CN102305843A - 铅或铅钙合金中是否含有锑的快速鉴定方法 - Google Patents
铅或铅钙合金中是否含有锑的快速鉴定方法 Download PDFInfo
- Publication number
- CN102305843A CN102305843A CN201110059149A CN201110059149A CN102305843A CN 102305843 A CN102305843 A CN 102305843A CN 201110059149 A CN201110059149 A CN 201110059149A CN 201110059149 A CN201110059149 A CN 201110059149A CN 102305843 A CN102305843 A CN 102305843A
- Authority
- CN
- China
- Prior art keywords
- lead
- antimony
- plumbum
- calcium alloy
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铅或铅钙合金中是否含有锑的快速鉴定方法，应用于铅酸蓄电池生产领域，其利用含锑的铅合金在滴了浓硝酸后会出现白色物质，而不含锑的铅或铅钙合金与浓硝酸不发生反应的原理，实现快捷地在现场检测出铅或铅钙合金中是否含有锑；对于Pb-Ca和Pb-Sb合金混淆时，能快速、及时的区分开两种合金，保证生产进度及产品质量，且操作简单、易掌握。
Description
技术领域
本发明涉及一种锑的快速鉴定方法，尤其涉及铅酸蓄电池行业中对铅或铅钙合金与锑或铅锑合金的快速区分方法。
背景技术
铅酸蓄电池常用的合金成份为Pb-Ca和Pb-Sb合金，如果是采用Pb-Ca生产的极板，将极板组成极群时就不允许使用任何Pb-Sb合金，因为这将导致形成3相PbSbCa，对电池的汇流排产生很大的腐蚀。由于Pb-Ca合金和Pb-Sb合金混用会造成电池腐蚀问题，而在生产使用中此两种合金时很容易混淆，发生电池质量问题。为达到准确的区别目的，同时要顾及生产效率，因此，行业中迫切需要一种简单快捷的区分、鉴定方法。
发明内容
本发明要解决的主要技术问题是，提供一种铅或铅钙合金中是否含有锑的快速鉴定方法，其能快速将锑或锑合金从铅或铅钙合金中区分出来，能用于避免Pb-Ca和Pb-Sb合金混用。
为解决上述技术问题，本发明提供一种铅或铅钙合金中是否含有锑的快速鉴定方法，其流程为：
A、将样品进行表面处理，产生到3-5平方厘米的平面；面积太大，浪费材料，面积太小，对比不明显，不以观察。
B、在平面上滴入1-2滴浓硝酸；这是定性分析，故滴1-2滴浓硝酸即可观察到现象。
C、静置1-5分钟；观察到现象时间与环境温度有关系。常温1分钟即可观察到现象，温度越高，反应越快，酸挥发越快，观察到现象的时间越短，现象越明显。
D、观察平面处是否产生白色物质；若产生白色物质则合金中含锑，未产生白色物质则合金中未含锑。
所述A步骤中，通过表面打磨产生所述平面。
所述B步骤中，浓硝酸指浓度为65％-68％的硝酸。这里浓度指质量分数。
所述C步骤中，样品中若含有锑，其与浓硝酸发生化学反应，化学式为：2Sb+10HNO3(浓)→Sb2O5+10NO2↑+5H2O
所述D步骤中，待平面处干燥后白色物质呈白色的粉末。
还包括有以下步骤：
E、对平面处白色物质进行清理；
F、样品转入蓄电池生产工艺。即试验后的器件可以用于电池制造。
所述平面处白色物质通过水洗擦干的方式清理。
本发明的有益效果是：
通过利用锑或铅锑合金在滴了浓硝酸后会出现白色物质，而不含锑的铅钙合金和电解铅与浓硝酸不发生反应的原理，实现方便快捷地在现场检测出铅或铅钙合金中是否含有锑；对于Pb-Ca和Pb-Sb合金混淆时，能快速、及时的区分开两种合金，保证生产进度及产品质量，且操作简单、易掌握。
附图说明
