CN102140240B - 用于与丙烯腈·丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体 - Google Patents
用于与丙烯腈·丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体 Download PDFInfo
- Publication number
- CN102140240B CN102140240B CN2010106183188A CN201010618318A CN102140240B CN 102140240 B CN102140240 B CN 102140240B CN 2010106183188 A CN2010106183188 A CN 2010106183188A CN 201010618318 A CN201010618318 A CN 201010618318A CN 102140240 B CN102140240 B CN 102140240B
- Authority
- CN
- China
- Prior art keywords
- weight percent
- sebs
- accounts
- hydrogenated styrene
- thermoplastic elastomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明是关于一种用于与丙烯腈?丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体,包括马来酸酐接枝氢化苯乙烯弹性体、氢化苯乙烯弹性体、矿物填充油、聚氨酯弹性体、无机纳米填料、抗氧化剂、紫外线吸收剂、乙烯-醋酸乙烯酯类聚物;其中,马来酸酐接枝氢化苯乙烯弹性体占重量百分比为5%、氢化苯乙烯弹性体占重量百分比为25%、矿物填充油占重量百分比为28%、聚氨酯弹性体占重量百分比为32%、无机纳米填料占重量百分比为8.8%、抗氧化剂占重量百分比为0.1%、紫外线吸收剂占重量百分比为0.1%、乙烯-醋酸乙烯酯类聚物占重量百分比为1%。
Description
技术领域
本发明涉及一种用于与丙烯腈•丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体。
背景技术
现有热塑性弹性体一般由ABS添加乙烯-醋酸乙烯酯类聚物制成。ABS树脂(丙烯腈-苯乙烯-丁二烯共聚物,ABS是Acrylonitrile Butadiene Styrene的首字母缩写)是一种强度高、韧性好、易于加工成型的热塑型高分子材料。因为其强度高、耐腐蚀、耐高温,所以常被用于制造仪器的塑料外壳。然而,ABS添加乙烯-醋酸乙烯酯类聚物制成的弹性体普遍存在表面效果差,产品粘合不完美的缺点。
发明内容
本发明要解决的技术问题是提供一种表面效果好、产品粘合得更完美的用于与丙烯腈•丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体。本发明是通过以下技术方案来实现的:
本发明的一种用于与丙烯腈•丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体,包括马来酸酐接枝氢化苯乙烯弹性体、氢化苯乙烯弹性体、矿物填充油、聚氨酯弹性体、无机纳米填料、抗氧化剂、紫外线吸收剂、乙烯-醋酸乙烯酯类聚物;其中,马来酸酐接枝氢化苯乙烯弹性体占重量百分比为5%、氢化苯乙烯弹性体占重量百分比为25%、矿物填充油占重量百分比为28%、聚氨酯弹性体占重量百分比为32%、无机纳米填料占重量百分比为8.8%、抗氧化剂占重量百分比为0.1%、紫外线吸收剂占重量百分比为0.1%、乙烯-醋酸乙烯酯类聚物占重量百分比为1%。
作为改进,所述氢化苯乙烯弹性体为SEBS,SEBS是以聚苯乙烯为末端段,以聚丁二烯加氢得到的乙烯-丁烯共聚物为中间弹性嵌段的三嵌段共聚物,SEBS不含不饱和双键,因此具有良好的稳定性和耐老化性,所述的SEBS采用的型号为SEBS G1650、SEBS G1651、SEBS G6933、SEBS 4033、SEBS 4055中的一种或者任意比例混合的多种。
作为改进,所述矿物填充油为石蜡基烷烃油,其闪点为200℃以上,在25℃下,粘度为15~20Cps。
作为改进,所述无机纳米填料为数目5000目以上的滑石粉、硫酸钡、碳酸钙、云母粉中的一种。
作为改进,所述抗氧化剂为抗氧化1010和抗氧化168按1:1~2比例混合的混合物。
本发明的一种用于与丙烯腈•丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体,由于包括马来酸酐接枝氢化苯乙烯弹性体、氢化苯乙烯弹性体、矿物填充油、聚氨酯弹性体、无机纳米填料、抗氧化剂、紫外线吸收剂、乙烯-醋酸乙烯酯类聚物,可以代替ABS添加乙烯-醋酸乙烯酯类聚物制成的弹性体,因此,其表面效果好,同时具有使产品粘合得更完美的好处。
具体实施方式
