CN101624501A - Inorganic-organic colored waterproofing agent - Google Patents
Inorganic-organic colored waterproofing agent Download PDFInfo
- Publication number
- CN101624501A CN101624501A CN200910305510A CN200910305510A CN101624501A CN 101624501 A CN101624501 A CN 101624501A CN 200910305510 A CN200910305510 A CN 200910305510A CN 200910305510 A CN200910305510 A CN 200910305510A CN 101624501 A CN101624501 A CN 101624501A
- Authority
- CN
- China
- Prior art keywords
- inorganic
- waterproofing agent
- agent
- organic
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an inorganic-organic colored waterproofing agent comprising the following components in percentage by weight: 1-20 percent of silicone resin solution, 0.5-5 percent of osmotic agent, 0.2-6 percent of adhesion agent, 0.05-8 percent of inorganic pigment, and the balance of water, wherein the sum of the percentages of all the components is 100 percent. The invention firstly adopts an inorganic-organic binary system as a novel liquid waterproofing agent; and meanwhile, by reasonably adjusting the proportion of the waterproofing agent and adding the inorganic pigment in the waterproofing agent, the invention not only can satisfy the waterproofing requirements on roofs, external walls or internal walls of buildings, but also can not pollute the surrounding environment and have longer service life than an organic waterproofing agent. Through the color presented by the pigment belonging to the inorganic-organic binary system, the invention can clearly differentiate which parts are coated and which parts are not coated in the coating process, thereby bringing great convenience to construction and achieving wide promotion and application values.
Description
Technical field
The invention belongs to the water-resisting agent technical field, especially relate to and a kind ofly can distinguish the inorganic-organic colored waterproofing agent that whether brushes water-resisting agent by color.
Background technology
At present both at home and abroad the building water-proof material of usefulness is generally the organic waterproof material, and most work-ing life of this water-proof material is shorter, and material is Powdered mostly, to bringing many difficulties on constructing.Some adopt the asphalt stone wet goods as water-proof material, and one can only be used for roof, and can give off an unpleasant smell under the irradiation of sunlight, and surrounding enviroment are caused comparatively serious pollution.Some adopt organic waterproof material substitution pitches etc. as water-proof material, but are leuco-pigment basically, in construction process continuously, which are difficult to distinguish partly applied, and which part did not apply, for construction has caused a lot of inconvenience.
Summary of the invention
The object of the present invention is to provide a kind of organic and inorganic binary colored waterproofing agent, water-resisting agent provided by the present invention, can play the excellent waterproof effect at roof or metope, which can apply by the color part of telling fully aware of again, which part does not also apply, and solves the defective that prior art exists.
For achieving the above object, the present invention adopts following technical scheme:
A kind of inorganic-organic colored waterproofing agent, comprise following component:
Silicon resin solution 1～20% (weight percentage);
Permeate agent 0.5～5%;
Tackifier 0.2～6%;
Mineral dye 0.05～8%;
All the other components are water, and each component sum is 100%.
Preferred scheme is: described inorganic organic colored waterproofing agent comprises following component:
Silicon resin solution 1～10% (weight percentage);
Permeate agent 0.5～3%;
Tackifier 0.2～3%;
Mineral dye 0.05～6%;
All the other components are water, and each component sum is 100%.
More preferred scheme is: described inorganic organic colored waterproofing agent comprises following component:
Silicon resin solution 1～5% (weight percentage);
Permeate agent 0.5～1.5%;
Tackifier 0.2～1.8%;
Mineral dye 0.05～3%;
All the other components are water, and each component sum is 100%.
More preferred scheme is: described inorganic organic colored waterproofing agent comprises following component:
Silicon resin solution 4% (weight percentage);
Permeate agent 1.2%;
Tackifier 0.6%;
Mineral dye 1.8%;
All the other components are water, and each component sum is 100%.
