CN102432264A - 阻燃浆料 - Google Patents
阻燃浆料 Download PDFInfo
- Publication number
- CN102432264A CN102432264A CN2011102593370A CN201110259337A CN102432264A CN 102432264 A CN102432264 A CN 102432264A CN 2011102593370 A CN2011102593370 A CN 2011102593370A CN 201110259337 A CN201110259337 A CN 201110259337A CN 102432264 A CN102432264 A CN 102432264A
- Authority
- CN
- China
- Prior art keywords
- percent
- slurry
- flame
- retardant
- inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了阻燃浆料，它是由无机骨料和无机乳液混合而成的浆料，无机骨料和无机乳液的重量组分分别是矿棉5％、膨胀珍珠岩34％、浓度为2％的羟乙基纤维素16％、岩棉6％、石棉灰5％、氧化锌2％、缩合磷酸铝3％、改性硅酸钾20％、改性硅溶胶9％，制备方法是先将改性硅酸钾和改性硅溶胶两种无机乳液加入容器中搅拌均匀，再分别加入各种骨料充分搅拌混合成浆料，经质量检测、定量包装、密封、入库备用。使用中，可以用本浆料在专用设备中挤压成板状或条状，填充粘固在预留的板缝中进行阻燃。也可以直接把本浆料填充在预留板缝中凝固后进行阻燃。具有无毒无害、无污染、重量轻、易施工，特别适用于建筑物外墙外保温装饰面复合板之间的防火施工使用。
Description
技术领域：
本发明涉及建筑材料，特别是一种用于填充固定在外墙外保温饰面复合板的板块之间，防止外来火源发生时，避免上下贯通燃烧的阻燃浆料。
背景技术：
目前市场上的A级防火材料有多种，如用外壳将石棉充填在外墙保温饰面复合板的板块之间进行防火阻燃的，也有用酚醛板的。存在的缺点是施工难度大、粘结强度差、达不到A级防火材料的要求。
发明内容：
本发明的目的是提供一种生产容易、施工方便、阻燃性能好，可达到A级防火材料要求的阻燃浆料。
本发明的技术方案是以如下方式完成的，它是由无机骨料和无机乳液混合而成的浆料，无机骨料和无机乳液的重量组分分别是矿棉5％、膨胀珍珠岩34％、浓度为2％的羟乙基纤维素16％、岩棉6％、石棉灰5％、氧化锌2％、缩合磷酸铝3％、改性硅酸钾20％、改性硅溶胶9％，制备方法是先将改性硅酸钾和改性硅溶胶两种无机乳液加入容器中搅拌均匀，再分别加入各种骨料充分搅拌混合成浆料，经质量检测、定量包装、密封、入库备用。
使用中，可以用本浆料在专用设备中挤压成板状或条状，填充粘固在预留的板缝中进行阻燃。也可以直接把本浆料填充在预留板缝中凝固后进行阻燃。具有无毒无害、无污染、重量轻、易施工、阻燃性能达到A级标准，导热指数为0.052W/mk，特别适用于建筑物外墙外保温装饰面复合板之间的防火施工使用。
具体实施方式：
本发明的阻燃浆料是采用无机乳液和无机骨料混合而成，具体制备方法是先将两种无机乳液改性硅酸钾20kg和改性硅溶胶9kg加入一个专用搅拌容器中搅拌均匀；再分别将无机骨料矿棉5kg、膨胀珍珠岩34kg、浓度为2％的羟乙基纤维素16kg、岩棉6kg、石棉灰5kg、氧化锌2kg、缩合磷酸铝3kg分别加入在专用搅拌容器中搅拌均匀成为浆料，再经质量检测、定量包装、密封、入库备用。
使用时，可以用本产品加工成防火板材，也可以直接将本产品浆料填充在饰面复合板的板缝之间，用于阻燃，具有无毒无害、重量轻、强度高、阻燃性能达到A级标准的要求，综合成本低的优点。
Claims (1)
1.阻燃浆料，它是由无机骨料和无机乳液混合而成的浆料，无机骨料和无机乳液的重量组分分别是矿棉5％、膨胀珍珠岩34％、浓度为2％的羟乙基纤维素16％、岩棉6％、石棉灰5％、氧化锌2％、缩合磷酸铝3％、改性硅酸钾20％、改性硅溶胶9％，制备方法是先将改性硅酸钾和改性硅溶胶两种无机乳液加入容器中搅拌均匀，再分别加入各种骨料充分搅拌混合成浆料，经质量检测、定量包装、密封、入库备用。