CN102501304A - 保温板的加工工艺 - Google Patents

保温板的加工工艺 Download PDF

Info

Publication number
CN102501304A
CN102501304A CN2011103725517A CN201110372551A CN102501304A CN 102501304 A CN102501304 A CN 102501304A CN 2011103725517 A CN2011103725517 A CN 2011103725517A CN 201110372551 A CN201110372551 A CN 201110372551A CN 102501304 A CN102501304 A CN 102501304A
Authority
CN
China
Prior art keywords
dry
temperature
warming plate
processing technology
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103725517A
Other languages
English (en)
Inventor
李金峰
赵永海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2011103725517A priority Critical patent/CN102501304A/zh
Publication of CN102501304A publication Critical patent/CN102501304A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种保温板的加工工艺，其特征在于，包括以下组份：膨胀珍珠岩30-50份，泡花碱30-50份，防水剂5-10份，其中，所述膨胀珍珠岩的颗粒大小为0.5-100mm。本发明的优点：本发明所加工的保温板主体的珍珠岩颗粒不会脱落，而且不存在安全隐患。

Description

保温板的加工工艺
技术领域
本发明涉及一种保温板的加工工艺。
背景技术
现有技术的隔热保温板的加工工艺在加工烘干完毕以后，其外部的珍珠岩颗粒有的容易脱落，在脱落的过程中，形成粉尘，对环境造成一定程度的污染，而且存在安全隐患。
发明内容
为克服现有技术的缺陷，本发明提供一种杜绝颗粒脱落和安全隐患的保温板的加工工艺。本发明的技术方案是：一种保温板的加工工艺，其特征在于，包括以下组份：
膨胀珍珠岩30-50份，泡花碱30-50份，防水剂5-10份，其中，所述膨胀珍珠岩的颗粒大小为5.1-20mm。
优选的，所述的各组分如下：膨胀珍珠岩40份，泡花碱40份，防水剂8份。
所述的保温板的加工工艺，包括以下步骤： 
（1）、将所述的各组分原料进行充分搅拌混合； 
（2）、将混合后的原材料置入透气的包装袋；
（3）、置入模具中进行压制，压强为20-60Mpa；
（4）、进行烘干，烘干分为低温区和高温区，首先进入低温区进行烘干，烘干温度为40-200℃，烘干时间5-10分钟；再进入高温区进行烘干，烘干温度为200-600℃，烘干时间20-40分钟；再次进入低温区进行烘干，烘干时间为10-20分钟，烘干温度40-200；
（5）、即得。
所述的透气的包装袋为网格状的玻纤布制作而成。
本发明的优点：本发明所加工的保温板主体的珍珠岩颗粒不会脱落，而且不存在安全隐患。
具体实施方式
实施例1：一种保温板的加工工艺，称取以下重量份的各组份：
膨胀珍珠岩30份，泡花碱30份，防水剂5份，所述的防水剂为有机硅防水剂，其中，所述膨胀珍珠岩的颗粒大小为0.5-100mm之间任意选取，经过试验，当珍珠岩颗粒的大小为0.5-100mm的时候，加工的保温板隔热保温效果以及和其它组份的混合效果更好，然后进行如下步骤：
（1）、将所述的各组分原料进行充分搅拌混合； 
（2）、将混合后的原材料置入透气的包装袋；所述的透气的包装袋为网格状的玻纤布制作而成；
（3）、置入模具中进行压制，压强为50Mpa；
（4）、进行烘干，烘干分为低温区和高温区，首先进入低温区进行烘干，烘干温度为40℃，烘干时间5-10分钟；再进入高温区进行烘干，烘干温度为200℃，烘干时间20-40分钟；再次进入低温区进行烘干，烘干时间为10-20分钟，烘干温度50；
烘干温度为40℃；
（5）、即得。
实施例2：一种保温板的加工工艺，称取以下重量份的各组份：
膨胀珍珠岩40份，泡花碱40份，防水剂8份，然后进行如下步骤：
（1）、将所述的各组分原料进行充分搅拌混合； 
（2）、将混合后的原材料置入透气的包装袋；所述的透气的包装袋为网格状的玻纤布制作而成；
（3）、置入模具中进行压制，压强为60Mpa；
（4）、进行烘干，烘干温度为500℃；
（5）、即得。
实施例3：一种保温板的加工工艺，称取以下重量份的各组份：
膨胀珍珠岩50份，泡花碱50份，防水剂10份，然后进行如下步骤：
（1）、将所述的各组分原料进行充分搅拌混合； 
（2）、将混合后的原材料置入透气的包装袋；所述的透气的包装袋为网格状的玻纤布制作而成；
（3）、置入模具中进行压制，压强为60Mpa；
（4）、进行烘干，烘干分为低温区和高温区，首先进入低温区进行烘干，烘干温度为100℃，烘干时间10分钟；再进入高温区进行烘干，烘干温度为600℃，烘干时间40分钟；再次进入低温区进行烘干，烘干时间为10-20分钟，烘干温度150℃；
（5）、即得。

Claims (4)

1.一种保温板的加工工艺，其特征在于，包括以下组份：
膨胀珍珠岩30-50份，泡花碱30-50份，防水剂5-10份，其中，所述膨胀珍珠岩的颗粒大小为5.1-20mm。
2.根据权利要求1所述的保温板的加工工艺，其特征在于，所述的各组分如下：膨胀珍珠岩40份，泡花碱40份，防水剂8份。
3.根据权利要求1或2所述的保温板的加工工艺，其特征在于，
包括以下步骤： 
（1）、将所述的各组分原料进行充分搅拌混合； 
（2）、将混合后的原材料置入透气的包装袋；
（3）、置入模具中进行压制，压强为20-60Mpa；
（4）、进行烘干，烘干分为低温区和高温区，首先进入低温区进行烘干，烘干温度为40-200℃，烘干时间5-10分钟；再进入高温区进行烘干，烘干温度为200-600℃，烘干时间20-40分钟；再次进入低温区进行烘干，烘干时间为10-20分钟，烘干温度40-200；
（5）、即得。
4.根据权利要求3所述的保温板的加工工艺，其特征在于，所述的透气的包装袋为网格状的玻纤布制作而成。
CN2011103725517A 2011-11-22 2011-11-22 保温板的加工工艺 Pending CN102501304A (zh)