CN102335652A - 手感弹性漆喷涂工艺 - Google Patents

手感弹性漆喷涂工艺 Download PDF

Info

Publication number
CN102335652A
CN102335652A CN2011102055005A CN201110205500A CN102335652A CN 102335652 A CN102335652 A CN 102335652A CN 2011102055005 A CN2011102055005 A CN 2011102055005A CN 201110205500 A CN201110205500 A CN 201110205500A CN 102335652 A CN102335652 A CN 102335652A
Authority
CN
China
Prior art keywords
curing agent
feel
spraying
elastomeric paint
paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102055005A
Other languages
English (en)
Inventor
陆琪宏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HANGZHOU SANJING ART CRAFT PLASTIC CO Ltd
Original Assignee
HANGZHOU SANJING ART CRAFT PLASTIC CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HANGZHOU SANJING ART CRAFT PLASTIC CO Ltd filed Critical HANGZHOU SANJING ART CRAFT PLASTIC CO Ltd
Priority to CN2011102055005A priority Critical patent/CN102335652A/zh
Publication of CN102335652A publication Critical patent/CN102335652A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种手感弹性漆喷涂工艺，所述工艺采用如下步骤：(1)喷涂底材的表面处理：对喷涂底材进行常规前处理，改变喷涂底材的表面性质；所述喷涂底材为高分子材料；(2)调制手感弹性漆：在手感弹性漆主剂中加入8％-12％重量比的固化剂；所述主剂中包含聚酯树脂；所述固化剂为异氰酸酯类固化剂；(3)稀释手感弹性漆：往上述调制好的手感弹性漆中加入25％-33％重量比的稀释水；(4)喷涂手感弹性漆，涂层厚度为30μm-35μm；(5)烘干：烘箱温度为70℃-80℃，烘烤时间为30min-60min。本发明的手感弹性漆喷涂工艺，应用范围更为广泛，可对多种高分子底材喷涂手感弹性漆；喷涂效果均匀且牢固，并提高了漆膜的耐磨度和柔软度。

