CN101818548A - 耐根刺防水卷材及加工工艺 - Google Patents
耐根刺防水卷材及加工工艺 Download PDFInfo
- Publication number
- CN101818548A CN101818548A CN200910009486A CN200910009486A CN101818548A CN 101818548 A CN101818548 A CN 101818548A CN 200910009486 A CN200910009486 A CN 200910009486A CN 200910009486 A CN200910009486 A CN 200910009486A CN 101818548 A CN101818548 A CN 101818548A
- Authority
- CN
- China
- Prior art keywords
- foil layer
- metal foil
- layer
- waterproof roll
- root thorn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种耐根刺防水卷材，包括复合在一起的改性沥青防水层、金属箔层和聚酯胎，其中所述聚酯胎是经特殊改性沥青预浸处理。本发明由改性沥青防水层、金属箔层和聚酯胎复合而成，其中聚酯胎经特殊改性沥青预浸处理，使之具有防水和阻止植物根穿透双重功能，能够承受植物根须穿刺，长久保持防水功能。
Description
技术领域
本发明涉及一种耐植物根刺防水卷材，尤其涉及一种采用改性沥青的耐植物根刺防水卷材及加工工艺。
背景技术
随着现代化城市规模的扩大，城市建筑物、道路面积逐增不减，从而导致绿地面积减小，城市尘埃吸附能力降低颗粒灰尘含量增加、空气干燥城市气温比周边气温高等现象。由此，进行城市绿化对于缓解城市这些现象，大幅度的提高城市空中景观，具有重要的意义。研究表明，在常规情况下，30％～50％的绿化覆盖绿才对一个城市的生态平衡具有临界意义，即达到或超过这一幅度，生态环境有望向良性循环发展，如达不到或下降，生态环境将面临恶化。目前国内城市中，绿化面积很少能满足可使城市生态平衡的条件。
进行城市绿化尤其使楼顶、地下车库顶的绿化势在必行。城市绿化指的是在种植屋面/顶面以绿色植物为主要覆盖物，配以植物生存所需要的营养土层、蓄水层以及屋面所需要的植物耐根刺层、蓄排水层、防水层、保温层等共同组成的屋面系统，具有节地、节能、降尘、降噪、增加城市绿化覆盖率、减少热岛效应、改善居住环境、实现雨水收集与延缓排放、延长种植面系统寿命等功能。
鉴于屋面/顶面的绿化建筑工程一次性投资大、维修费用高，若发生渗漏则不易进行维修，因此在进行屋面/顶面的绿化工程设计时，必须做好防水系统这一关，避免出现施工完后2-3年就出现屋面/顶面渗漏现象，而普通的防水系统构建于屋面/顶面的绿化工程中，对种植屋面/顶面系统的质量没有保证，这是由于植物根系将会对普通的防水产生巨大的破坏力。
发明内容
本发明所要解决的技术问题在于克服上述现有技术之不足，提供一种热接缝可靠耐久、抗拉强度高、延伸率大且适用能力强的耐根刺防水卷材。
本发明所要解决的另一个技术问题在于克服上述现有技术之不足，提供一种生产工艺流程简单、易于生产且生产成本低的耐根刺防水卷材加工工艺。
按照本发明提供的耐根刺防水卷材，包括复合在一起的改性沥青防水层、金属箔层和聚酯胎，其中所述聚酯胎是经特殊改性沥青预浸处理。
按照本发明提供的耐根刺防水卷材还具有如下附属技术特征：
所述改性沥青是在沥青中加入SBS或APP、APAO、SBR、软化剂、增粘树脂、填料、抗老化剂、增塑剂、阻根剂中的一种或多种。
所述特殊改性沥青是指由增粘树脂改性的沥青，其中增粘树脂为石油树脂、古马隆树脂或萜烯树脂。
所述金属箔层为铜箔层。
所述聚酯胎为经改性沥青预浸的长纤聚酯无纺布胎体，所述聚酯胎等于大于250g/m2。
所述金属箔层的厚度为0.03mm-0.09mm。
包括依次复合在一起的PE膜层、改性沥青防水层、金属箔层、经特殊改性沥青预浸处理后的聚酯胎、改性沥青防水层和PE膜层。
