CN102534339A - 用于生产立铣刀毛坯混合料的制备方法 - Google Patents

用于生产立铣刀毛坯混合料的制备方法 Download PDF

Info

Publication number
CN102534339A
CN102534339A CN2012100023451A CN201210002345A CN102534339A CN 102534339 A CN102534339 A CN 102534339A CN 2012100023451 A CN2012100023451 A CN 2012100023451A CN 201210002345 A CN201210002345 A CN 201210002345A CN 102534339 A CN102534339 A CN 102534339A
Authority
CN
China
Prior art keywords
preparation
cutter blank
produce
total
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100023451A
Other languages
English (en)
Inventor
霍理
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGZHOU XILI ALLOY TOOLS CO LTD
Original Assignee
CHANGZHOU XILI ALLOY TOOLS CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGZHOU XILI ALLOY TOOLS CO LTD filed Critical CHANGZHOU XILI ALLOY TOOLS CO LTD
Priority to CN2012100023451A priority Critical patent/CN102534339A/zh
Publication of CN102534339A publication Critical patent/CN102534339A/zh
Pending legal-status Critical Current

Abstract

本发明属于合金刀具材料的制备方法领域，具体是一种用于生产立铣刀毛坯混合料的制备方法。它包括将WC和Co粉按比例与球磨过程控制剂一同投入球磨机内，在球磨过程中加入司盘，经过70-120H湿磨制成均匀散弥的浆料，通过筛网过滤卸出，并将其干燥。本发明提高了刀具毛坯混合料的性能，用该毛坯混合料制成的刀具使用寿命长。

Description

用于生产立铣刀毛坯混合料的制备方法
技术领域
本发明属于合金刀具材料的制备方法领域，具体是一种用于生产立铣刀毛坯混合料的制备方法。
背景技术
立铣刀、铰刀、钻头对其制造材料有着苛刻的要求，它要求其必须同时具备材质硬度高，即人们常说的“双高”，而目前公知技术生产的刀具坯料，由于其原料选择、化学成分、混合料制备工艺选择不当造成烧结产品瑕疵，最终导致大大降低刀具使用寿命。
发明内容
本发明要解决的问题是提供一种生产刀具毛坯混合料的制备方法，它是刀具毛坯的混合料，采用该混合料制造刀具毛坯料后能延长刀具的使用寿命，提高烧结成品的合格率。
本发明提供了如下技术方案：
用于生产立铣刀毛坯混合料的制备方法，它包括将WC和Co粉按比例与球磨过程控制剂一同投入球磨机内，在球磨过程中加入司盘，经过70-120H湿磨制成均匀散弥的浆料，通过筛网过滤卸出，并将其干燥；
WC：质量百分比含量为88％-90％，窄的粒度分布Fsss0.6-0.8um，总碳含量为6.15％-6.18％，化合碳含量为≥6.13％，在WC碳化时加入质量百分比小于等于2％的Cr3C2、VC，Cr3C2、VC的Fsss在1um以下；
Co：选用0.8-1um的球形或近似球形钴粉，质量百分比为10％-12％；
过程控制剂：按总的球磨粉料质量的20％-35％加入；
司盘：总的球磨粉料总量每300kg加入40-60ml。
所述的过程控制剂为庚烷或无水酒精。
所述的筛网为400目。
所述的干燥步骤在真空或者喷雾条件下进行。
所述的司盘加入量为总的球磨粉料总量每300kg加入50ml。
本发明提高了刀具毛坯混合料的综合性能，用该毛坯混合料制成的刀具使用寿命长。
具体实施方式
实施例1，用于生产立铣刀毛坯混合料的制备方法，它包括将WC和Co粉按比例与球磨过程控制剂一同投入球磨机内，对WC要求是低的杂质含量、低的含氧量，在球磨过程中加入司盘，经过70小时湿磨制成均匀散弥的浆料，通过筛网过滤卸出，并将其干燥；
WC：质量百分比含量为88％，窄的粒度分布Fsss0.6-0.8um，总碳含量为6.15％，化合碳含量为6.5％，高的化合碳说明碳化程度高，接近或达到了理论碳含量，因此不存在W2C相，这对于合金性能有着十分积极地影响，在WC碳化时加入质量百分比等于2％的Cr3C2、VC，Cr3C2、VC的Fsss在0.1um；
Co：选用0.8um的球形或近似球形钴粉，质量百分比为10％；
过程控制剂：按总的球磨粉料质量的20％加入，为了减少范德华引力的相互作用；
司盘：总的球磨粉料总量每300kg加入40ml，使分散体系更趋稳定；
其中过程控制剂为庚烷或无水酒精；筛网为400目；干燥步骤在真空或者喷雾条件下进行。
司盘加入量也可以为总的球磨粉料总量每300kg加入50ml。
实施例2，实施例1，用于生产立铣刀毛坯混合料的制备方法，它包括将WC和Co粉按比例与球磨过程控制剂一同投入球磨机内，对WC要求是低的杂质含量、低的含氧量，在球磨过程中加入司盘，经过120小时湿磨制成均匀散弥的浆料，通过筛网过滤卸出，并将其干燥；
WC：质量百分比含量为89％，窄的粒度分布Fsss0.8um，总碳含量为6.15％，化合碳含量为6.18％，高的化合碳说明碳化程度高，接近或达到了理论碳含量，因此不存在W2C相，这对于合金性能有着十分积极地影响，在WC碳化时加入质量百分比等于1％的Cr3C2、VC，Cr3C2、VC的Fsss在0.5um；
Co：选用1um的球形或近似球形钴粉，质量百分比为10％；
过程控制剂：按总的球磨粉料质量的35％加入，为了减少范德华引力的相互作用；
司盘：总的球磨粉料总量每300kg加入60ml，使分散体系更趋稳定；其中过程控制剂为庚烷或无水酒精；筛网为400目；干燥步骤在真空或者喷雾条件下进行。
上述两个实施例中，如果WC的含量为90％，则加入极微量的Cr3C2、VC，Cr3C2、VC。

Claims (5)

1.用于生产立铣刀毛坯混合料的制备方法，它包括将WC和Co粉按比例与球磨过程控制剂一同投入球磨机内，在球磨过程中加入司盘，经过70-120H湿磨制成均匀散弥的浆料，通过筛网过滤卸出，并将其干燥；
WC：质量百分比含量为88％-90％，窄的粒度分布Fsss0.6-0.8um，总碳含量为6.15％-6.18％，化合碳含量为≥6.13％，在WC碳化时加入质量百分比小于等于2％的Cr3C2、VC，Cr3C2、VC的Fsss在1um以下；
Co：选用0.8-1um的球形或近似球形钴粉，质量百分比为10％-12％；
过程控制剂：按总的球磨粉料质量的20％-35％加入；
司盘：总的球磨粉料总量每300kg加入40-60ml。
2.根据权利要求1所述的用于生产立铣刀毛坯混合料的制备方法，其特征在于：所述的过程控制剂为庚烷或无水酒精。
3.根据权利要求1所述的用于生产立铣刀毛坯混合料的制备方法，其特征在于：所述的筛网为400目。
4.根据权利要求1所述的用于生产立铣刀毛坯混合料的制备方法，其特征在于：所述的干燥步骤在真空或者喷雾条件下进行。
5.根据权利要求1所述的用于生产立铣刀毛坯混合料的制备方法，其特征在于：所述的司盘加入量为总的球磨粉料总量每300kg加入50ml。
CN2012100023451A 2012-01-06 2012-01-06 用于生产立铣刀毛坯混合料的制备方法 Pending CN102534339A (zh)