Description

手感弹性漆喷涂工艺
技术领域
本发明涉及一种喷漆工艺，具体讲是一种手感弹性漆喷涂工艺。
背景技术
手感弹性漆就是一种上漆后的物件表面能给人以柔和质感的油漆。手感弹性漆对手感的要求一般有两种，一类是类似橡胶或人类皮肤的弹性感觉。第二类象绒毛的弹性感觉。
给底材喷涂手感弹性漆可满足某些产品对光滑、细腻、柔软触感的需求，一般而言所述底材为ABS塑料(即丙烯腈-丁二烯-苯乙烯塑料)，而且喷涂后的烘烤参数往往没有明确设置，手感弹性漆和塑料表面的结合度不够好，漆膜不仅容易脱落，而且容易被刮伤和磨损。
而在其他高分子底材上喷涂手感弹性漆，更是存在很大的技术缺陷，不仅漆膜的耐磨度和柔软度无法满足品质要求，而且上漆往往不够均匀。
发明内容
本发明所要解决的技术问题是提供一种可在多种高分子材料上喷涂、上漆效果佳、有较好的耐磨度和柔软度的手感弹性漆喷涂工艺。
为解决上述技术问题，本发明的手感弹性漆喷涂工艺，它包括如下步骤：
(1)喷涂底材的表面处理：对喷涂底材进行常规前处理，改变喷涂底材的表面性质；所述喷涂底材为高分子材料；
(2)调制手感弹性漆：在手感弹性漆主剂中加入8％-12％重量比的固化剂；所述主剂中包含聚酯树脂；所述固化剂为异氰酸酯类固化剂；
(3)稀释手感弹性漆：往上述调制好的手感弹性漆中加入25％-33％重量比的稀释水；
(4)喷涂手感弹性漆，涂层厚度为30μm-35μm；
(5)烘干：烘箱温度为70℃-80℃，烘烤时间为30min-60min。
作为优选，所述喷涂底材为尼龙、丙烯腈-丁二烯-苯乙烯塑料(ABS塑料)、聚碳酸酯(PC)树脂、聚丙烯共聚物(PP)、聚乙烯共聚物(PE)、苯乙烯-丁二烯共聚物(K料)。
作为优选，所述聚酯树脂为带羟基的直链聚酯树脂或带羟基、有少许支链的改性聚酯树脂。
作为优选，所述固化剂为HDI(即六亚甲基二异氰酸酯)三聚体型固化剂或HDI缩二脲型固化剂。
作为进一步优选，所述HDI三聚体型固化剂为拜耳N3390、拜耳N3300、旭化成TPA-100、旭化成TPA-90、罗迪亚HDT90，所述HDI缩二脲型固化剂为拜耳N75或旭化成75-MPX。
本发明的手感弹性漆喷涂工艺，与现有技术相比，具有如下优点：
(1)应用范围更为广泛，可对多种高分子底材喷涂手感弹性漆；
(3)通过调整固化剂和稀释水的分量，促进高分子底材和手感弹性漆的有机结合，使喷涂效果均匀且牢固，并提高了漆膜的耐磨度和柔软度；
(4)通过调整烘箱温度和烘烤时间，进一步改善了漆膜的耐磨度和柔软度。
具体实施方式
下面结合具体实施例对本发明作进一步详细的说明，但本发明不局限于以下实施例。
实施例1
(1)喷涂底材的表面处理：对尼龙进行常规前处理，改变其表面性质；
(2)调制手感弹性漆：在含直链聚酯树脂的手感弹性漆主剂中加入8％重量比的固化剂拜耳N3300；
(3)稀释手感弹性漆：往上述调制好的手感弹性漆中加入25％重量比的稀释水；
(4)喷涂手感弹性漆，涂层厚度为30μm；
(5)烘干：烘箱温度为70℃，烘烤时间为40min。
烘干后产品表面用干净手触摸，有光滑、细腻、柔软的触感；
用指甲横刮和竖刮，没有将漆膜刮伤，也没有留下明显痕迹，指甲印痕基本上可以抹净。
实施例2
(1)喷涂底材的表面处理：对PC料进行常规前处理，改变其表面性质；
(2)调制手感弹性漆：在含直链聚酯树脂的手感弹性漆主剂中加入12％重量比的固化剂拜耳N75；
(3)稀释手感弹性漆：往上述调制好的手感弹性漆中加入30％重量比的稀释水；
(4)喷涂手感弹性漆，涂层厚度为30μm；
(5)烘干：烘箱温度为80℃，烘烤时间为50min。
烘干后产品表面用干净手触摸，有光滑、细腻、柔软的触感；
用指甲横刮和竖刮，没有将漆膜刮伤，也没有留下明显痕迹，指甲印痕基本上可以抹净。
实施例3
(1)喷涂底材的表面处理：对PP料进行常规前处理，改变其表面性质；
(2)调制手感弹性漆：在含改性聚酯树脂的手感弹性漆主剂中加入12％重量比的固化剂拜耳N3390；
(3)稀释手感弹性漆：往上述调制好的手感弹性漆中加入28％重量比的稀释水；
(4)喷涂手感弹性漆，涂层厚度为35μm；
(5)烘干：烘箱温度为75℃，烘烤时间为60min。
烘干后产品表面用干净手触摸，有光滑、细腻、柔软的触感；
用指甲横刮和竖刮，没有将漆膜刮伤，也没有留下明显痕迹，指甲印痕基本上可以抹净。
实施例4
(1)喷涂底材的表面处理：对PE料进行常规前处理，改变其表面性质；
(2)调制手感弹性漆：在含改性聚酯树脂的手感弹性漆主剂中加入12％重量比的固化剂罗迪亚HDT90；
(3)稀释手感弹性漆：往上述调制好的手感弹性漆中加入33％重量比的稀释水；
(4)喷涂手感弹性漆，涂层厚度为35μm；
(5)烘干：烘箱温度为75℃，烘烤时间为50min。
烘干后产品表面用干净手触摸，有光滑、细腻、柔软的触感；
用指甲横刮和竖刮，没有将漆膜刮伤，也没有留下明显痕迹，指甲印痕基本上可以抹净。
实施例5
(1)喷涂底材的表面处理：对ABS塑料进行常规前处理，改变其表面性质；
(2)调制手感弹性漆：在含改性聚酯树脂的手感弹性漆主剂中加入10％重量比的固化剂拜耳N3300；
(3)稀释手感弹性漆：往上述调制好的手感弹性漆中加入30％重量比的稀释水；
(4)喷涂手感弹性漆，涂层厚度为30μm；
(5)烘干：烘箱温度为70℃，烘烤时间为50min。
烘干后产品表面用干净手触摸，有光滑、细腻、柔软的触感；
用指甲横刮和竖刮，没有将漆膜刮伤，也没有留下明显痕迹，指甲印痕基本上可以抹净。
实施例6
(1)喷涂底材的表面处理：对K料进行常规前处理，改变其表面性质；
(2)调制手感弹性漆：在含直链聚酯树脂的手感弹性漆主剂中加入9％重量比的固化剂拜耳N3300；
(3)稀释手感弹性漆：往上述调制好的手感弹性漆中加入30％重量比的稀释水；
(4)喷涂手感弹性漆，涂层厚度为35μm；
(5)烘干：烘箱温度为70℃，烘烤时间为55min。
烘干后产品表面用干净手触摸，有光滑、细腻、柔软的触感；
用指甲横刮和竖刮，没有将漆膜刮伤，也没有留下明显痕迹，指甲印痕基本上可以抹净。
实施例7
(1)喷涂底材的表面处理：对K料进行常规前处理，改变其表面性质；
(2)调制手感弹性漆：在含改性聚酯树脂的手感弹性漆主剂中加入12％重量比的固化剂旭化成TPA-90；
(3)稀释手感弹性漆：往上述调制好的手感弹性漆中加入32％重量比的稀释水；
(4)喷涂手感弹性漆，涂层厚度为30μm；
(5)烘干：烘箱温度为70℃，烘烤时间为50min。
烘干后产品表面用干净手触摸，有光滑、细腻、柔软的触感；
用指甲横刮和竖刮，没有将漆膜刮伤，也没有留下明显痕迹，指甲印痕基本上可以抹净。
实施例8
(1)喷涂底材的表面处理：对PP料进行常规前处理，改变其表面性质；
(2)调制手感弹性漆：在含改性聚酯树脂的手感弹性漆主剂中加入10％重量比的固化剂旭化成TPA-90；
(3)稀释手感弹性漆：往上述调制好的手感弹性漆中加入30％重量比的稀释水；
(4)喷涂手感弹性漆，涂层厚度为30μm；
(5)烘干：烘箱温度为80℃，烘烤时间为60min。
烘干后产品表面用干净手触摸，有光滑、细腻、柔软的触感；
用指甲横刮和竖刮，没有将漆膜刮伤，也没有留下明显痕迹，指甲印痕基本上可以抹净。