按照本发明提供的耐根刺防水卷材加工工艺，包括如下步骤，
展开，将聚酯胎和金属箔层展开；
预浸，通过使用特殊改性沥青对聚酯胎进行预浸；
压挤，将预浸后的聚酯胎与金属箔层压挤复合在一起；
盖料，在复合后的聚酯胎和金属箔层上涂盖改性沥青防水层；
定型，对复合在一起的各层进行定型。
按照本发明提供的耐根刺防水卷材加工工艺还具有如下附属技术特征：
在预浸步骤中采用的改性沥青是采用增粘树脂和高分子改性剂对沥青进行改性；在盖料步骤中采用的改性沥青是采用高分子弹性体、软化剂、耐老化剂和填料对沥青进行改性。
在盖料步骤之后还包括有覆膜步骤，对聚酯胎和金属箔层复合形成的基层的两面复合PE膜。
按照本发明提供的耐根刺防水卷材与现有技术相比具有如下优点：本发明由改性沥青防水层、金属箔层和聚酯胎复合而成，其中聚酯胎经特殊改性沥青预浸处理，使之具有防水和阻止植物根穿透双重功能，能够承受植物根须穿刺，长久保持防水功能；其次，本发明可形成高强度防水层，抵抗压力水能力强，并耐穿刺、耐咯破、耐撕裂、耐疲劳、耐腐蚀、耐老化；再次，本发明采用上述材料形成的层结构，具有施工方便且热接可靠耐久、抗拉强度，延伸率大，对基层收缩变形和开裂的适应能力强具有良好的阻根和防水性能和极佳的耐植物根穿刺性能，且不影响植物的生长，对环境和种植土无任何污染。
按照本发明提供的耐跟测防水卷材的加工工艺具有如下优点：本发明的加工工艺流程简单，易于生产，而且可降低生产成本；该防水卷材集防水和阻根为一体，只需一次施工即可达到防水和阻根的目的，施工工艺简单，降低工程造价，解决了植物根系穿刺防水层的问题，和阻根、防水两次施工复杂的问题、广泛适用于是城市绿化环保的屋面/顶面工程中。
附图说明
图1是本发明的结构示意图。
图2是本发明的加工工艺流程图。
具体实施方式
参见图1，在本发明给出的一种耐根刺防水卷材的实施例，包括复合在一起的改性沥青防水层1、金属箔层2和聚酯胎3，其中所述聚酯胎是经特殊改性沥青预浸处理。在本实施例中，包括依次复合在一起的PE膜层4、改性沥青防水层1、金属箔层2、经特殊改性沥青预浸的聚酯胎3、改性沥青防水层1和PE膜层4。当然，也可以是其他形式的层状结构，但主要是要具有改性沥青防水层1、金属箔层2和聚酯胎3三个基本组成。从而使得该卷材具有阻根和防水功能的效果。本发明中的聚酯胎3经过特殊改性沥青预浸处理后，使其具有防水和阻止植物根穿透双重功能，能够承受植物根须穿刺，长久保持防水功能。同时，还可以提高聚酯胎3的粘结强度。
本发明中的所述改性沥青是在沥青中加入SBS或APP、APAO、SBR、软化剂、增粘树脂、填料、抗老化剂、增塑剂、阻根剂中的一种或多种。
在本发明中所述改性沥青是SBS或APP改性沥青。其中，SBS为弹性体改性沥青，是以苯乙烯-丁二烯-苯乙烯(SBS)热塑性弹性体作改性剂。APP为塑性体改性沥青，用高质量的塑性体(APP)改性沥青浸涂而制成，它除具有普通塑性体(APP)改性沥青的基本性能外，还具有很好的耐热性和耐低温性。APAO(无定型烯径共聚物)是用特种催化剂，单独以丙烯或乙烯，1-丁烯进行合聚反应而得，是无定型烯烃共聚物。SBR为通用型合成橡胶。
所述金属箔层2为铜箔层，所述金属箔层可以根据不同的植物选定不同厚度。在这里所述金属箔层的厚度为0.03mm-0.09mm。具体而言，可以根据不同的植物选择0.03mm、0.05mm、0.07mm和0.09mm。金属箔层具有密度大、强度高等特点，使植物根无法穿透，同时又不影响植物的正常生长，当植物根遇到金属箔层时，植物根将产生逆向生长的现象，起到有效阻根功能，防止种植植物破坏防水层和建筑结构。而将金属箔层的厚度限定为上述尺寸，可以很好的兼顾金属箔层的阻根效果和金属箔层厚度之间的关系。根据不同的植物根的穿刺强度不同，上述尺寸规格可以完全满足。同时，也使金属箔层的用料降低。
本发明给出的上述实施例中，所述聚酯胎3为经改性沥青预浸的长纤聚酯无纺布胎体，所述聚酯胎等于大于250g/m2。长纤聚酯无纺布具有较大的延伸，和较高的拉伸强度等特点，满足于不同的建筑基层。
