CN105694263A - 一种耐油弹性体电缆料的制备方法 - Google Patents
一种耐油弹性体电缆料的制备方法 Download PDFInfo
- Publication number
- CN105694263A CN105694263A CN201410679079.5A CN201410679079A CN105694263A CN 105694263 A CN105694263 A CN 105694263A CN 201410679079 A CN201410679079 A CN 201410679079A CN 105694263 A CN105694263 A CN 105694263A
- Authority
- CN
- China
- Prior art keywords
- parts
- antioxidant
- oil
- cable material
- resistant elastomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种耐油弹性体电缆料，以重量份计，所述电缆料的原料配方如下：PVC-1300树脂20-60份，ABS树脂30-50份，丙烯酸酯共聚弹性体10-40份，偏苯三酸三辛酯35-75份，环氧大豆油5-20份，复合稳定剂4-8份，抗氧剂0.2-0.8份，纳米碳酸钙10-50份，润滑剂0.2-0.8份，所述丙烯酸酯共聚弹性体是丙烯酸丁酯、苯乙烯和丙烯腈的共聚物，且含有功能性羧基基团。本发明配方和制备工艺简单，且本发明所得电缆料性能优异，热老化试验可通过135℃×240h；耐油性能试验可通过(2#油)100℃×168h；材料低温冲击脆化温度低于-30℃；20℃时体积电阻率≥1.0×1012Ω.m；200℃热稳定时间≥180min。
Description
技术领域
本发明涉及一种电线电缆用绝缘料，具体涉及一种耐油弹性体绝缘料或护套料。
背景技术
现有技术中，耐油弹性体电缆料通常存在如下不足：1)200℃稳定时间小；2)20℃体积电阻率只能达到1.0*1011Ω.m；3)不能通过135℃*240h热老化试验。
CN103205034A公开了一种电线电缆用丁腈-PVC复合物弹性体绝缘料的制备方法，其绝缘料以丁腈橡胶和PVC树脂为主体成分，加以多种促进剂，多种防老剂，增塑剂，填料等，配方复杂，而且所得绝缘料高温稳定性和热老化性较差，体积电阻小。
发明内容
本发明所要解决的技术问题是提供一种耐油弹性体电缆料。
为解决以上技术问题，本发明所采用的技术方案如下：
一种耐油弹性体电缆料的制备方法，其特征在于：包括以下步骤：
(1)配备原料配方：以重量份计，所述电缆料的原料配方如下：PVC-1300树脂70份，ABS树脂60份，丙烯酸酯共聚弹性体50份，偏苯三酸三辛酯80份，环氧大豆油30份，复合稳定剂10份，抗氧剂2份，纳米碳酸钙60份，润滑剂2份，所述丙烯酸酯共聚弹性体是丙烯酸丁酯、苯乙烯和丙烯腈的共聚物，且含有功能性羧基基团，抗氧剂为选自抗氧剂1010、抗氧剂168、抗氧剂300、抗氧剂1024、酚类抗氧剂、胺类抗氧剂、硫代双酚类抗氧剂以及亚磷酸酯类抗氧剂的一种或多种的组合，复合稳定剂为钙锌复合稳定剂，所述的润滑剂为选自含氟流变剂、硅酮母粒以及硬脂酸盐中的一种或多种的组合；
(2)将上述步骤（1）的配方加入高速混合机中，混合至60～70℃后加入润滑剂，高速混合，出料待用；
(3)将步骤(1)所得物料投入双密炼机混炼，再通过双锥混炼机进入双阶螺杆挤出机，在温度150℃～180℃下混炼，挤出造粒，即得所述耐油弹性体电缆料。
由于上述技术方案运用，本发明与现有技术相比具有下列优点：
(1)本发明配方和制备工艺简单；
(2)本发明所得电缆料性能优异，具体如下：
①热老化试验可通过135℃×240h(拉伸强度变化率、断裂伸长率变化率±20％)；
②耐油性能试验可通过(2#油)100℃×168h(拉伸强度变化率、断裂伸长率变化率±40％)；
③材料低温冲击脆化温度低于-30℃；
④20℃时体积电阻率≥1.0×1012Ω.m；
⑤200℃热稳定时间≥180min。
具体实施方式
以下结合具体实施例对本发明做进一步详细说明。应理解，这些实施例是用于说明本发明的基本原理、主要特征和优点，而本发明不受以下实施例的限制。
一种耐油弹性体电缆料的制备方法，其特征在于：包括以下步骤：
(1)配备原料配方：以重量份计，所述电缆料的原料配方如下：PVC-1300树脂70份，ABS树脂60份，丙烯酸酯共聚弹性体50份，偏苯三酸三辛酯80份，环氧大豆油30份，复合稳定剂10份，抗氧剂2份，纳米碳酸钙60份，润滑剂2份，所述丙烯酸酯共聚弹性体是丙烯酸丁酯、苯乙烯和丙烯腈的共聚物，且含有功能性羧基基团，抗氧剂为选自抗氧剂1010、抗氧剂168、抗氧剂300、抗氧剂1024、酚类抗氧剂、胺类抗氧剂、硫代双酚类抗氧剂以及亚磷酸酯类抗氧剂的一种或多种的组合，复合稳定剂为钙锌复合稳定剂，所述的润滑剂为选自含氟流变剂、硅酮母粒以及硬脂酸盐中的一种或多种的组合；
(2)将上述步骤（1）的配方加入高速混合机中，混合至60～70℃后加入润滑剂，高速混合，出料待用；
(3)将步骤(1)所得物料投入双密炼机混炼，再通过双锥混炼机进入双阶螺杆挤出机，在温度150℃～180℃下混炼，挤出造粒，即得所述耐油弹性体电缆料
上述实施例只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。
Claims (1)
1.一种耐油弹性体电缆料的制备方法，其特征在于：包括以下步骤：
(1)配备原料配方：以重量份计，所述电缆料的原料配方如下：PVC-1300树脂70份，ABS树脂60份，丙烯酸酯共聚弹性体50份，偏苯三酸三辛酯80份，环氧大豆油30份，复合稳定剂10份，抗氧剂2份，纳米碳酸钙60份，润滑剂2份，所述丙烯酸酯共聚弹性体是丙烯酸丁酯、苯乙烯和丙烯腈的共聚物，且含有功能性羧基基团，抗氧剂为选自抗氧剂1010、抗氧剂168、抗氧剂300、抗氧剂1024、酚类抗氧剂、胺类抗氧剂、硫代双酚类抗氧剂以及亚磷酸酯类抗氧剂的一种或多种的组合，复合稳定剂为钙锌复合稳定剂，所述的润滑剂为选自含氟流变剂、硅酮母粒以及硬脂酸盐中的一种或多种的组合；
(2)将上述步骤（1）的配方加入高速混合机中，混合至60～70℃后加入润滑剂，高速混合，出料待用；
(3)将步骤(1)所得物料投入双密炼机混炼，再通过双锥混炼机进入双阶螺杆挤出机，在温度150℃～180℃下混炼，挤出造粒，即得所述耐油弹性体电缆料。