CN101744393B - 香味仿真水果的制备方法及其制得的香味仿真水果 - Google Patents
香味仿真水果的制备方法及其制得的香味仿真水果 Download PDFInfo
- Publication number
- CN101744393B CN101744393B CN 200910199783 CN200910199783A CN101744393B CN 101744393 B CN101744393 B CN 101744393B CN 200910199783 CN200910199783 CN 200910199783 CN 200910199783 A CN200910199783 A CN 200910199783A CN 101744393 B CN101744393 B CN 101744393B
- Authority
- CN
- China
- Prior art keywords
- preparation
- plasticizer
- pvc
- material composition
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种香味仿真水果的制备方法及其制得的香味仿真水果，该制备方法包括将下述物料组合物采用搪胶工艺进行制作，该物料组合物含有下列重量百分比的组分：25～45％的聚氯乙烯树脂、25～45％的聚氯乙烯糊树脂、10～25％的主增塑剂、4～15％的辅增塑剂以及1～8％的日用香精。本发明还公开了一种用于上述制备方法的搪胶物料组合物。本发明首次将搪胶工艺应用于仿真水果的制作，主要材质使用环保混合材料，制得的仿真水果不仅仿真度高，且香味持续时间可在1年左右。
Description
技术领域
本发明涉及塑料仿真装饰品领域，特别涉及一种香味仿真水果的制备方法及其制得的香味仿真水果，以及一种用于制备香味仿真水果的物料组合物。
背景技术
仿真水果产品日渐成为人们日常家居装饰用的优选物品，目前市场上销售的仿真水果一般通过发泡或者吹塑工艺制备，材质主要为聚苯乙烯、聚氨酯、交联聚乙烯、聚乙烯、酚醛及环氧树脂等泡沫塑料，这些产品大多为实心产品，多数没有香味。有部分加香的仿真水果也只是将香精涂抹或者喷涂在产品表面，香味持续时间在半个月以内。
中国专利94228990.0公开了一种四季芳香仿真水果，其特点是仿真水果外形为水果外形，其果体上分布有毛细孔，使香液通过果体上的毛细孔，散发出香气。为节省香液，上述果体内还可设置有盛有香液的储液器，利用储液器散发香气。该实用新型虽然可以通过不断补充香液而维持芳香味，但结构复杂且成本较高。
发明内容
本发明要解决的技术问题是提供一种制备简单、成本较低、仿真度高且香味持续时间长的香味仿真水果及其制备方法，以及用于制备香味仿真水果的物料组合物。
本发明人通过诸多试验发现：如在物料中添加香精，则现有的泡沫塑料原料会和香精发生化学反应，导致成形困难或者不能成形；另外，发泡方法制作的水果，需要在泡沫塑料模型外部再涂一层保护层，这个保护层会阻止香精向外散发；而吹塑工艺制作的水果因为成形温度太高，导致香精蒸发，而且吹塑制作的水果壁很薄，无法包含足量香精，另外吹塑制成的水果仿真度很差。发明人另辟蹊径，摸索出一种采用聚氯乙烯树脂(PVC)作为主要材质，加入一定比例的香精，适用于搪胶(搪塑)工艺的物料组合物配方，成功地将现有的搪胶工艺应用于仿真水果的生产，不仅制备工艺简单、成本较低，而且制得的产品为空心但可保持高仿真度、并长时间保持香味。其中，搪胶工艺为现常用于塑料玩具领域的生产工艺，其采用环保、无毒的聚氯乙烯树脂、聚氯乙烯糊树脂作为主要材质，并常规辅以增塑剂、抗热油等组成物料组合物，然而其材质偏软，且制得的产品一般为空心，而仿真水果需要一定的硬度保持形状，并要求持香时间长，故在现有搪胶物料组合物中加入的香精需在一定范围，香精太多会造成产品成形后香精缓慢以液体形式溢出，香精太少会造成留香时间不足香气很淡。
