CN101857369B - 古亚金釉及其制备方法 - Google Patents

古亚金釉及其制备方法 Download PDF

Info

Publication number
CN101857369B
CN101857369B CN200910111437.1A CN200910111437A CN101857369B CN 101857369 B CN101857369 B CN 101857369B CN 200910111437 A CN200910111437 A CN 200910111437A CN 101857369 B CN101857369 B CN 101857369B
Authority
CN
China
Prior art keywords
glaze
ancient
submetallic
gloss
dioxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN200910111437.1A
Other languages
English (en)
Other versions
CN101857369A (zh
Inventor
郑国明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN200910111437.1A priority Critical patent/CN101857369B/zh
Publication of CN101857369A publication Critical patent/CN101857369A/zh
Application granted granted Critical
Publication of CN101857369B publication Critical patent/CN101857369B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及陶瓷领域，具体涉及古亚金釉由钾长石、碳酸钙、石英、滑石粉、高岭土、玻璃粉、二氧化锰、二氧化铜、三氧化二镍各物质混合加水研磨而成，“古亚金釉”耐酸碱及抗氧化能力强，釉面稳定历久如新，光泽熠熠生辉，但不油腻，在柔和的灯光下，从不同的角度、不同的侧面，会有着不同的神奇效果，并且随着灯光的强弱其光泽发生奇妙的变化，但光线明亮时，其金色光泽显得清冷高雅，而但光线就得阴暗时，釉面又显出神奇的暖色光泽。

