CN102352139B - 水溶性超细特种炭黑 - Google Patents

水溶性超细特种炭黑 Download PDF

Info

Publication number
CN102352139B
CN102352139B CN201110253775.6A CN201110253775A CN102352139B CN 102352139 B CN102352139 B CN 102352139B CN 201110253775 A CN201110253775 A CN 201110253775A CN 102352139 B CN102352139 B CN 102352139B
Authority
CN
China
Prior art keywords
carbon black
water
soluble
carbon
superfine special
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201110253775.6A
Other languages
English (en)
Other versions
CN102352139A (zh
Inventor
张常熙
张勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TANGYIN QICHANG CHEMICAL CO Ltd
Original Assignee
TANGYIN QICHANG CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TANGYIN QICHANG CHEMICAL CO Ltd filed Critical TANGYIN QICHANG CHEMICAL CO Ltd
Priority to CN201110253775.6A priority Critical patent/CN102352139B/zh
Publication of CN102352139A publication Critical patent/CN102352139A/zh
Application granted granted Critical
Publication of CN102352139B publication Critical patent/CN102352139B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及炭黑技术领域，涉及一种水溶性超细特种炭黑水材料。将炭黑、分散剂NNO按一定重量配比进行充分混配均匀，并升温至120℃～130℃，对炭黑表面的自由基进行改性，对改性后的炭黑进行气流粉碎至800～1200目，提高其分散性，使之具备与水很好的相溶性。本发明的水溶性超细特种炭黑，利用表面活性剂，在炭黑表面自由基上进行“接枝”，使炭黑的表面能降低到与所用载体相近，提高炭黑的极性，使之与水很好地相溶，成为无毒无害的水溶性炭黑产品。

Description

水溶性超细特种炭黑
技术领域
本发明涉及炭黑技术领域，涉及一种水溶性超细特种炭黑材料。
背景技术
炭黑是重要的化工原料，广泛应用于橡胶、化纤、塑料、建筑等行业中。工业炭黑分为橡胶用炭黑和特种色素炭黑，国内生产的大多数是制造轮胎用的橡胶炭黑，而特种色素炭黑生产则处于起步阶段，炭黑的主要成份是碳元素，它只溶于有机溶剂，如苯、二甲苯等。这些溶剂在使用过程中都有不同程度的毒性，造成污染环境，危害人体健康。发达国家已不准使用，国内很多行业也都禁用或限制使用。因此，开发以水为溶剂的环保型炭黑产品，替代有机溶剂的炭黑产品，是当前炭黑材料科技研发的重点项目。水溶性超细特种炭黑广泛应用于高档轿车漆、数码喷墨、高档化纤、环保涂料、塑料制品等。随着国内、外逐步限制有机溶剂炭黑的使用，水溶性超细特种炭黑产品的市场前景更加广阔。从化学工艺技术层面上分析，普通炭黑的基本元素是碳，而碳元素是不溶于水的，是没有极性的。而涂料、油漆、油墨、建筑材料等使用的介质，通常是有极性。根据化学原理，极性相近，相溶性越好；反之，相容性越差。所以在极性介质中，非极性炭黑是很难均匀分散到介质中，而导致产品的流变性差，不仅影响产品的性能，而且也不利于产品的加工和使用。分散剂NNO，也叫扩散剂NNO ，化学名称：亚甲基双萘磺酸钠，亚甲基二萘磺酸钠，萘磺酸盐甲醛缩合物，组成：亚甲基双萘磺酸钠；分子式：CH2(C10H6SO3Na)2 或 C21H14O6S2Na2 ；分子量：472.44 ；CAS号：36290-04-7；外形：米棕色粉状；溶解性能：分散剂NNO易溶于任何硬度的水中；稳定性：耐酸、耐碱、耐热、耐硬水、耐无机盐； 性能：分散剂NNO具有优良扩散性和保护胶体性能，但无渗透起泡等表面活性，对蛋白质及聚酰胺纤维有亲和力，对棉、麻等纤维无亲和力。
发明内容
本发明的目的在于提供一种水溶性超细特种炭黑，对炭黑表面的自由基进行改性，降低其表面能，使其与水的表面能相近并产生亲水离子基，经气流粉碎至所需细度。
水溶性超细特种炭黑，将炭黑、分散剂NNO按重量配比100：0.5～6.5充分混配均匀，并升温至120℃～130℃，对炭黑表面的自由基进行改性，对改性后的炭黑进行气流粉碎至800～1200目，提高其分散性，使之具备与水很好的相溶性。
本发明的水溶性超细特种炭黑，利用表面活性剂，在炭黑表面自由基上进行“接枝”，使炭黑的表面能降低到与所用载体相近，提高炭黑的极性，使之与水很好地相溶，成为无毒无害的水溶性炭黑产品。
具体实施方式
下面具体说明实现本发明的实现方式：
从化学工艺技术层面上分析，普通炭黑的基本元素是碳，而碳元素是不溶于水的，是没有极性的。而涂料、油漆、油墨、建筑材料等使用的介质，通常是有极性的。根据化学原理，极性相近，相溶性越好；反之，相溶性越差。所以在极性介质中，非极性炭黑是很难均匀分散在其中，而导致产品的流变性差，不仅影响产品的性能，而且也不利于产品的加工和使用。本发明在炭黑表面自由基上“接枝”，增加极性官能团，使之变水不分散性为可分散性。采用一种磺酸盐（NNO）类型的表面活性剂在一定温度压力下，对炭黑表面的自由基进行改性，降低其表面能，使炭黑与水的表面能相近并产生新水离子基，“接枝”后的炭黑与水有很好的相溶性，且大大提高了产品性能。
实施例1、依次称取炭黑、分散剂NNO，100㎏、0.5㎏；将其充分混配均匀，并升温至120℃～130℃，对炭黑表面的自由基进行改性，对改性后的炭黑进行气流粉碎至800目，提高其分散性，使之具备与水很好的相溶性。
实施例2、依次称取炭黑、分散剂NNO，100㎏、6.5㎏；将其充分混配均匀，并升温至120℃～130℃，对炭黑表面的自由基进行改性，对改性后的炭黑进行气流粉碎至1200目，提高其分散性，使之具备与水很好的相溶性。
实施例2、依次称取炭黑、分散剂NNO，100㎏、4.5㎏；将其充分混配均匀，并升温至120℃～130℃，对炭黑表面的自由基进行改性，对改性后的炭黑进行气流粉碎至1000目，提高其分散性，使之具备与水很好的相溶性。
　　根据本发明的配方和工艺，会有无数种组合，在实施例中不可能一一列举，只要属于本发明的实质内容以内的配方和工艺组合，都属于本发明的保护范围，此处不再赘述。

Claims (1)

1.水溶性超细特种炭黑的制备方法，其特征在于：将炭黑、分散剂NNO按重量配比100：0.5～6.5充分混配均匀，并升温至120℃～130℃，对炭黑表面的自由基进行改性，对改性后的炭黑进行气流粉碎至800～1200目。
CN201110253775.6A 2011-08-31 2011-08-31 水溶性超细特种炭黑 Active CN102352139B (zh)