CN102746585A - 一种聚丙烯绝缘电缆料及其制备方法 - Google Patents

一种聚丙烯绝缘电缆料及其制备方法 Download PDF

Info

Publication number
CN102746585A
CN102746585A CN2012101923039A CN201210192303A CN102746585A CN 102746585 A CN102746585 A CN 102746585A CN 2012101923039 A CN2012101923039 A CN 2012101923039A CN 201210192303 A CN201210192303 A CN 201210192303A CN 102746585 A CN102746585 A CN 102746585A
Authority
CN
China
Prior art keywords
parts
ethylene
rubber
attapulgite
nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012101923039A
Other languages
English (en)
Other versions
CN102746585B (zh
Inventor
沈志海
沈志荣
邹强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Huahai Special Cable Group Co Ltd
Original Assignee
Anhui Huahai Special Cable Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Huahai Special Cable Group Co Ltd filed Critical Anhui Huahai Special Cable Group Co Ltd
Priority to CN201210192303.9A priority Critical patent/CN102746585B/zh
Publication of CN102746585A publication Critical patent/CN102746585A/zh
Application granted granted Critical
Publication of CN102746585B publication Critical patent/CN102746585B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种聚丙烯绝缘电缆料及其制备方法,其组成原料的重量份为:三元乙丙橡胶80-110、纳米凹凸棒土30-50、氯醚橡胶50-70、乙烯-丙烯酸甲酯共聚物EMA1125AC美国杜邦 10-20、半补强炭黑2-4、海泡石80-90、氧化锌4-7、硫化剂MOCA 2-4、2-硫醇基苯骈咪唑1-4、硅烷偶联剂KH550 3-5、硬酯酸钙1-3、抗氧剂DLTP 3-5、硬酯酸单甘油酯2-3、古马隆2-4、三氧化锑50-70和硼酸锌3-5。本发明由于采用三元乙丙橡胶、纳米凹凸棒土、氯醚橡胶、乙烯-丙烯酸甲酯共聚物EMA1125AC美国杜邦高分子材料并用作为本发明的基础材料,解决了电缆材料不能满足在高温强腐蚀的环境下工作使用现状,具有绝缘耐火抗的特性。

Description

一种聚丙烯绝缘电缆料及其制备方法
技术领域
本发明涉及一种聚丙烯绝缘电缆料及其制备方法,属于电缆料技术领域。 
背景技术
随着经济的迅速发展,电线电缆在各个行业、领域中都得到广泛的应用。随着电气火灾事故的频繁发生,电线电缆的阻燃问题逐渐引起世界各国的重视。电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素,在火灾中妨碍了人们的安全撤离和灭火工作,使生命财产遭到严重损失。同时随着通讯事业、汽车工业和计算机工业的发展,特别是航空导线、汽车用线、高温仪表电缆、石油钻井平台电缆等许多场合,越来越需要使用绝缘电缆料。 
发明内容
本发明的目的是提供一种聚丙烯绝缘电缆料及其制备方法,本发明由于采用三元乙丙橡胶、纳米凹凸棒土、氯醚橡胶、乙烯-丙烯酸甲酯共聚物EMA 1125AC 美国杜邦高分子材料并用作为本发明的基础材料,解决了电缆材料不能满足在高温强腐蚀的环境下工作使用现状,具有绝缘耐火抗的特性。 
为实现上述目的本发明的采用如下技术方案: 
聚丙烯绝缘电缆料,其组成原料的重量份为:三元乙丙橡胶80-110、纳米凹凸棒土130-150、氯醚橡胶50-70、乙烯-丙烯酸甲酯共聚物EMA 1125AC 美国杜邦  10-20、半补强炭黑 2-4、海泡石80-90、氧化锌 4-7、硫化剂MOCA   2-4、2-硫醇基苯骈咪唑1-4、硅烷偶联剂KH550  3-5、硬酯酸钙1-3、抗氧剂DLTP  3-5、硬酯酸单甘油酯2-3、古马隆2-4、三氧化锑50-70 和硼酸锌3-5。
聚丙烯绝缘电缆料,其组成原料的重量份为:三元乙丙橡胶95、纳米凹凸棒土140、氯醚橡胶60、乙烯-丙烯酸甲酯共聚物EMA 1125AC 美国杜邦  15、半补强炭黑 3、海泡石85、氧化锌 5、硫化剂MOCA  3、2-硫醇基苯骈咪唑2.5、硅烷偶联剂KH550  4、硬酯酸钙2、抗氧剂DLTP  4、硬酯酸单甘油酯2.5、古马隆3、三氧化锑60 和硼酸锌4。 
聚丙烯绝缘电缆料的制备方法,包括以下步骤: 
(1)按组成原料的重量份称取各原料,将三元乙丙橡胶、纳米凹凸棒土、氯醚橡胶、乙烯-丙烯酸甲酯共聚物EMA 1125AC 美国杜邦混合均匀,得到混合料A;
(2)在上述步骤(1)中的混合料A中按重量份加入半补强炭黑、海泡石、氧化锌、硫化剂MOCA、2-硫醇基苯骈咪唑、硅烷偶联剂KH550 、硬酯酸钙、抗氧剂DLTP、硬酯酸单甘油酯、古马隆、三氧化锑和硼酸锌,常温下低速搅拌3-5分钟,使得混合均匀,得到混合料B;
(3)将上述步骤(2)得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼、造粒,控制温度130-150℃,得到成品。
本发明的优点: 
本发明由于采用三元乙丙橡胶、纳米凹凸棒土、氯醚橡胶、乙烯-丙烯酸甲酯共聚物EMA 1125AC 美国杜邦高分子材料并用作为本发明的基础材料,解决了电缆材料不能满足在高温强腐蚀的环境下工作使用现状,具有绝缘耐火抗的特性。
具体实施方式
实施例1:聚丙烯绝缘电缆料,其组成原料的重量份为:三元乙丙橡胶95、纳米凹凸棒土140、氯醚橡胶60、乙烯-丙烯酸甲酯共聚物EMA 1125AC 美国杜邦  15、半补强炭黑 3、海泡石85、氧化锌 5、硫化剂MOCA  3、2-硫醇基苯骈咪唑2.5、硅烷偶联剂KH550  4、硬酯酸钙2、抗氧剂DLTP  4、硬酯酸单甘油酯2.5、古马隆3、三氧化锑60 和硼酸锌4。 
聚丙烯绝缘电缆料的制备方法,包括以下步骤: 
(1)按组成原料的重量份称取各原料,将三元乙丙橡胶、纳米凹凸棒土、氯醚橡胶、乙烯-丙烯酸甲酯共聚物EMA 1125AC 美国杜邦混合均匀,得到混合料A;
(2)在上述步骤(1)中的混合料A中按重量份加入半补强炭黑、海泡石、氧化锌、硫化剂MOCA、2-硫醇基苯骈咪唑、硅烷偶联剂KH550 、硬酯酸钙、抗氧剂DLTP、硬酯酸单甘油酯、古马隆、三氧化锑和硼酸锌,常温下低速搅拌3-5分钟,使得混合均匀,得到混合料B;
(3)将上述步骤(2)得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼、造粒,控制温度130-150℃,得到成品。
本发明制得的聚丙烯绝缘电缆料性能: 

