CN102304352A - 一种钻井液降滤失剂 - Google Patents
一种钻井液降滤失剂 Download PDFInfo
- Publication number
- CN102304352A CN102304352A CN201110127803A CN201110127803A CN102304352A CN 102304352 A CN102304352 A CN 102304352A CN 201110127803 A CN201110127803 A CN 201110127803A CN 201110127803 A CN201110127803 A CN 201110127803A CN 102304352 A CN102304352 A CN 102304352A
- Authority
- CN
- China
- Prior art keywords
- parts
- solution
- sulfonated
- sodium carbonate
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种钻井液降滤失剂，其制备方法是：先将40克去离子水放入反应釜内，再把2克碳酸钠加入釜中搅拌使之溶解，再把5克2-丙烯酰胺基-2-甲基丙烯磺酸加入上述溶液内中和，将15克丙烯酰胺和0.6克乙烯基吡咯烷酮依次倒入中和溶液内搅拌溶解，再依次将0.1克过硫酸铵和0.1克过硫酸氢钠加入溶液内搅拌均匀，把溶液转入捏合釜中反应聚合，然后将2克甲醛、40克磺化褐煤和40克磺甲基酚醛树脂倒入捏合釜内搅拌均匀，取出聚合物料，放在烘干设备上烘干，再粉碎，过80目筛即可。适用于各种水基钻井液和在高温深井、盐膏层中使用，具有抗高温、抗盐性能好的优点。
Description
技术领域：
本发明涉及钻井液性能的控制，特别是一种具有抗高温、抗盐的钻井液降滤失剂。
背景技术：
在石油钻井过程中，遇到的地层日趋复杂，特别是在特殊井、超深井和复杂井数量越来越多的情况下，现有的钻井液降滤失剂由于抗高温、抗盐性能较差，增加外加剂的用量后，粘度也随之提高，特别是在钙、镁离子含量高的情况下，钻井液的性能更加难以控制，现有的钻井液降滤失剂已不能满足钻井需要。
发明内容：
本发明的目的是提供一种具有抗高温、抗盐性能好的钻井液降滤失剂。
本发明的技术方案是以如下方式完成的，它包括有以下重量组份：2一丙烯胺基一2一甲基丙烯磺酸5份，丙烯酰胺15份，碳酸钠2份，去离子水40份，过硫酸铵0.1份，磺化褐煤40份，磺甲基酚醛树脂40份，甲醛2份，乙烯基吡咯烷酮0.6份，其制备方法是：①先将去离子水放入反应釜内，再把碳酸钠加入釜中搅拌使之溶解，②再把2一丙烯酰胺基一2一甲基丙烯磺酸加入上述溶液内中和，保持中和的PH值为10-12，③将丙烯酰胺和乙烯基吡咯烷酮依次倒入中和溶液内进行搅拌溶解，再依次将过硫酸铵和过硫酸氢钠加入溶液内搅拌均匀，再把溶液转入捏合釜中保持温度在34-38℃静置反应聚合5个小时，④然后将甲醛、磺化褐煤和磺甲基酚醛树脂倒入捏合釜内搅拌均匀，取出聚合物料，放在烘干设备上于100-105℃温度烘干，把料块粉碎，过80目筛即是本剂。
本发明的钻井液降滤失剂具有抗高温、抗盐性能好的优点，可适用于各种水基钻井液和在高温深井、盐膏层中使用。
具体实施方式：
本发明有以下实施例：一种石油钻井液降滤失剂：①先称取40克去离子水放入反应釜内，再把2克碳酸钠加入去离子水中搅拌溶解；②称取5克2-丙烯酰胺基-二甲基丙烯磺酸加入上述溶液内中和，保持PH值为10-12。③将15克丙烯酰胺和0.6克乙烯基吡咯烷酮倒入溶液内，搅拌溶解，再依次将0.1克过硫酸铵和0.1克过硫酸氢钠加入溶液内搅拌均匀，再放入捏合釜中静置保持温度34-38℃观察其反应，待其聚合后养护5个小时；④将2克甲醛、40克磺化褐煤和40克磺甲基酚醛树脂倒入捏合釜内，搅拌均匀，取出聚合物料放在烘干设备上于100-105℃温度下烘干，将料块粉碎过80目筛即是本降滤失剂。经检测，本品外观呈深棕色粉末或颗粒，细度80目。通过量为95％，经200℃养护后，钻井液常温常压淡水失水量≤10ml，饱和盐水≤15ml。150℃高温高压失水淡水≤30ml，饱和盐水≤35ml。
Claims (1)
1.一种钻井液降滤失剂，它包括有以下重量组份：2一丙烯胺基一2一甲基丙烯磺酸5份，丙烯酰胺15份，碳酸钠2份，去离子水40份，过硫酸铵0.1份，磺化褐煤40份，磺甲基酚醛树脂40份，甲醛2份，乙烯基吡咯烷酮0.6份，其制备方法是：①先将去离子水放入反应釜内，再把碳酸钠加入釜中搅拌使之溶解，②再把2一丙烯酰胺基一2一甲基丙烯磺酸加入上述溶液内中和，保持中和的PH值为10-12，③将丙烯酰胺和乙烯基吡咯烷酮依次倒入中和溶液内进行搅拌溶解，再依次将过硫酸铵和过硫酸氢钠加入溶液内搅拌均匀，再把溶液转入捏合釜中保持温度在34-38℃静置反应聚合5个小时，④然后将甲醛、磺化褐煤和磺甲基酚醛树脂倒入捏合釜内搅拌均匀，取出聚合物料，放在烘干设备上于100-105℃温度烘干，把料块粉碎，过80目筛即是本剂。