CN101704533B - 一种基于煤系高岭土合成的lsx型沸石分子筛 - Google Patents

一种基于煤系高岭土合成的lsx型沸石分子筛 Download PDF

Info

Publication number
CN101704533B
CN101704533B CN2009102723428A CN200910272342A CN101704533B CN 101704533 B CN101704533 B CN 101704533B CN 2009102723428 A CN2009102723428 A CN 2009102723428A CN 200910272342 A CN200910272342 A CN 200910272342A CN 101704533 B CN101704533 B CN 101704533B
Authority
CN
China
Prior art keywords
molecular sieve
zeolite molecular
type zeolite
kaolin
lsx type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009102723428A
Other languages
English (en)
Other versions
CN101704533A (zh
Inventor
周志辉
吕振华
刘红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia Baotou Steel Hefa Rare Earth Co ltd
Wuhan University of Science and Engineering WUSE
Original Assignee
Wuhan University of Science and Engineering WUSE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan University of Science and Engineering WUSE filed Critical Wuhan University of Science and Engineering WUSE
Priority to CN2009102723428A priority Critical patent/CN101704533B/zh
Publication of CN101704533A publication Critical patent/CN101704533A/zh
Application granted granted Critical
Publication of CN101704533B publication Critical patent/CN101704533B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种基于煤系高岭土合成的LSX型沸石分子筛。其技术方案是：按摩尔比为(1.07～2.86)K2O∶7.15(K2O+Na2O)∶Al2O3∶2.2SiO2∶(120～180)H2O∶0.01晶种配置合成液。其合成工艺是：按上述摩尔比在反应釜中先将高岭土充分溶解于水，在强力搅拌下缓慢加入氢氧化钠和氢氧化钾，再加入晶种，于室温条件下搅拌陈化4～6小时；再在60～80℃条件下搅拌晶化1～3小时，然后在90～100℃条件下继续搅拌晶化3～5小时，最后将晶化后的产物用水洗至pH为11，烘干，即得LSX型沸石分子筛。本发明利用内蒙古煤系高岭土代替传统的化工原料，成本低；所合成的LSX型沸石分子筛吸水率在30.8wt％以上；同时提高了内蒙古煤系高岭土的利用率及附加值，具有节能减排及资源全利用的特点。

