CN101864255A - 一种高性能负离子卷烟搭口胶及其制备方法 - Google Patents
一种高性能负离子卷烟搭口胶及其制备方法 Download PDFInfo
- Publication number
- CN101864255A CN101864255A CN 201010211568 CN201010211568A CN101864255A CN 101864255 A CN101864255 A CN 101864255A CN 201010211568 CN201010211568 CN 201010211568 CN 201010211568 A CN201010211568 A CN 201010211568A CN 101864255 A CN101864255 A CN 101864255A
- Authority
- CN
- China
- Prior art keywords
- cigarettes
- lap adhesive
- releasing
- vinyl acetate
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种高性能负离子卷烟搭口胶及其制备方法,其原料为:乙酸乙烯酯-乙烯共聚乳液,乙酸乙烯-丙烯酸酯多元共聚乳液,负离子添加剂,表面活性剂,碳酸氧钠,抑泡剂和去离子水;负离子添加剂经表面处理后,通过超声波分散成稳定的分散液;在反应釜中投入乙酸乙烯酯-乙烯共聚乳液和乙酸乙烯-丙烯酸酯多元共聚乳液,搅拌,加碳酸氢钠调PH值为5-7加适量抑泡剂后,再将负离子分散体加入反应釜乳液中继续搅拌,过滤即得到成品;该搭口胶能有效地控制卷烟搭口胶中挥发和半挥发有害成分,用于粘接卷烟烟支搭口,在烟支燃烧时烟气中粒相物接触时会电解释放负离子,封闭烟气中有害物质,并将其中和、降解,可提高卷烟安全性,改善卷烟烟气中辛辣味。
Description
【技术领域】本发明涉及一种高性能负离子卷烟搭口胶及其制备方法,属卷烟搭口胶技术领域。
【背景技术】卷烟用胶是卷烟工业中一个很重要的卷烟材料,它参与烟支燃烧,其结构性能对烟气成分产生不可忽视的影响,更为重要的是对卷烟安全性的影响。国内外目前卷烟生产所用卷烟搭口胶其生产方法是采用乙酸乙烯酯和乙烯或丙烯酸酯等单体共聚而成,其性能可满足卷烟生产工艺要求,但卷烟用胶中挥发性与半挥发性成分(苯系物总量、邻苯二甲酸酯类总量、甲醛、乙酸乙烯酯)在卷烟烟支燃烧时产生辛辣味,相映也有害吸烟者健康。因此,对烟气中有害物质的抑制,有效改善卷烟烟气辛辣味是中国卷烟工业重点研究的课题。
【发明内容】为克服现有卷烟材料,特别是卷烟搭口胶参与烟支燃烧产生的上述缺陷,本发明的目的是提供高性能负离子卷烟搭口胶,用以抑制烟气中有害物质,有效改善卷烟烟气辛辣味;本发明的另一个目的是提供高性能负离子卷烟搭口胶的制备方法。
为解决其技术问题,本发明人经过几年的研究并根据二00九年全国烟草标准化技术委员会烟用材料技术委员会发布的中华人民共和国烟草行业YCXXX-2009烟用水基胶(卷烟用胶)中挥发性与半挥发性成分限量技术标准,要求卷烟用胶具有安全和环保性能,通过对原材料的选择,配方的设计以及对生产过程的改进,终于研制出高性能负离子卷烟搭口胶,有效地控制了卷烟搭口胶挥发和半挥发性有害成分,并对烟气中有害物质有抑制性作用,改善了卷烟烟气中的辛辣味,是目前被消费者所极易接受的产品。这种高性能负离子卷烟搭口胶由下述原料的重量份比组成:
乙酸乙烯酯-乙烯共聚乳液 750-850份,
乙酸乙烯-丙烯酸酯多元共聚乳液 80-120份,
负离子添加剂 10-20份,
表面活性剂 3-5份,
碳酸氢钠 0.5-1份,
抑泡剂 0.5-1份,
去离子水 50-100份。
其中,所述负离子添加剂为纯天然羟基负离子远红外功能添加剂;
表面活性剂为酯肪醇聚氧乙烯醚;
抑泡剂为聚乙二醇酯或RHODOLINE(罗地亚)DF681F或RHODOLINE(罗地亚)DF691;
高性能负离子卷烟搭口胶的制备方法,它包括如下步骤:
