CN102381729A - 一种球状四氧化三铁的制备方法 - Google Patents

一种球状四氧化三铁的制备方法 Download PDF

Info

Publication number
CN102381729A
CN102381729A CN2011102112737A CN201110211273A CN102381729A CN 102381729 A CN102381729 A CN 102381729A CN 2011102112737 A CN2011102112737 A CN 2011102112737A CN 201110211273 A CN201110211273 A CN 201110211273A CN 102381729 A CN102381729 A CN 102381729A
Authority
CN
China
Prior art keywords
preparation
spherical
reaction
settled solution
under
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011102112737A
Other languages
English (en)
Other versions
CN102381729B (zh
Inventor
陶菲菲
王林霞
沈永淼
张涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Shaoxing
Original Assignee
University of Shaoxing
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Shaoxing filed Critical University of Shaoxing
Priority to CN 201110211273 priority Critical patent/CN102381729B/zh
Publication of CN102381729A publication Critical patent/CN102381729A/zh
Application granted granted Critical
Publication of CN102381729B publication Critical patent/CN102381729B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种球状四氧化三铁的制备方法，涉及纳米材料制备领域，本发明以六水合三氯化铁为铁源，乙二醇为溶剂，常温常压下完全溶解，得到澄清溶液；再将乙酸铵加入所配制的澄清溶液中，混合得棕色澄清溶液；然后密封放置于反应釜内，加热反应12-24h；反应结束后，将反应得到的混合物进行离心分离，得到的黑色固体即为球状四氧化三铁；本发明的制备方法使用的原料易得，工艺简单，球状粒子的尺寸易于控制，可以合成出形状均一、尺寸可控的球状四氧化三铁。

