CN102344137B - 一种活性炭的制备方法 - Google Patents
一种活性炭的制备方法 Download PDFInfo
- Publication number
- CN102344137B CN102344137B CN2010102449996A CN201010244999A CN102344137B CN 102344137 B CN102344137 B CN 102344137B CN 2010102449996 A CN2010102449996 A CN 2010102449996A CN 201010244999 A CN201010244999 A CN 201010244999A CN 102344137 B CN102344137 B CN 102344137B
- Authority
- CN
- China
- Prior art keywords
- temperature
- carbon slag
- activation
- suction filtration
- carbonization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种活性炭的制备方法，以柠檬酸废渣为原料，经过水解、抽滤、干燥、造粒、碳化和活化等步骤制得。本发明因为对柠檬酸废渣进行了回收利用，从而减轻废渣对环境造成的污染；并且采用气体活化法以柠檬酸废渣作为原料生产活性炭，无污染，安全环保，工艺简单；同时因为原料资源丰富，生产成本低；进一步也节约了治理环境污染的费用，取得较高的循环经济效果。
Description
技术领域
本发明涉及活性炭领域，具体涉及一种利用柠檬酸废渣制备活性炭的方法。
背景技术
柠檬酸是一种应用广泛的有机酸，可作为酸味剂和增稠剂，还可以作为清洗剂使用，广泛用于食品、饮料、医药、化工、洗涤剂等行业。受出口刺激，我国国内柠檬酸产量由2001年的38万吨增长到2005年的70万吨，2006年约80万吨，年均增加12.5%，成为世界第一柠檬酸生产大国，产量约占世界的70%。而目前多数企业在用发酵法生产柠檬酸过程中，大量的柠檬酸废渣没有综合利用，直接外排。
活性炭，是一种具有巨大比表面、多孔结构的炭。按其原料分类可分为煤质活性炭、木质炭、果壳炭和骨质炭；按其形态可分为柱状炭、破碎炭、粉末炭和纤维活性炭。活性炭的主要原料为煤、木材、果壳等富含碳元素的有机材料，通过活化而形成具有吸附能力的复杂的孔隙结构。孔隙中半径大于20000nm的为大孔，介于150-20000nm的为中孔，小于150nm的为微孔。活性炭的吸附作用主要发生在这些空隙和表面上，活性炭孔壁上大量的分子可以产生强大的引力将水和空气中的杂质吸引到孔隙中。活性炭的吸附可分为物理吸附和化学吸附。物理吸附主要发生在活性炭丰富的微孔中，用于去除水和空气中杂质，这些杂质的分子直径必须小于活性炭的孔径。不同的原材料和加工工艺造成活性炭不同的微孔结构、比表面积和孔径，适用于不同的需求。活性炭不仅含有碳元素，而且在其表面含有官能团，与被吸附的物质发生化学反应。介质中的杂质通过物理吸附和化学吸附不断进入活性炭的多孔结构中，使活性炭吸附饱和、吸附效果下降。吸附饱和后的活性炭需要进行活化再生，恢复其吸附能力，重复使用。
目前，活性炭广泛应用于水处理、溶剂回收、食品饮料提纯、空气净化、脱硫、载体、医药、黄金提炼、防毒、半导体、原子能及生物工程、纳米材料、高效催化剂载体等领域。
发明内容
为解决上述问题，本发明的目的在于提供一种活性炭的制备方法，可以对柠檬酸废渣回收利用，减轻废渣对环境造成的污染，同时工艺简单、无污染，且生产成本低，又取得较高的循环经济效果。
为达到上述目的，本发明采用的技术方案是：一种活性炭的制备方法，包括以下步骤：
（1）水解：在反应釜内泵入质量浓度为25%-35%的1800-2200L盐酸，蒸汽加热至60-70℃，再投入800-1200㎏发酵法生产柠檬酸过程中产生的废渣，蒸汽升温至90-105℃，水解反应2-5.5小时；
