CN102558722A - 填充有石墨和玻璃纤维的聚四氟乙烯材料及其制造方法 - Google Patents

填充有石墨和玻璃纤维的聚四氟乙烯材料及其制造方法 Download PDF

Info

Publication number
CN102558722A
CN102558722A CN2011104407193A CN201110440719A CN102558722A CN 102558722 A CN102558722 A CN 102558722A CN 2011104407193 A CN2011104407193 A CN 2011104407193A CN 201110440719 A CN201110440719 A CN 201110440719A CN 102558722 A CN102558722 A CN 102558722A
Authority
CN
China
Prior art keywords
graphite
under
speed
spun glass
filled
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011104407193A
Other languages
English (en)
Inventor
屈灏
张超
吕舟旗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN TIANSU BINHAI FLUORINE PLASTIC PRODUCTS CO Ltd
Original Assignee
TIANJIN TIANSU BINHAI FLUORINE PLASTIC PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN TIANSU BINHAI FLUORINE PLASTIC PRODUCTS CO Ltd filed Critical TIANJIN TIANSU BINHAI FLUORINE PLASTIC PRODUCTS CO Ltd
Priority to CN2011104407193A priority Critical patent/CN102558722A/zh
Publication of CN102558722A publication Critical patent/CN102558722A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种填充有石墨和玻璃纤维的聚四氟乙烯材料及其制造方法。所述的填充有石墨和玻璃纤维的聚四氟乙烯材料是由聚四氟乙烯和作为填充剂的石墨和玻璃纤维以100∶1-10∶10-30的重量比共混后经挤压及烧结而制成。本发明提供的填充有石墨、玻璃纤维的聚四氟乙烯材料是在充分利用聚四氟乙烯材料优异性能的基础上，通过填充石墨、玻璃纤维来改善其耐磨耗、耐蠕变、硬度、热传导以及线膨胀系数等方面的性能，并且有效地利用聚四氟乙烯的滑动特性，更好地发挥无油润滑、密封性能，因此可使其适用范围更加广泛。另外，本制造方法简单、操作方便。

