CN102206422B - 溶剂型自粘防水卷材用基层处理剂 - Google Patents
溶剂型自粘防水卷材用基层处理剂 Download PDFInfo
- Publication number
- CN102206422B CN102206422B CN2011100972404A CN201110097240A CN102206422B CN 102206422 B CN102206422 B CN 102206422B CN 2011100972404 A CN2011100972404 A CN 2011100972404A CN 201110097240 A CN201110097240 A CN 201110097240A CN 102206422 B CN102206422 B CN 102206422B
- Authority
- CN
- China
- Prior art keywords
- solvent
- adhesive waterproof
- primer
- asphalt modifier
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种防水卷材用处理剂，特别是涉及一种溶剂型自粘防水卷材用基层处理剂。构成处理剂的组分与质量百分比为：沥青30%～33%，溶剂30%～35%，软化油4%～6%，第一组份沥青改性剂4%～6%，第二组份沥青改性剂8%～12%，填充剂16%～20%。本发明解决了一般油性沥青基层处理剂的有毒有污染、剥离强度低、耐热性和低温性能差等问题，具有剥离强度高、高低温性能好、环保无毒等优点，是一种先进的溶剂型自粘防水卷材用基层处理剂。
Description
技术领域
本发明涉及一种防水卷材用处理剂，具体地说涉及一种溶剂型自粘防水卷材用基层处理剂。
背景技术
自粘防水卷材是一种很有发展前景的新型防水材料。因此具有独特的性能如自愈性、冷施工等优势，在我国的应用越来越广泛。但因其在低温条件下施工困难，表现为与基层处理剂粘结不牢，造成与基层剥离，对于立面情况尤其严重。
与自粘防水卷材配套的基层处理剂一般都为溶剂型沥青基层处理剂，此类基层处理剂溶剂挥发时间长、剥离强度低、耐热性和低温性能差，而且一般选用苯、甲苯或二甲苯作为溶剂，这类基层处理剂不仅长期危害施工工人的健康，还对环境有着不良影响。水乳型沥青类基层处理剂由于基层渗透性较差，且与防水卷材的粘结力不强，更为严重的是气温低于零度时，就会结冰造成破乳而无法使用。
发明内容
本发明的目的在于针对现有技术的缺陷，提供一种溶剂型自粘防水卷材用基层处理剂，该处理剂解决了一般沥青类基层处理剂的干燥时间长、剥离强度低、耐热性和低温性能差、有毒污染、冬季施工效果不好等问题。尤其是采用环保无毒的90号溶剂汽油，极大地改善了环境友好性，不损害施工工人的身体健康。
实现上述目的采用以下技术方案：一种溶剂型自粘防水卷材用基层处理剂，将构成基层处理剂的原料混合搅拌加热制得成品，所述的原料组分及质量百分比如下：沥青 30%～33%，溶剂 30%～35%，软化油4%～6%，第一组份沥青改性剂 4%～6%，第二组份沥青改性剂 8%～12%，填充剂16%～20%。
优选的，原料组分与质量百分比如下：
沥青 30%，溶剂 35%，软化油5%，第一组份沥青改性剂 4%，第二组份沥青改性剂 10%，填充剂16%。
所述的沥青是沥青为针入度为80～110，软化点为42～52℃延度为1000mm以上的石油沥青。
所述的溶剂为馏程为60～90℃的90号溶剂汽油。
所述的软化油为侧二线油或是侧三线油。
所述的第一组份沥青改性剂为熔融指数为1.0～3.0的苯乙烯-丁二烯-苯乙烯嵌段共聚物（SBS）。
所述的第二组份沥青改性剂为粉末丁苯橡胶或粉末丁基橡胶。所述的填充剂为重质碳酸钙、滑石粉或云母粉。
本发明自粘防水卷材用基层处理剂具有以下优点：
在基层表面形成一层致密的涂层，可以充当隔汽层。粘结力强大。较其他溶剂型沥青处理剂，环保无毒、不起鼓、耐久性更好。寒冬季节施工不依靠热熔就能提供与基层强大的粘结效果。
具体实施方式
下面结合具体实施例对本发明做进一步的描述。
实施例1
原料组分与质量百分数如下：
