CN107629500A - 一种隧道防火涂料 - Google Patents

一种隧道防火涂料 Download PDF

Info

Publication number
CN107629500A
CN107629500A CN201710969169.1A CN201710969169A CN107629500A CN 107629500 A CN107629500 A CN 107629500A CN 201710969169 A CN201710969169 A CN 201710969169A CN 107629500 A CN107629500 A CN 107629500A
Authority
CN
China
Prior art keywords
parts
fire
proof coating
tunnels
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710969169.1A
Other languages
English (en)
Inventor
杨松林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Jianzhong Energy Technology Co Ltd
Original Assignee
Jiangsu Jianzhong Energy Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Jianzhong Energy Technology Co Ltd filed Critical Jiangsu Jianzhong Energy Technology Co Ltd
Priority to CN201710969169.1A priority Critical patent/CN107629500A/zh
Publication of CN107629500A publication Critical patent/CN107629500A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种隧道防火涂料,其原料按重量份包括:耐火水泥90份、叔醋乳液16‑31份、膨胀蛭石30‑55份、聚醋酸乙烯酯乳液13‑26份、聚苯胺乳液3‑16份、阻燃剂11‑35份、膨胀珍珠岩6‑13份、云母粉6‑11份、海泡石11‑35份、氢氧化铝12‑19份、重质碳酸钙4‑15份、活性硅藻土12‑30份、硼酸钾12‑19份、羧甲基纤维素1‑2.5份、流平剂0.2‑3份、硅烷偶联剂3‑9份。本发明提出的隧道防火涂料,其防火性能好,耐腐蚀性强,粘结强度高,使用寿命长。

Description

一种隧道防火涂料
技术领域
本发明涉及涂料技术领域,尤其涉及一种隧道防火涂料。
背景技术
在交通运输通道的建设过程中,隧道以其便捷、造价低等优势受到了规划建设者的青睐。海底隧道也得到了快速发展。由于海底隧道具有规模大、里程长的特点,再加上其结构相对密闭、交通流量大,在海底隧道内一旦发生火灾,灭火相当困难,因此,提高隧道防火能力十分重要。在海底隧道表面喷涂防火涂料,是使隧道免于受到破坏的重要措施之一。但是由于我国隧道防火涂料研发和应用起步较晚,现有的防火涂料其耐火极限、粘结强度等性能还有待完善。
发明内容
本发明的目的是为了解决现有技术中存在的缺点,而提出的一种隧道防火涂料,其防火性能好,耐腐蚀性强,粘结强度高,使用寿命长。
为了实现上述目的,本发明采用了如下技术方案:
一种隧道防火涂料,其原料按重量份包括:耐火水泥90份、叔醋乳液16-31份、膨胀蛭石30-55份、聚醋酸乙烯酯乳液13-26份、聚苯胺乳液3-16份、阻燃剂11-35份、膨胀珍珠岩6-13份、云母粉6-11份、海泡石11-35份、氢氧化铝12-19份、重质碳酸钙4-15份、活性硅藻土12-30份、硼酸钾12-19份、羧甲基纤维素1-2.5份、流平剂0.2-3份、硅烷偶联剂3-9份。
其中,所述阻燃剂按重量份由3-16份双季戊四醇、5-18份三聚磷酸铝和11-15份可膨胀石墨组成。
优选地,耐火水泥、叔醋乳液、聚醋酸乙烯酯乳液、聚苯胺乳液的重量比为90:16-31:13-26:3-16。
优选地,膨胀珍珠岩、云母粉、海泡石、氢氧化铝、重质碳酸钙、活性硅藻土、硼酸钾的重量比为6-13:6-11:11-35:12-19:4-15:12-30:12-19。
优选地,所述阻燃剂按重量份由7份双季戊四醇、10份三聚磷酸铝、和3份可膨胀石墨组成。
优选地,所述硅烷偶联剂为乙烯基三乙氧基硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷中的一种或者两种的混合物。
本发明中,以耐火水泥、叔醋乳液、聚醋酸乙烯酯乳液、聚苯胺乳液配合作为成膜物质,通过调节其比例,使各原料的相容性好,性能协同促进,使得到的涂膜热稳定性好、成炭能力强,与基体的粘结强度高,提高了涂层的膨胀和防火性能,同时改善了防火涂料的耐腐蚀性能;膨胀珍珠岩、云母粉、海泡石、氢氧化镁、重质碳酸钙、硅藻土、纳米氢氧化铝、硼酸锌配合作为无机填料,改善了防火涂料的强度,同时与阻燃剂配合,提高了防火涂料的成炭率、抗氧化性和热稳定性,改善了涂料的防火性能,其中,无机填料在防火涂料中起到隔热和防止热氧分解的作用,阻燃剂中的可膨胀石墨穿插到了膨胀层中,起到了结构支撑作用,维持了防火涂料的强度。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白,以下结合具体实施例,对本发明进行进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
实施例1
一种隧道防火涂料,其原料按重量份包括:耐火水泥90份、叔醋乳液17份、膨胀蛭石31份、聚醋酸乙烯酯乳液14份、聚苯胺乳液4份、阻燃剂15份、膨胀珍珠岩7份、云母粉6份、海泡石13份、氢氧化铝13份、重质碳酸钙4份、活性硅藻土13份、硼酸钾12份、羧甲基纤维素1份、流平剂0.2份、硅烷偶联剂4份。
其中,所述阻燃剂按重量份由7份双季戊四醇、10份三聚磷酸铝和3份可膨胀石墨组成;
所述轻质碳酸钙的粒径为10-30nm;所述纳米氢氧化铝的粒径为50-75nm。
实施例2
一种隧道防火涂料,其原料按重量份包括:耐火水泥90份、叔醋乳液18份、膨胀蛭石44份、聚醋酸乙烯酯乳液16份、聚苯胺乳液8份、阻燃剂15份、膨胀珍珠岩9份、云母粉7份、海泡石16份、氢氧化铝16份、重质碳酸钙9份、活性硅藻土18份、硼酸钾16份、羧甲基纤维素1.5份、流平剂0.5份、硅烷偶联剂5份。
其中,所述阻燃剂按重量份由2份双季戊四醇、12份三聚磷酸铝和5份可膨胀石墨组成。
6、实施例3
一种隧道防火涂料,其原料按重量份包括:耐火水泥90份、叔醋乳液31份、膨胀蛭石55份、聚醋酸乙烯酯乳液26份、聚苯胺乳液16份、阻燃剂35份、膨胀珍珠岩13份、云母粉11份、海泡石35份、氢氧化铝19份、重质碳酸钙15份、活性硅藻土30份、硼酸钾19份、羧甲基纤维素2.5份、流平剂3份、硅烷偶联9份。
其中,所述阻燃剂按重量份由8份双季戊四醇、5份三聚磷酸铝、9份红磷和3份可膨胀石墨组成。
以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,根据本发明的技术方案及其发明构思加以等同替换或改变,都应涵盖在本发明的保护范围之内。

