CN104529317A - Energy-saving building wall colored-coating mortar and preparation method thereof - Google Patents

Energy-saving building wall colored-coating mortar and preparation method thereof Download PDF

Info

Publication number
CN104529317A
CN104529317A CN201410727647.4A CN201410727647A CN104529317A CN 104529317 A CN104529317 A CN 104529317A CN 201410727647 A CN201410727647 A CN 201410727647A CN 104529317 A CN104529317 A CN 104529317A
Authority
CN
China
Prior art keywords
parts
water
energy
preparation
building wall
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410727647.4A
Other languages
Chinese (zh)
Inventor
杨雪玲
龚健冲
白延林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henan Polytechnic Institute
Original Assignee
Henan Polytechnic Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henan Polytechnic Institute filed Critical Henan Polytechnic Institute
Priority to CN201410727647.4A priority Critical patent/CN104529317A/en
Publication of CN104529317A publication Critical patent/CN104529317A/en
Pending legal-status Critical Current

Abstract

Energy-saving building wall colored-coating mortar and its preparation method relate to the field of building materials. The mortar provided by the invention is composed of the following substances, by weight, 10-20 parts of Portland cement, 1-8 parts of high-strength cement, 85-120 parts of river sand, 0.5-2 parts of color pigments, 0.05-0.5 part of water-proofing powder, 2-15 parts of glass beads and 10-25 parts of water. According to the energy-saving building wall colored-coating mortar and its preparation method, sources of the raw materials are wide, preparation is easy and costs are low. Various colors of the mortar can be prepared. The traditional process of coating a building exterior wall firstly with cement and then with various colors of paints is replaced. Construction processes are simplified. The mortar doesn't fade. The preparation method is time-saving and labor-saving.