Description

一种球状四氧化三铁的制备方法
技术领域：
本发明涉及纳米材料制备领域，尤其是一种利用溶剂热法合成球状四氧化三铁的制备方法。
背景技术：
四氧化三铁（Fe3O4）是一种重要的尖晶石型铁氧体，是面向21世纪的新型高功能无机材料，由于其在光、电、医药、磁介等方面具有一般块体材料无可比拟的特殊性能和新用途，所以在国防、环境工程、表面工程、化工、电子及半导体材料等领域，具有非常广泛的应用前景。
在过去的几十年里，各种制备四氧化三铁的方法倍受关注，到目前为止，已经发展了多种合成方法，如化学共沉淀法、油/水乳液法、热分解法、溶剂热合成法、声化学法、喷射分解法、弧放电法、燃烧合成法等。尽管四氧化三铁的制备研究已经取得很大进步，但是各种合成方法都存在不足。科技发展的不断进步对制备方法必然提出新的要求，不断完善现有的制备方法、探索新的合成路线，仍然是摆在科技工作者面前的重要课题。
发明内容：
本发明的目的是提供一种具有良好分散性、粒径均一、大小可控的球状四氧化三铁的制备方法。
本发明采取的技术方案如下，一种球状四氧化三铁的制备方法，包括以下步骤：
（1）、以六水合三氯化铁为铁源，乙二醇为溶剂，常温常压下，磁力搅拌使三氯化铁完全溶解，得到澄清溶液；
（2）、将乙酸铵加入步骤（1）所配制的澄清溶液中，在磁力搅拌作用下，充分混合得棕色澄清溶液；
（3）、将步骤（2）所配制的溶液密封放置于聚四氟乙烯内衬的不锈钢反应釜内，并将该反应釜置于烘箱中，以5℃/min的加热速率升温至190-200℃，并在该温度下反应12-24 h；
（4）、步骤（3）反应结束后，将反应得到的混合物进行离心分离，得到的黑色固体即为球状四氧化三铁；
（5）、将球状四氧化三铁用无水乙醇清洗干净后，在80℃的烘箱中烘干即可得成品。
进一步的设置如下：
步骤3中：加热温度为200℃，反应时间为24 h；
步骤3中：加热温度为195℃，反应时间为24 h；
步骤3中：加热温度为190℃，反应时间为12 h；
步骤5中：烘干时间为6 h以上，优选为6-8 h。
本发明的有益效果如下；
本发明的制备方法使用的原料易得，工艺简单，球状粒子的尺寸易于控制，可以合成出形状均一、尺寸可控的球状四氧化三铁。
附图说明：
图1是按实施例一所述方法制备的球状四氧化三铁的扫描电子显微镜（SEM）照片（SEM，JEOL JSM-6360LV，加速电压为10kV）；
图2是按实施例二所述方法制备的球状四氧化三铁的扫描电子显微镜（SEM）照片（SEM，JEOL JSM-6360LV，加速电压为10kV）；
图3是按实施例三所述方法制备的球状四氧化三铁的扫描电子显微镜（SEM）照片（SEM，JEOL JSM-6310LV，加速电压为10kV）。
具体实施方式：
实施例1：
按照制备过程进行，在常温常压下将3×10-3 mol FeCl3·6H2O加入25 mL乙二醇中，通过磁力搅拌，使六水合三氯化铁完全溶解，得到澄清溶液。将1.5×10-3 mol乙酸铵加入上述澄清溶液中，在磁力搅拌作用下，使其充分混合得棕色澄清溶液。将该棕色澄清溶液密封放置于容积为30 mL的聚四氟乙烯内衬的不锈钢反应釜中，并将该反应釜置于烘箱中，以5 ℃/min的加热速率升温至200 ℃，并在该温度下反应24 h。待反应结束后将得到的混合物经过离心机在10000 r/min速率下分离1 min，将得到的黑色固体用无水乙醇清洗5次以上，得到的固体在80 ℃的烘箱中进行烘干，烘干时间6 h，即可得产品。取微量上述制备的产品用无水乙醇分散得悬浊液，将此悬浊液滴在扫描电子显微镜的样品台上，自然晾干，再离子溅射镀上一层约5 nm的金属铂膜后，即可进行扫描电子显微镜（SEM）的观察（图1）。通过表征可知，产物为直径约500 nm的四氧化三铁微球。
实施例2：
按照制备过程进行，在常温常压下将3×10-3 mol FeCl3·6H2O加入25 mL乙二醇中，通过磁力搅拌，使六水合三氯化铁完全溶解，得到澄清溶液。将1.5×10-3 mol乙酸铵加入上述澄清溶液中，在磁力搅拌作用下，使其充分混合得棕色澄清溶液。将该棕色澄清溶液密封放置于容积为30 mL的聚四氟乙烯内衬的不锈钢反应釜中，并将该反应釜置于烘箱中，以5 ℃/min的加热速率升温至195 ℃，并在该温度下反应24 h。待反应结束后将得到的混合物经过离心机在10000 r/min速率下分离1 min，将得到的黑色固体用无水乙醇清洗5次以上，得到的固体在80 ℃的烘箱中进行烘干，烘干时间8 h，即可得产品。取微量上述制备的产品用无水乙醇分散得悬浊液，将此悬浊液滴在扫描电子显微镜的样品台上，自然晾干，再离子溅射镀上一层约5 nm的金属铂膜后，即可进行扫描电子显微镜（SEM）的观察（图2）。通过表征可知，产物为直径约400 nm的四氧化三铁微球。
实施例3：
按照制备过程进行，在常温常压下将1×10-3 mol FeCl3·6H2O加入25 mL乙二醇中，通过磁力搅拌，使六水合三氯化铁完全溶解，得到澄清溶液。将1.5×10-3 mol乙酸胺加入上述澄清溶液中，在磁力搅拌作用下，使其充分混合得棕色澄清溶液。将该棕色澄清溶液密封放置于容积为30 mL的聚四氟乙烯内衬的不锈钢反应釜中，并将该反应釜置于烘箱中，以5 ℃/min的加热速率升温至190 ℃，并在该温度下反应12 h。待反应结束后将得到的混合物经过离心机在10000 r/min速率下分离1 min，将得到的黑色固体用无水乙醇清洗5次以上，得到的固体在80 ℃的烘箱中进行烘干，烘干时间8 h，即可得产品。取微量上述制备的产品用无水乙醇分散得悬浊液，将此悬浊液滴在扫描电子显微镜的样品台上，自然晾干，再离子溅射镀上一层约5 nm的金属铂膜后，即可进行扫描电子显微镜（SEM）的观察（图3）。通过表征可知，产物为直径约300 nm的四氧化三铁微球。

Claims (5)

1.一种球状四氧化三铁的制备方法，其特征在于，包括以下步骤：
（1）、以六水合三氯化铁为铁源，乙二醇为溶剂，常温常压下，磁力搅拌使三氯化铁完全溶解，得到澄清溶液；
（2）、将乙酸铵加入步骤（1）所配制的澄清溶液中，在磁力搅拌作用下，充分混合得棕色澄清溶液；
（3）、将步骤（2）所配制的溶液密封放置于聚四氟乙烯内衬的不锈钢反应釜内，并将该反应釜置于烘箱中，以5℃/min的加热速率升温至190-200℃，并在该温度下反应12-24 h；
（4）、步骤（3）反应结束后，将反应得到的混合物进行离心分离，得到的黑色固体即为球状四氧化三铁；
（5）、将球状四氧化三铁用无水乙醇清洗干净后，在80℃的烘箱中烘干即可得成品。
2.根据权利要求1所述的一种球状四氧化三铁的制备方法，其特征在于：步骤3中：加热温度为200℃，反应时间为24 h。
3.根据权利要求1所述的一种球状四氧化三铁的制备方法，其特征在于：步骤3中：加热温度为195℃，反应时间为24 h。
4.根据权利要求1所述的一种球状四氧化三铁的制备方法，其特征在于：步骤3中：加热温度为190℃，反应时间为12h。
5.根据权利要求1所述的一种球状四氧化三铁的制备方法，其特征在于：步骤5中：烘干时间为6-8 h。
CN 201110211273 2011-07-27 2011-07-27 一种球状四氧化三铁的制备方法 Active CN102381729B (zh)