More preferred scheme is: described silicon resin solution is a Union carbide A-162, tetraethoxy, and one or several mixtures in the dimethyldiethoxysilane and alkali lye and water mix.
More preferred scheme is: described permeate agent is the isobutyl-triethoxyl silane.
More preferred scheme is: described tackifier are aminopropyl-triethoxy alkane and ferric chloride in aqueous solution.
More preferred scheme is: described mineral dye is a ferric oxide, Z 250, ironic hydroxide, chromoxide green, cologne earth, one or more mixtures in the titanium dioxide.
The present invention compared with prior art has following advantage and beneficial effect:
The present invention initiates and adopts the organic and inorganic binary system as the new liquid water-resisting agent, simultaneously, ratio by reasonable adjustment water-resisting agent, in water-resisting agent, add mineral dye, can satisfy the requirement of buildings roof, exterior wall or interior wall waterproof, and can not pollute surrounding enviroment, and work-ing life is longer than organic waterproof agent.The color that the pigment of the present invention by the organic and inorganic binary system embodies can know that discrimination which part in applying process applied, and which part did not also apply, and construction is brought great convenience, and application value is widely arranged.
Embodiment
Below in conjunction with specific embodiment the present invention is described in further details:
1 one kinds of organic and inorganic binary systems of embodiment, comprise following component: silicon resin solution 4% (weight percentage), silicon resin solution is preferably Union carbide A-162, tetraethoxy, and one or several mixtures in the dimethyldiethoxysilane and alkali lye and water mix; Permeate agent isobutyl-triethoxyl silane 1.2%; Tackifier 0.6% mix for aminopropyl-triethoxy alkane and ferric chloride in aqueous solution; Mineral dye 1.8% is preferably ferric oxide (black), Z 250 (redness), ironic hydroxide (yellow), chromoxide green (green), cologne earth (brown), several equal weight mark blended solution of titanium dioxide (white); All the other components of water are pure water, supply 100%.During configuration, organic and inorganic component is dissolved in pure water with each, and after the filtration, high-speed stirring is configured to solution under the normal temperature.Because the organism in the organic and inorganic binary system is in stirring and dissolving and apply in the air drying process, molecule forms crosslinking structure, can form the waterproof layer of densification, play very good waterproof effect, in conjunction with the color of mineral dye, very convenient during feasible applying, and can well play aesthetic.
During use, above-mentioned water-resisting agent is applied in the roof or the metope that need apply waterproof layer, natural air drying, present tangible color, its waterproof effect is considerably beyond national standard, and just can tell which place applied this waterproof layer at a glance, and which place did not apply this waterproof layer.
2 one kinds of organic and inorganic binary systems of embodiment, comprise following component: silicon resin solution 4% (weight percentage), silicon resin solution is preferably Union carbide A-162, tetraethoxy, and one or several mixtures in the dimethyldiethoxysilane and alkali lye and water mix; Permeate agent isobutyl-triethoxyl silane 1.2%; Tackifier 0.6% mix for aminopropyl-triethoxy alkane and ferric chloride in aqueous solution; Mineral dye 1.8% is preferably the ferric oxide (black) of single kind, Z 250 (redness), ironic hydroxide (yellow), chromoxide green (green), cologne earth (brown), titanium dioxide (white) solution; All the other components of water are pure water, supply 100%.During configuration, organic and inorganic component is dissolved in pure water with each, and after the filtration, high-speed stirring is configured to solution under the normal temperature.
During use, the water-resisting agent of the single mineral dye of above-mentioned dissolving is applied in the roof or the metope that need apply waterproof layer, apply certain area respectively, natural air drying presents tangible color band, and its waterproof effect is considerably beyond national standard, and just can tell which place applied this waterproof layer at a glance, which place did not apply this waterproof layer, and presented the band of different color, and was very attractive in appearance.