在本发明给出的上述实施例中，采用的改性沥青分类两类：一是对长纤聚酯胎体进行预浸的改性沥青。另一类改性沥青是用于胎体涂盖料，从而形成改性沥青防水层。其采用高分子弹性体、软化剂、耐老化剂和填料等改善沥青的耐高低温性能，和延伸性能，采用热熔施工可使改性沥青与基层密严粘结，达到极佳的防水效果。
参见图2，在本发明给出的一种耐根刺防水卷材加工工艺，包括如下步骤，
展开，将聚酯胎和金属箔层展开；
预浸，通过使用特殊改性沥青对聚酯胎进行预浸；本发明设置了预浸步骤，使聚酯胎经改性沥青处理，提高了其粘结性和防水效果。
压挤，将聚酯胎与金属箔层压挤复合在一起；
盖料，在复合后的聚酯胎和金属箔层上涂盖改性沥青防水层；
定型，对复合在一起的各层进行定性。
本发明可以采用普通的改性沥青卷材生产线进行生产，金属箔片与长纤聚酯胎体是在生产线上进行复合的，金属箔片的厚度可根据种植植物的不同而选择；长纤聚酯胎体经改性沥青预浸后与金属箔片复合，采取的复合方式为挤压辊压挤，解决了目前市场上金属复合聚酯胎做改性沥青增强层预浸不透的现象。
在预浸步骤中采用的改性沥青是采用增粘树脂和高分子改性剂对沥青进行改性。其中增粘树脂可以为石油树脂、古马隆树脂或萜烯树脂等。在盖料步骤中采用的改性沥青是采用高分子弹性体、软化剂、耐老化剂和填料对沥青进行改性。
具有阻根和防水功能的效果，阻根指的是通过生产线上复合金属箔层和聚酯胎体，使胎体坚固，从而达到阻根的的功能；而防水指的是优质的改性沥青通过热熔施工与基层粘结致密，热接缝可靠耐久，从而达到工程防水的效果。
在本发明给出的上述实施例中，在盖料步骤之后还包括有覆膜步骤，对聚酯胎和金属箔层复合形成的基层的两面复合PE膜。所述PE膜层起到保护的作用。
本发明的改性沥青卷材加工工艺将不同厚度的金属箔层、聚酯胎体复合在一起，无需更改改性沥青卷材的生产设备、工艺简单，采用预浸的方法，经挤压将金属箔层与聚酯胎体复合在一起，粘结良好。
当然，在本发明给出的上述加工工艺中，更具体而言，还可以包括涂油、冷却、储存、计量、卷材和包装等步骤。这些步骤都可以采用现有技术中常规生产工艺。本发明的生产方法简单，该防水卷材采用热熔施工方法，解决了植物根刺防水层的问题，广泛用于屋面、楼面、地下车库顶面的等绿化工程之中。
Claims (10)
1.一种耐根刺防水卷材，其特征在于：包括复合在一起的改性沥青防水层、金属箔层和聚酯胎，其中所述聚酯胎是经特殊改性沥青预浸处理。
2.根据权利要求1所述的耐根刺防水卷材，其特征在于：所述改性沥青是在沥青中加入SBS或APP、APAO、SBR、软化剂、增粘树脂、填料、抗老化剂、增塑剂、阻根剂中的一种或多种。
3.根据权利要求1所述的耐根刺防水卷材，其特征在于：所述特殊改性沥青是指由增粘树脂改性的沥青，其中增粘树脂为石油树脂、古马隆树脂或萜烯树脂。
4.根据权利要求1所述的耐根刺防水卷材，其特征在于：所述金属箔层为铜箔层或铜箔层。
5.根据权利要求1所述的耐根刺防水卷材，其特征在于：所述聚酯胎为经改性沥青预浸的长纤聚酯无纺布胎体，所述聚酯胎等于大于250g/m2。
6.根据权利要求1所述的耐根刺防水卷材，其特征在于：所述金属箔层的厚度为0.03mm-0.09mm。
7.根据权利要求1所述的耐根刺防水卷材，其特征在于：包括依次复合在一起的PE膜层、改性沥青防水层、金属箔层、经特殊改性沥青预浸处理后的聚酯胎、改性沥青防水层和PE膜层。
8.一种耐根刺防水卷材加工工艺，其特征在于：包括如下步骤，
展开，将聚酯胎和金属箔层展开；
预浸，通过使用特殊改性沥青对聚酯胎进行预浸；
压挤，将预浸后的聚酯胎与金属箔层压挤复合在一起；
盖料，在复合后的聚酯胎和金属箔层上涂盖改性沥青防水层；
定型，对复合在一起的各层进行定型。
9.如权利要求8所述的耐根刺防水卷材加工工艺，其特征在于：在预浸步骤中采用的改性沥青是采用增粘树脂和高分子改性剂对沥青进行改性；在盖料步骤中采用的改性沥青是采用高分子弹性体、软化剂、耐老化剂和填料对沥青进行改性。
10.如权利要求8所述的耐根刺防水卷材加工工艺，其特征在于：在盖料步骤之后还包括有覆膜步骤，对聚酯胎和金属箔层复合形成的基层的两面复合PE膜。