Claims (3)

1.一种聚丙烯绝缘电缆料,其特征在于其组成原料的重量份为:三元乙丙橡胶80-110、纳米凹凸棒土130-150、氯醚橡胶50-70、乙烯-丙烯酸甲酯共聚物EMA 1125AC 美国杜邦  10-20、半补强炭黑 2-4、海泡石80-90、氧化锌 4-7、硫化剂MOCA   2-4、2-硫醇基苯骈咪唑1-4、硅烷偶联剂KH550  3-5、硬酯酸钙1-3、抗氧剂DLTP  3-5、硬酯酸单甘油酯2-3、古马隆2-4、三氧化锑50-70 和硼酸锌3-5。
2.根据权利要求1所述的聚丙烯绝缘电缆料,其特征在于其组成原料的重量份为:三元乙丙橡胶95、纳米凹凸棒土140、氯醚橡胶60、乙烯-丙烯酸甲酯共聚物EMA 1125AC 美国杜邦  15、半补强炭黑 3、海泡石85、氧化锌 5、硫化剂MOCA  3、2-硫醇基苯骈咪唑2.5、硅烷偶联剂KH550  4、硬酯酸钙2、抗氧剂DLTP  4、硬酯酸单甘油酯2.5、古马隆3、三氧化锑60 和硼酸锌4。
3.一种如权利要求1所述的聚丙烯绝缘电缆料的制备方法,其特征在于包括以下步骤:
(1)按组成原料的重量份称取各原料,将三元乙丙橡胶、纳米凹凸棒土、氯醚橡胶、乙烯-丙烯酸甲酯共聚物EMA 1125AC 美国杜邦混合均匀,得到混合料A;
(2)在上述步骤(1)中的混合料A中按重量份加入半补强炭黑、海泡石、氧化锌、硫化剂MOCA、2-硫醇基苯骈咪唑、硅烷偶联剂KH550 、硬酯酸钙、抗氧剂DLTP、硬酯酸单甘油酯、古马隆、三氧化锑和硼酸锌,常温下低速搅拌3-5分钟,使得混合均匀,得到混合料B;
(3)将上述步骤(2)得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼、造粒,控制温度130-150℃,得到成品。
CN201210192303.9A 2012-06-12 2012-06-12 一种聚丙烯绝缘电缆料及其制备方法 Expired - Fee Related CN102746585B (zh)