Description

古亚金釉及其制备方法
技术领域
本发明涉及陶瓷领域，具体涉及古亚金釉及其制备方法。
背景技术
德化窑以生产白瓷著称于世，其品质精良是古代其它窑口所不能比拟的，其产品备受世人喜爱，由于原材料配方的不同，使德化窑白瓷产品的质地和釉面色泽效果也不同，在民间叫法和学术上，明代德化窑白瓷：从白瓷特征被分为“乳白”、“象牙白”、“猪油白”、“葱根白”、“鹅绒白”等，而从工艺上有“日用瓷”、“日用工艺瓷”、“人物塑像”、“宗教塑像”等，因此，明代以来最具有代表性就是何朝宗的宗教塑像，而当时陶瓷材质的宗教塑像几乎都是白瓷，另外表现宗教塑像的材质还有：铜制品、木制品等。从这几种材质上来分析，铜制品会氧化、木制品会腐烂，能保藏时间最久且最完好的只有陶瓷。
发明内容
本发明目的是提供古亚金釉及其制备方法，该古亚金釉是一种窑变瓷，是在一定气氛下产生结晶和分相，综合体现的一种特殊效果，颜色呈金色，华而不艳，非常适合体现宗教题材的塑像和器皿。
古亚金釉由钾长石、碳酸钙、石英、滑石粉、高岭土、玻璃粉、二氧化锰、二氧化铜、三氧化二镍各物质混合加水研磨而成，其制备方法为：按如下比例称取：钾长石35～50％、碳酸钙10～20％、石英3～5％、滑石粉5～10％、高岭土3～5％、玻璃粉3～5％、二氧化锰8～18％、二氧化铜1～3％、三氧化二镍1～3％，各物质混合后加40～60％水研磨而成古亚金釉，再将古亚金釉用喷枪喷施于“中国白”陶瓷胎体上，按一般的陶瓷烧制方法，在高温1200～1300℃的状态下烧制得古亚金釉工艺品。
“古亚金釉”耐酸碱及抗氧化能力强，釉面稳定历久如新，光泽熠熠生辉，但不油腻，在柔和的灯光下，从不同的角度、不同的侧面，会有着不同的神奇效果，并且随着灯光的强弱其光泽发生奇妙的变化，但光线明亮时，其金色光泽显得清冷高雅，而但光线就得阴暗时，釉面又显出神奇的暖色光泽。
具体实施方式
实施例1
按如下比例称取：钾长石35～50％、碳酸钙10～20％、石英3～5％、滑石粉5～10％、高岭土3～5％、玻璃粉3～5％、二氧化锰8～18％、二氧化铜1～3％、三氧化二镍1～3％，各物质混合后加40～60％水研磨而成古亚金釉，再将古亚金釉用喷枪喷施于“中国白”陶瓷胎体上，按一般的陶瓷烧制方法，在高温1200～1300℃的状态下烧制得古亚金釉工艺品。
实施例2
古亚金釉的加工方法，按比例称取：钾长石450千克、碳酸钙140千克、石英40千克、滑石粉90千克、高岭土45千克、玻璃粉45千克、二氧化锰140千克、二氧化铜25千克、三氧化二镍25千克，各物质混合后加550千克水研磨而成，再将古亚金釉用喷枪喷施于“中国白”陶瓷胎体上，按一般的陶瓷烧制方法，在高温1300℃的状态下烧制得古亚金釉工艺品，该古亚金釉属亚光釉，手感好，不油腻，颜色呈金色，华而不艳，非常适合体现宗教题材的塑像和器皿，应用闻名世界“德化瓷都”的传统塑像工艺为基础，结合应用“古亚金釉”来装饰，是举世无双的新工艺，因而“古亚金釉”被陶瓷界专家和收藏界专家视为稀世珍宝。
实施例3
古亚金釉的加工方法，按比例称取：钾长石450千克、碳酸钙145千克、石英45千克、滑石粉90千克、高岭土45千克、玻璃粉45千克、二氧化锰130千克、二氧化铜25千克、三氧化二镍25千克。各物质混合后加500千克水研磨而成，再将古亚金釉用喷枪喷施于“中国白”陶瓷胎体上，按一般的陶瓷烧制方法，在高温1280℃的状态下烧制得古亚金釉工艺品，“古亚金釉”是一种窑变瓷，是在一定气氛下产生结晶和分相，综合体现的一种特殊效果，耐人寻味，华而不艳，庄重古扑，该釉属亚光釉，手感好，不油腻，非常适合体现宗教题材的塑像和器皿的施釉。应用“古亚金釉”与塑像或器皿结合装饰及生产，有着极其新颖的效果。如：作品《佛光普照》古亚金釉，其作品参照《造像量度经》为标准，塑像结构匀称，线条遒劲稳健，体态严谨，生动有致。塑像是用德化瓷都、闻名世界的中国白来做坯体，衣服的颜色用举世罕见且最新发明的“古亚金釉”，肤色用亚光黑釉来体现，底座再用铁锈釉来表现，此塑像的型、色结合装饰已达到世界佛教产品中举世无双的鼎新艺品，装饰效果显得华而不艳，庄重古扑，佛光普照，典雅耐看，气势雄浑刚劲，庄严肃穆，端庄凝重中渗透出无限的智慧和慈悲的情怀。和谐统一的形式美。德化的传统工艺与高档的色釉结合，德化传统瓷塑与现代雕塑技法的融合，圆雕与捏塑的结合，线条疏与密的搭配……这些因素在作品上组织得丰富多彩又井然有序，有很强的立体感、重量感，栩栩如生，形成多样化中的统一。

Claims (1)

1.古亚金釉，其特征是：由钾长石、碳酸钙、石英、滑石粉、高岭土、玻璃粉、二氧化锰、二氧化铜、三氧化二镍各物质混合加水研磨而成，按如下比例称取：钾长石35～50％、碳酸钙10～20％、石英3～5％、滑石粉5～10％、高岭土3～5％、玻璃粉3～5％、二氧化锰8～18％、二氧化铜1～3％、三氧化二镍1～3％，各物质混合后加40～60％水研磨而成古亚金釉，再将古亚金釉用喷枪喷施于“中国白”陶瓷胎体上，按一般的陶瓷烧制方法，在高温1200～1300℃的状态下烧制得古亚金釉工艺品。
CN200910111437.1A 2009-04-09 2009-04-09 古亚金釉及其制备方法 Expired - Fee Related CN101857369B (zh)