CN102140342A - 一种铝酸盐Ce、Mn共激活的绿色荧光粉及其制备方法与用途 - Google Patents

一种铝酸盐Ce、Mn共激活的绿色荧光粉及其制备方法与用途 Download PDF

Info

Publication number
CN102140342A
CN102140342A CN2010101042751A CN201010104275A CN102140342A CN 102140342 A CN102140342 A CN 102140342A CN 2010101042751 A CN2010101042751 A CN 2010101042751A CN 201010104275 A CN201010104275 A CN 201010104275A CN 102140342 A CN102140342 A CN 102140342A
Authority
CN
China
Prior art keywords
fluorescent powder
green fluorescent
percent
aluminate
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010101042751A
Other languages
English (en)
Inventor
曾维亮
蒋葵明
刘兆辉
曾国里
刘清玲
邓丹妮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN STEADY NEW MATERIAL CO Ltd
Original Assignee
HUNAN STEADY NEW MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN STEADY NEW MATERIAL CO Ltd filed Critical HUNAN STEADY NEW MATERIAL CO Ltd
Priority to CN2010101042751A priority Critical patent/CN102140342A/zh
Publication of CN102140342A publication Critical patent/CN102140342A/zh
Pending legal-status Critical Current

Abstract

本发明属于发光材料领域，公开了一种用于灯用或者显示用铝酸盐绿色荧光粉。其分子式为：(CeMn)MgAl11O19，各原料重量比为：氧化铝65-80％，氧化铈9-12％，碳酸锰4-6％，氧化镁5-7％，再加入0.2-0.5％的助熔剂BaF2或H3BO3，制备方法为高温固相法。各原料优选重量比为氧化铝∶氧化铈∶碳酸锰∶氧化镁＝0.75∶0.12∶0.055∶0.06。该稀土铝酸盐绿色荧光粉能被250-300nm紫外光激发，发出高效绿光，制备工艺简单，成熟易于产业化，因此本发明可作为一种新型的灯用或者显示用绿色荧光粉。

Description

一种铝酸盐Ce、Mn共激活的绿色荧光粉及其制备方法与用途
技术领域
本发明属于发光材料领域，特别涉及一种铝酸盐Ce、Mn共激活的绿色荧光粉及其制备方法。
背景技术
绿色荧光粉广泛使用在显示和照明领域，如显示器、照明荧光灯、霓虹灯、装饰用彩色荧光灯等。目前使用的绿色荧光粉多为Tb或者Eu激活荧光体，虽然其性能优能，但Tb、Eu价格昂贵，造成荧光粉的制造成本偏高，另外一种常用的的绿色荧光粉Zn2SiO4:Mn[参考文献CN1290401]，虽然其价格低廉，但这种荧光粉有较长的余辉，造成在应用中有拖尾现象，在许多应用中受到限制。
发明内容
本发明的目的是提供一种Ce、Mn共激活铝酸盐绿色荧光粉；
本发明的另一目的是提供一种Ce、Mn共激活铝酸盐绿色荧光粉的制备方法。
本发明Ce、Mn共激活铝酸盐绿色荧光粉的分子为：(CeMn)Mg Al11O19
本发明Ce、Mn共激活铝酸盐绿色荧光粉的制备方法包括以下步骤：
(1)称取Al2O3100g、CeO214g-16g、MnCO36g-8g、MgO6.5g-8g，加入0.2-0.5％的助熔剂BaF2或H3BO3，(各原料重量比为：氧化铝65-80％，氧化铈9-12％，碳酸锰4-6％，氧化镁5-7％)得到混合物并混合均匀；
(2)将混好的原料放入空气隧道窑中1500-1550度灼烧2～4小时，取出降温至室温；
(3)将灼烧过的粉体碾碎过50目筛；
(4)将筛好的粉放入氢气还原炉中1400～1450度灼烧2～4小时，取出降温至室温，得到半成品，测试相对亮度、发射主峰、粒度等指标；
(5)将半成品碾碎、粗筛洗涤、湿筛、离心、烘干过100目筛，测试综合数据，得到成品。
本发明Ce、Mn共激活铝酸盐绿色荧光粉的制备，各原料优选重量比为氧化铝∶氧化 铈∶碳酸锰∶氧化镁5-7％＝0.75∶0.12∶0.055∶0.06。
本发明Ce、Mn共激活铝酸盐绿色荧光粉能高效地被250-300nm紫外光激发，发出高效绿光，发射主峰在515nm，用于荧光灯中稳定性好、发光强度高。制备工艺简单、易于产业化，因此本发明可作为一种新型的灯用或者显示用绿色荧光粉。
具体实施方式
下面对本发明作一详细说明
铝酸盐绿色荧光粉的化学式(CeMn)Mg Al11O19。称取Al2O3100g、CeO214g-16g、MnCO36g-8g、MgO6.5g-8g，加入0.2-0.5％的助熔剂BaF2或H3BO3，得到混合物并混合均匀；将混好的原料放入空气隧道窑中1500～1550度灼烧2～4小时，取出降温至室温；将灼烧过的粉体碾碎过50目筛；将筛好的粉放入氢气还原炉中1400～1450度灼烧2～4小时，取出降温至室温，得到半成品并测试相对亮度、发射主峰、粒度等指标，将半成品碾碎、粗筛洗涤、湿筛、离心，烘干过100目筛，测试综合数据，得到成品。用荧光光谱测试仪测试其发射主峰为515nm。
本发明Ce、Mn共激活铝酸盐绿色荧光粉的制备，各原料优选重量比为氧化铝∶氧化铈∶碳酸锰∶氧化镁5-7％＝0.75∶0.12∶0.055∶0.06。

Claims (3)

1.一种铝酸盐绿色荧光粉，其特征在于：所述的绿色荧光粉的分子式为：(CeMn)MgAl11O19。
2.根据权利要求1所述的铝酸盐绿色荧光粉，其特征是，荧光光谱测试其发射主峰为515nm。
3.根据权利要求1所述的铝酸盐绿色荧光粉的制备方法，其特征是：所述的方法步骤包括：
(1)称取Al2O3100g、CeO214g-16g、MnCO36g-8g、MgO6.5g-8g，加入0.20.5％的助熔剂BaF2或H3BO3；各原料重量比为：氧化铝65-80％，氧化铈9-12％，碳酸锰4-6％，氧化镁5-7％，得到混合物并混合均匀；
(2)将混好的原料放入空气隧道窑中1500～1550度灼烧2～4小时，取出降温至室温；
(3)将灼烧过的粉体碾碎过50目筛；
(4)将筛好的粉放入氢气还原炉中1400～1450度灼烧2～4小时，取出降温至室温，得到半成品，测试相对亮度、发射主峰、粒度；
(5)将半成品碾碎、粗筛洗涤、湿筛、离心、烘干过100目筛，测试综合数据，得到成品。
CN2010101042751A 2010-02-02 2010-02-02 一种铝酸盐Ce、Mn共激活的绿色荧光粉及其制备方法与用途 Pending CN102140342A (zh)