3 one kinds of organic and inorganic binary systems of embodiment, comprise following component: silicon resin solution 4% (weight percentage), silicon resin solution is preferably Union carbide A-162, tetraethoxy, and one or several mixtures in the dimethyldiethoxysilane and alkali lye and water mix; Permeate agent isobutyl-triethoxyl silane 1.2%; Tackifier 0.6% mix for aminopropyl-triethoxy alkane and ferric chloride in aqueous solution; Mineral dye 1.8% is preferably the ferric oxide (black) of single kind, Z 250 (redness), and ironic hydroxide (yellow) solution accounts for mineral dye gross weight fractional 80%; Complementary interpolation chromoxide green (green) on above-mentioned three kinds of dominant hue bases then, cologne earth (brown), titanium dioxide (white) solution accounts for mineral dye gross weight fractional 20%; All the other components of water are pure water, supply 100%.During configuration, organic and inorganic component is dissolved in pure water with each, and after the filtration, high-speed stirring is configured to solution under the normal temperature.Form the organic and inorganic water-resisting agent of very distinct red, yellow, the black three kinds of colors of color, during use, can apply respectively, also can intersect and apply, also the organic and inorganic water-resisting agent of three kinds of colors can be mixed wherein two kinds or three kinds, according to needs, be configured to the water-resisting agent of different color to color.
During use, the water-resisting agent of the single mineral dye of above-mentioned dissolving is applied in the roof or the metope that need apply waterproof layer, natural air drying, present tangible color band, its waterproof effect is considerably beyond national standard, and just can tell which place applied this waterproof layer at a glance, and which place did not apply this waterproof layer, and present the band of different color, very attractive in appearance.
Above content be in conjunction with concrete preferred implementation to further describing that the present invention did, can not assert that concrete enforcement of the present invention is confined to these explanations.For the general technical staff of the technical field of the invention, without departing from the inventive concept of the premise, can also make some simple deduction or replace, all should be considered as belonging to protection scope of the present invention.
Claims (8)
1. inorganic-organic colored waterproofing agent comprises following component:
Silicon resin solution 1～20% (weight percentage);
Permeate agent 0.5～5%;
Tackifier 0.2～6%;
Mineral dye 0.05～8%;
All the other components are water, and each component sum is 100%.
2. as claimed in claim 1 inorganic organic-colored waterproofing agent, comprise following component:
Silicon resin solution 1～10% (weight percentage);
Permeate agent 0.5～3%;
Tackifier 0.2～3%;
Mineral dye 0.05～6%;
All the other components are water, and each component sum is 100%.
3. as claimed in claim 2 inorganic-organic colored waterproofing agent, comprise following component:
Silicon resin solution 1～5% (weight percentage);
Permeate agent 0.5～1.5%;
Tackifier 0.2～1.8%;
Mineral dye 0.05～3%;
All the other components are water, and each component sum is 100%.
4. inorganic organic colored waterproofing agent as claimed in claim 3 comprises following component: silicon resin solution 4% (weight percentage);
Permeate agent 1.2%;
Tackifier 0.6%;
Mineral dye 1.8%;
All the other components are water, and each component sum is 100%.
As claim 1-4 each described inorganic-organic colored waterproofing agent, it is characterized in that: described silicon resin solution is a Union carbide A-162, tetraethoxy, one or several mixtures in the dimethyldiethoxysilane and alkali lye and water mix.
6. as claimed in claim 5 inorganic-organic colored waterproofing agent, it is characterized in that: described permeate agent is the isobutyl-triethoxyl silane.
7. as claimed in claim 6 inorganic-organic colored waterproofing agent, it is characterized in that: described tackifier are aminopropyl-triethoxy alkane and ferric chloride in aqueous solution.
8. as claimed in claim 7 inorganic-organic colored waterproofing agent, it is characterized in that: described mineral dye is a ferric oxide, Z 250, ironic hydroxide, chromoxide green, cologne earth, one or more mixtures in the titanium dioxide.