Claims (8)

1.一种手感弹性漆喷涂工艺，其特征在于：所述工艺采用如下步骤：
(1)喷涂底材的表面处理：对喷涂底材进行常规前处理，改变喷涂底材的表面性质；所述喷涂底材为高分子材料；
(2)调制手感弹性漆：在手感弹性漆主剂中加入8％-12％重量比的固化剂；所述主剂中包含聚酯树脂；所述固化剂为异氰酸酯类固化剂；
(3)稀释手感弹性漆：往上述调制好的手感弹性漆中加入25％-33％重量比的稀释水；
(4)喷涂手感弹性漆，涂层厚度为30μm-35μm；
(5)烘干：烘箱温度为70℃-80℃，烘烤时间为30min-60min。
2.根据权利要求1所述的手感弹性漆喷涂工艺，其特征在于：所述喷涂底材为尼龙、丙烯腈-丁二烯-苯乙烯塑料、聚碳酸酯树脂、聚丙烯共聚物、聚乙烯共聚物、苯乙烯-丁二烯共聚物。
3.根据权利要求1所述的手感弹性漆喷涂工艺，其特征在于：所述聚酯树脂为带羟基的直链聚酯树脂或带羟基、有少许支链的改性聚酯树脂。
4.根据权利要求1所述的手感弹性漆喷涂工艺，其特征在于：所述固化剂为HDI三聚体型固化剂或HDI缩二脲型固化剂。
5.根据权利要求4所述的手感弹性漆喷涂工艺，其特征在于：所述HDI三聚体型固化剂为拜耳N3390、拜耳N3300、旭化成TPA-100、旭化成TPA-90、罗迪亚HDT90，所述HDI缩二脲型固化剂为拜耳N75或旭化成75-MPX。
6.根据权利要求1所述的手感弹性漆喷涂工艺，其特征在于：所述喷涂底材为尼龙、丙烯腈-丁二烯-苯乙烯塑料、聚碳酸酯树脂、聚丙烯共聚物、聚乙烯共聚物、苯乙烯-丁二烯共聚物；所述聚酯树脂为带羟基的直链聚酯树脂或带羟基、有少许支链的改性聚酯树脂。
7.根据权利要求6所述的手感弹性漆喷涂工艺，其特征在于：所述固化剂为HDI三聚体型固化剂或HDI缩二脲型固化剂。
8.根据权利要求7所述的手感弹性漆喷涂工艺，其特征在于：所述HDI三聚体型固化剂为拜耳N3390、拜耳N3300、旭化成TPA-100、旭化成TPA-90、罗迪亚HDT90，所述HDI缩二脲型固化剂为拜耳N75或旭化成75-MPX。
CN2011102055005A 2011-07-21 2011-07-21 手感弹性漆喷涂工艺 Pending CN102335652A (zh)