CN102633308A - 一种利用硫酸亚铁母液生产氧化铁黑的方法 - Google Patents

一种利用硫酸亚铁母液生产氧化铁黑的方法 Download PDF

Info

Publication number
CN102633308A
CN102633308A CN2012101556400A CN201210155640A CN102633308A CN 102633308 A CN102633308 A CN 102633308A CN 2012101556400 A CN2012101556400 A CN 2012101556400A CN 201210155640 A CN201210155640 A CN 201210155640A CN 102633308 A CN102633308 A CN 102633308A
Authority
CN
China
Prior art keywords
ferrous sulfate
iron oxide
mother liquor
oxide black
copperas solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012101556400A
Other languages
English (en)
Inventor
郭焦星
吴彭森
陈建立
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HENAN BAILILIAN CHEMICAL CO Ltd
Original Assignee
HENAN BAILILIAN CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HENAN BAILILIAN CHEMICAL CO Ltd filed Critical HENAN BAILILIAN CHEMICAL CO Ltd
Priority to CN2012101556400A priority Critical patent/CN102633308A/zh
Publication of CN102633308A publication Critical patent/CN102633308A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种利用硫酸亚铁母液生产氧化铁黑的方法，包括将将生产一水硫酸亚铁工艺中产生的母液用清洗离心机的水稀释成用于生产氧化铁黑的硫酸亚铁溶液，然后与过量纯碱在一起用水蒸汽加热反应，然后过滤、水洗、烘干、粉碎后制得铁黑成品。该发明将硫酸亚铁的分离工艺和氧化铁黑的生产工艺结合起来，不但可以减少大量酸性母液的处理，环保意义大，而且能大大降低氧化铁黑的生产成本。

