CN102140340A - 一种Mn激活的绿色荧光粉及其制备方法与用途 - Google Patents
一种Mn激活的绿色荧光粉及其制备方法与用途 Download PDFInfo
- Publication number
- CN102140340A CN102140340A CN201010104279XA CN201010104279A CN102140340A CN 102140340 A CN102140340 A CN 102140340A CN 201010104279X A CN201010104279X A CN 201010104279XA CN 201010104279 A CN201010104279 A CN 201010104279A CN 102140340 A CN102140340 A CN 102140340A
- Authority
- CN
- China
- Prior art keywords
- fluorescent powder
- green fluorescent
- percent
- preparation
- grams
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于发光材料领域，公开了一种用于灯用或者显示用绿色荧光粉。Mn激活铝酸盐绿色荧光粉的分子式为：(Ba，Mn)MgAl10O17。称取Al2O3100g、BaCO320g-26g、MnCO37g-9g、MgO6.5g-8g，加入0.2-0.5％的助熔剂BaF2或H3BO3，各原料重量比为：氧化铝65-80％，碳酸钡5-8％，碳酸锰5-7％，氧化镁5-7％，制备方法为高温固相法。各原料优选重量比为氧化铝∶碳酸钡∶碳酸锰∶氧化镁＝0.8∶0.10∶0.065∶0.07。该绿色荧光粉能被250-300nm紫外光激发，发出高效绿光，制备工艺简单，成熟易于产业化，因此本发明可作为一种新型的灯用或者显示用绿色荧光粉。
Description
技术领域
本发明属于发光材料领域，特别涉及一种铝酸盐Mn激活的绿色荧光粉及其制备方法。
背景技术
绿色荧光粉广泛使用在显示和照明领域，如显示器、照明荧光灯、霓虹灯、装饰用彩色荧光灯等。目前使用的绿色荧光粉多为Tb或者Eu激活荧光体，虽然其性能优能，但Tb、Eu价格昂贵，造成荧光粉的制造成本偏高。在霓虹灯、装饰用彩色荧光灯等领域应用成本偏高不适用。
发明内容
本发明的目的是提供一种Mn激活铝酸盐绿色荧光粉；
本发明的另一目的是提供一种Mn激活铝酸盐绿色荧光粉的制备方法。
本发明Mn激活铝酸盐绿色荧光粉的分子为：((Ba，Mn)MgAl10O17本发明Mn激活铝酸盐绿色荧光粉的制备方法包括以下步骤：
(1)称取Al2O3100g、BaCO320g-26g、MnCO37g-9g、MgO6.5g-8g，加入0.2-0.5％的助熔剂BaF2或H3BO3，(各原料重量比为：氧化铝65-80％，碳酸钡5-8％，碳酸锰5-7％，氧化镁5-7％)得到混合物并混合均匀；
(2)将混好的原料放入空气隧道窑中1500-1550度灼烧2～4小时，取出降温至室温；
(3)将灼烧过的粉体碾碎过50目筛；
(4)将筛好的粉放入氢气还原炉中1400～1450度灼烧2～4小时，取出降温至室温，得到半成品，测试相对亮度、发射主峰、粒度等指标；
(5)将半成品碾碎、粗筛洗涤、湿筛、离心、烘干过100目筛，测试综合数据，得到成品。
本发明Mn激活铝酸盐绿色荧光粉的制备，各原料优选重量比为氧化铝∶碳酸钡∶碳酸锰∶氧化镁＝0.8∶0.10∶0.065∶0.07。
本发明Mn激活铝酸盐绿色荧光粉能高效地被250-300nm紫外光激发，发出高效绿光， 发射主峰在514nm，用于荧光灯中稳定性好、发光强度高。制备工艺简单、易于产业化，因此本发明可作为一种新型的灯用或者显示用绿色荧光粉。
具体实施方式
下面对本发明作一详细说明
Mn激活铝酸盐绿色荧光粉的分子为：((Ba，Mn)MgAl10O17。称取Al2O3100g、BaCO320g-26g、MnCO37g-9g、MgO6.5g-8g，加入0.2-0.5％的助熔剂BaF2或H3BO3，(各原料重量比为：氧化铝65-80％，碳酸钡5-8％，碳酸锰5-7％，氧化镁5-7％)得到混合物并混合均匀，将混好的原料放入空气隧道窑中1500～1550度灼烧2～4小时，取出降温至室温；将灼烧过的粉体碾碎过50目筛；将筛好的粉放入氢气还原炉中1400～1450度灼烧2～4小时，取出降温至室温，得到半成品并测试相对亮度、发射主峰、粒度等指标，将半成品碾碎、粗筛洗涤、湿筛、离心，烘干过100目筛，测试综合数据，得到成品。用荧光光谱测试仪测试其发射主峰为514nm。
本发明Mn共激活铝酸盐绿色荧光粉的制备，各原料优选重量比为氧化铝∶碳酸钡∶碳酸锰∶氧化镁＝0.8∶0.10∶0.065∶0.07。
Claims (3)
1.一种铝酸盐绿色荧光粉，其特征在于：所述的绿色荧光粉的分子式为：((Ba，Mn)MgAl10O17。
2.根据权利要求1所述的铝酸盐绿色荧光粉，其特征是，荧光光谱测试其发射主峰为514nm。
3.根据权利要求1所述的铝酸盐绿色荧光粉的制备方法，其特征是：所述的方法步骤包括：
(1)称取Al2O3100g、Ba CO320g-26g、MnCO37g-9g、MgO6.5g-8g，加入0.2-0.5％的助熔剂BaF2或H3BO3；各原料重量比为：氧化铝65-80％，碳酸钡5-8％，碳酸锰5-7％，氧化镁5-7％，得到混合物并混合均匀；
(2)将混好的原料放入空气隧道窑中1500～1550度灼烧2～4小时，取出降温至室温；
(3)将灼烧过的粉体碾碎过50目筛；
(4)将筛好的粉放入氢气还原炉中1400～1450度灼烧2～4小时，取出降温至室温，得到半成品，测试相对亮度、发射主峰、粒度；
(5)将半成品碾碎、粗筛洗涤、湿筛、离心、烘干过100目筛，测试综合数据，得到成品。