CN101967060A - 一种日用瓷器的烧制方法 - Google Patents

一种日用瓷器的烧制方法 Download PDF

Info

Publication number
CN101967060A
CN101967060A CN2009101131199A CN200910113119A CN101967060A CN 101967060 A CN101967060 A CN 101967060A CN 2009101131199 A CN2009101131199 A CN 2009101131199A CN 200910113119 A CN200910113119 A CN 200910113119A CN 101967060 A CN101967060 A CN 101967060A
Authority
CN
China
Prior art keywords
firing
glaze
temperature
product
biscuit
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2009101131199A
Other languages
English (en)
Other versions
CN101967060B (zh
Inventor
苏志强
苏志坚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Province Jia Shunyi product limited-liability company
Original Assignee
FUJIAN PROVINCE DEHUA COUNTY YUNZI CERAMICS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUJIAN PROVINCE DEHUA COUNTY YUNZI CERAMICS Co Ltd filed Critical FUJIAN PROVINCE DEHUA COUNTY YUNZI CERAMICS Co Ltd
Priority to CN200910113119A priority Critical patent/CN101967060B/zh
Publication of CN101967060A publication Critical patent/CN101967060A/zh
Application granted granted Critical
Publication of CN101967060B publication Critical patent/CN101967060B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种日用瓷器的烧制方法，特别是指一种碗类与杯类高档日用瓷器的烧制方法，包括如下步骤：步骤一，将修整好的坯体干燥后，放入窑炉进行800～900℃低温素烧，并将素烧坯打磨光滑；步骤二，素烧坯施釉后，将制品口沿与底脚的釉料去除；步骤三，采用倒扣的方式，将制品直接放在耐火棚板上进行第一次的高温釉烧；步骤四，将制品翻过来后先将其口沿清理干净，对制品的口沿局部施釉后，再次放入窑炉，正立放置进行第二次的高温釉烧，冷却后得到成品。和现有的低温素烧高温釉烧或高温素烧低温釉烧的烧制方法相比，本发明操作方便，烧成品造型轻巧，优等品率高，特别适用于各种碗类与杯类高档日用瓷器产品的生产。