Claims (7)

1.一种隧道防火涂料,其特征在于,其原料按重量份包括:耐火水泥90份、叔醋乳液16-31份、膨胀蛭石30-55份、聚醋酸乙烯酯乳液13-26份、聚苯胺乳液3-16份、阻燃剂11-35份、膨胀珍珠岩6-13份、云母粉6-11份、海泡石11-35份、氢氧化铝12-19份、重质碳酸钙4-15份、活性硅藻土12-30份、硼酸钾12-19份、羧甲基纤维素1-2.5份、流平剂0.2-3份、硅烷偶联剂3-9份。
其中,所述阻燃剂按重量份由3-16份双季戊四醇、5-18份三聚磷酸铝和11-15份可膨胀石墨组成。
2.根据权利要求1所述隧道防火涂料,其特征在于,耐火水泥、叔醋乳液、聚醋酸乙烯酯乳液、聚苯胺乳液的重量比为90:16-31:13-26:3-16。
3.根据权利要求1所述隧道防火涂料,其特征在于,膨胀珍珠岩、云母粉、海泡石、氢氧化铝、重质碳酸钙、活性硅藻土、硼酸钾的重量比为6-13:6-11:11-35:12-19:4-15:12-30:12-19。
4.根据权利要求1所述隧道防火涂料,其特征在于,其原料按重量份包括耐火水泥90份、叔醋乳液16份、膨胀蛭石30份、聚醋酸乙烯酯乳液13份、聚苯胺乳液3份、阻燃剂11份、膨胀珍珠岩6份、云母粉6份、海泡石11份、氢氧化铝12份、重质碳酸钙4份、活性硅藻土12份、硼酸钾12份、羧甲基纤维素1份、流平剂0.2份、硅烷偶联剂3份。
5.根据权利要求1所述隧道防火涂料,其特征在于,所述阻燃剂按重量份由7份双季戊四醇、10份三聚磷酸铝、和13份可膨胀石墨组成。
6.根据权利要求1所述隧道防火涂料,其特征在于,所述重质碳酸钙的粒径为10-30nm;所述纳米氢氧化铝的粒径为50-75nm。
7.根据权利要求1-6中任一项所述隧道防火涂料,其特征在于,所述硅烷偶联剂为乙烯基三乙氧基硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷中的一种或者两种的混合物。
CN201710969169.1A 2017-10-18 2017-10-18 一种隧道防火涂料 Pending CN107629500A (zh)