CN105036764A - 一种高温冶炼保温层环保材料 - Google Patents

一种高温冶炼保温层环保材料 Download PDF

Info

Publication number
CN105036764A
CN105036764A CN201510356026.4A CN201510356026A CN105036764A CN 105036764 A CN105036764 A CN 105036764A CN 201510356026 A CN201510356026 A CN 201510356026A CN 105036764 A CN105036764 A CN 105036764A
Authority
CN
China
Prior art keywords
parts
powder
environmental protection
thermal insulation
insulation layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510356026.4A
Other languages
English (en)
Inventor
韩家玉
李江
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Sheng Yun Environmental Protection (group) Ltd By Share Ltd
Original Assignee
Anhui Sheng Yun Environmental Protection (group) Ltd By Share Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Sheng Yun Environmental Protection (group) Ltd By Share Ltd filed Critical Anhui Sheng Yun Environmental Protection (group) Ltd By Share Ltd
Priority to CN201510356026.4A priority Critical patent/CN105036764A/zh
Publication of CN105036764A publication Critical patent/CN105036764A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种高温冶炼保温层环保材料,由以下重量份数的原料制成:微孔莫来石骨料10-22份,云母粉3-9份,毛蛤壳粉3-6份,牡蛎壳粉9-11份,改性剂3-6份,珍珠岩2-6份,膨润土2-5份,硅酸盐棉9-10份,次磷酸镁1-7份,滑石粉1-3份,海泡石30-50份,硅藻土10-11份,空心玻璃微珠2-9份,石墨粉1-9份,高岭土3-7份,硅藻土6-9份,开孔膨胀珍珠岩7-8份,石灰6-9份,成核剂1-5份,滑石粉2-4份,锑基纳米复合环保阻燃剂3-8份。本发明具有良好的保温性能,使用寿命长、不老化,具有防腐功能,不燃烧性能好,社会效益和经济效益高。

