CN102161811A - 替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体 - Google Patents
替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体 Download PDFInfo
- Publication number
- CN102161811A CN102161811A CN 201010612057 CN201010612057A CN102161811A CN 102161811 A CN102161811 A CN 102161811A CN 201010612057 CN201010612057 CN 201010612057 CN 201010612057 A CN201010612057 A CN 201010612057A CN 102161811 A CN102161811 A CN 102161811A
- Authority
- CN
- China
- Prior art keywords
- weight percent
- ethylene
- vinyl acetate
- acetate copolymer
- accounts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是关于一种替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,包括氢化苯乙烯弹性体、无机纳米填料、矿物填充油、乙烯-醋酸乙烯酯共聚物、抗氧化剂;其中,氢化苯乙烯弹性体占重量百分比为25%-40%、无机纳米填料占重量百分比为10%-20%、矿物填充油占重量百分比为30%-45%、乙烯-醋酸乙烯酯共聚物占重量百分比为3%-10%、抗氧化剂占重量百分比为0.1%-0.4%。因此,其弹性高、成本低,同时不会腐蚀设置,不会对人体造成影响。
Description
技术领域
本发明涉及一种替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体。
背景技术
现有发泡弹性体一般由EVA制成,EVA是由乙烯和醋酸乙烯酯共聚而制得的热塑性树脂。工业产品的醋酸乙烯酯含量为5%~95%,各品种间性能差别较大。一般随着醋酸乙烯酯含量增加,结晶度硬度刚性和热变形温度逐渐降低,而光泽度、透明度耐冲击性柔韧性耐应力开裂性在溶剂中的可溶性、热收缩性和热焊性等却有不同程度提高。然而,EVA制成的弹性体其弹性不 高,而且成本高,同时EVA中的酸性物质会腐蚀设备,产生的气味会对人体造成影响。
发明内容
本发明要解决的技术问题是提供一种弹性高、成本低,同时不会腐蚀设置,不会对人体造成影响的替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体。本发明是通过以下技术方案来实现的:
本发明的一种替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,包括氢化苯乙烯弹性体、无机纳米填料、矿物填充油、乙烯-醋酸乙烯酯共聚物、抗氧化剂;其中,氢化苯乙烯弹性体占重量百分比为25%-40%、无机纳米填料占重量百分比为10%-20%、矿物填充油占重量百分比为30%-45%、乙烯-醋酸乙烯酯共聚物占重量百分比为3%-10%、抗氧化剂占重量百分比为0.1%-0.4%。
作为改进,其中,氢化苯乙烯弹性体占重量百分比为25%、无机纳米填料占重量百分比为20%、矿物填充油占重量百分比为45%、乙烯-醋酸乙烯酯共聚物占重量百分比为9.6%、抗氧化剂占重量百分比为0.4%。
作为改进,其中,氢化苯乙烯弹性体占重量百分比为35%、无机纳米填料占重量百分比为17%、矿物填充油占重量百分比为42%、乙烯-醋酸乙烯酯共聚物占重量百分比为5.8%、抗氧化剂占重量百分比为0.2%。。
作为改进,其中,氢化苯乙烯弹性体占重量百分比为40%、无机纳米填料占重量百分比为15%、矿物填充油占重量百分比为40%、乙烯-醋酸乙烯酯共聚物占重量百分比为4.9%、抗氧化剂占重量百分比为0.1%。
作为改进,所述矿物填充油为石蜡基烷烃油,其闪点为200℃以上,在25℃下,粘度为15~20Cps。
作为改进,所述无机纳米填料为数目5000目以上的滑石粉、硫酸钡、碳酸钙、云母粉中的一种。
作为改进,所述抗氧化剂为抗氧化1010和抗氧化168按1:1~2比例混合的混合物。
