CN101811874B - 一种纳米氧化锆复合陶瓷的合成方法 - Google Patents

一种纳米氧化锆复合陶瓷的合成方法 Download PDF

Info

Publication number
CN101811874B
CN101811874B CN 201010147570 CN201010147570A CN101811874B CN 101811874 B CN101811874 B CN 101811874B CN 201010147570 CN201010147570 CN 201010147570 CN 201010147570 A CN201010147570 A CN 201010147570A CN 101811874 B CN101811874 B CN 101811874B
Authority
CN
China
Prior art keywords
composite ceramics
zirconia composite
nanometer zirconia
synthetic method
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201010147570
Other languages
English (en)
Other versions
CN101811874A (zh
Inventor
邓旭亮
林元华
自伟
胡晓阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201010147570 priority Critical patent/CN101811874B/zh
Publication of CN101811874A publication Critical patent/CN101811874A/zh
Application granted granted Critical
Publication of CN101811874B publication Critical patent/CN101811874B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种纳米氧化锆复合陶瓷的合成方法，具体为：采用液相包覆法制备含量为20～30wt％的CePO4包覆的3Y-TZP纳米粉体；将粉体进行干压和冷静压成型；无压烧结成致密块体。本发明通过控制包覆过程及烧结过程的一切可控的因素，摸索出生产优良可加工性能纳米氧化锆复合陶瓷的条件，以获得复合陶瓷的优良的可加工性能。

Description

一种纳米氧化锆复合陶瓷的合成方法
技术领域
本发明涉及材料科学领域，尤其是一种具有较好可加工性能的纳米氧化锆复合陶瓷的合成方法。
背景技术
氧化锆陶瓷属于生物惰性陶瓷，具有三种同素异型结构，即单斜相(m-ZrO2)、四方相(t-ZrO2)、立方相(c-ZrO2)，三相的转变关系为：
一些稳定剂如Y2O3可以将氧化锆在室温下稳定在四方相，其中
Figure GSA00000083555300011
3mol％Y2O3稳定的氧化锆(3Y-TZP)具有很好的生物相容性和高强度高韧性等特点，是一种新型的牙科修复材料。近年来，在牙科学家和材料学家的共同努力下，3Y-TZP作为牙修复体的增强、增韧材料，表面改性材料以及牙种植体，全瓷修复材料等方面取得了较大的进展，但由于氧化锆硬度太大，难于加工等特点，一定程度上阻碍了其应用。目前的加工方法多采用二次烧结的方法，即先烧结成易于加工的疏松结构，加工后再次烧结，这就降低了加工的准确性，增加了加工的复杂性。
为提高氧化锆的可加工性，现在主要采用添加辅助成分制备复合陶瓷的方法，即修饰纳米级的氧化锆颗粒形成一种核-壳包覆的结构，改善其加工等一系列性能。按反应体系的状态，包覆可分为固相包覆法、气相包覆法和液相包覆法；按包覆的性质可分为物理包覆法和化学包覆法；按壳层物质的性质可分为金属包覆法、无机包覆法和有机包覆法等等。是将固相或液相或气相的物质按一定的比例混合，在一定的条件下发生物理或化学变化实现包覆。
发明内容
针对现有技术存在的问题，本发明的目的在于提供一种纳米氧化锆复合陶瓷的合成方法，通过该方法制得的纳米氧化锆复合陶瓷具有很好的可加工性能。
为实现上述目的，本发明一种纳米氧化锆复合陶瓷的合成方法，具体为：
1)采用液相包覆法制备含量为20～30wt％的CePO4包覆的3Y-TZP纳米粉体；
2)将粉体进行干压和冷静压成型；
3)无压烧结成致密块体。
进一步，所述步骤1)中CePO4含量的最优值为25wt％。
进一步，所述步骤1)中纳米粉体制备过程为：将设定量的3Y-TZP粉体配置成悬浮液，超声分散后，将设定量的分散剂、脱模剂加入3Y-TZP悬浮液中，进行超声分散；加入溶解的计算量的磷酸氢二铵，进行超声分散；用磷酸将混合均匀的悬浮液调Ph值为3.5～4.5，滴入溶解的计算量的硝酸铈，控制反应温度为45～55℃，在搅拌下进行反应；絮凝完全后将上层清液倒出，把下层固相含量较大的部分进行离心分离，最后在烘箱中烘干，研磨后煅烧，再研磨后制得纳米粉体。
进一步，所述Ph最优值为4.0。
进一步，所述反应温度最优值为50℃。
进一步，所述研磨后煅烧温度为800℃。
进一步，所述步骤3)中的烧结温度为1200℃～1500℃。
进一步，所述烧结温度的最优值为1400℃。
本发明一种纳米氧化锆复合陶瓷的合成方法，通过控制包覆过程及烧结过程的一切可控的因素，摸索出生产优良可加工性能纳米氧化锆复合陶瓷的条件，以获得复合陶瓷的优良的可加工性能。
附图说明
图1a为CePO4粉末的TEM图；
图1b为3Y-TZP粉体的TEM图；
图1c为25wt％CePO4包覆的3Y-TZP粉体的TEM图；
图2不同CePO4含量包覆的3Y-TZP粉体的XRD曲线图；
图3a为不同烧结温度的块体的相对密度曲线图；
图3b为不同烧结温度的块体的线性收缩率曲线图；
图4为不同CePO4含量烧结的块体的可加工指数曲线图；
图5为不同温度烧结块体的硬度和弯曲强度；
图6为不同烧结温度的块体的断裂韧性和可加工指数曲线图。
具体实施方式
本发明在液相包覆法的基础上，通过控制反应溶液的浓度，温度Ph值，控制反应过程，制备出含量分别为20wt％，25wt％，30wt％的CePO4包覆的3Y-TZP纳米粉体，然后通过干压和冷等静压后，分别在1200℃，1300℃，1350℃，1400℃，1450℃，1500℃的不同的温度无压烧结，测试可加工性能，分析不同条件下样品的性能。
如表1所示，为本发明中所用的各个组分：
Figure GSA00000083555300031
将称量好的3Y-TZP粉体配置成3％的质量百分比浓度的悬浮液，超声分散15分钟后；按3Y-TZP质量的2％称量分散剂聚乙二醇、和氧化锆质量的1.5％称量脱模剂柠檬酸铵，在50℃度下溶于去离子水中后加入到3Y-TZP悬浮液中，再超声分15分钟；然后加入溶解的计算量的磷酸氢二铵，再超声15分钟；用磷酸将混合均匀的悬浮液调Ph值到3.5，缓慢滴入溶解的计算量的硝酸铈，控制反应温度为50℃，搅拌下反应2小时。絮凝完全后将上层清液倒出，把下层固相含量较大的部分进行离心分离。最后在烘箱中烘干，研磨后800℃煅烧，再研磨后制得20wt％、25wt％、30wt％的的CePO4包覆的3Y-TZP纳米粉体。
如图1a、图1b、图1c所示，分别为CePO4粉末的TEM图、3Y-TZP粉体的TEM图、25wt％CePO4包覆的3Y-TZP粉体的TEM图。
如图2所示，将上述得到的20wt％、25wt％、30wt％CePO4含量的氧化锆粉体进行xrd分析，并分别进行干压，冷等静压成型后在1200℃，1300℃，1350℃，1400℃，1450℃，1500℃温度下烧结致密，测试其相对密度和线性收缩率，测试图如图3a、图3b所示。
如图4、图5、图6所示，将1300℃，1350℃，1400℃，1450℃烧结的样品进行硬度、弯曲强度、断裂韧性的测试，并计算不同温度下的样品可加工性能，
经过综合分析，通过控制包覆过程及烧结过程的一切可控的因素，摸索出生产优良可加工性能纳米氧化锆复合陶瓷的条件，即为在Ph为4、温度50℃、3Y-TZP浓度为3wt％时可取得的包覆效果好，当CePO4含量为25wt％，烧结温度为1400℃时制得的复合陶瓷具有很好的可加工性能。