（2）抽滤：将上述水解后物料放入抽滤桶中进行抽滤，抽滤后的碳渣用自来水漂洗2-3次，再用质量浓度为1%-3%的氢氧化钠溶液或氢氧化铵溶液漂洗至中性，收集碳渣；
（3）干燥：将上述碳渣放入气流干燥器进行干燥，气流干燥器进口温度为140-160℃，出口温度为80-90℃，干燥至碳渣含水量为6%以下；
（4）造粒：将干燥好的碳渣按重量比100:5的比例掺入重焦油、沥青或羧甲基纤维素（CMC），充分混合后再挤压成颗粒状，制成颗粒碳渣；
（5）碳化、活化：将颗粒碳渣采用连续式回转炉法在内热式回转炉里以水蒸气、二氧化碳或空气为活化剂进行碳化、活化，即得成品活性炭，其中内热式回转炉炉头温度为900-950℃，炉尾温度为200-250℃，碳化区温度为400-420℃，活化区温度为880-900℃，碳化时间为2-2.7小时，活化时间为0.3-1小时。
其中，步骤（5）中内热式回转炉筒体转速为1-3r/min。
其中，步骤（1）中投入800-1200㎏发酵法生产柠檬酸过程中产生的废渣后，将蒸汽升温至95-105℃，水解反应2-5.5小时。能够大大提高了生产效率。
其中，步骤（5）中活化剂为空气，内热式回转炉筒体转速为2.5r/min，炉头温度为930℃，炉尾温度为215℃，碳化区温度为410℃，碳化时间为2.5小时，活化区温度为890℃，活化时间为0.5小时。
本发明采用连续式回转炉法制作活性炭，碳化、活化一道在内热式回转炉里完成，筒体用钢板制成，内衬耐火砖，在中部外套大齿轮，借以推动筒体转动，两端各有一对齿轮，支承筒体重量，炉头、炉尾均有密封装置，炭化、活化炉采用轻质柴油作为燃料，采用温度自控调节来达到。
同时，本发明采用气体活化法，活化剂通过炽热的碳层、并于碳层发生活化反应进行活化。
采用上述技术方案后，因为对柠檬酸废渣进行了回收利用，从而减轻废渣对环境造成的污染；并且采用气体活化法以柠檬酸废渣作为原料生产活性炭，无污染，安全环保，工艺简单；同时因为原料资源丰富，生产成本低；进一步也节约了治理环境污染的费用，取得较高的循环经济效果。
具体实施方式
下面结合具体实施例对本发明做进一步的说明。
实施例一
（1）水解：在反应釜内泵入质量浓度为30%的盐酸2000L，蒸汽加热至65℃，再投入1000㎏柠檬酸废渣，蒸汽升温至100℃，水解反应2.5小时。
（2）抽滤：将上述水解后物料放入抽滤桶中进行抽滤，抽滤后的碳渣用自来水漂洗2次，再用质量浓度为2%的氢氧化钠溶液漂洗至中性，收集碳渣。
（3）干燥：将上述碳渣放入气流干燥器进行干燥，气流干燥器进口温度为150℃，出口温度为85℃，干燥至碳渣含水量为6%以下；
（4）造粒：将干燥好的碳渣按重量比100:5的比例掺入羧甲基纤维素（CMC），充分混合后再挤压成颗粒状，制成颗粒碳渣；
（5）碳化、活化：将颗粒碳渣采用连续式回转炉法在内热式回转炉里进行碳化、活化，即得成品活性炭，其中内热式回转炉炉头温度为920℃，炉尾温度为220℃，碳化区温度为410℃，活化区温度为890℃，碳化时间为2.4小时，活化时间为0.6小时，筒体转速为2r/min，活化剂为空气。
所得成品活性炭136kg，纯度为92.5%。
实施例二
（1）水解：在反应釜内泵入质量浓度为25%的盐酸2200L，蒸汽加热至60℃，再投入1200㎏柠檬酸废渣，蒸汽升温至105℃，水解反应5小时。
（2）抽滤：将上述水解后物料放入抽滤桶中进行抽滤，抽滤后的碳渣用自来水漂洗3次，再用质量浓度为3%的氢氧化铵溶液漂洗至中性，收集碳渣。
（3）干燥：将上述碳渣放入气流干燥器进行干燥，气流干燥器进口温度为140℃，出口温度为80℃，干燥至碳渣含水量为6%以下；
（4）造粒：将干燥好的碳渣按重量比100:5的比例掺入重焦油，充分混合后再挤压成颗粒状，制成颗粒碳渣；