本发明为一种替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,由于包括氢化苯乙烯弹性体、无机纳米填料、矿物填充油、乙烯-醋酸乙烯酯共聚物、抗氧化剂,可以代替EVA,因此,其具有弹性高、成本低,同时不会腐蚀设置,不会对人体造成影响。
具体实施方式
本发明的一种替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,包括氢化苯乙烯弹性体、无机纳米填料、矿物填充油、乙烯-醋酸乙烯酯共聚物、抗氧化剂;其中,氢化苯乙烯弹性体占重量百分比为25%-40%、无机纳米填料占重量百分比为10%-20%、矿物填充油占重量百分比为30%-45%、乙烯-醋酸乙烯酯共聚物占重量百分比为3%-10%、抗氧化剂占重量百分比为0.1%-0.4%。因此,其具有弹性高、成本低,同时不会腐蚀设置,不会对人体造成影响。
实施例一:其中,氢化苯乙烯弹性体占重量百分比为25%、无机纳米填料占重量百分比为20%、矿物填充油占重量百分比为45%、乙烯-醋酸乙烯酯共聚物占重量百分比为9.6%、抗氧化剂占重量百分比为0.4%。
实施例二:其中,氢化苯乙烯弹性体占重量百分比为35%、无机纳米填料占重量百分比为17%、矿物填充油占重量百分比为42%、乙烯-醋酸乙烯酯共聚物占重量百分比为5.8%、抗氧化剂占重量百分比为0.2%。。
实施例三:,其中,氢化苯乙烯弹性体占重量百分比为40%、无机纳米填料占重量百分比为15%、矿物填充油占重量百分比为40%、乙烯-醋酸乙烯酯共聚物占重量百分比为4.9%、抗氧化剂占重量百分比为0.1%。
上述实施例中,所述矿物填充油为石蜡基烷烃油,其闪点为200℃以上,在25℃下,粘度为15~20Cps。所述无机纳米填料为数目5000目以上的滑石粉、硫酸钡、碳酸钙、云母粉中的一种。所述抗氧化剂为抗氧化1010和抗氧化168按1:1~2比例混合的混合物。
本发明为一种替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,由于包括氢化苯乙烯弹性体、无机纳米填料、矿物填充油、乙烯-醋酸乙烯酯共聚物、抗氧化剂,可以代替EVA,因此,其具有弹性高、成本低,同时不会腐蚀设置,不会对人体造成影响。
Claims (7)
1.一种替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,包括氢化苯乙烯弹性体、无机纳米填料、矿物填充油、乙烯-醋酸乙烯酯共聚物、抗氧化剂;其中,氢化苯乙烯弹性体占重量百分比为25%-40%、无机纳米填料占重量百分比为10%-20%、矿物填充油占重量百分比为30%-45%、乙烯-醋酸乙烯酯共聚物占重量百分比为3%-10%、抗氧化剂占重量百分比为0.1%-0.4%。
2.根据权利要求1所述的替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,其特征在于:其中,氢化苯乙烯弹性体占重量百分比为25%、无机纳米填料占重量百分比为20%、矿物填充油占重量百分比为45%、乙烯-醋酸乙烯酯共聚物占重量百分比为9.6%、抗氧化剂占重量百分比为0.4%。
3.根据权利要求1所述的替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,其特征在于:其中,氢化苯乙烯弹性体占重量百分比为35%、无机纳米填料占重量百分比为17%、矿物填充油占重量百分比为42%、乙烯-醋酸乙烯酯共聚物占重量百分比为5.8%、抗氧化剂占重量百分比为0.2%。
4. 根据权利要求1所述的替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,其特征在于:其中,氢化苯乙烯弹性体占重量百分比为40%、无机纳米填料占重量百分比为15%、矿物填充油占重量百分比为40%、乙烯-醋酸乙烯酯共聚物占重量百分比为4.9%、抗氧化剂占重量百分比为0.1%。
5.根据权利要求1所述的替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,其特征在于:所述矿物填充油为石蜡基烷烃油,其闪点为200℃以上,在25℃下,粘度为15~20Cps。
6.根据权利要求1所述的替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,其特征在于:所述无机纳米填料为数目5000目以上的滑石粉、硫酸钡、碳酸钙、云母粉中的一种。
7.根据权利要求1所述的替代与乙烯-醋酸乙烯酯共聚物混合发泡的热塑性弹性体,其特征在于:所述抗氧化剂为抗氧化1010和抗氧化168按1:1~2比例混合的混合物。