Description

一种利用硫酸亚铁母液生产氧化铁黑的方法
技术领域
本发明涉及一种利用硫酸亚铁母液生产氧化铁黑的方法。 
背景技术
目前，化工厂在生产一水硫酸亚铁成品时，离心分离过程中产生的硫酸亚铁母液，通常是直接排放到污水处理站中和处理，但是所产生的母液中硫酸亚铁的含量是45%～50%，这就造成了资源的严重浪费。而在氧化铁黑的生产工艺中，需要进行硫酸亚铁的溶解工段，此过程需要投入大量设备以及人力，复杂且耗时耗力。 
发明内容
针对现有技术的不足，本发明提供一种利用硫酸亚铁母液生产氧化铁黑的方法，将硫酸亚铁的分离工艺和铁黑的生产工艺结合起来，不但可以减少大量酸性母液处理，而且能大大降低铁黑的生产成本。 
为了实现上述目的，本发明的技术方案是：一种利用硫酸亚铁母液生产氧化铁黑的方法，其特征是：该方法包括以下步骤： 
1）将生产一水硫酸亚铁工艺中产生的母液用清洗离心机的水稀释成用于生产氧化铁黑的硫酸亚铁溶液；
2）将硫酸亚铁溶液与纯碱以2.3:1～2.8:1的比例置于反应釜中，用水蒸汽加热进行氧化反应，氧化反应温度设置在95～110℃；
3）氧化反应完全后，进行过滤、水洗、烘干、粉碎等操作，最后制得铁黑成品。
进一步，所述的硫酸亚铁溶液中硫酸亚铁的含量为30％---35%。 
本发明的有益效果是：将硫酸亚铁的分离工艺和氧化铁黑的生产工艺结合起来，不但可以减少大量酸性母液处理，而且能大大降低氧化铁黑的生产成本。将硫酸亚铁母液，用洗离心机水稀释用于生产铁黑，铁黑生产线上的就不再需要溶解设备。另外，冲洗离心机的母水可以回收，用以硫酸亚铁的母液的稀释，可以避免硫酸亚铁的冷却结晶堵塞，保证系统的正常运行。 
具体实施方式
下面结合实施例对本发明进行进一步说明。 
具体实施例1： 
一种利用硫酸亚铁母液生产氧化铁黑的方法，其特征是：该方法包括以下步骤：
1）将生产一水硫酸亚铁工艺中产生的母液用清洗离心机的水稀释成硫酸亚铁的含量为33％的硫酸亚铁溶液；
2）将硫酸亚铁溶液与纯碱以2.6:1的比例置于反应釜中，用水蒸汽加热进行氧化反应，氧化反应温度设置在100℃；
3）氧化反应完全后，进行过滤、水洗、烘干、粉碎等操作，最后制得铁黑成品。
具体实施例2： 
一种利用硫酸亚铁母液生产氧化铁黑的方法，其特征是：该方法包括以下步骤：
1）将生产一水硫酸亚铁工艺中产生的母液用清洗离心机的水稀释成硫酸亚铁的含量为33％的硫酸亚铁溶液；
2）将硫酸亚铁溶液与纯碱以2.4:1的比例置于反应釜中，用水蒸汽加热进行氧化反应，氧化反应温度设置在105℃；
3）氧化反应完全后，进行过滤、水洗、烘干、粉碎等操作，最后制得铁黑成品。
具体实施例3： 
一种利用硫酸亚铁母液生产氧化铁黑的方法，其特征是：该方法包括以下步骤：
1）将生产一水硫酸亚铁工艺中产生的母液用清洗离心机的水稀释成硫酸亚铁的含量为33.5％的硫酸亚铁溶液；
2）将硫酸亚铁溶液与纯碱以2.5:1的比例置于反应釜中，用水蒸汽加热进行氧化反应，氧化反应温度设置在100℃；
3）氧化反应完全后，进行过滤、水洗、烘干、粉碎等操作，最后制得铁黑成品。
具体实施例4： 
一种利用硫酸亚铁母液生产氧化铁黑的方法，其特征是：该方法包括以下步骤：
1）将生产一水硫酸亚铁工艺中产生的母液用清洗离心机的水稀释成硫酸亚铁的含量为33％的硫酸亚铁溶液；
2）将硫酸亚铁溶液与纯碱以2.4:1的比例置于反应釜中，用水蒸汽加热进行氧化反应，氧化反应温度设置在100℃；
3）氧化反应完全后，进行过滤、水洗、烘干、粉碎等操作，最后制得铁黑成品。
经测算，2.5万吨/年一水硫酸亚铁产生的母液可生产5000吨/年的铁黑。这样，用蒸汽溶解的硫酸亚铁全部回收，硫酸亚铁收率提高到90％以上，铁黑成本也大幅降低。另外，冲洗离心机的母水可以回收，用以一水硫酸亚铁的母液的稀释，可以避免亚铁的冷却结晶堵塞，保证系统的正常运行。 
凡在不脱离本发明核心的情况下做出的简单的变形或修改均落入本发明的保护范围。 

Claims (3)

1.一种利用硫酸亚铁母液生产氧化铁黑的方法，其特征是：该方法包括以下步骤：
1）将生产一水硫酸亚铁工艺中产生的母液用清洗离心机的水稀释成用于生产氧化铁黑的硫酸亚铁溶液；
将硫酸亚铁溶液与纯碱以2.3:1～2.8:1的比例置于反应釜中，用水蒸汽加热进行氧化反应，氧化反应温度设置在95～110℃；
氧化反应完全后，进行过滤、水洗、烘干、粉碎等操作，最后制得铁黑成品。
2.根据权利要求1所述的利用硫酸亚铁母液生产铁黑颜料的方法，其特征是：所述的硫酸亚铁溶液中硫酸亚铁的含量为30％---35%。
3.根据权利要求1所述的利用硫酸亚铁母液生产铁黑颜料的方法，其特征是：所述的硫酸亚铁溶液中硫酸亚铁的含量为33％。
CN2012101556400A 2012-05-19 2012-05-19 一种利用硫酸亚铁母液生产氧化铁黑的方法 Pending CN102633308A (zh)