首先将负离子添加剂经表面处理后,分散在去离子水中,通过超声波分散成稳定的分散体,在反应釜中投入乙酸乙烯酯-乙烯共聚乳液和乙酸乙烯酯多元共聚功能乳液搅拌100-140分钟,经脱味装置脱味后用碳酸氢钠调至pH值为5-7,加入适当抑泡剂后,再将负离子分散体慢慢加入反应釜乳液中继续搅拌50-70分钟,过滤得到成品。
高性能负离子卷烟搭口胶的用途有:
高性能负离子卷烟搭口胶用于卷烟生产粘接卷烟烟支搭口的胶粘剂。适用于国产或进口不同型号的高中速卷接机组。与现有卷烟烟支搭口的胶粘剂相比,本发明有如下特点和显著的进步:
(1)、高性能负离子卷烟搭口胶粘接烟支成膜物与空气中水份或烟支燃烧时烟气中粒相物接触时发生电解释放负离子,封闭烟气中有害物质并将其有害物质中和、降解烟气有害气体(正离子)和异味除掉;
(2)、卷烟搭口胶中产生的负离子可对大肠杆菌、金黄色葡萄球菌有抑菌和杀菌作用,可有效抑制烟支搭口霉菌的滋生,保持了烟支贮存稳定性;
(3)、卷烟搭口胶成膜物无低分子物迁移折出,搭口表面平整光滑,聚合物的限氧指数比现有搭口胶低,烟支搭口燃烧好,无辛辣味;
(4)、高性能负离子卷烟搭口胶添加的是纯天然负离子材料,无毒、无放射性、无副作用。
【具体实施方式】下面结合实施例对本发明进一步说明。
实施例1:高性能负离子卷烟搭口胶制备方法,它包括如下步骤:
首先是备料:按如下重量份比备齐如下原料:原料的重量份比是:
进口的乙酸乙烯酯-乙烯共聚乳液 800份
乙酸乙烯-丙烯酸酯多元共聚功能乳液 100份
负离子添加剂 15份
表面活性剂 4份
碳酸氢钠 0.8份
抑泡剂 0.8份
去离子水 80份
再将负离子添加剂经表面处理后,分散在去离子水中,通过超声波分散成稳定的分散体,在反应釜中投入乙酸乙烯酯-乙烯共聚乳液和乙酸乙烯-丙烯酸酯多元共聚功能乳液搅拌120分钟,经脱味装置脱味后用0.8份碳酸氢钠调至pH值为5-7,加入0.8份抑泡剂后,再将负离子分散体慢慢加入反应釜乳液中继续搅拌60分钟,最后用150目滤网过滤得到成品。
其中:负离子添加剂为纯天然羟基负离子远红外功能添加剂;
表面活性剂为酯肪醇聚氧乙烯醚;
抑泡剂为聚乙二醇酯或RHODOLINE(罗地亚)DF681F或RHODOLINE(罗地亚)DF691;
用本实施例制备出的卷烟搭口胶与现有卷烟搭口胶在挥发性和半挥发性成分方面的技术对比结果如下表:Mg/kg=ppm
结果显示:本实施例制备出的卷烟搭口胶的技术指标明显优于现有卷烟搭口胶,具有推广应用价值。
实施例2:高性能负离子卷烟搭口胶制备方法,它包括如下步骤:
首先是备料:按如下重量份比备齐如下原料:原料的重量份比是:
进口的乙酸乙烯酯-乙烯共聚乳液 850份
乙酸乙烯-丙烯酸酯多元共聚功能乳液 120份
负离子添加剂 20份
表面活性剂 5份
碳酸氢钠 1份
抑泡剂 1份
去离子水 100份
其余步骤同实施例1的步骤。
实施例3:高性能负离子卷烟搭口胶制备方法,它包括如下步骤:
首先是备料:按如下重量份比备齐如下原料:原料的重量份比是:
进口的乙酸乙烯酯-乙烯共聚乳液 750份
乙酸乙烯-丙烯酸酯多元共聚功能乳液 80份
负离子添加剂 10份
表面活性剂 3份
碳酸氢钠 0.5份
抑泡剂 0.5份
去离子水 50份
其余步骤同实施例1的步骤。
Claims (3)
1.一种高性能负离子卷烟搭口胶,其特征是:这种高性能负离子卷烟搭口胶由下述原料的重量份比组成:
乙酸乙烯酯-乙烯共聚乳液 750-850份,
乙酸乙烯-丙烯酸酯多元共聚乳液 80-120份,
负离子添加剂 10-20份,
表面活性剂 3-5份,
碳酸氢钠 0.5-1份,
抑泡剂 0.5-1份,
去离子水 50-100份。
2.根据权利要求1所述的高性能负离子卷烟搭口胶,其特征是:所述负离子添加剂为纯天然羟基负离子远红外功能添加剂;表面活性剂为酯肪醇聚氧乙烯醚;抑泡剂为聚乙二醇酯或RHODOLINE(罗地亚)DF681F或RHODOLINE(罗地亚)DF691。
3.一种权利要求1所述高性能负离子卷烟搭口胶的制备方法,其特征是:它包括如下步骤:
首先将负离子添加剂经表面处理后,分散在去离子水中,通过超声波分散成稳定的分散体,在反应釜中投入乙酸乙烯酯-乙烯共聚乳液和乙酸乙烯-丙烯酸酯多元共聚乳液,搅拌100-140分钟,经脱味装置脱味后用碳酸氢钠调至pH值为5-7,加入适量抑泡剂后,再将负离子分散体慢慢加入反应釜乳液中继续搅拌50-70分钟,过滤得到成品。