CN102328484A - 一种环保拉伸缠绕膜 - Google Patents

一种环保拉伸缠绕膜 Download PDF

Info

Publication number
CN102328484A
CN102328484A CN201110049819A CN201110049819A CN102328484A CN 102328484 A CN102328484 A CN 102328484A CN 201110049819 A CN201110049819 A CN 201110049819A CN 201110049819 A CN201110049819 A CN 201110049819A CN 102328484 A CN102328484 A CN 102328484A
Authority
CN
China
Prior art keywords
lldpe
percent
mass
mlldpe
intermediate layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201110049819A
Other languages
English (en)
Inventor
陈建朝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XIAMEN JUFU PLASTIC PRODUCTS CO Ltd
Original Assignee
XIAMEN JUFU PLASTIC PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XIAMEN JUFU PLASTIC PRODUCTS CO Ltd filed Critical XIAMEN JUFU PLASTIC PRODUCTS CO Ltd
Priority to CN201110049819A priority Critical patent/CN102328484A/zh
Publication of CN102328484A publication Critical patent/CN102328484A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种拉伸缠绕膜，按重量百分比由80%中间层和两个10%表层组成，表层由9.8～0%LLDPE、0～7%MLLDPE（即茂金属线性低密度聚乙烯）和0.2～3%聚异丁烯混合而成，中间层由79～0%LLDPE、0～65%MLLDPE和1～15%NHC2（NanoHybridCapsule2即纳米复合胶囊）混合而成。本发明减少了燃烧时二氧化碳的排放量。