沥青 30%，溶剂 35%，软化油5%，第一组份沥青改性剂 4%，第二组份沥青改性剂 10%，填充剂16%。将六种物质放入容器中混合加热，加热温度为180-200℃，得到成品处理剂。
沥青为针入度为80～110，软化点为42～52℃，延度为1000mm以上的石油沥青。本发明采用中石油秦皇岛分公司的90号重交沥青。
溶剂为馏程为60～90℃的90号溶剂汽油。本发明采用市售的90号汽油。
软化油为侧二线油或是侧三线油。本发明采用大庆石化的侧二线油。
第一组份沥青改性剂为熔融指数为1.0～3.0的苯乙烯-丁二烯-苯乙烯嵌段共聚物（SBS）。本发明采用茂名石化的SBS1301。
第二组份沥青改性剂为粉末丁苯橡胶或粉末丁基橡胶。本发明采用齐鲁石化的粉末丁苯橡胶。
填充料采用市售200目重质碳酸钙。
将上述六种原料按照质量百分比秤取放入容器中混合搅拌加热至180-200℃，自然冷却后为成品基层处理剂。
采用Q/RDSC11-2011企业标准进行检测，结果如下：
| 项目 | 技术指标 | 实测值 |
| 粘度，mPa·S | 规定值±30% | 5 |
| 表干时间，h ≤ | 2 | 1 |
| 剥离强度，N/mm ≥ | 1.5 | 1.9 |
| 浸水后剥离强度，N/mm ≥ | 1.5 | 1.9 |
| 耐热性，℃ | 70℃，无流淌 | 合格 |
| 低温柔性，℃ | -15℃，无裂纹 | 合格 |
| 灰分，% ≤ | 2 | 0.2 |
实施例2
原料组分与质量百分数如下：
沥青 33%，溶剂 30%，软化油4%，第一组份沥青改性剂 5%，第二组份沥青改性剂 8%，填充剂20%。将六种物质放入容器中混合加热，加热温度为180-200℃，得到成品处理剂。
沥青为针入度为80～110，软化点为42～52℃，延度为1000mm以上的石油沥青。本发明采用中石油秦皇岛分公司的90号重交沥青。
溶剂为馏程为60～90℃的90号溶剂汽油。本发明采用市售的90号汽油。
软化油为侧二线油或是侧三线油。本发明采用大庆石化的侧二线油。
第一组份沥青改性剂为熔融指数为1.0～3.0的苯乙烯-丁二烯-苯乙烯嵌段共聚物（SBS）。本发明采用岳阳石化的SBS1401。
第二组份沥青改性剂为粉末丁苯橡胶或粉末丁基橡胶。本发明采用燕山石化的丁基橡胶。
填充料是市售800目云母粉。
将上述六种原料按照质量百分比秤取放入容器中混合搅拌加热至180-200℃，自然冷却后为成品基层处理剂。
采用Q/RDSC11-2011企业标准进行检测，结果如下：
| 项目 | 技术指标 | 实测值 |
| 粘度，mPa·S | 规定值±30% | 5 |
| 表干时间，h ≤ | 2 | 1 |
| 剥离强度，N/mm ≥ | 1.5 | 1.8 |
| 浸水后剥离强度，N/mm ≥ | 1.5 | 1.8 |
| 耐热性，℃ | 70℃，无流淌 | 合格 |
| 低温柔性，℃ | -15℃，无裂纹 | 合格 |
| 灰分，% ≤ | 2 | 0.2 |
以上公开的仅为本发明的具体实施例，虽然本发明以较佳的实施例揭示如上，但本发明并非局限于此，任何本领域的技术人员能思之的变化，在不脱离本发明的设计思想和范围内，对本发明进行各种改动和润饰，都应落在本发明的保护范围之内。
Claims (4)
1.一种溶剂型自粘防水卷材用基层处理剂，将构成基层处理剂的原料混合搅拌加热制得成品，其特征在于，所述的原料组分及质量百分比如下：沥青 30%～33%，溶剂 30%～35%，软化油4%～6%，第一组份沥青改性剂 4%～6%，第二组份沥青改性剂 8%～12%，填充剂16%～20%，所述的溶剂为馏程为60～90℃的90号溶剂汽油，所述的第一组份沥青改性剂为熔融指数为1.0～3.0的苯乙烯-丁二烯-苯乙烯嵌段共聚物，所述的第二组份沥青改性剂为粉末丁苯橡胶或粉末丁基橡胶。
2.根据权利要求1所述的溶剂型自粘防水卷材用基层处理剂，其特征在于，所述的沥青为针入度为80～110，软化点为42～52℃，延度为1000mm以上的石油沥青。
3.根据权利要求1所述的溶剂型自粘防水卷材用基层处理剂，其特征在于，所述的软化油为侧二线油或是侧三线油。
4.根据权利要求1所述的溶剂型自粘防水卷材用基层处理剂，其特征在于，所述的填充剂为重质碳酸钙、滑石粉或云母粉。