN201210170364.5A priority Critical patent/CN102676959B/zh
Publication of CN102676959A publication Critical patent/CN102676959A/zh
Application granted granted Critical
Publication of CN102676959B publication Critical patent/CN102676959B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种铝合金高低温去应力时效方法，其工艺步骤：1）将高温炉提前预热到170～190℃，再将铝合金产品放进高温炉内保温2～4小时；2）将高温炉提前预热到140～160℃，再将铝合金产品放进高温炉内保温0.5～1.5小时；3）将低温炉提前预冷到-50～-60℃，再将铝合金产品在40秒以内从高温炉转移到低温炉内，并保温0.5～1.5小时；4）重复循环步骤2）和步骤3）共2～4次。通过高温炉和低温炉进行时效工艺处理，处理后精密加工尺寸稳定，精度可达0.005mm以下高精度尺寸要求，实现一般所不能达到的制造要求；缩短生产周期，精密加工后产品尺寸稳定性好且精度非常高。

Description

铝合金高低温去应力时效方法
技术领域
本发明涉及一种铝合金高低温去应力时效方法。
背景技术
对于航空薄壁零件制造，常用工艺为：原材料（棒、板或铸件）-粗加工-自然时效-精加工。
实际加工过程中，因原材料生产厂商缩短制造周期或未完全按照制造工艺执行，在机械加工生产商精密加工后材料内应力释放导致产品变形进而使尺寸超差。一般机械加工厂考虑缩短产品交期在粗加工后增加人工时效工艺，人工时效工艺对于一般精度或产品使用条件不恶劣的条件还能勉强适用，对于高要求军事器械显得欠缺。
发明内容
本发明的目的是克服现有技术存在的不足，提供一种铝合金高低温去应力时效方法。
本发明的目的通过以下技术方案来实现：
铝合金高低温去应力时效方法，包括以下步骤：
1）将高温炉提前预热到170～190℃，再将铝合金产品放进高温炉内保温 2～4小时；
2）将高温炉提前预热到140～160℃，再将铝合金产品放进高温炉内保温0.5～1.5小时；
3）将低温炉提前预冷到-50～-60℃，再将铝合金产品在40秒以内从高温炉转移到低温炉内，并保温0.5～1.5小时；
4）重复循环步骤2）和步骤3）共2～4次。
进一步地，上述的铝合金高低温去应力时效方法，包括以下步骤：
1）将高温炉提前预热到180℃，再将铝合金产品放进高温炉内保温 3小时；
2）将高温炉提前预热到150℃，再将铝合金产品放进高温炉内保温1小时；
3）将低温炉提前预冷到-55℃，再将铝合金产品在40秒以内从高温炉转移到低温炉内，并保温1小时；
4）重复循环步骤2）和步骤3）共3次。
本发明技术方案突出的实质性特点和显著的进步主要体现在：
通过高温炉和低温炉进行时效工艺处理，处理后精密加工尺寸稳定，精度可达0.005mm以下高精度尺寸要求，实现一般所不能达到的制造要求；缩短生产周期，精密加工后产品尺寸稳定性好且精度非常高。航空薄壁件或高精度精密铝合金零件都可参照此工艺，适当修正过程参数可满足高精度产品要求。
具体实施方式
铝合金棒、板或铸件毛坯粗加工后，进入高低温时效工艺，其步骤：
1）将高温炉提前预热到170～190℃，再将铝合金产品放进高温炉内保温 2～4小时；
2）将高温炉提前预热到140～160℃，再将铝合金产品放进高温炉内保温0.5～1.5小时；
3）将低温炉提前预冷到-50～-60℃，再将铝合金产品在40秒以内从高温炉转移到低温炉内，并保温0.5～1.5小时；
4）重复循环步骤2）和步骤3）共2～4次，再精密机械加工。
最佳的时效工艺是：
1）将高温炉提前预热到180℃，再将铝合金产品放进高温炉内保温 3小时；
2）将高温炉提前预热到150℃，再将铝合金产品放进高温炉内保温1小时；
3）将低温炉提前预冷到-55℃，再将铝合金产品在40秒以内从高温炉转移到低温炉内，并保温1小时；
4）重复循环步骤2）和步骤3）共3次。
通过高温炉和低温炉进行时效工艺处理，处理后精密加工尺寸稳定，精度可达0.005mm以下高精度尺寸要求，实现一般所不能达到的制造要求；缩短生产周期，精密加工后产品尺寸稳定性好且精度非常高。航空薄壁件或高精度精密铝合金零件都可参照此工艺，适当修正过程参数可满足高精度产品要求。
需要理解到的是：以上所述仅是本发明的优选实施方式，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以作出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (2)

1.铝合金高低温去应力时效方法，其特征在于包括以下步骤：
1）将高温炉提前预热到170～190℃，再将铝合金产品放进高温炉内保温 2～4小时；
2）将高温炉提前预热到140～160℃，再将铝合金产品放进高温炉内保温0.5～1.5小时；
3）将低温炉提前预冷到-50～-60℃，再将铝合金产品在40秒以内从高温炉转移到低温炉内，并保温0.5～1.5小时；
4）重复循环步骤2）和步骤3）共2～4次。
2.根据权利要求1所述的铝合金高低温去应力时效方法，其特征在于包括以下步骤：
1）将高温炉提前预热到180℃，再将铝合金产品放进高温炉内保温 3小时；
2）将高温炉提前预热到150℃，再将铝合金产品放进高温炉内保温1小时；
3）将低温炉提前预冷到-55℃，再将铝合金产品在40秒以内从高温炉转移到低温炉内，并保温1小时；
4）重复循环步骤2）和步骤3）共3次。
CN201210170364.5A 2012-05-29 2012-05-29 铝合金高低温去应力时效方法 Active CN102676959B (zh)