Description

一种基于煤系高岭土合成的LSX型沸石分子筛
技术领域
本发明属于矿物加工技术及沸石分子筛制备领域。具体涉及一种基于煤系高岭土合成的LSX型沸石分子筛。
背景技术
目前人工沸石分子筛的制备方法主要是以化学试剂为原料，通过传统的水热法合成的，尽管其合成技术已相当成熟，但是其成本较高。
高岭土是常见的一种粘土矿物集合体，主要矿物高岭石的理想化学式为Al2Si4O10(OH)8。经研究发现高岭土在一定温度下焙烧可以脱去结构水，转化为具有很高活性的偏高岭土，而且相比化学原料大大降低了成本，从而成为沸石分子筛的理想合成原料，近些年已经引起了各国研究者的广泛关注。
LSX型(低硅X)沸石分子筛一种应用广泛的空气分离剂，具有氮气吸附容量大、氮氧分离系数高以及脱附容易等优点。在诸如变压吸附分离和真空变压吸附分离中均有广泛大的应用。因此急需一种工艺简单、成本低廉的合成方法。目前很没有报道用煤系高岭土合成LSX型沸石分子筛。
高岭土为我国资源优势矿种，总储量大，价格低廉，内蒙古发现的煤系高岭土储量已达60亿吨以上，并且随着勘探技术的提高，探明的储量在持续增加。目前绝大部分内蒙古煤系高岭土没有被开发利用，仅被开发利用的那部分高岭土，主要用于制备附加值较低的煅烧高岭土，高岭土价值没有完全发挥出来。
发明内容
本发明目的是以内蒙古煤系高岭土为原料，提供一种成本低、吸水率高于行业标准、资源综合利用的基于煤系高岭土合成的LSX型(低硅X)沸石分子筛制备技术。
为实现上述目的，本发明采用的技术方案是：将高岭土、水、氢氧化钠、氢氧化钾和晶种按摩尔比为(1.07～2.86)K2O∶7.15(K2O+Na2O)∶Al2O3∶2.2SiO2∶(120～180)H2O∶0.01晶种配置合成液；其合成工艺是：按上述摩尔比在反应釜中先将高岭土充分溶解于水中，在强力搅拌下缓慢加入氢氧化钠和氢氧化钾，再加入晶种，于室温条件下搅拌陈化4～6小时；再在60～80℃条件下搅拌晶化1～3小时，然后在90～100℃条件下继续搅拌晶化3～5小时，最后将晶化后的产物用水洗至pH为11，烘干，即得LSX型沸石分子筛。
其中：高岭土为内蒙古煤系高岭土，其主要化学组分是：高岭石≥96.0wt％，三氧化二铁≤0.5wt％，二氧化钛≤1.5wt％，氧化镁≤0.1wt％，氧化钙≤0.05wt％；烘干是在140～160℃条件下干燥8小时。
本发明利用内蒙古煤系高岭土代替传统的化工原料，减少化工原料的消耗，成本低；所合成的LSX型沸石分子筛吸水率在30.8wt％以上，高于行业标准；同时提高了内蒙古煤系高岭土的利用率及附加值，具有节能减排及资源全利用的特点，为地方经济发展提供新的增长点。
具体实施方式
下面结合具体实施方式对本发明做进一步的描述，并非对本发明保护范围的限制：
实施例1
一种基于煤系高岭土合成的LSX型沸石分子筛：将高岭土、水、氢氧化钠、氢氧化钾和晶种按摩尔比为(1.07～1.9)K2O∶7.15(K2O+Na2O)∶Al2O3∶2.2SiO2∶(120～150)H2O∶0.01晶种配置合成液。其合成工艺是：按上述摩尔比在反应釜中先将高岭土充分溶解于水中，在强力搅拌下缓慢加入氢氧化钠和氢氧化钾，再加入晶种，于室温条件下搅拌陈化4～6小时；再在60～80℃条件下搅拌晶化1～3小时，然后在90～100℃条件下继续搅拌晶化3～5小时，最后将晶化后的产物用水洗至pH为11，烘干，即得LSX型沸石分子筛。
在本实施例中：高岭土为内蒙古煤系高岭土，其主要化学组分是：高岭石≥96.0wt％，三氧化二铁≤0.5wt％，二氧化钛≤1.5wt％，氧化镁≤0.1wt％，氧化钙≤0.05wt％；烘干是在140～160℃条件下干燥8小时。
本实施例所制备的LSX型沸石分子筛，吸水率为30.8wt％，高于行业标准。
实施例2：
一种基于煤系高岭土合成的LSX型沸石分子筛：将高岭土、水、氢氧化钠、氢氧化钾和晶种按摩尔比为(1.9～2.86)K2O∶7.15(K2O+Na2O)∶Al2O3∶2.2SiO2∶(150～180)H2O∶0.01晶种配置合成液。
其合成工艺和原料同实施例1。
本实施例所制备的LSX型沸石分子筛，吸水率为31.7wt％，高于行业标准。
本具体实施方式利用内蒙古煤系高岭土代替传统的化工原料，减少化工原料的消耗，成本低，所合成的LSX型沸石分子筛吸水率在30.8wt％以上，高于行业标准；同时提高了内蒙古煤系高岭土的利用率及附加值，具有了节能减排及资源全利用的特点。

Claims (3)

1.一种基于煤系高岭土合成的LSX型沸石分子筛，其特征在于将高岭土、水、氢氧化钠、氢氧化钾和晶种按摩尔比为(1.07～2.86)K2O∶7.15(K2O+Na2O)∶Al2O3∶2.2SiO2∶(120～180)H2O∶0.01晶种配制合成液；其合成工艺是：按上述摩尔比在反应釜中先将高岭土充分溶解于水中，在强力搅拌下缓慢加入氢氧化钠和氢氧化钾，再加入晶种，于室温条件下搅拌陈化4～6小时；再在60～80℃条件下搅拌晶化1～3小时，然后在90～100℃条件下继续搅拌晶化3～5小时，最后将晶化后的产物用水洗至pH为11，烘干，即得LSX型沸石分子筛。
2.根据权利要求1所述的基于煤系高岭土合成的LSX型沸石分子筛，其特征在于所述的高岭土为内蒙古煤系高岭土，其主要化学组分是：高岭石≥96.0wt％，三氧化二铁≤0.5wt％，二氧化钛≤1.5wt％，氧化镁≤0.1wt％，氧化钙≤0.05wt％。
3.根据权利要求1所述的基于煤系高岭土合成的LSX型沸石分子筛，其特征在于所述的烘干是在140～160℃条件下干燥8小时。 
CN2009102723428A 2009-09-29 2009-09-29 一种基于煤系高岭土合成的lsx型沸石分子筛 Expired - Fee Related CN101704533B (zh)