Description

Energy-saving building wall color look plastering mortar material and preparation method
Technical field
The present invention relates to material of construction, particularly relate to energy-saving building wall color look plastering mortar material and preparation method.
Background technology
The plastering mortar material of construction wall is current architectural indispensable material, along with the development of society, modern building body stands in great numbers, the requirement of people to architectural decorative art also improves constantly, thus to the coordination of urban whole environmental color, especially the exterior wall color of building body has certain requirement, and the exterior wall of traditional building body be smear cement, after whitewash the color designed again as required, this form of construction work had both been wasted material and had been too increased operational procedure, wasted time and energy.
Summary of the invention
The present invention is intended to the deficiency for existing in background technology, and provides a kind of energy-saving building wall color look plastering mortar material and preparation method, can replace smearing cement outside traditional wall and add coating two kinds of effects.
Energy-saving building wall color look plastering mortar material of the present invention, by following material by weight proportioning form: silicate cement 10 ~ 20 parts, high-strength cement 1 ~ 8 part, 85 ~ 120 parts, river sand, coloured pigment 0.5 ~ 2 part, water-proofing powder 0.05 ~ 0.5 part, glass microballon 2 ~ 15 parts and 10 ~ 25 parts, water.
Optimum ratio of the present invention is: silicate cement 12 ~ 17 parts, high-strength cement 3 ~ 6 parts, 95 ~ 110 parts, river sand, coloured pigment 1 ~ 1.5 part, water-proofing powder 0.1 ~ 0.3 part, glass microballon 5 ~ 10 opinion part and 15 ~ 20 parts, water.
In the present invention, described coloured pigment is titanium white, barba hispanica, carbon black, red iron oxide, the mixing of one or more arbitrary proportions of iron oxide yellow; Described high-strength cement is thick high-strength cement and/or thin high-strength cement.
The preparation method of energy-saving building wall color look plastering mortar material of the present invention, realizes through the following steps:
A, by silicate cement 10 ~ 20 parts, high-strength cement 1 ~ 8 part, 85 ~ 120 parts, river sand, pigment 0.5 ~ 2 part, glass microballon 2 ~ 15 parts, water-proofing powder 0.05 ~ 0.5 part of mixing and stirring;
B, a step compound is added water 10 ~ 25 parts, stir, be i.e. obtained finished product.
Energy-saving building wall color look plastering mortar material of the present invention and preparation method, raw material sources are extensive, preparation easily, cost is low, the mortar of shades of colour can be prepared, instead of tradition first whitewashes different colours coating again on external wall operation with cement, simplify operational procedure, colour-fast, time saving and energy saving.
Embodiment
Below in conjunction with embodiment, the present invention is described further, the following stated, only to preferred embodiment of the present invention, not do other forms of restriction to the present invention, any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed to the Equivalent embodiments of equal change.Everyly do not depart from the present invention program's content, any simple modification done following examples according to technical spirit of the present invention or equivalent variations, all drop in protection scope of the present invention.
Embodiment 1
Energy-saving building wall color look plastering mortar material of the present invention, by following material by weight proportioning form: silicate cement 10 parts, high-strength cement 8 parts, 85 parts, river sand, barba hispanica 2 parts, water-proofing powder 0.05 part, glass microballon 15 parts and 10 parts, water;
Its preparation method is:
A, by silicate cement part, high-strength cement part, river sand part, pigment part, glass microballon part, water-proofing powder part mixing and stirring,
B, a step compound is added water 10 ~ 25 parts, stir, be i.e. obtained finished product.
Embodiment 2
Energy-saving building wall color look plastering mortar material of the present invention, by following material by weight proportioning form: 325# silicate cement 20 parts, high-strength cement 1 part, 120 parts, river sand, coloured pigment 0.5 part, water-proofing powder 0.5 part, glass microballon 2 parts and 25 parts, water;
Its preparation method is with embodiment 1.
Embodiment 3
Energy-saving building wall color look plastering mortar material of the present invention, be by following material by weight proportioning make: 425# silicate cement 12 parts, high-strength cement 6 parts, 95 parts, river sand, iron oxide yellow 1.5 parts, water-proofing powder 0.1 part, glass microballon 10 parts and 15 parts, water;
Its preparation method is with embodiment 1.
Embodiment 4
Energy-saving building wall color look plastering mortar material of the present invention, be by following material by weight proportioning make: 425 #silicate cement 17 parts, high-strength cement 3 parts, 110 parts, river sand, carbon black 0.5 part, titanium white 0.5 part, water-proofing powder 0.3 part, glass microballon 5 parts and 20 parts, water;
Its preparation method is with embodiment 1.
Embodiment 5
Energy-saving building wall color look plastering mortar material of the present invention, be by following material by weight proportioning make: 325# silicate cement 15 parts, high-strength cement 5 parts, 105 parts, river sand, red iron oxide 1.2 parts, water-proofing powder 0.2 part, glass microballon 8 parts and 18 parts, water;
Its preparation method is with embodiment 1.

Claims (4)

1. energy-saving building wall color look plastering mortar material, by following material by weight proportioning form: silicate cement 10 ~ 20 parts, high-strength cement 1 ~ 8 part, 85 ~ 120 parts, river sand, coloured pigment 0.5 ~ 2 part, water-proofing powder 0.05 ~ 0.5 part, glass microballon 2 ~ 15 parts and 10 ~ 25 parts, water.
2. energy-saving building wall color look plastering mortar material as claimed in claim 1, its preferred weight number proportioning is: silicate cement 12 ~ 17 parts, high-strength cement 3 ~ 6 parts, 95 ~ 110 parts, river sand, coloured pigment 1 ~ 1.5 part, water-proofing powder 0.1 ~ 0.3 part, glass microballon 5 ~ 10 parts and 15 ~ 20 parts, water.
3. energy-saving building wall color look plastering mortar material as claimed in claim 1 or 2, is characterized in that described coloured pigment is titanium white, barba hispanica, carbon black, red iron oxide, one or more mixing of iron oxide yellow.
4. prepare the preparation method of energy-saving building wall color look plastering mortar material according to claim 1, realize through the following steps:
A, by silicate cement 10 ~ 20 parts, high-strength cement 1 ~ 8 part, 85 ~ 120 parts, river sand, pigment 0.5 ~ 2 part, glass microballon 2 ~ 15 parts, water-proofing powder 0.05 ~ 0.5 part of mixing and stirring;
B, a step compound is added water 10 ~ 25 parts, stir, be i.e. obtained finished product.
CN201410727647.4A 2014-12-01 2014-12-01 Energy-saving building wall colored-coating mortar and preparation method thereof Pending CN104529317A (en)