CN101948576B - 一种用于汽车油管抗龟裂老化的共混材料 - Google Patents

一种用于汽车油管抗龟裂老化的共混材料 Download PDF

Info

Publication number
CN101948576B
CN101948576B CN2010102851895A CN201010285189A CN101948576B CN 101948576 B CN101948576 B CN 101948576B CN 2010102851895 A CN2010102851895 A CN 2010102851895A CN 201010285189 A CN201010285189 A CN 201010285189A CN 101948576 B CN101948576 B CN 101948576B
Authority
CN
China
Prior art keywords
agent
oil pipe
aging
cracking
rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2010102851895A
Other languages
English (en)
Other versions
CN101948576A (zh
Inventor
吴忠生
庞瑞科
邓中华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shiyan Yinsen Industry & Trade Co Ltd
Original Assignee
Shiyan Yinsen Industry & Trade Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shiyan Yinsen Industry & Trade Co Ltd filed Critical Shiyan Yinsen Industry & Trade Co Ltd
Priority to CN2010102851895A priority Critical patent/CN101948576B/zh
Publication of CN101948576A publication Critical patent/CN101948576A/zh
Application granted granted Critical
Publication of CN101948576B publication Critical patent/CN101948576B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种用于汽车油管抗龟裂老化的共混材料，采用最易可得的材料丁腈橡胶和氯丁橡胶共混，具体是丁腈橡胶；氯丁橡胶；硫化剂；促进剂；活性剂；防老剂；抗氧剂；填充剂；操作剂在一定的温度环境下炼胶、挤出硫化制成成品。其价格低廉，可制得一种兼具耐臭氧性和耐油性等综合性能的油管；其材料相容性好，配合剂分散均匀，不存在海岛相结构；易加工，抗老化性好，耐臭氧性能优异，硬度、强度等各项物理机械性能均优良，挤出工艺性和硫化工艺性好，可延长产品的使用寿命，特别适用于耐油胶管产品。

Description

一种用于汽车油管抗龟裂老化的共混材料
技术领域
本发明涉及汽车油管零部件，具体是一种用于汽车油管抗龟裂老化的共混材料。
背景技术
随着汽车的使用要求性能越来越高，对汽车零部件性能要求也日益提高；汽车用橡胶管一方面要求材料具备耐油性能，另一方面要求其具备抗臭氧性能，以防止在生产和使用一段时间后发生龟裂；后来通过在丁腈橡胶中加入部分聚氯乙烯塑料，耐臭氧性能得到大大改善，但因塑料盒橡胶融合性差，导致产品的质量跟不上。
发明内容
本发明的目的在于提供一种综合性能优异，适合挤出加工的一种用于汽车油管抗龟裂老化的共混材料。
为此本发明的技术方案为，一种用于汽车油管抗龟裂老化的共混材料，包括丁腈橡胶，其特征在于：所述的共混材料按重量份数的由以下原料制成：
丁腈橡胶60～70    氯丁橡胶30～45
硫化剂1～2        促进剂1～2
活性剂5～8        防老剂4.0～5.0
抗氧剂0.8～1.2    填充剂80～130
操作剂15～25
有益效果：
硫化剂对橡胶在高温下产生交联作用。
促进剂和活性剂提高交联反应速度，提高胶料的综合性能。
抗氧剂使共混材料在加工和使用过程中保持材料稳定，避免性能发生变化。
防老剂有效防护丁腈橡胶/氯丁橡胶共混材料的热氧老化，延长其使用寿命。
填充剂使共混材料具备足够强度和硬度，使胶管制品能承受一定抗爆破压力。
操作剂使共混材料有利于混炼和挤出硫化加工。
本发明采用最易可得的材料丁腈橡胶和氯丁橡胶共混，价格低廉，可制得一种兼具耐臭氧性和耐油性等综合性能的油管材料；材料相容性好，配合剂分散均匀，不存在海岛相结构；易加工，抗老化性好，耐臭氧性能优异，硬度、强度等各项物理机械性能均优良，挤出工艺性和硫化工艺性好，可延长产品的使用寿命，特别适用于耐油胶管产品。
具体实施方式
以下结合具体实例，对本发明作进一步详细说明。
实例中的硬度按GB/T 531.1-2008测定，拉伸强度和扯断伸长率按GB/T528-2009测定，100℃×70H老化按GB/T 3512-2001测定，100℃×70H耐3号油性能按GB/T 1690-2006测定，耐臭氧性能(50PPHM×200H)按D47 1100测定。100℃×70H(压缩率25％，ф29×12.5)压缩永久变形按GB/T 7759-1996测定。
实施实例1～4
表1原材料配比(重量份数)
Figure BSA00000274731700031
制备方法如下：
第一步：按上述重量百分比称取原料
第二步：用橡胶密炼机在80℃～120℃之间将橡胶和活性剂、防老剂、填充剂混合均匀。
第三步：采用二段炼胶在40℃～60℃之间在开炼机上将硫化促进剂加入并混合均匀.
第四步：在70℃条件下挤出。
第五步：在150℃×30分钟条件下硫化成型。
表2按上述方法制备的丁腈橡胶/氯丁橡胶共混材料，主要性能见下。
Figure BSA00000274731700032
以上实验数据证明本发明具有一定质量稳定性，适合耐油油管的加工，也适用于密封条的加工和制作。

Claims (4)

1.一种用于汽车油管抗龟裂老化的共混材料，其特征在于：其原料组分和重量份数如下：丙烯腈含量32％的丁腈橡胶为70；氯丁橡胶CR2321为30；硫化剂硫磺1.5；促进剂DM为1.5；活性剂氧化锌为5；防老剂BLE为4；抗氧剂4010NA为2；填充剂快压出炭黑为100；操作剂DOP为15。
2.一种用于汽车油管抗龟裂老化的共混材料，其特征在于：其原料组分和重量份数如下：丙烯腈含量32％的丁腈橡胶为70；氯丁橡胶CR2321为30；硫化剂硫磺1.5；促进剂DM为1.5；活性剂氧化锌为5；防老剂BLE为4；抗氧剂4010NA为2；填充剂快压出炭黑为130；操作剂DOP为15。
3.一种用于汽车油管抗龟裂老化的共混材料，其特征在于：其原料组分和重量份数如下：丙烯腈含量32％的丁腈橡胶为65；氯丁橡胶CR2321为35；硫化剂硫磺1.5；促进剂DM为1.5；活性剂氧化锌为5；防老剂BLE为4；抗氧剂4010NA为2；填充剂快压出炭黑为100；操作剂DOP为15。
4.一种用于汽车油管抗龟裂老化的共混材料，其特征在于：其原料组分和重量份数如下：丙烯腈含量32％的丁腈橡胶为60；氯丁橡胶CR2321为40；硫化剂硫磺1.5；促进剂DM为1.5；活性剂氧化锌为5；防老剂BLE为4；抗氧剂4010NA为2；填充剂快压出炭黑为100；操作剂DOP为15。
CN2010102851895A 2010-09-14 2010-09-14 一种用于汽车油管抗龟裂老化的共混材料 Expired - Fee Related CN101948576B (zh)