（5）碳化、活化：将颗粒碳渣采用连续式回转炉法在内热式回转炉里进行碳化、活化，即得成品活性炭，其中内热式回转炉炉头温度为900℃，炉尾温度为200℃，碳化区温度为400℃，活化区温度为880℃，碳化时间为2.7小时，活化时间为0.3小时，筒体转速为1r/min，活化剂为水蒸气。
所得成品活性炭160kg，纯度为92%。
实施例三
（1）水解：在反应釜内泵入质量浓度为25%的盐酸1800L，蒸汽加热至70℃，再投入800㎏柠檬酸废渣，蒸汽升温至90℃，水解反应2小时。
（2）抽滤：将上述水解后物料放入抽滤桶中进行抽滤，抽滤后的碳渣用自来水漂洗2次，再用质量浓度为1%的氢氧化钠溶液漂洗至中性，收集碳渣。
（3）干燥：将上述碳渣放入气流干燥器进行干燥，气流干燥器进口温度为160℃，出口温度为90℃，干燥至碳渣含水量为6%以下；
（4）造粒：将干燥好的碳渣按重量比100:5的比例掺入沥青，充分混合后再挤压成颗粒状，制成颗粒碳渣；
（5）碳化、活化：将颗粒碳渣采用连续式回转炉法在内热式回转炉里进行碳化、活化，即得成品活性炭，其中内热式回转炉炉头温度为950℃，炉尾温度为250℃，碳化区温度为420℃，活化区温度为900℃，碳化时间为2小时，活化时间为1小时，筒体转速为3r/min，活化剂为二氧化碳。
所得成品活性炭106kg，纯度为93.5%。
实施例四
（1）水解：在反应釜内泵入质量浓度为35%的盐酸2000L，蒸汽加热至68℃，再投入1100㎏柠檬酸废渣，蒸汽升温至105℃，水解反应5.5小时。
（2）抽滤：将上述水解后物料放入抽滤桶中进行抽滤，抽滤后的碳渣用自来水漂洗3次，再用质量浓度为2.5%的氢氧化铵溶液漂洗至中性，收集碳渣。
（3）干燥：将上述碳渣放入气流干燥器进行干燥，气流干燥器进口温度为150℃，出口温度为85℃，干燥至碳渣含水量为6%以下；
（4）造粒：将干燥好的碳渣按重量比100:5的比例掺入羧甲基纤维素（CMC），充分混合后再挤压成颗粒状，制成颗粒碳渣；
（5）碳化、活化：将颗粒碳渣采用连续式回转炉法在内热式回转炉里进行碳化、活化，即得成品活性炭，其中内热式回转炉炉头温度为910℃，炉尾温度为210℃，碳化区温度为405℃，活化区温度为885℃，碳化时间为2.5小时，活化时间为0.5小时，筒体转速为2r/min，活化剂为空气。
所得成品活性炭148kg，纯度为92.5%。
实施例五
（1）水解：在反应釜内泵入质量浓度为30%的盐酸2000L，蒸汽加热至70℃，再投入1000㎏柠檬酸废渣，蒸汽升温至90℃，水解反应4小时。
（2）抽滤：将上述水解后物料放入抽滤桶中进行抽滤，抽滤后的碳渣用自来水漂洗3次，再用质量浓度为3%的氢氧化铵溶液漂洗至中性，收集碳渣。
（3）干燥：将上述碳渣放入气流干燥器进行干燥，气流干燥器进口温度为155℃，出口温度为88℃，干燥至碳渣含水量为6%以下；
（4）造粒：将干燥好的碳渣按重量比100:5的比例掺入沥青，充分混合后再挤压成颗粒状，制成颗粒碳渣；
（5）碳化、活化：将颗粒碳渣采用连续式回转炉法在内热式回转炉里进行碳化、活化，即得成品活性炭，其中内热式回转炉炉头温度为9040℃，炉尾温度为230℃，碳化区温度为415℃，活化区温度为895℃，碳化时间为2.2小时，活化时间为0.8小时，筒体转速为1.5r/min，活化剂为二氧化碳。
所得成品活性炭140kg，纯度为92.5%。
实施例六
（1）水解：在反应釜内泵入质量浓度为30%的盐酸1800L，蒸汽加热至65℃，再投入900㎏柠檬酸废渣，蒸汽升温至95℃，水解反应3.5小时。
（2）抽滤：将上述水解后物料放入抽滤桶中进行抽滤，抽滤后的碳渣用自来水漂洗2次，再用质量浓度为1%的氢氧化钠溶液漂洗至中性，收集碳渣。
（3）干燥：将上述碳渣放入气流干燥器进行干燥，气流干燥器进口温度为145℃，出口温度为83℃，干燥至碳渣含水量为6%以下；
（4）造粒：将干燥好的碳渣按重量比100:5的比例掺入重焦油，充分混合后再挤压成颗粒状，制成颗粒碳渣；