Claims (6)

1.一种纳米氧化锆复合陶瓷的合成方法，其特征在于，该方法具体为：
1)采用液相包覆法制备含量为20～30wt％的CePO4包覆的3Y-TZP纳米粉体；
2)将粉体进行干压和冷静压成型；
3)无压烧结成致密块体。
其中，所述步骤1)中纳米粉体制备过程为：将设定量的3Y-TZP粉体配置成悬浮液，超声分散后，将设定量的分散剂、脱模剂加入3Y-TZP悬浮液中，进行超声分散；加入溶解的计算量的磷酸氢二铵，进行超声分散；用磷酸将混合均匀的悬浮液调pH值为3.5～4.5，滴入溶解的计算量的硝酸铈，控制反应温度为45～55℃，在搅拌下进行反应；絮凝完全后将上层清液倒出，把下层固相含量较大的部分进行离心分离，最后在烘箱中烘干，研磨后煅烧，再研磨后制得纳米粉体；所述研磨后煅烧温度为800℃。
2.如权利要求1所述的纳米氧化锆复合陶瓷的合成方法，其特征在于，所述步骤1)中CePO4含量的最优值为25wt％。
3.如权利要求1所述的纳米氧化锆复合陶瓷的合成方法，其特征在于，所述pH最优值为4.0。
4.如权利要求1所述的纳米氧化锆复合陶瓷的合成方法，其特征在于，所述反应温度最优值为50℃。
5.如权利要求1所述的纳米氧化锆复合陶瓷的合成方法，其特征在于，所述步骤3)中的烧结温度为1200℃～1500℃。
6.如权利要求5所述的纳米氧化锆复合陶瓷的合成方法，其特征在于，所述烧结温度的最优值为1400℃。
CN 201010147570 2010-04-14 2010-04-14 一种纳米氧化锆复合陶瓷的合成方法 Expired - Fee Related CN101811874B (zh)