CN103102120B - 一种装饰砂浆及其制备方法 - Google Patents

一种装饰砂浆及其制备方法 Download PDF

Info

Publication number
CN103102120B
CN103102120B CN201210547848.7A CN201210547848A CN103102120B CN 103102120 B CN103102120 B CN 103102120B CN 201210547848 A CN201210547848 A CN 201210547848A CN 103102120 B CN103102120 B CN 103102120B
Authority
CN
China
Prior art keywords
parts
water
decoration mortar
mortar
thixotropic agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210547848.7A
Other languages
English (en)
Other versions
CN103102120A (zh
Inventor
王杨崴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHONGQING BAISHIDE BUILDING MATERIALS Co Ltd
Original Assignee
CHONGQING BAISHIDE BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHONGQING BAISHIDE BUILDING MATERIALS Co Ltd filed Critical CHONGQING BAISHIDE BUILDING MATERIALS Co Ltd
Priority to CN201210547848.7A priority Critical patent/CN103102120B/zh
Publication of CN103102120A publication Critical patent/CN103102120A/zh
Application granted granted Critical
Publication of CN103102120B publication Critical patent/CN103102120B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种装饰砂浆及其制备方法,目的是提供一种耐候性好、粘附力强、机械强度高的外墙装饰砂浆及其制备方法。它由如下重量份组成:300~500份白水泥、300~500份石英砂、30~50份乳胶粉、3~6份保水剂、80~150份双飞粉、1~3份触变剂、1~4份减水剂、0.5~2份聚丙烯纤维、3~6份木质纤维、5~15份聚乙烯醇;将双飞粉加入搅拌机搅拌均匀,然后加入其他组分的预混物,搅拌均匀即得装饰砂浆;使用时只需加入适量水混合均匀即可。本发明方法简单,制备的外墙装饰砂浆具有良好的耐高低温性能,及耐老化性,高机械强度,与基底的粘结力好,防开裂效果好的特点,且绿色环保,成本低廉。

Description

_种装饰砂浆及其制备方法
技术领域
[0001] 本发明涉及一种装饰砂浆及其制备方法。
背景技术
[0002] 装饰砂浆主要通过在砂浆中添加不同颜料得到不同颜色的装饰砂浆,用于墙面的 装饰,通过抹涂不同颜色的装饰砂浆、塑造不同的立体图案,使得墙面既能受到保护又能变 得美观。一般的装饰砂浆抹涂在墙面上,由于经过日照雨淋严寒酷暑的温差应力,或其他机 械外力的作用,会发生损伤和脱落,使得墙面既得不到保护,也破坏了其美感。
发明内容
[0003] 本发明的主要目的是提供一种耐候性好、粘附力强、机械强度高的装饰砂浆及其 制备方法。
[0004] 一种装饰砂浆,其特征在于:由如下重量份组成:由如下重量份组成:300~500 份白水泥、300~500份石英砂、30~50份乳胶粉、3~6份保水剂、80~150份双飞粉、 1~3份触变剂、1~4份减水剂、0. 5~2份聚丙稀纤维、3~6份木质纤维、5~15份聚乙 稀醇。
[0005] 进一步优选的是,所述的装饰砂浆由如下重量份组成:所述的装饰砂浆由如下重 量份组成:380~480份白水泥、300~400份石英砂、35~45份乳胶粉、4~6份保水剂、 80~120份双飞粉、2份触变剂、1~3份减水剂、0. 5~1. 2份聚丙烯纤维、4~6份木质纤 维、8~12份聚乙稀醇。
[0006] 更进一步优选的是,所述的外墙腻子粉的组成为:所述的装饰砂浆由如下重量份 组成:400~450份白水泥、350~385份石英砂、34~40份乳胶粉、4~5份保水剂、90~ 110份双飞粉、2份触变剂、2份减水剂、1份聚丙烯纤维、5份木质纤维、10~11份聚乙烯醇。
[0007] 所述的白水泥、石英砂、乳胶粉细度为70~140目。颗粒过大或过小会降低砂浆 的强度和粘度。
[0008] 所述的触变剂为聚酰胺蜡、氢化蓖麻油中的一种。
[0009] 所述的保水剂为所述的保水剂为聚丙烯酰胺、聚丙烯酸钠、聚丙烯酸钾、淀粉接枝 丙烯酸盐共聚交联物、乙基纤维素、羧甲基纤维素钠、甲基纤维素、羟丙基甲基纤维素、羟基 纤维素乙醚、淀粉酯、膨润土、高岭土、硅藻土中的一种。
[0010] 为进一步提高本发明的保坍性,所述的减水剂为聚羧酸高性能减水剂。
[0011] 所述的装饰砂浆的制备方法为:将双飞粉加入搅拌机搅拌均匀,然后加入如下组 分预混物:白水泥、石英砂、乳胶粉、保水剂、触变剂、减水剂、聚丙烯纤维、木质纤维、聚乙烯 醇。继续搅拌混合均匀即得装饰砂浆。使用时只需加入适量水混合均匀即可。装饰砂浆中 加入适量颜料粉就制成不同颜色的彩色装饰砂浆。
[0012] 上述技术方案中单体的用量是参与反应的最佳原料比例,但是本领域技术人员可 以根据本发明的教导进行等同的变化。例如:因为工业生产本身的误差导致的参数变化与 本发明的技术方案等同。
[0013] 本发明制备的装饰砂浆产品具有良好的耐高低温性能,及耐老化性,高机械强度, 尤其是抗压强度高,使得本发明适用于塑造凹凸立体图案,此外,本发明制备的装饰砂浆产 品与基底的粘结力好,防开裂效果好,且绿色环保,成本低廉。
具体实施方式
[0014] 为使本领域技术人员更加清楚和明确本发明的技术方案,特提供下面优选的实施 例,但本发明的技术思想并不限于以下实施例。
[0015] 实施例一
[0016] 将100kg双飞粉加入搅拌机搅拌均匀,然后加入按照如下重量比配方预混的预混 物:450kg白水泥、385kg石英砂、40kg乳胶粉、5kg保水剂、2kg触变剂、2kg减水剂、lkg聚 丙烯纤维、5kg木质纤维、10kg聚乙烯醇。继续搅拌混合均匀即得装饰砂浆。
[0017] 实施例二
[0018] 将110kg双飞粉加入搅拌机搅拌均匀,然后加入按照如下重量比配方预混的预混 物:400kg白水泥、350kg石英砂、40kg乳胶粉、5kg保水剂、2kg触变剂、2kg减水剂、0. 8kg聚 丙烯纤维、5kg木质纤维、11kg聚乙烯醇。继续搅拌混合均匀即得装饰砂浆。
[0019] 实施例三
[0020] 将90kg双飞粉加入搅拌机搅拌均勾,然后加入按照如下重量比配方预混的预混 物:420kg白水泥、360kg石英砂、34kg乳胶粉、4kg保水剂、2kg触变剂、2kg减水剂、lkg聚 丙烯纤维、5kg木质纤维、11kg聚乙烯醇。继续搅拌混合均匀即得装饰砂浆。
[0021] 实施例一的产品由重庆市计量质量检测研究院依据JC/T1024-2007《墙体饰面砂 浆》标准进行性能检测,测试结果如下表所示。
[0022]
Figure CN103102120BD00041
[0023] 从测试结果可以看到,本发明制备的装饰砂浆耐高低温性能好,经过老化试验后 其粘结强度仅降低了 〇. 〇8MPa;且机械强度高,抗压强度可达10. 63MPa;其粘结强度也较 高,耐碱性好。