图1为本发明实验效果图。
具体实施方式
下面通过具体实施方式结合附图对本发明作进一步详细说明。
一种铅或铅钙合金中是否含有锑的快速鉴定方法，流程为：
A、将样品进行表面处理，产生到3-5平方厘米的平面；
B、在平面上滴入1-2滴浓硝酸；
C、静置1-5分钟；
D、观察平面处是否产生白色物质；若产生白色物质则合金中含锑，未产生白色物质则合金中未含锑。
在实施时，
所述A步骤中，通过表面打磨产生所述平面。可以是抛光机打磨，也可以是简单的手工打磨。
所述B步骤中，浓硝酸指质量份数为65％-68％的硝酸。这里采用的是实验室常用硝酸浓度，提高可操作性。
所述C步骤中，样品中若含有锑，其与浓硝酸发生化学反应，化学式为：2Sb+10HNO3(浓)→Sb2O5+10NO2↑+5H2O。
所述D步骤中，待平面处干燥后白色物质呈白色的粉末。
实施时，还可包括有以下步骤：
E、对平面处白色物质进行清理；
F、样品转入蓄电池生产工艺。
因为该检验方法的简单性与便捷性，故可在达到准确的验证结果同时，保证生产不中断。
所述平面处白色物质可以通过水洗擦干的方式清理。
本发明原理通过实验验证的方法如下：
实验器材及药品：Pb-Ca合金块、电解铅块(纯铅)、Pb-Sb合金三份(Sb含量分别为0.1％、0.2％、0.5％)各两块，浓硝酸(质量份数65％-68％)，玻璃棒。
实验原理：锑能够与浓硝酸反应生产颜色为白色或黄色晶体的五氧化二锑。而钙、铅不与浓硝酸反应。
化学式：2Sb+10HNO3(浓)→Sb2O5+10NO2↑+5H2O
实验方法：将预先配置好的几种样品平放在试验台上，朝上的一面为处理过的干净且平整的面。用玻璃棒蘸取浓硝酸分别滴两滴硝酸在合金的表面上。静置1-2分钟，即可观察到现象。
实验现象：含有锑的合金在滴加浓硝酸一分钟后表面出现白色物质，表面的硝酸干了之后为白色的粉末。而不含锑的铅钙合金和电解铅表面均未出现白色物质，表面没有任何反应迹象。
如图1所示，上下对应的样品成分相同；自左至右，前三对是含有锑的铅钙合金，含锑量依次分别是：0.1％、0.2％、0.5％。第四对为不含锑的铅钙合金。最后一个是电解铅快。可以很明显的看到含有锑的合金表面有白色的物质，是锑的氧化物。而不含锑的铅钙合金表面和纯的电解铅表面则看不到反应和白色粉末的出现。
以上内容是结合具体的实施方式对本发明所作的进一步详细说明，不能认定本发明的具体实施只局限于这些说明。对于本发明所属技术领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干简单推演或替换，都应当视为属于本发明的保护范围。
Claims (7)
1.一种铅或铅钙合金中是否含有锑的快速鉴定方法，其特征在于，流程为：
A、将样品进行表面处理，产生到3-5平方厘米的平面；
B、在平面上滴入1-2滴浓硝酸；
C、静置1-5分钟；
D、观察平面处是否产生白色物质；若产生白色物质则合金中含锑，未产生白色物质则合金中未含锑。
2.如权利要求1所述的铅或铅钙合金中是否含有锑的快速鉴定方法，其特征在于，所述A步骤中，通过表面打磨产生所述平面。
3.如权利要求1所述的铅或铅钙合金中是否含有锑的快速鉴定方法，其特征在于，所述B步骤中，浓硝酸指质量份数为65％-68％的硝酸。
4.如权利要求1所述的铅或铅钙合金中是否含有锑的快速鉴定方法，其特征在于，所述C步骤中，样品中若含有锑，其与浓硝酸发生化学反应，化学式为：2Sb+10HNO3(浓)→Sb2O5+10NO2↑+5H2O。
5.如权利要求1所述的铅或铅钙合金中是否含有锑的快速鉴定方法，其特征在于，所述D步骤中，待平面处干燥后白色物质呈白色的粉末。
6.如权利要求1至5任一项所述的铅或铅钙合金中是否含有锑的快速鉴定方法，其特征在于，还包括有以下步骤：
E、对平面处白色物质进行清理；
F、样品转入蓄电池生产工艺。
7.如权利要求6所述的铅或铅钙合金中是否含有锑的快速鉴定方法，其特征在于，所述平面处白色物质通过水洗擦干的方式清理。