Description

填充有石墨和玻璃纤维的聚四氟乙烯材料及其制造方法
技术领域
本发明属于耐摩擦、密封材料技术领域，特别是涉及一种填充有石墨和玻璃纤维的聚四氟乙烯材料及其制造方法。
背景技术
由于聚四氟乙烯是一种具有优异的耐高低温性能和化学稳定性、非粘附性、耐候性、阻燃性和良好自润滑性的氟塑料树脂，因此已在化工、石油、纺织、医疗和机械等领域获得广泛应用。但其缺点是耐磨耗性差、导热系数小、热膨胀系数大，因此适用范围受到限制，所以为了克服上述这些缺点，本领域的技术人员都在试图对聚四氟乙烯材料进行改性，以改善其性能。
发明内容
为了解决上述问题，本发明的目的在于提供一种耐磨性好，导热系数大，热膨胀系数小，因此适用范围广的填充有石墨和玻璃纤维的聚四氟乙烯材料。
本发明的另一个目的在于提供一种上述填充有石墨和玻璃纤维的聚四氟乙烯材料的制造方法。
为了达到上述目的，本发明提供的填充有石墨和玻璃纤维的聚四氟乙烯材料是由聚四氟乙烯和作为填充剂的石墨和玻璃纤维以100∶1-10∶10-30的重量比共混后经挤压及烧结而制成。
本发明提供的填充有石墨和玻璃纤维的聚四氟乙烯材料的制造方法包括按顺序进行的下列步骤：
1)将聚四氟乙烯和作为填充剂的石墨和玻璃纤维以100∶1-10∶10-30的重量比在混料机中共混1-3分钟而制成混配料；
2)在由外模、上压模和下压模组成的普通模具内部空间中放入上述混配料，然后在5-20Mpa的压强、15-30mm/min的加压速率下保压6-20min而完成压制成型，之后卸压、出模而得到半成品毛坯；
3)将上述半成品毛坯放入烧结炉中进行烧结即可制成所述的填充有石墨和玻璃纤维的聚四氟乙烯材料。
3、根据权利要求2所述的填充有石墨和玻璃纤维的聚四氟乙烯材料的制造方法，其特征在于：所述的步骤3)中半成品毛坯的烧结过程是首先在20-60℃/h的速率下升温，升温至300℃时保温5-8小时；然后在10-40℃/h的速率下升温，升温至330℃时保温5-8小时；再在10-20℃/h的速率下升温，升温至380℃时保温7-10小时；然后在10-20℃/h的速率下降温，降温至330℃时保温7-10小时；再在10-40℃/h的速率下降温，降温至300℃时保温5-8小时；最后在50℃/h的速率下降温至250℃后自然冷却至室温。
本发明提供的填充有石墨、玻璃纤维的聚四氟乙烯材料是在充分利用聚四氟乙烯材料优异性能的基础上，通过填充石墨、玻璃纤维来改善其耐磨耗、耐蠕变、硬度、热传导以及线膨胀系数等方面的性能，并且有效地利用聚四氟乙烯的滑动特性，更好地发挥无油润滑、密封性能，因此可使其适用范围更加广泛。另外，本制造方法简单、操作方便。
附图说明
图1为采用本发明提供的填充有石墨和玻璃纤维的聚四氟乙烯材料制造方法时所使用的模具将混配料压制成半成品毛坯过程示意图。
图2为本发明提供的填充有石墨和玻璃纤维的聚四氟乙烯材料制造方法中烧结过程中时间—温度控制图。
具体实施方式
下面结合附图和具体实施例对本发明提供的填充有石墨和玻璃纤维的聚四氟乙烯材料及其制造方法进行详细说明。
实施例1：
如图1、图2所示，本实施例提供的填充有石墨和玻璃纤维的聚四氟乙烯材料的制造方法包括按顺序进行的下列步骤：
1)将聚四氟乙烯和作为填充材料的石墨和玻璃纤维以100∶5∶15的重量比在混料机中共混2分钟而制成混配料；
2)在由外模1、上压模2和下压模4组成的普通模具内部空间中放入上述混配料3，然后在14Mpa的压强、15mm/min的加压速率下保压9min而完成压制成型，之后卸压、出模而得到半成品毛坯；
3)将上述半成品毛坯放入烧结炉中，如图2所示，首先在50℃/h的速率下升温，升温至300℃时保温5小时；然后在30℃/h的速率下升温，升温至330℃时保温6小时；再在20℃/h的速率下升温，升温至380℃时保温10小时；然后在20℃/h的速率下降温，降温至330℃时保温7小时；再在30℃/h的速率下降温，降温至300℃时保温5小时；最后在50℃/h的速率下降温至250℃后自然冷却至室温，即可制成所述的填充有石墨和玻璃纤维的聚四氟乙烯材料。
实施例2：
如图1、图2所示，本实施例提供的填充有石墨和玻璃纤维的聚四氟乙烯材料的制造方法包括按顺序进行的下列步骤：
1)将聚四氟乙烯和作为填充材料的石墨和玻璃纤维以100∶3∶25的重量比在混料机中共混2分钟而制成混配料；
2)在由外模1、上压模2和下压模4组成的普通模具内部空间中放入上述混配料3，然后在14Mpa的压强、15mm/min的加压速率下保压10min而完成压制成型，之后卸压、出模而得到半成品毛坯；
3)将上述半成品毛坯放入烧结炉中，如图2所示，首先在50℃/h的速率下升温，升温至300℃时保温7小时；然后在30℃/h的速率下升温，升温至330℃时保温6小时；再在20℃/h的速率下升温，升温至380℃时保温10小时；然后在20℃/h的速率下降温，降温至330℃时保温8小时；再在30℃/h的速率下降温，降温至300℃时保温7小时；最后在50℃/h的速率下降温至250℃后自然冷却至室温，即可制成所述的填充有石墨和玻璃纤维的聚四氟乙烯材料。
实施例3：
如图1、图2所示，本实施例提供的填充有石墨和玻璃纤维的聚四氟乙烯材料的制造方法包括按顺序进行的下列步骤：
1)将聚四氟乙烯和作为填充材料的石墨和玻璃纤维以100∶8∶10的重量比在混料机中共混2分钟而制成混配料；
2)在由外模1、上压模2和下压模4组成的普通模具内部空间中放入上述混配料3，然后在15Mpa的压强、20mm/min的加压速率下保压10min而完成压制成型，之后卸压、出模而得到半成品毛坯；
3)将上述半成品毛坯放入烧结炉中，如图2所示，首先在50℃/h的速率下升温，升温至300℃时保温6小时；然后在30℃/h的速率下升温，升温至330℃时保温5小时；再在20℃/h的速率下升温，升温至380℃时保温10小时；然后在20℃/h的速率下降温，降温至330℃时保温8小时；再在30℃/h的速率下降温，降温至300℃时保温6小时；最后在50℃/h的速率下降温至250℃后自然冷却至室温，即可制成所述的填充有石墨和玻璃纤维的聚四氟乙烯材料。

Claims (3)

1.一种填充有石墨和玻璃纤维的聚四氟乙烯材料，其特征在于：所述的填充有石墨和玻璃纤维的聚四氟乙烯材料是由聚四氟乙烯和作为填充剂的石墨和玻璃纤维以100∶1-10∶10-30的重量比共混后经挤压及烧结而制成。
2.一种如权利要求1所述的填充有石墨和玻璃纤维的聚四氟乙烯材料的制造方法，其特征在于：所述的制造方法包括按顺序进行的下列步骤：
1)将聚四氟乙烯和作为填充剂的石墨和玻璃纤维以100∶1-10∶10-30的重量比在混料机中共混1-3分钟而制成混配料；
2)在由外模(1)、上压模(2)和下压模(4)组成的普通模具内部空间中放入上述混配料(3)，然后在5-20Mpa的压强、15-30mm/min的加压速率下保压6-20min而完成压制成型，之后卸压、出模而得到半成品毛坯；
3)将上述半成品毛坯放入烧结炉中进行烧结即可制成所述的填充有石墨和玻璃纤维的聚四氟乙烯材料。
3.根据权利要求2所述的填充有石墨和玻璃纤维的聚四氟乙烯材料的制造方法，其特征在于：所述的步骤3)中半成品毛坯的烧结过程是首先在20-60℃/h的速率下升温，升温至300℃时保温5-8小时；然后在10-40℃/h的速率下升温，升温至330℃时保温5-8小时；再在10-20℃/h的速率下升温，升温至380℃时保温7-10小时；然后在10-20℃/h的速率下降温，降温至330℃时保温7-10小时；再在10-40℃/h的速率下降温，降温至300℃时保温5-8小时；最后在50℃/h的速率下降温至250℃后自然冷却至室温。
CN2011104407193A 2011-12-26 2011-12-26 填充有石墨和玻璃纤维的聚四氟乙烯材料及其制造方法 Pending CN102558722A (zh)