Claims (6)

1. 一种装饰砂浆,其特征在于:由如下重量份组成:300~500份白水泥、300~500份 石英砂、30~50份乳胶粉、3~6份保水剂、80~150份双飞粉、1~3份触变剂、1~4份 减水剂、〇. 5~2份聚丙稀纤维、3~6份木质纤维、5~15份聚乙稀醇; 所述的白水泥、石英砂、乳胶粉细度为70~140目; 所述的触变剂为聚酰胺蜡、氢化蓖麻油中的一种。
2. 根据权利要求1所述的装饰砂浆,其特征在于:所述的装饰砂浆由如下重量份组成: 380~480份白水泥、300~400份石英砂、35~45份乳胶粉、4~6份保水剂、80~120份 双飞粉、2份触变剂、1~3份减水剂、0. 5~1. 2份聚丙烯纤维、4~6份木质纤维、8~12 份聚乙烯醇。
3. 根据权利要求2所述的装饰砂浆,其特征在于:所述的装饰砂浆由如下重量份组成: 400~450份白水泥、350~385份石英砂、34~40份乳胶粉、4~5份保水剂、90~110份 双飞粉、2份触变剂、2份减水剂、1份聚丙烯纤维、5份木质纤维、10~11份聚乙烯醇。
4. 根据权利要求1~3中任意一项所述的装饰砂浆,其特征在于:所述的保水剂为聚 丙烯酰胺、聚丙烯酸钠、聚丙烯酸钾、淀粉接枝丙烯酸盐共聚交联物、乙基纤维素、羧甲基纤 维素钠、甲基纤维素、羟丙基甲基纤维素、羟基纤维素乙醚、淀粉酯、膨润土、高岭土、硅藻土 中的一种。
5. 根据权利要求4所述的装饰砂浆,其特征在于:所述的减水剂为聚羧酸高性能减水 剂。
6. 根据权利要求1~3中任意一项所述的装饰砂浆的制作方法,其特征在于:将双飞 粉加入搅拌机搅拌均匀,然后加入如下组分预混物:白水泥、石英砂、乳胶粉、保水剂、触变 剂、减水剂、聚丙烯纤维、木质纤维、聚乙烯醇,继续搅拌混合均匀即得装饰砂浆。
CN201210547848.7A 2012-12-17 2012-12-17 一种装饰砂浆及其制备方法 Active CN103102120B (zh)