Description

一种日用瓷器的烧制方法
技术领域
本发明涉及一种日用瓷器的烧制方法，特别是指一种碗类与杯类高档日用瓷器的烧制方法。
背景技术
多年来，为解决日用瓷器的变形问题，广大的陶瓷科技工作者与生产企业进行了大量的试验与研究工作，从陶瓷泥料配方、成型、干燥直到烧成的生产各个环节进行全过程控制，在器型的设计上除了协调美观之外，一般均要在杯碟碗盘类制品的口沿处增设一道加厚边；在烧成方面，目前比较常用的烧制方法主要有低温素烧高温釉烧与高温素烧低温釉烧两种形式，但均有利弊。
当采用低温素烧高温釉烧的方法来克服碗盘类制品的变形缺陷时，在高温素烧过程中就必须将施过釉的坯体倒扣在特制的垫饼上烧制，虽然制品的变形量较小，但是制品的口沿没有釉，不符合高档瓷的要求，同时垫饼只能使用一次，浪费较大，目前景德镇的薄胎瓷器基本使用这种烧制方法；现在的骨质瓷、高石英质瓷与鲁玉瓷等高档瓷器都是采用高温素烧低温釉烧的方法烧制，高温素烧时坯体不上釉，要用特制的垫饼或仿形匣钵托住坯体防止变形，将高温素烧坯磨光施低温熔块釉，为防止产品变形，必须采用低温釉烧，釉烧的温度一般要比高温素烧低100℃以上，存在的主要问题是低温熔块釉的釉面硬度太低，满足不了西餐刀具的长期刻划使用。
发明内容
本发明的主要目的在于克服现有技术中日用瓷器在烧制过程中的变形问题，提供一种方法简便、烧制产品造型轻巧的高档日用瓷器的烧制方法。
本发明采用如下的技术方案：
一种日用瓷器的烧制方法，包括如下步骤：
步骤一，将修整好的坯体干燥后，放入窑炉进行800～900℃低温素烧，并将素烧坯打磨光滑；
步骤二，素烧坯施釉后，将制品口沿与底脚的釉料去除；
步骤三，采用倒扣的方式，将制品直接放在耐火棚板上进行第一次的高温釉烧；
步骤四，将制品翻过来后先将其口沿清理干净，对制品的口沿局部施釉后，再次放入窑炉，正立放置进行第二次的高温釉烧，冷却后得到成品。
进一步地，所述第一次和第二次高温釉烧的温度相同，该温度由坯料和釉料的配方确定。
进一步地，所述耐火棚板的的表面平整，并涂刷有氧化铝涂层。
进一步地，所述步骤四中，在施口沿部分的釉料时，为提高釉层的附着力，釉浆中添加有CMC、PVA等胶粘剂。
另外，本发明的烧制方法对瓷器的材质和配方没有特殊限制，适用于各工厂生产的现有产品。
本发明将低温素烧后的施釉坯体直接倒扣在平整的耐火棚板上进行高温釉烧，不需要特制的垫饼或匣钵，器型的口沿也不需要传统的增厚边，经过第一次的高温釉烧后，制品的形状已经定型，而且变形量很小；翻过来口沿施釉后在同样的温度下，再正立放置放在耐火棚板上高温釉烧一次，让口沿的釉料与其他部位的釉料融合在一起，在确保口沿光滑的同时，烧成后制品的釉面硬度比熔块釉更高。和现有的低温素烧高温釉烧或高温素烧低温釉烧的烧制方法相比，本发明的烧制方法操作方便，烧成品造型轻巧，优等品率高，特别适用于各种碗类与杯类高档日用瓷器产品的生产。
附图说明
图1为采用本发明一种日用陶瓷的烧制方法进行第一次烧制时碗倒扣在棚板上时的结构示意图；
图2为采用本发明一种日用陶瓷的烧制方法进行第二次烧制时碗正立在棚板上时的结构示意图；
图3为采用本发明一种日用陶瓷的烧制方法烧制的碗的断面结构示意图；
图4为采用传统方法烧制的碗的断面结构示意图；
图5为采用本发明一种日用陶瓷的烧制方法烧制的杯的断面结构示意图。
具体实施方式
以下通过具体实施方式对本发明进行进一步说明。首先参照图1至图5，为采用本发明一种日用陶瓷的烧制方法烧制的碗、杯与采用传统方法烧制的碗的对比结构示意图。
实施例一建白瓷”饭碗的烧制
步骤一，取真空练泥好的“建白瓷”泥10kg；
步骤二，用阴模滚压成型制得饭碗的坯体10件；
步骤三，修整后扣在垫饼上烘干；
步骤四，将坯体放进窑炉于900℃低温素烧一次；
步骤五，将素烧坯磨光后，在坯体的正反两面均匀地施上一层“建白瓷”釉；
步骤六，用湿润的海绵小心将碗口沿与底脚处的釉层擦除；
步骤七，将涂刷有氧化铝涂料的碳化硅耐火棚板的表面整理平整；
步骤八，将釉坯小心地倒扣在耐火棚板上，注意碗与碗之间不能相碰，应留有适当的空隙；
步骤九，按照传统“建白瓷”的烧成曲线温度，在1320℃高火保温30min后停火；
步骤十，将冷却后的瓷坯取出，将碗口部清理干净，用喷枪喷上一层“建白瓷”釉；
步骤十一，把口沿施釉的半成品，正立着放在涂刷有氧化铝涂料的碳化硅耐火棚板上，用与上述相同的烧成方法，于1320℃进行第二次的高温釉烧；
步骤十二，冷却后出炉，即可得到成品，成品的优等品率90％，合格率100％。实施例二高级茶杯的烧制
步骤一，取真空练泥好的瓷泥15kg；
步骤二，用阴模滚压成型制得茶杯的坯体20件；
步骤三，修整后扣在垫饼上烘干；
步骤四，将坯体放进窑炉于850℃低温素烧一次；
步骤五，将素烧坯磨光后，在坯体的正反两面均匀地施上一层瓷釉；
步骤六，用湿润的海绵小心将杯口沿与底脚处的釉层擦除；
步骤七，将涂刷有氧化铝涂料的碳化硅耐火棚板的表面整理平整；
步骤八，将釉坯小心地倒扣在耐火棚板上，注意杯与杯之间不能相碰，应留有适当的空隙；
步骤九，按照一般茶杯的烧成曲线温度，在1300℃高火保温30min后停火；
步骤十，将冷却后的瓷坯取出，将杯口部清理干净，用喷枪喷上一层瓷釉；
步骤十一，把口沿施釉的半成品，正立着放在涂刷有氧化铝涂料的碳化硅耐火棚板上，用与上述相同的烧成方法，于1300℃进行第二次的高温釉烧；
步骤十二，冷却后出炉，即可得到成品，成品的优等品率90％，合格率100％。
上述仅为本发明的两个具体实施方式，但本发明的设计构思并不局限于此，凡利用此构思对本发明进行非实质性的改动，均应属于侵犯本发明保护范围的行为。

Claims (4)

1.一种日用瓷器的烧制方法，其特征在于：包括如下步骤：
步骤一，将修整好的坯体干燥后，放入窑炉进行800～900℃低温素烧，并将素烧坯打磨光滑；
步骤二，素烧坯施釉后，将制品口沿与底脚的釉料去除；
步骤三，采用倒扣的方式，将制品直接放在耐火棚板上进行第一次的高温釉烧；
步骤四，将制品翻过来后先将其口沿清理干净，对制品的口沿局部施釉后，再次放入窑炉，正立放置进行第二次的高温釉烧，冷却后得到成品。
2.如权利要求1所述的一种日用瓷器的烧制方法，其特征在于：所述第一次和第二次高温釉烧的温度相同，该温度由坯料和釉料的配方确定。
3.如权利要求1或2所述的一种日用瓷器的烧制方法，其特征在于：所述耐火棚板的的表面平整，并涂刷有氧化铝涂层。
4.如权利要求1或2所述的一种日用瓷器的烧制方法，其特征在于：所述步骤四中，在施口沿部分的釉料时，釉浆中添加有胶粘剂。
CN200910113119A 2009-12-30 2009-12-30 一种日用瓷器的烧制方法 Active CN101967060B (zh)