Description

一种环保拉伸缠绕膜
技术领域
本发明涉及一种包装用拉伸缠绕膜，特别与拉伸缠绕膜的结构有关。 
背景技术
拉伸缠绕膜大多采用线性低密度聚乙烯（ Linear Low Density Polyethylene ），英文缩写为LLDPE制成。LLDPE是通常在低温度和压力下，由乙烯和高级的a烯烃如丁烯、己烯或辛烯共聚合而生成。按共聚单体类型。LLDPE产品无毒、无味、无臭，呈乳白色颗粒，具有强度高、韧性好、刚性强、耐热、耐寒等优点，还具有良好的耐环境应力开裂、耐撕裂强度等性能，并可耐酸、碱、有机溶剂等。线形低密度聚乙烯由于较高的抗张强度、较好的抗穿刺和抗撕裂性能，主要用于制造薄膜。 
现有技术中，拉伸缠绕膜的结构按重量百分比由80%中间层和两个10%表层组成，中间层为LLDPE，表层为LLDPE。 
上述拉伸缠绕膜废弃后，作为垃圾被焚烧处理时，发热的塑料先液化后气化，气化的可燃性气体与周围的氧相结合(即氧化)，形成可燃性混合气，即产生了“火焰”，经燃烧热分解的部分则变成二氧化碳和水。大量的二氧化碳被排放，促使大气的温室效应随之增强，已引起全球气候变暖等一系列严重问题，引起了全世界各国的关注。 
因此，研发一种新型拉伸缠绕膜，以减少燃烧时二氧化碳的排放量，实有必要。 
发明内容
本发明的目在于提供一种环保拉伸缠绕膜，以减少燃烧时二氧化碳的排放量。 
为了达成上述目的，本发明的解决方案是： 
一种拉伸缠绕膜，按重量百分比由80%中间层和两个10%表层组成，表层由9.8～0%LLDPE、0～7%MLLDPE（即茂金属线性低密度聚乙烯）和0.2～3%聚异丁烯混合而成，中间层由79～0%LLDPE、0～65%MLLDPE和1～15%NHC2（Nano Hybrid Capsule2即纳米复合胶囊）混合而成。
所述表层由9.8～7%LLDPE和0.2～3%聚异丁烯混合而成，中间层由77～65%LLDPE和3～15%NHC2混合而成。 
所述表层由8.8～0%LLDPE、1～7%MLLDPE和0.2～3%聚异丁烯混合而成，中间层由78～0%LLDPE 、1～65%MLLDPE和1～15%NHC2混合而成。 
所述表层由8.8～0%LLDPE、1～7%MLLDPE和0.2～3%聚异丁烯混合而成，中间层由77～65%LLDPE和3～15%NHC2混合而成。 
所述表层由9.8～7%LLDPE和0.2～3%聚异丁烯混合而成，中间层由78～0%LLDPE 、1～65%MLLDPE和1～15%NHC2混合而成。 
采用上述方案后，本发明因为在中间层加入了NHC2，所谓NHC2是一种新型的塑料添加剂，它是通过在备受关注的作为环境协调型溶媒的超临界液体里，有效利用二氧化碳的这种新技术研制而成的纳米胶囊。所以，当本发明的新型拉伸缠绕膜废弃后，作为垃圾被焚烧时，聚乙烯热分解表面发生龟裂，然后氧气侵入，此时NHC2能够吸收结合侵入的氧，生成纤密的碳化膜（阻塞膜），通过阻塞效果阻断氧的侵入，使可发热性物质与氧难以结合促进其碳化，从而减少燃烧时二氧化碳的排放量。 
具体实施方式
本发明揭示的一种拉伸缠绕膜，按重量百分比由80%中间层和两个10%表层组成，表层由9.8～0%LLDPE、0～7%MLLDPE和0.2～3%聚异丁烯混合而成，中间层由79～0%LLDPE、0～65%MLLDPE和1～15%NHC2混合而成。 
本发明的加工流程如下。 
一、拌料工艺配方 
实施例一：
工艺配方（每100公斤配比比例）：两个表层各9.8～7公斤LLDPE和0.2～3公斤聚异丁烯，中间层79～65公斤LLDPE和1～15公斤NHC2。
实施例二： 
工艺配方（每100公斤配比比例）：两个表层各8.8～0公斤LLDPE、1～7公斤MLLDPE和0.2～3公斤聚异丁烯，中间层由78～0公斤LLDPE、1～65公斤MLLDPE和1～15公斤NHC2。
实施例三： 
工艺配方（每100公斤配比比例）：两个表层各8.8～0公斤LLDPE、1～7公斤MLLDPE和0.2～3公斤聚异丁烯，中间层79～65公斤LLDPE和1～15公斤NHC2。
实施例四： 
工艺配方（每100公斤配比比例）：两个表层各8.8～0公斤LLDPE、1～7公斤MLLDPE和0.2～3公斤聚异丁烯，中间层由78～0公斤LLDPE、1～65公斤MLLDPE和1～15公斤NHC2。
二、主要的温度控制（整体加热时间约为1.5-2小时）： 
模头的温度：230～260度（前后），230～260度（左右）；
换网联接体：230～260度；
机筒温度：1）160～180度  2）210～230度  3）230～260度。
三、挤压成型（规格）：450mm*(0.015～0.025)mm；500mm*(0.015～0.025)mm。 
四、包装：采用纸箱、塑料袋、编制袋等包装。 
上述实施例并非限定本发明的产品形态和式样，任何所属技术领域的普通技术人员对其所做的适当变化或修饰，皆应视为不脱离本发明的专利范畴。 

Claims (5)

1.一种拉伸缠绕膜，按重量百分比由80%中间层和两个10%表层组成，其特征在于：表层由9.8～0%LLDPE、0～7%MLLDPE和0.2～3%聚异丁烯混合而成，中间层由79～0%LLDPE、0～65%MLLDPE和1～15%NHC2混合而成。
2.如权利要求1所述的一种拉伸缠绕膜，其特征在于：所述表层由9.8～7%LLDPE和0.2～3%聚异丁烯混合而成，中间层由79～65%LLDPE和1～15%NHC2混合而成。
3.如权利要求1所述的一种拉伸缠绕膜，其特征在于：所述表层由8.8～0%LLDPE、1～7%MLLDPE和0.2～3%聚异丁烯混合而成，中间层由78～0%LLDPE、1～65%MLLDPE和1～15%NHC2混合而成。
4.如权利要求1所述的一种拉伸缠绕膜，其特征在于：所述表层由8.8～0%LLDPE、1～7%MLLDPE和0.2～3%聚异丁烯混合而成，中间层由79～65%LLDPE和1～15%NHC2混合而成。
5.如权利要求1所述的一种拉伸缠绕膜，其特征在于：所述表层由9.8～7%LLDPE和0.2～3%聚异丁烯混合而成，中间层由78～0%LLDPE、1～65%MLLDPE和1～15%NHC2混合而成。
CN201110049819A 2011-03-02 2011-03-02 一种环保拉伸缠绕膜 Pending CN102328484A (zh)