因此，本发明通过下列技术方案来解决上述问题。首先，本发明提供一种用于制备香味仿真水果的物料组合物，其主要采用搪胶材质，含有下列重量百分比的组分：25～45％的聚氯乙烯树脂、25～45％的聚氯乙烯糊树脂、10～25％的主增塑剂、4～15％的辅增塑剂以及1～8％的日用香精。
根据本发明，所说的聚氯乙烯树脂(PVC)是指现常用于搪胶工艺的软PVC，又称PVC粗粉。所说的聚氯乙烯糊树脂是指在前述PVC粉中加入增塑剂和稳定剂，使用增塑剂将PVC溶胀，然后再粉碎或者研磨从而制备出的PVC糊粉末，又称PVC细粉、PVC幼粉。
根据本发明，同现有搪胶物料组合物，首选常用的柠檬酸酯如柠檬酸三丁酯(TBC)、乙酰柠檬酸三丁酯(ATBC)等作为主增塑剂，显然获得美国FDA批准的作为安全无毒的主增塑剂均可使用。所说的辅增塑剂也为搪胶领域常用的辅助增塑剂，包括邻苯二甲酸酯类如邻苯二甲酸二异壬酯(DINP)、邻苯二甲酸二葵酯(DIDP)、邻苯二甲酸二辛酯(DOP)，脂肪族二元酸酯类如己二酸二辛酯(DOA)、癸二酸二辛酯(DOS)，环氧化合物类如环氧油酸丁酯、环氧化大豆油及环氧油酸丁酯，磷酸酯如磷酸三甲苯酯(TCP)、磷酸甲苯二苯酯(CDP)，聚合型增塑剂如己二酸丙二醇聚酯，苯多酸酯如1，2，4-偏苯三酸三异辛酯，含氯增塑剂如氯化石蜡、五氯硬酯酸甲酯，烷基磺酸酯以及多元醇酯。本发明的辅增塑剂可以选自上述材料中的一种或多种，优选无毒、环保的原料，如脂肪族二元酸酯类、环氧化合物类。
至于“日用香精”是指现常用于日用品加香领域的香精，如化妆品、空气清新剂中的产品；当然本发明优选各种果香味的香精。
较佳地，所述的物料组合物包括下列重量百分比的组分：30～40％的聚氯乙烯树脂、30～40％的聚氯乙烯糊树脂、15～20％的柠檬酸酯、6～10％的辅增塑剂以及2～6％的日用香精。
当然，根据需要，本发明上述的物料组合物还可以添加其它辅料。例如：由于原始的PVC幼粉和PVC粗粉本品为白色物料，制得的产品则为无色半透明，故可以根据不同水果加入不同的颜料，优选有机颜料，例如双(对氯苯基)-1.4-二酮吡咯并吡咯(254号红)、艳佳丽红、喹吖啶酮红、酞菁绿及异吲哚啉酮黄等，加入量通常占物料组合物重量的0.1～1％；当然，也可直接选用已加有色料的已处理过的PVC幼粉和PVC粗粉产品。另外，本发明物料组合物中还可加入现搪胶工艺中的稳定剂如二月桂酸二正丁基锡(DBTL)，脱模剂如聚乙烯醇等。
更佳地，所述的物料组合物由下列重量百分比的组分组成：35％的聚氯乙烯树脂、35％的聚氯乙烯糊树脂、18％的柠檬酸酯、7.5％的辅增塑剂、0.5％的有机颜料以及4％的日用香精。
其次，本发明还提供一种香味仿真水果的制备方法，其包括将本发明上述物料组合物采用搪胶工艺进行制作。该物料组合物含有下列重量百分比的组分：25～45％的聚氯乙烯树脂、25～45％的聚氯乙烯糊树脂、10～25％的主增塑剂、4～15％的辅增塑剂以及1～8％的日用香精；较佳地包括30～40％的聚氯乙烯树脂、30～40％的聚氯乙烯糊树脂、15～20％的柠檬酸酯、6～10％的辅增塑剂以及2～6％的日用香精；更佳地上述的物料组合物还可以含有占物料组合物重量0.1～1％的颜料，特别是有机颜料；在本发明一较佳实施例中，本发明物料组合物由下列重量百分比的组分组成：35％的聚氯乙烯树脂、35％的聚氯乙烯糊树脂、18％的柠檬酸酯、7.5％的辅增塑剂、0.5％的有机颜料以及4％的日用香精。
本发明制备方法采用上述搪胶物料组合物作为原料，可以通过现有常规搪胶工艺进行生产。较佳地，所述的制备方法包括下列步骤：聚氯乙烯树脂、聚氯乙烯糊树脂、主增塑剂和辅增塑剂混合，按需加入颜料，搅拌均匀，进行抽真空以除去低沸点的挥发物及水分和空气后，再加入日用香精，继续搅拌使香精和先前PVC物料完全融合，将搅拌好的混合物料加入仿真水果模具，用模具盖密封好模具腔体，将模具在250～350摄氏度下烘烤2～5分钟后再将模具取出，冷却，打开模盖，取出成型的产品。
较佳地，第一次所述的搅拌时间为5～60分钟；加入香精后继续搅拌的时间为5～30分钟。