本发明的一种用于与丙烯腈•丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体,包括马来酸酐接枝氢化苯乙烯弹性体、氢化苯乙烯弹性体、矿物填充油、聚氨酯弹性体、无机纳米填料、抗氧化剂、紫外线吸收剂、乙烯-醋酸乙烯酯类聚物;其中,马来酸酐接枝氢化苯乙烯弹性体占重量百分比为3%-5%、氢化苯乙烯弹性体占重量百分比为15%-30%、矿物填充油占重量百分比为25%-40%、聚氨酯弹性体占重量百分比为30%-55%、无机纳米填料占重量百分比为0%-25%、抗氧化剂占重量百分比为0.1%-0.2%、紫外线吸收剂占重量百分比为0.1%-0.2%、乙烯-醋酸乙烯酯类聚物占重量百分比为1%-3%。因此,其具有使产品粘合得更完美的好处。
实施例一:其中,马来酸酐接枝氢化苯乙烯弹性体占重量百分比为5%、氢化苯乙烯弹性体占重量百分比为25%、矿物填充油占重量百分比为28%、聚氨酯弹性体占重量百分比为32%、无机纳米填料占重量百分比为8.8%、抗氧化剂占重量百分比为0.1%、紫外线吸收剂占重量百分比为0.1%、乙烯-醋酸乙烯酯类聚物占重量百分比为1%。
实施例二:其中,马来酸酐接枝氢化苯乙烯弹性体占重量百分比为4%、氢化苯乙烯弹性体占重量百分比为20%、矿物填充油占重量百分比为26%、聚氨酯弹性体占重量百分比为40%、无机纳米填料占重量百分比为7.7%、抗氧化剂占重量百分比为0.15%、紫外线吸收剂占重量百分比为0.15%、乙烯-醋酸乙烯酯类聚物占重量百分比为2%。
实施例三:,其中,马来酸酐接枝氢化苯乙烯弹性体占重量百分比为3%、氢化苯乙烯弹性体占重量百分比为20%、矿物填充油占重量百分比为30%、聚氨酯弹性体占重量百分比为37%、无机纳米填料占重量百分比为6.8%、抗氧化剂占重量百分比为0.2%、紫外线吸收剂占重量百分比为0.2%、乙烯-醋酸乙烯酯类聚物占重量百分比为3%。
上述实施例中,所述氢化苯乙烯弹性体为SEBS,SEBS是以聚苯乙烯为末端段,以聚丁二烯加氢得到的乙烯-丁烯共聚物为中间弹性嵌段的三嵌段共聚物,SEBS不含不饱和双键,因此具有良好的稳定性和耐老化性,本发明所采用型号为SEBS G1650、SEBS G1651、SEBS G6933、SEBS 4033、SEBS 4055中的一种或者任意比例混合的多种。所述矿物填充油为石蜡基烷烃油,其闪点为200℃以上,在25℃下,粘度为15~20Cps。所述无机纳米填料为数目5000目以上的滑石粉、硫酸钡、碳酸钙、云母粉中的一种。所述抗氧化剂为抗氧化1010和抗氧化168按1:1~2比例混合的混合物。
比例混合的混合物。本发明的一种用于与丙烯腈•丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体,由于包括马来酸酐接枝氢化苯乙烯弹性体、氢化苯乙烯弹性体、矿物填充油、聚氨酯弹性体、无机纳米填料、抗氧化剂、紫外线吸收剂、乙烯-醋酸乙烯酯类聚物,可以代替ABS添加乙烯-醋酸乙烯酯类聚物制成的弹性体,因此,其表面效果好,同时具有使产品粘合得更完美的好处。
Claims (5)
1.一种用于与丙烯腈•丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体,包括马来酸酐接枝氢化苯乙烯弹性体、氢化苯乙烯弹性体、矿物填充油、聚氨酯弹性体、无机纳米填料、抗氧化剂、紫外线吸收剂、乙烯-醋酸乙烯酯类聚物;其中,马来酸酐接枝氢化苯乙烯弹性体占重量百分比为5%、氢化苯乙烯弹性体占重量百分比为25%、矿物填充油占重量百分比为28%、聚氨酯弹性体占重量百分比为32%、无机纳米填料占重量百分比为8.8%、抗氧化剂占重量百分比为0.1%、紫外线吸收剂占重量百分比为0.1%、乙烯-醋酸乙烯酯类聚物占重量百分比为1%。
2. 根据权利要求1所述的用于与丙烯腈•丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体,其特征在于:所述氢化苯乙烯弹性体为SEBS,SEBS是以聚苯乙烯为末端段,以聚丁二烯加氢得到的乙烯-丁烯共聚物为中间弹性嵌段的三嵌段共聚物,SEBS不含不饱和双键,因此具有良好的稳定性和耐老化性,所述的SEBS采用的型号为SEBS G1650、SEBS G1651、SEBS G6933、SEBS 4033、SEBS 4055中的一种或者任意比例混合的多种。
3.根据权利要求1所述的用于与丙烯腈•丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体,其特征在于:所述矿物填充油为石蜡基烷烃油,其闪点为200℃以上,在25℃下,粘度为15~20Cps。
4.根据权利要求1所述的用于与丙烯腈•丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体,其特征在于:所述无机纳米填料为数目5000目以上的滑石粉、硫酸钡、碳酸钙、云母粉中的一种。
5.根据权利要求1所述的用于与丙烯腈•丁二烯和苯乙烯三元共聚物射粘的热塑性弹性体,其特征在于:所述抗氧化剂为抗氧化1010和抗氧化168按1:1~2比例混合的混合物。