（5）碳化、活化：将颗粒碳渣采用连续式回转炉法在内热式回转炉里进行碳化、活化，即得成品活性炭，其中内热式回转炉炉头温度为930℃，炉尾温度为215℃，碳化区温度为410℃，活化区温度为890℃，碳化时间为2.5小时，活化时间为0.5小时，筒体转速为2.5r/min，活化剂为空气。
所得成品活性炭120kg，纯度为95%。
实施例七
（1）水解：在反应釜内泵入质量浓度为25%的盐酸2200L，蒸汽加热至75℃，再投入1100㎏柠檬酸废渣，蒸汽升温至100℃，水解反应4.5小时。
（2）抽滤：将上述水解后物料放入抽滤桶中进行抽滤，抽滤后的碳渣用自来水漂洗3次，再用质量浓度为2.5%的氢氧化钠溶液漂洗至中性，收集碳渣。
（3）干燥：将上述碳渣放入气流干燥器进行干燥，气流干燥器进口温度为150℃，出口温度为85℃，干燥至碳渣含水量为6%以下；
（4）造粒：将干燥好的碳渣按重量比100:5的比例掺入羧甲基纤维素（CMC），充分混合后再挤压成颗粒状，制成颗粒碳渣；
（5）碳化、活化：将颗粒碳渣采用连续式回转炉法在内热式回转炉里进行碳化、活化，即得成品活性炭，其中内热式回转炉炉头温度为900℃，炉尾温度为200℃，碳化区温度为410℃，活化区温度为890℃，碳化时间为2.6小时，活化时间为0.4小时，筒体转速为2r/min，活化剂为空气。
所得成品活性炭146kg，纯度为93%。
上述具体实施例1-7中，本发明均采用连续式回转炉法制作活性炭，碳化、活化一道在内热式回转炉里完成，筒体用钢板制成，内衬耐火砖，在中部外套大齿轮，借以推动筒体转动，两端各有一对齿轮，支承筒体重量，炉头、炉尾均有密封装置，炭化、活化炉采用轻质柴油作为燃料，采用温度自控调节来达到。
同时，本发明采用气体活化法，活化剂通过炽热的碳层、并于碳层发生活化反应进行活化。
本发明采用气体活化法以柠檬酸废渣作为原料制备活性炭，因为对柠檬酸废渣进行了回收利用，从而减轻废渣对环境造成的污染；并且采用气体活化法以柠檬酸废渣作为原料生产活性炭，无污染、安全环保，工艺简单；同时因为原料资源丰富，生产成本低；进一步也节约了治理环境污染的费用，取得较高的循环经济效果。
Claims (4)
1.一种活性炭的制备方法，其特征在于，包括以下步骤：
（1）水解：在反应釜内泵入质量浓度为25%-35%的1800-2200L盐酸，蒸汽加热至60-70℃，再投入800-1200㎏发酵法生产柠檬酸过程中产生的废渣，蒸汽升温至90-105℃，水解反应2-5.5小时；
（2）抽滤：将上述水解后物料放入抽滤桶中进行抽滤，抽滤后的碳渣用自来水漂洗2-3次，再用质量浓度为1%-3%的氢氧化钠溶液或氢氧化铵溶液漂洗至中性，收集碳渣；
（3）干燥：将上述碳渣放入气流干燥器进行干燥，气流干燥器进口温度为140-160℃，出口温度为80-90℃，干燥至碳渣含水量为6%以下；
（4）造粒：将干燥好的碳渣按重量比100:5的比例掺入重焦油、沥青或羧甲基纤维素（CMC），充分混合后再挤压成颗粒状，制成颗粒碳渣；
（5）碳化、活化：将颗粒碳渣采用连续式回转炉法在内热式回转炉里以水蒸气、二氧化碳或空气为活化剂进行碳化、活化，即得成品活性炭，其中内热式回转炉炉头温度为900-950℃，炉尾温度为200-250℃，碳化区温度为400-420℃，活化区温度为880-900℃，碳化时间为2-2.7小时，活化时间为0.3-1小时。
2.根据权利要求1所述的一种活性炭的制备方法，其特征在于，步骤（5）中内热式回转炉筒体转速为1-3r/min。
3.根据权利要求1所述的一种活性炭的制备方法，其特征在于，步骤（1）中投入800-1200㎏发酵法生产柠檬酸过程中产生的废渣后，将蒸汽升温至95-105℃，水解反应2-5.5小时。
4.据权利要求1所述的一种活性炭的制备方法，其特征在于，步骤（5）中活化剂为空气，内热式回转炉筒体转速为2.5r/min，炉头温度为930℃，炉尾温度为215℃，碳化区温度为410℃，碳化时间为2.5小时，活化区温度为890℃，活化时间为0.5小时。