由于现有搪胶物料，即聚氯乙烯树脂、聚氯乙烯糊树脂、主增塑剂和辅增塑剂混合过程中产生的低沸点的挥发物及水分和空气对最终产品的气味和产品质量有影响，故加入香精前尽可能将其除尽。本发明优选使用真空机抽真空5～20分钟。
而为了尽可能避免香精蒸发但保证产品质量，上述模具烘烤的温度优选260～280℃。
较佳地，为使产品外观更光整，所述的制备方法还包括将取出的成型产品除去毛刺，进行修正。
同现有搪胶工艺，取模后冷却至50～90℃开盖，而去毛刺的温度也优选在50～90℃。
更佳地，如果物料组合物中选用的PVC幼粉和PVC粗粉为未处理的白色粉末，也未加入颜料；或者含有色料的物料组合物制得的最终产品颜色不能满足需要，则成型产品修正之后再根据要求上色，例如喷涂颜色。
另外，为提高仿真度，根据需要，部分仿真水果如苹果、梨等可以在成型的产品主体上装配(如粘贴)塑料(PP、PVC、PE、ABS、EVA等)或纸制的仿真水果柄和/或底。
其中，本发明所说的仿真水果模具可根据现有搪胶工艺的制模要求，以及所需制备的水果形状、图案自行制模或购买商业模具，此为本领域人员所公知。而为了产业化生产，本发明制备方法中的各个操作步骤可选用现有搪胶工艺中的机械设备，如抽真空选用真空机、模具烘烤选用加热炉等。
另外，本发明还提供一种由上述制备方法制得的香味仿真水果，该香味仿真水果不仅仿真度高、且香味持续时间长，可达一年左右。
本发明还提供聚氯乙烯树脂和聚氯乙烯糊树脂等搪胶材料，特别是本发明的PVC搪胶物料组合物在制备香味仿真水果中的应用。
本发明首次将搪胶工艺应用于仿真水果的制作，主要材质使用环保混合材料，制备工艺简单、成本低，制得的仿真水果中空但不仅仿真度高，且香味可持续1年左右。
具体实施方式
下面用实施例来进一步说明本发明，但本发明并不受其限制。其中，未特殊说明的百分比均为占物料组合物总量的重量百分比，未特殊说明温度的生产工艺均在常温下进行，通常为4～30℃。所采用的原料及设备均为常规市售产品。
实施例1
搪胶物料组合物：35％的聚氯乙烯树脂白色粉末、35％的聚氯乙烯糊树脂白色粉末、18％的主增塑剂柠檬酸酯(TBC)、7.5％的辅增塑剂(环氧油酸丁酯)、0.5％颜料(酞菁绿)以及4％的日用香精(青苹果香精)。
将柠檬酸酯和辅增塑剂混合，再加入聚氯乙烯树脂、聚氯乙烯糊树脂及颜料，搅拌30分钟，用真空机抽真空10分钟后，加入日用香精，继续搅拌15分钟，将搅拌好的混合物料加入仿真苹果模具，用模具盖密封好模具腔体，将模具置入加热炉中在270摄氏度下烘烤4分钟后再将模具取出，在常温水中冷却至70℃，打开模盖，取出成型的产品，再冷却至50℃后除去毛刺，进行修正。取出成型的产品之后再根据需要喷涂绿颜色。根据需要，再粘贴塑料的仿真水果柄和底。
制得的仿真青苹果仿真度高，香味可持续12个月。
实施例2
搪胶物料组合物：25％的聚氯乙烯树脂白色粉末、45％的聚氯乙烯糊树脂白色粉末、10％的柠檬酸酯(ATBC)、15％的辅增塑剂(DOA)、4.9％的日用香精(红蛇果香精)以及0.1％的艳佳丽红颜料。
将柠檬酸酯和辅增塑剂混合，再加入聚氯乙烯树脂、聚氯乙烯糊树脂及颜料，搅拌5分钟，用真空机抽真空5分钟后，加入日用香精，继续搅拌5分钟，将搅拌好的混合物料加入仿真红蛇果模具，用模具盖密封好模具腔体，将模具置入加热炉中在350摄氏度下烘烤2分钟后再将模具取出，在常温水中冷却至80℃，打开模盖，取出成型的产品，再冷却60℃后除去毛刺，进行修正。根据需要，再粘贴纸质的仿真水果柄和底。
制得的仿真红蛇果仿真度高，香味可持续9个月。
实施例3
搪胶物料组合物：45％的聚氯乙烯树脂白色粉末、25％的聚氯乙烯糊树脂白色粉末、17％的柠檬酸酯(TBC)、4％的辅增塑剂(DINP)、8％的日用香精(香蕉香精)以及1％的异吲哚啉酮黄。
将聚氯乙烯树脂、聚氯乙烯糊树脂、柠檬酸酯、辅增塑剂及颜料混合，搅拌60分钟，用真空机抽真空20分钟后，加入日用香精，继续搅拌30分钟，将搅拌好的混合物料加入仿真香蕉模具，用模具盖密封好模具腔体，将模具置入加热炉中在250摄氏度下烘烤5分钟后再将模具取出，在常温水中冷却至50℃，打开模盖，取出成型的产品，除去毛刺，进行修正。取出成型的产品之后再根据需要喷涂颜色。
