CN102399401B - 一种环保型电缆填充料及其制备方法 - Google Patents

一种环保型电缆填充料及其制备方法 Download PDF

Info

Publication number
CN102399401B
CN102399401B CN2011103151809A CN201110315180A CN102399401B CN 102399401 B CN102399401 B CN 102399401B CN 2011103151809 A CN2011103151809 A CN 2011103151809A CN 201110315180 A CN201110315180 A CN 201110315180A CN 102399401 B CN102399401 B CN 102399401B
Authority
CN
China
Prior art keywords
environment
friendly cable
stopping composition
preparation
cable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2011103151809A
Other languages
English (en)
Other versions
CN102399401A (zh
Inventor
常珍国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xuzhou Dongxing Energy Co ltd
Original Assignee
CHIZHOU LINGZHI HUAJIAN MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHIZHOU LINGZHI HUAJIAN MATERIAL TECHNOLOGY Co Ltd filed Critical CHIZHOU LINGZHI HUAJIAN MATERIAL TECHNOLOGY Co Ltd
Priority to CN2011103151809A priority Critical patent/CN102399401B/zh
Publication of CN102399401A publication Critical patent/CN102399401A/zh
Application granted granted Critical
Publication of CN102399401B publication Critical patent/CN102399401B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种环保型电缆填充料及其制备方法，其主要是由组成原料聚氯乙烯树脂、酚醛树脂、聚丙烯、三聚氰酸三烯丙酯、硅烷偶联剂、钛酸酯、氧化锌、秸秆灰烬、石墨、碳酸钙、防老剂、阻燃剂和硅酸铅按一定混合比例制得。本发明的环保型电缆填充料具有化学结构稳定、不被微生物分解、凝胶性能好，膨胀能力高，电缆的电气性能提高，延长了电缆的使用寿命，节约了资源。

Description

一种环保型电缆填充料及其制备方法
技术领域
本发明涉及电缆用辅料领域，具体涉及一种环保型电缆填充料及其制备方法。
背景技术
我国高压电力电缆的应用非常的普遍和广泛，在高压电力电缆大多敷设在地下其环境大多较为潮湿。水分很易渗透到电缆结构内部.因此在正常高压通电情况下电应力理论认为，电缆在生产和运行过程中的内部应力是促进水树枝生长的主要原因。当电缆在经受电压和水时，在高压工频电场中，极性水分子产生强烈的迁移并将电场能转化为动能和热能，获得巨大能量的水分子在绝缘内部剧烈运动。当水分子能量足以打断电缆绝缘层XLPE分子链的时候，就会在绝缘内部产生细微的裂纹，导体附近的XLPE绝缘的应变就会增加，而在应变较大的区域(如杂质和气孔等处)便生成水树枝。大大降低绝缘材料的绝缘水平，从而缩短了电缆的使用寿命，造成巨大的经济损失。
我公司开发的电缆用纵向阻水型填充条材料，主要是通过在电缆成缆过程中纵向填充堵水条材料，将能吸收大量水，膨胀度高，且在热作用下具有较高凝胶粘度和足够耐热性能，且便于电缆生产行业的方便应用，该材料具有实现电缆堵水材料的化学结构稳定、不被微生物分解、凝胶性能好、有一定的膨胀能力和膨胀速度要求。
发明内容
为了缓解现有技术的不足和缺陷，本发明公开了一种环保型电缆填充料及其制备方法，本发明的环保型电缆填充料具有化学结构稳定、不被微生物分解、凝胶性能好，膨胀能力高，电缆的电气性能提高，延长了电缆的使用寿命，节约了资源。
为实现上述目的本发明采用的技术方案如下：
环保型电缆填充料，其特征在于其组成原料的重量份为：
Figure BDA0000099529260000011
Figure BDA0000099529260000021
所述的环保型电缆填充料，其特征在于：所述的防老剂为防老剂4010；所述的阻燃剂选自氢氧化镁或氢氧化铝中的一种或混合物。
所述的环保型电缆填充料的制备方法，其特征在于包括以下步骤：
(1)按组成原料的重量份称取各原料，混合均匀，装入挤塑机料斗，挤塑机的机筒温度控制在130-190℃，生成熔融态混合料；
(2)在熔融态混合料中冲入氮气，取出依次通过75-95℃的热水槽和室温水槽，风干得到成品。
本发明的有益效果：
本发明的环保型电缆填充料具有化学结构稳定、不被微生物分解、凝胶性能好，膨胀能力高，电缆的电气性能提高，延长了电缆的使用寿命，节约了资源。
具体实施方式
实施例1：环保型电缆填充料，其组成原料的重量份为：
Figure BDA0000099529260000031
环保型电缆填充料的制备方法，包括以下步骤：
(1)按组成原料的重量份称取各原料，混合均匀，装入挤塑机料斗，挤塑机的机筒温度控制在130-190℃，生成熔融态混合料；
(2)在熔融态混合料中冲入氮气，取出依次通过75-95℃的热水槽和室温水槽，风干得到成品。
实施例2：环保型电缆填充料，其组成原料的重量份为：
Figure BDA0000099529260000032
环保型电缆填充料的制备方法，包括以下步骤：
(1)按组成原料的重量份称取各原料，混合均匀，装入挤塑机料斗，挤塑机的机筒温度控制在130-190℃，生成熔融态混合料；
(2)在熔融态混合料中冲入氮气，取出依次通过75-95℃的热水槽和室温水槽，风干得到成品。
实施例3：本发明的环保型电缆填充料物理、机械和阻燃性能，如下表1：
表1：
  性能   单位   测试值   试验方法
  拉伸强度   Mpa   13.7   GB1040
  断裂伸长率   ％   223   GB1040
  冲击脆化温度   -20℃   通过   GB5470
  热变形   ％   17.7   GB8815
  20℃体积电阻率   Ω.m   1.88×1011   GB1410
  介电强度   MV/m   24.5   GB1408
  氧指数   -   52.5   GB2406

Claims (3)

1.一种环保型电缆填充料，其特征在于其组成原料的重量份为：
Figure FDA0000298166141
所述的阻燃剂选自氢氧化镁或氢氧化铝中的一种或混合物。
2.根据权利要求1所述的环保型电缆填充料，其特征在于：所述的防老剂为防老剂4010。
3.一种如权利要求1所述的环保型电缆填充料的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份称取各原料，混合均匀，装入挤塑机料斗，挤塑机的机筒温度控制在130-190℃，生成熔融态混合料；
（2）在熔融态混合料中冲入氮气，取出依次通过75-95℃的热水槽和室温水槽，风干得到成品。
CN2011103151809A 2011-10-18 2011-10-18 一种环保型电缆填充料及其制备方法 Expired - Fee Related CN102399401B (zh)