Description

一种高温冶炼保温层环保材料
技术领域
[0001] 本发明属于环保材料技术领域,具体是一种高温冶炼保温层环保材料。
背景技术
[0002] 近年来,随着国家经济建设进入高速发展的阶段,国内化工、石油、电力、冶金、轻工、食品、医药、交通、国防等行业,对保温材料的年需求量达15亿立方。其中,对硅酸读保温材料的市场需求己达到5亿立方,年均需求增幅高达25%以上。特别是国家对建筑业强制使用优质保温材料的政策,进一步扩大了国内对硅酸读保温材料的需求量。而面对高速增长的市场需求和广泛应用,对硅酸保温材料提出了更高的要求,不仅要导热系数更低、使用温度更宽、粘接力更强,而且要求耐急冷急热性能好,不发生开裂,无毒无尘无污染。现有
的硅酸馍保温材料还不能达到许多应用领域的要求。
[0003] 在冶金炼钢工业过程中,转炉冶炼后高温钢水经过钢包和中间包最后铸成坯体,在冶炼工艺涉及的所有高温熔融容器内必须砌筑耐火材料,常规耐火材料衬分为工作层、保温层、永久层。由于常规使用的耐火材料保温性能不好,钢水在容器内温度下降’快,为保证钢材的性能,必须提高钢水的最初温度,以满足工艺需要。在热风和热力管道中,为了保证高温气体在输送过程中的温度,在管道内砌筑耐火材料。在高温窑炉使用中,为保证窑炉的保温效果,同时提高窑炉内衬使用寿命,常采用由重质砖和轻质耐火材料组合砌筑,导致窑炉内衬热容量大,热效率降低。由于传统轻质保温材料强度低,不能直接用于工作层,必须用多层耐火材料砌筑,使得管径增大。
发明内容
[0004] 本发明的目的在于克服现有技术缺陷,提供一种高温冶炼保温层环保材料。
[0005] 本发明的目的可以通过以下技术方案实现:
一种高温冶炼保温层环保材料,由以下重量份数的原料制成:微孔莫来石骨料10-22份,云母粉3-9份,毛蛤壳粉3-6份,牡蛎壳粉9-11份,改性剂3-6份,珍珠岩2_6份,膨润土2-5份,硅酸盐棉9-10份,次磷酸镁1-7份,滑石粉1-3份,海泡石30-50份,硅藻土 10-11份,空心玻璃微珠2-9份,石墨粉1-9份,高岭土 3-7份,硅藻土 6-9份,开孔膨胀珍珠岩
7-8份,石灰6-9份,成核剂1-5份,滑石粉2-4份,锑基纳米复合环保阻燃剂3_8份。
[0006] 优选的,所述的一种高温冶炼保温层环保材料,由以下重量份数的原料制成:微孔莫来石骨料15份,云母粉4份,毛蛤壳粉4份,牡蛎壳粉10份,改性剂4份,珍珠岩5份,膨润土 3份,硅酸盐棉10份,次磷酸镁5份,滑石粉2份,海泡石35份,硅藻土 12份,空心玻璃微珠4份,石墨粉4份,高岭土 5份,硅藻土 8份,开孔膨胀珍珠岩7份,石灰7份,成核剂4份,滑石粉3份,锑基纳米复合环保阻燃剂5份。
[0007] 本发明的有益效果:具有强度高、比重小、耐火度高和导热系数小等特点。使用本发明的高温设备,可减少热损失,延长设备寿命,节约能源,降低成本。
具体实施方式
[0008] 为了便于本领域技术人员理解,下面结合具体实施例对本发明作进一步的说明。
[0009] 实施例1
一种高温冶炼保温层环保材料,由以下重量份数的原料制成:微孔莫来石骨料15份,云母粉4份,毛蛤壳粉4份,牡蛎壳粉10份,改性剂4份,珍珠岩5份,膨润土 3份,硅酸盐棉10份,次磷酸镁5份,滑石粉2份,海泡石35份,硅藻土 12份,空心玻璃微珠4份,石墨粉4份,高岭土 5份,硅藻土 8份,开孔膨胀珍珠岩7份,石灰7份,成核剂4份,滑石粉3份,锑基纳米复合环保阻燃剂5份。
[0010] 以上内容仅仅是对本发明所作的举例和说明,所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代,只要不偏离发明或者超越本权利要求书所定义的范围,均应属于本发明的保护范围。

Claims (2)

1.一种高温冶炼保温层环保材料,其特征在于,由以下重量份数的原料制成:微孔莫来石骨料10-22份,云母粉3-9份,毛蛤壳粉3-6份,牡蛎壳粉9_11份,改性剂3_6份,珍珠岩2-6份,膨润土 2-5份,硅酸盐棉9-10份,次磷酸镁1-7份,滑石粉1_3份,海泡石30-50份,娃藻土 10-11份,空心玻璃微珠2-9份,石墨粉1-9份,高岭土 3-7份,娃藻土 6_9份,开孔膨胀珍珠岩7-8份,石灰6-9份,成核剂1-5份,滑石粉2-4份,锑基纳米复合环保阻燃剂3-8份。
2.根据权利要求1所述的一种高温冶炼保温层环保材料,其特征在于,由以下重量份数的原料制成:微孔莫来石骨料15份,云母粉4份,毛蛤壳粉4份,牡蛎壳粉10份,改性剂4份,珍珠岩5份,膨润土 3份,硅酸盐棉10份,次磷酸镁5份,滑石粉2份,海泡石35份,硅藻土 12份,空心玻璃微珠4份,石墨粉4份,高岭土 5份,硅藻土 8份,开孔膨胀珍珠岩7份,石灰7份,成核剂4份,滑石粉3份,锑基纳米复合环保阻燃剂5份。
CN201510356026.4A 2015-06-25 2015-06-25 一种高温冶炼保温层环保材料 Pending CN105036764A (zh)