CN102153323B - 一种瓷质墙、地砖用胶粘剂 - Google Patents
一种瓷质墙、地砖用胶粘剂 Download PDFInfo
- Publication number
- CN102153323B CN102153323B CN201010615360A CN201010615360A CN102153323B CN 102153323 B CN102153323 B CN 102153323B CN 201010615360 A CN201010615360 A CN 201010615360A CN 201010615360 A CN201010615360 A CN 201010615360A CN 102153323 B CN102153323 B CN 102153323B
- Authority
- CN
- China
- Prior art keywords
- cement
- adhesive
- floor tile
- glue
- waste residue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明属于胶粘剂技术领域,具体涉及一种瓷质墙、地砖用胶粘剂,该种瓷质墙、地砖用胶粘剂,它由以下重量百分比的原料组成:水泥15-50%、防水胶10-25%,河沙20-50%,装修废渣粉10-30%,所述水泥为硅酸盐水泥,所述防水胶为聚合物水泥基防水胶。本发明粘结强度高、强耐老化、耐四季温差变化的能力强,使用本发明粘合的瓷质墙、地砖不会出现空鼓、开裂、渗水和脱落现象。
Description
技术领域
本发明属于胶粘剂技术领域,具体涉及一种瓷质墙、地砖用胶粘剂。
背景技术
随着生活水平的提高,人们对装修的质量要求也要求越来越高,由于瓷质墙、地砖具有美观、易清洁等优点,越来越多的人在装修中选择使用瓷质墙、地砖。
在各种类型的底材上安装瓷质墙、地砖时必然要使用到胶粘剂,虽然胶粘剂在装修中的用量很小,但其作用却不容忽视,胶粘剂的成份会影响瓷质墙、地砖粘结的强度、防水性和耐久性。
现有技术中,通常采用普通水泥、防水砂浆或普通墙地砖胶粘剂,但是由于普通水泥、防水砂浆或普通墙地砖胶粘剂粘结材料的粘结强度差、容易老化,使其粘合的瓷质墙、地砖出现空鼓、开裂、渗水和脱落等现象。
发明内容
本发明的目的是提供一种粘结强度高、强耐老化的瓷质墙、地砖用胶粘剂,使用本发明粘合的瓷质墙、地砖不会出现空鼓、开裂、渗水和脱落现象。
本发明的目的是这样实现的:
一种瓷质墙、地砖用胶粘剂,它由以下重量百分比的原料组成:
水泥 15-50%
防水胶 10-25%
河沙 20-50%
装修废渣粉 10-30%,
其中,所述水泥为硅酸盐水泥;
其中,所述防水胶为聚合物水泥基防水胶,采用黑豹牌聚合物水泥基防水胶。
优选的,它由以下重量百分比的原料组成:
水泥 20-40%
防水胶 15-20%
河沙 30-40%
装修废渣粉 15-25%。
更为优选的,它由以下重量百分比的原料组成:
水泥 35%
防水胶 15%
河沙 25%
装修废渣粉 25%。
其中,所述装修废渣粉包括灰沙和混凝土块。
其中,所述装修废渣粉的粒径为0.01-2mm。
其中,所述河沙的粒径为0.01-2mm。
将水泥、防水胶、河沙、装修废渣粉按比例混合并搅拌均匀,即可使用。
本发明的有益效果为:该种瓷质墙、地砖用胶粘剂,它由以下重量百分比的原料组成:水泥15-50%、防水胶10-25%,河沙20-50%,装修废渣粉10-30%,所述水泥为硅酸盐水泥,所述防水胶为聚合物水泥基防水胶。本发明粘结强度高、强耐老化、耐四季温差变化的能力强,使用本发明粘合的瓷质墙、地砖不会出现空鼓、开裂、渗水和脱落现象。