制得的仿真香蕉仿真度高，香味可持续12个月。
实施例4
搪胶物料组合物：31％的聚氯乙烯树脂白色粉末、32％的聚氯乙烯糊树脂白色粉末、25％的柠檬酸酯(ATBC)、10％的辅增塑剂(DOS)、1％的日用香精(柠檬香精)以及1％的异吲哚啉酮黄。
将柠檬酸酯和辅增塑剂混合，再加入聚氯乙烯树脂、聚氯乙烯糊树脂及颜料，搅拌10分钟，用真空机抽真空10分钟后，加入日用香精，继续搅拌10分钟，将搅拌好的混合物料加入仿真柠檬模具，用模具盖密封好模具腔体，将模具置入加热炉中在280摄氏度下烘烤4分钟后再将模具取出，在常温水中冷却至90℃，打开模盖，取出成型的产品，除去毛刺，进行修正。取出成型的产品之后再根据需要喷涂颜色。
制得的仿真柠檬仿真度高，香味可持续3个月。
实施例5
搪胶物料组合物：35％的聚氯乙烯树脂白色粉末、35％的聚氯乙烯糊树脂黄色粉末、18％的柠檬酸酯(ATBC)、8％的辅增塑剂(TCP)以及4％的日用香精(芒果香精)。
制备工艺除了不加入颜料，采用芒果模具外，余同实施例4。
制得的仿真芒果仿真度高，香味可持续10个月。
显然，上述实施例中的PVC及PVC糊原料可选用其它颜色物料，而柠檬酸酯可替换成现有其它搪胶工艺的主增塑剂，辅增塑剂、日用香精及颜料等也可替换成其它现有材料，根据需要物料组合物中还可加入稳定剂及脱模剂，这些均为本领域技术人员所知，在此不再赘述。
Claims (10)
1.一种香味仿真水果的制备方法，其特征在于其包括将下述物料组合物采用搪胶工艺进行制作，该物料组合物含有下列重量百分比的组分：25～45％的聚氯乙烯树脂、25～45％的聚氯乙烯糊树脂、10～25％的主增塑剂、4～15％的辅增塑剂以及1～8％的日用香精；所述的主增塑剂为柠檬酸酯；所述的辅增塑剂选自邻苯二甲酸酯类、脂肪族二元酸酯类、环氧化合物类中的一种或多种。
2.如权利要求1所述的制备方法，其特征在于所述的物料组合物由下列重量百分比的组分组成：35％的聚氯乙烯树脂、35％的聚氯乙烯糊树脂、18％的柠檬酸酯、7.5％的辅增塑剂、0.5％的有机颜料以及4％的日用香精。
3.如权利要求1或2所述的制备方法，其特征在于所述的制备方法包括下列步骤：聚氯乙烯树脂、聚氯乙烯糊树脂、主增塑剂和辅增塑剂混合，按需加入颜料，搅拌均匀，进行抽真空以除去低沸点的挥发物、水分和空气后，再加入日用香精，继续搅拌使香精和先前物料完全融合，将搅拌好的混合物料加入仿真水果模具，用模具盖密封好模具腔体，将模具在250～350摄氏度下烘烤2～5分钟后再将模具取出，冷却，打开模盖，取出成型的产品。
4.如权利要求3所述的制备方法，其特征在于所述的搅拌时间为5～60分钟，加入香精后继续搅拌的时间为5～30分钟，所述的抽真空是指采用真空机抽真空5～20分钟，所述模具烘烤的温度为260～280℃，所述冷却的温度为50～90℃。
5.如权利要求3所述的制备方法，其特征在于所述的制备方法还包括将取出的成型产品除去毛刺，进行修正；之后再根据需要上色。
6.如权利要求4所述的制备方法，其特征在于所述的制备方法还包括将取出的成型产品除去毛刺，进行修正；之后再根据需要上色。
7.如权利要求1～6任一项所述的制备方法制得的香味仿真水果。
8.一种用于制备香味仿真水果的物料组合物，其特征在于含有下列重 量百分比的组分：25～45％的聚氯乙烯树脂、25～45％的聚氯乙烯糊树脂、10～25％的主增塑剂、4～15％的辅增塑剂以及1～8％的日用香精；所述的主增塑剂为柠檬酸酯；所述的辅增塑剂选自邻苯二甲酸酯类、脂肪族二元酸酯类、环氧化合物类中的一种或多种。
9.如权利要求8所述的物料组合物，其特征在于所述的物料组合物由下列重量百分比的组分组成：35％的聚氯乙烯树脂、35％的聚氯乙烯糊树脂、18％的柠檬酸酯、7.5％的辅增塑剂、0.5％的有机颜料以及4％的日用香精。
10.聚氯乙烯树脂和聚氯乙烯糊树脂在制备香味仿真水果中的应用。