具体实施方式
下面通过实施例对本发明作进一步说明,但本发明的实施范围并不限于此。
实施例1
一种瓷质墙、地砖用胶粘剂,它由以下原料组成:硅酸盐水泥15g、聚合物水泥基防水胶25g、粒径为0.01-2mm的河沙40g、粒径为0.01-2mm的包含有灰沙和混凝土块的装修废渣粉20g,将上述重量的硅酸盐水泥、聚合物水泥基防水胶、河沙、装修废渣粉按比例混合并搅拌均匀,即可使用。
本实施例制得的胶粘剂粘结强度高、强耐老化、耐四季温差变化的能力强,使用本实施例制得的胶粘剂粘合的瓷质墙、地砖不会出现空鼓、开裂、渗水和脱落现象。
实施例2
一种瓷质墙、地砖用胶粘剂,它由以下原料组成:硅酸盐水泥25g、聚合物水泥基防水胶20g、粒径为0.01-2mm的河沙25g、粒径为0.01-2mm的包含有灰沙和混凝土块的装修废渣粉30g,将上述重量的硅酸盐水泥、聚合物水泥基防水胶、河沙、装修废渣粉按比例混合并搅拌均匀,即可使用。
本实施例制得的胶粘剂粘结强度高、强耐老化、耐四季温差变化的能力强,使用本实施例制得的胶粘剂粘合的瓷质墙、地砖不会出现空鼓、开裂、渗水和脱落现象。
实施例3
一种瓷质墙、地砖用胶粘剂,它由以下原料组成:硅酸盐水泥35g、聚合物水泥基防水胶15g、粒径为0.01-2mm的河沙25g、粒径为0.01-2mm的包含有灰沙和混凝土块的装修废渣粉25g,将上述重量的硅酸盐水泥、聚合物水泥基防水胶、河沙、装修废渣粉按比例混合并搅拌均匀,即可使用。
本实施例制得的胶粘剂粘结强度高、强耐老化、耐四季温差变化的能力强,使用本实施例制得的胶粘剂粘合的瓷质墙、地砖不会出现空鼓、开裂、渗水和脱落现象。
实施例4
一种瓷质墙、地砖用胶粘剂,它由以下原料组成:硅酸盐水泥50g、聚合物水泥基防水胶10g、粒径为0.01-2mm的河沙40g、粒径为0.01-2mm的包含有灰沙和混凝土块的装修废渣粉10g,将上述重量的硅酸盐水泥、聚合物水泥基防水胶、河沙、装修废渣粉按比例混合并搅拌均匀,即可使用。
本实施例制得的胶粘剂粘结强度高、强耐老化、耐四季温差变化的能力强,使用本实施例制得的胶粘剂粘合的瓷质墙、地砖不会出现空鼓、开裂、渗水和脱落现象。
以上所述仅是本发明的较佳实施方式,故凡依本发明专利申请范围所述的构造、特征及原理所做的等效变化或修饰,均包括于本发明专利申请范围内。
Claims (5)
1.一种瓷质墙、地砖用胶粘剂,其特征在于:它由以下重量百分比的原料组成:
水泥 15-50%
防水胶 10-25%
河沙 20-50%
装修废渣粉 10-30%,
其中,所述水泥为硅酸盐水泥;
其中,所述防水胶为聚合物水泥基防水胶;
其中,所述河沙的粒径为0.01-2mm;
其中,所述装修废渣粉的粒径为0.01-2mm。
2.根据权利要求1所述的一种瓷质墙、地砖用胶粘剂,其特征在于:它由以下重量百分比的原料组成:
水泥 20-40%
防水胶 15-20%
河沙 30-40%
装修废渣粉 15-25%。
3.根据权利要求1所述的一种瓷质墙、地砖用胶粘剂,其特征在于:它由以下重量百分比的原料组成:
水泥 35%
防水胶 15%
河沙 25%
装修废渣粉 25%。
4.根据权利要求1所述的一种瓷质墙、地砖用胶粘剂,其特征在于:所述装修废渣粉包括灰沙和混凝土块。
5.根据权利要求1-4任一项所述的一种瓷质墙、地砖用胶粘剂,其特征在于:将水泥、防水胶、河沙、装修废渣粉按比例混合并搅拌均匀,即可使用。